Low-temperature plasma nitrocarburizing treatments are applied to improve the surface properties of austenitic stainless steels by forming an expanded austenite layer without impairing the excellent corrosion resistance of the steel. Here, low-temperature active screen plasma nitrocarburizing (ASPNC) was investigated in an industrial-scale cold-wall reactor to compare the effects of two active screen materials: (i) a steel active screen with the addition of methane as a gaseous carbon-containing precursor and (ii) an active screen made of carbon-fibre-reinforced carbon (CFC) as a solid carbon precursor. By using both active screen materials, ASPNC treatments at variable plasma conditions were conducted using AISI 316L. Moreover, insight into the plasma-chemical composition of the H2-N2 plasma for both active screen materials was gained by laser absorption spectroscopy (LAS) combined with optical emission spectroscopy (OES). It was found that, in the case of a CFC active screen in a biased condition, the thickness of the nitrogen-expanded austenite layer increased, while the thickness of the carbon-expanded austenite layer decreased compared to the non-biased condition, in which the nitrogen- and carbon-expanded austenite layers had comparable thicknesses. Furthermore, the crucial role of biasing the workload to produce a thick and homogeneous expanded austenite layer by using a steel active screen was validated.

This thesis is on fatigue crack growth experiments and assessments of fatigue crack growth rates. Both constant and variable amplitude loads in two different materials are considered; a nickel based super-alloy Inconel 718 and a stainless steel 316L. The considered load levels extend from small scale yielding (SSY) to large scale yielding (LSY) for both materials. The effect of different load schemes on the fatigue crack growth rates is investigated on Inconel 718 and compact tension specimens in Paper A. It is concluded that load decreasing schemes give a to high Paris law exponent compared to constant or increasing load amplitude schemes. Inconel 718 is further analyzed in Paper B where growth rates at variable amplitude loading in notched tensile specimens are assessed. The predictions are based on the fatigue crack growth parameters obtained in Paper A. The crack closure levels are taken into consideration and it is concluded that linear elastic fracture mechanics is incapable of predicting the growth rates in notches that experience large plastic cyclic strains. Even if crack closure free fatigue parameters are used and residual stresses due to plasticity are included. It is also concluded that crack closure free and nominal fatigue crack growth data predict the growth rates equally well. However, if the crack closure free parameters are used, then it is possible to make a statement in advance on the prediction in relation to the experimental outcome. This is not possible with nominal fatigue crack growth parameters. The last three papers consider fatigue crack growth in stainless steel 316L. Here the load is defined as the crack tip opening displacement parameter. Paper C constitutes an investigation on the effect of plastic deformation on the potential drop and consequently the measured crack length. It is concluded that the nominal calibration equation obtained in the undeformed geometry can be used at large plastic deformations. However, two conditions must be met: the reference potential must be taken in the deformed geometry and the reference potential needs to be adjusted at every major change of plastic deformation. The potential drop technique is further used in Paper D and Paper E for crack length measurements at monotonic LSY. Constant amplitude loads are considered in Paper D and two different variable amplitude block loads are investigated in Paper E. The crack tip opening displacement is concluded in Paper D to be an objective parameter able to characterize the load state in two different geometries and at the present load levels. Furthermore, if the crack tip opening displacement is controlled in an experiment and the local load ratio set to zero, then only monotonic LSY will appear due to extensive isotropic hardening, i.e. elastic shake-down. This is also the reason why the linear elastic stress-intensity factor successfully could merge all growth rates, extending from SSY to monotonic LSY along a single line in a Paris law type of diagram, even though the generally accepted criteria for SSY is never fulfilled. For the variable amplitude loads investigated in Paper E, the effect of plastic deformation on measured potential drop is more pronounced. However, also here both the crack tip opening displacement parameter and the linear elastic stress-intensity factor successfully characterized the load state. / <p>QC 20130108</p>

No description available.

High-performance materials such as stainless steels and nickel based super alloys are widely used in demanding applications where high mechanical and thermal properties are required. The applications of super alloys are mainly found in jet engines, power plants and gas turbines demanding high fatigue strength, corrosion and oxidation resistance as well as wear resistant properties. In order to use them, they go through various machining processes such as milling, turning, cutting, polishing etc. until the final product is achieved. Modern manufacturing industries employs various machining tools and technologies to improve the machining process of heat resistant super alloys. However, there are still challenges which needs to be addressed. Among them, adhesive wear of the machining tools is one of the main wear mechanism during the tribological interaction of tool and workpiece, preventing them to achieve the desired quality and surface finish of the end product. Moreover, it damages the tool reducing its lifecycle and in return, increasing the production cost. Among the cutting tools tungsten carbide (WC/Co) tools coated with TiAlN coating due to their good high temperature performance are extensively used. Nonetheless, these coatings still face issue like adhesive wear, abrasion, oxidation at higher temperature damaging the tools and subsequent machining. Therefore, it is imperative to understand the initiation mechanism of adhesive wear during the tribological interaction of super alloys and coated cutting tool material. In this research work, the tribological response of two coatings deposited by physical vapour deposition (PVD), having the composition Ti60Al40N and Ti40Al60N have been studied against two super alloys material, i.e. Inconel 718 and stainless steel 316L. A high temperature SRV (Schwingung (Oscillating), Reibung (Friction), Verschleiß (Wear)) reciprocation friction and wear test set up was employed to investigate the friction behaviour, wear rate and dominant wear mechanisms.  For Ti60Al40N coating, the experimental results revealed that generally, friction increases in case of sliding against Inconel 718 up to 400 °C and drops at 760 °C. A high wear volume at room temperature and a decrease to a minimum at 760 °C has been observed for Inconel 718. On the other side, Stainless steel 316L (SS 316L) faces a continuous rise in friction coefficient with highest value at 760 °C during sliding against Ti60Al40N coating. Wear is highest at 400 °C for SS 316L pin. The worn surfaces shows that both workpiece materials experience increase in material transfer due to adhesive wear with rise in temperature. At 400 °C, adhesion is the primary wear mechanism for both workpiece materials. A further rise in temperature to 760 °C promotes the adhesive wear through oxides formation on both material surfaces.  Similarly, Ti40Al60N coating shows the same friction behaviour with change in average steady state friction values for both material of Inconel 718 and SS 316L. Both workpiece materials responds in a similar way to wear volume loss, i.e. lowest at room temperature and highest at 760 °C. For Inconel 718, transfer of coating constituents on to the Inconel 718 pin surface was detected and associated with coating rupture and peeling, exacerbating with rise in temperature. Adhesion, abrasion, and oxidation are primary wear mechanisms at 400 °C and 760 °C. For SS 316L, coating transfer only happen at 400 °C. No damage of coating at 40 °C, a complete damage at 400 °C, and formation of dense porous oxides layers at 760 °C have been noticed. At 400 °C, adhesion, abrasion, and chipping while at 760 °C, adhesion, three body abrasion, ploughing and oxidation are the main wear mechanisms.

Étude du comportement d'un acier inoxydable 316L et d'un Inconel 718 dans le cadre d'un schéma thermomécanique à mémoire discrète constitué d'une équation multivoque, d'un critère d'inversion et d'un algorithme. Analyse détaillée des propriétés du comportement d'hystérésis pure. Etude des modules tangents aux courbes de charge. Mise en évidence de la restauration des propriétés du matériau après inversion et de la non-existence d'une discontinuité elastique-plastique dans le diagramme contrainte-déformation. Description de l'écrouissage en déformation à partir d'une analyse de la microstructure