Realising Si-based electrically driven light emitters in a process technology compatible with mainstream microelectronics CMOS technology is key requirement for the implementation of low-cost Si-based optoelectronics and thus one of the big challenges of semiconductor technology. This work has focused on the development of microcavity enhanced silicon LEDs (MCLEDs), including their design, fabrication, and experimental as well as theoretical analysis. As a light emitting layer the abrupt pn-junction of a Si diode was used, which was fabricated by ion implantation of boron into n-type silicon. Such forward biased pn-junctions exhibit room-temperature EL at a wavelength of 1138 nm with a reasonably high power efficiency of 0.1%. Two MCLEDs emitting light at the resonant wavelength about 1150 nm were demonstrated: a) 1-lambda MCLED with the resonator formed by 90 nm thin metallic CoSi2 mirror at the bottom and semitransparent distributed Bragg reflector (DBR) on the top; b) 5.5-lambda MCLED with the resonator formed by high reflecting DBR at the bottom and semitransparent top DBR. Using the appoach of the 5.5-lambda MCLED with two DBRs the extraction efficiency is enhanced by about 65% compared to the silicon bulk pn-junction diode.

Realising Si-based electrically driven light emitters in a process technology compatible with mainstream microelectronics CMOS technology is key requirement for the implementation of low-cost Si-based optoelectronics and thus one of the big challenges of semiconductor technology. This work has focused on the development of microcavity enhanced silicon LEDs (MCLEDs), including their design, fabrication, and experimental as well as theoretical analysis. As a light emitting layer the abrupt pn-junction of a Si diode was used, which was fabricated by ion implantation of boron into n-type silicon. Such forward biased pn-junctions exhibit room-temperature EL at a wavelength of 1138 nm with a reasonably high power efficiency of 0.1%. Two MCLEDs emitting light at the resonant wavelength about 1150 nm were demonstrated: a) 1-lambda MCLED with the resonator formed by 90 nm thin metallic CoSi2 mirror at the bottom and semitransparent distributed Bragg reflector (DBR) on the top; b) 5.5-lambda MCLED with the resonator formed by high reflecting DBR at the bottom and semitransparent top DBR. Using the appoach of the 5.5-lambda MCLED with two DBRs the extraction efficiency is enhanced by about 65% compared to the silicon bulk pn-junction diode.

In der vorliegenden Arbeit wird das Hauptaugenmerk auf die Untersuchung der Auswirkungen einer Modifikation der zugänglichen Prozessparameter auf die funktionalen Eigenschaften oxidischer Dünnfilme während der gepulsten Laserabscheidung (PLD) gelegt. Der erste Teil der Arbeit stellt die Herstellung von BaTiO3/SrTiO3-Mehrfach-Heterostrukturen auf thermisch und chemisch vorbehandelten SrTiO3-Substraten mittels gepulster Laserabscheidung (PLD) vor. Die zugängliche in-situ Wachstumskontrolle durch ein reflection high-energy electron diffraction (RHEED)-System ermöglicht es die Wachstumsprozesse in Echtzeit zu überwachen. Angestrebt wird ein stabiler zwei-dimensionaler Wachstumsmodus, der neben glatten Grenzflächen auch eine hohe Dünnfilmqualität ermöglicht. Es wird erstmals die prinzipielle Anwendbarkeit von BaTiO3/SrTiO3-Heterostrukturen als Bragg-Spiegel aufgezeigt. Für BaTiO3- sowie SrTiO3-Dünnfilme wurden die PLD-Parameter Substrattemperatur, Sauerstoffpartialdruck, Energiedichte des Lasers sowie Flussdichte der Teilchen variiert und die Auswirkungen auf die strukturellen, optischen und Oberflächeneigenschaften mittels Röntgendiffraktometrie (XRD), spektraler Ellipsometrie (SE) und Rasterkraftmikroskopie (AFM) beleuchtet. Im zweiten Teil werden ZnO/MgxZn1−xO-Quantengrabenstrukturen hetero- und homoepitaktisch auf thermisch vorbehandelten a-Saphir- respektive m- und a-orientierten ZnO-Einkristallen vorgestellt. Die Realisierung eines zwei-dimensionalen „layer-by-layer“ Wachstumsmodus wird für die Quantengrabenstrukturen aufgezeigt. Die Quantengrabenbreite lässt sich aus beobachteten RHEED-Oszillationen exakt bestimmen. Ein Vergleich zwischen, mittels Photolumineszenz gemessenen Quantengrabenübergangsenergien als Funktion der Grabenbreite mit theoretisch ermittelten Werten wird vorgestellt, wobei der Unterschied zwischen polaren und nicht-polaren Strukturen mit Blick auf eine Anwendung aufgezeigt wird. Für c-orientierte ZnO-Dünnfilme wird das Wachstum im Detail untersucht und ein alternativer Abscheideprozess im so genannten Intervall PLD-Verfahren vorgestellt. Die Verifizierung der theoretischen Prognose einer ferromagnetischen Ordnung mit einer Curie-Temperatur oberhalb Raumtemperatur (RT) für kubische, Mangan stabilisierte Zirkondioxid (MnSZ)-Dünnfilme stellt den dritten Teil der Arbeit dar. Die strukturellen Eigenschaften der Dünnfilme werden mittels XRD, AFM sowie Transmissionselektronenmikroskopie (TEM) untersucht. Die Bedingungen einer erfolgreichen Stabilisierung der kubischen Kristallphase durch den Einbau von Mn wird aufgezeigt. Mittels Röntgenphotoelektronenspektroskopie (XPS) sowie Elektronenspinresonanz (EPR) wird der Ladungszustand der, in der Zirkondioxidmatrix eingebauten, Mn-Ionen ermittelt. Die elektrischen Eigenschaftenwerden durch Strom-Spannungsmessungen(IU) sowie der Leitungstyp durch Seebeck-Effekt Messungen charakterisiert. Zur Erhöhung der Leitfähigkeit werden die MnSZ Dünnfilme in verschiedenen Atmosphären thermisch behandelt und Veränderungen durch IU-Messungen aufgezeigt. Ergebnisse von optischen Untersuchungen mittels Transmissionsmessungen und KL werden präsentiert. Superconducting quantum interference device (SQUID)-Magnetometrie wird zur Charakterisierung der magnetischen Eigenschaften genutzt. Magnetische Ordnungen im Bereich zwischen 5 K ≤ T ≤ 300 K werden untersucht und der Einfluss von Defekten sowie einer thermischen Behandlung in verschiedenen Atmosphären auf die magnetischen Eigenschaften diskutiert.

In der vorliegenden Arbeit wird das Hauptaugenmerk auf die Untersuchung der Auswirkungen einer Modifikation der zugänglichen Prozessparameter auf die funktionalen Eigenschaften oxidischer Dünnfilme während der gepulsten Laserabscheidung (PLD) gelegt. Der erste Teil der Arbeit stellt die Herstellung von BaTiO3/SrTiO3-Mehrfach-Heterostrukturen auf thermisch und chemisch vorbehandelten SrTiO3-Substraten mittels gepulster Laserabscheidung (PLD) vor. Die zugängliche in-situ Wachstumskontrolle durch ein reflection high-energy electron diffraction (RHEED)-System ermöglicht es die Wachstumsprozesse in Echtzeit zu überwachen. Angestrebt wird ein stabiler zwei-dimensionaler Wachstumsmodus, der neben glatten Grenzflächen auch eine hohe Dünnfilmqualität ermöglicht. Es wird erstmals die prinzipielle Anwendbarkeit von BaTiO3/SrTiO3-Heterostrukturen als Bragg-Spiegel aufgezeigt. Für BaTiO3- sowie SrTiO3-Dünnfilme wurden die PLD-Parameter Substrattemperatur, Sauerstoffpartialdruck, Energiedichte des Lasers sowie Flussdichte der Teilchen variiert und die Auswirkungen auf die strukturellen, optischen und Oberflächeneigenschaften mittels Röntgendiffraktometrie (XRD), spektraler Ellipsometrie (SE) und Rasterkraftmikroskopie (AFM) beleuchtet. Im zweiten Teil werden ZnO/MgxZn1−xO-Quantengrabenstrukturen hetero- und homoepitaktisch auf thermisch vorbehandelten a-Saphir- respektive m- und a-orientierten ZnO-Einkristallen vorgestellt. Die Realisierung eines zwei-dimensionalen „layer-by-layer“ Wachstumsmodus wird für die Quantengrabenstrukturen aufgezeigt. Die Quantengrabenbreite lässt sich aus beobachteten RHEED-Oszillationen exakt bestimmen. Ein Vergleich zwischen, mittels Photolumineszenz gemessenen Quantengrabenübergangsenergien als Funktion der Grabenbreite mit theoretisch ermittelten Werten wird vorgestellt, wobei der Unterschied zwischen polaren und nicht-polaren Strukturen mit Blick auf eine Anwendung aufgezeigt wird. Für c-orientierte ZnO-Dünnfilme wird das Wachstum im Detail untersucht und ein alternativer Abscheideprozess im so genannten Intervall PLD-Verfahren vorgestellt. Die Verifizierung der theoretischen Prognose einer ferromagnetischen Ordnung mit einer Curie-Temperatur oberhalb Raumtemperatur (RT) für kubische, Mangan stabilisierte Zirkondioxid (MnSZ)-Dünnfilme stellt den dritten Teil der Arbeit dar. Die strukturellen Eigenschaften der Dünnfilme werden mittels XRD, AFM sowie Transmissionselektronenmikroskopie (TEM) untersucht. Die Bedingungen einer erfolgreichen Stabilisierung der kubischen Kristallphase durch den Einbau von Mn wird aufgezeigt. Mittels Röntgenphotoelektronenspektroskopie (XPS) sowie Elektronenspinresonanz (EPR) wird der Ladungszustand der, in der Zirkondioxidmatrix eingebauten, Mn-Ionen ermittelt. Die elektrischen Eigenschaftenwerden durch Strom-Spannungsmessungen(IU) sowie der Leitungstyp durch Seebeck-Effekt Messungen charakterisiert. Zur Erhöhung der Leitfähigkeit werden die MnSZ Dünnfilme in verschiedenen Atmosphären thermisch behandelt und Veränderungen durch IU-Messungen aufgezeigt. Ergebnisse von optischen Untersuchungen mittels Transmissionsmessungen und KL werden präsentiert. Superconducting quantum interference device (SQUID)-Magnetometrie wird zur Charakterisierung der magnetischen Eigenschaften genutzt. Magnetische Ordnungen im Bereich zwischen 5 K ≤ T ≤ 300 K werden untersucht und der Einfluss von Defekten sowie einer thermischen Behandlung in verschiedenen Atmosphären auf die magnetischen Eigenschaften diskutiert.:Inhaltsverzeichnis 1. Einleitung . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4 2. Grundlagen . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 9 2.1. Thermodynamische Grundlagen . . . . . . . . . . . . . . . . . . . . . . . . 9 2.1.1. Konzept der Übersättigung . . . . . . . . . . . . . . . . . . . . . . . . . . 9 2.1.2. Beschreibung der Grenz- bzw. Oberfläche . . . . . . . . . . . . . . 10 2.2. Keimbildung . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 12 2.2.1. Thermodynamische Grundlagen der Keimbildung . . . . . .. . . . 12 2.2.2. Atomistische Beschreibung der Keimbildung . . . . . . . . . . . . . 14 2.3. Besonderheiten der Schichtbildung in Homo- und Heteroepitaxie 16 2.3.1. Homoepitaxie . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 16 2.3.2. Heteroepitaxie . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 18 2.4. Wachstumskinetik in der gepulsten Laserabscheidung . . . . . . . 19 3. Experimentelle Details 21 3.1. Probenherstellung – Gepulste Laser Abscheidung (PLD) . . . . . . 21 3.1.1. Allgemeine Grundlagen der PLD . . . . . . . .. . . . . . . . . . . . . . . . 21 3.1.2. Reflection high-energy electron diffraction . . . . . . . . . . . . . . . 23 3.1.3. PLD-Kammer mit in-situ RHEED . . . . . . . . . . . . . . . . . . . . . . . . 27 3.1.4. PLD-Kammer ohne in-situ RHEED . . . . . . . . . . . . . . . . . . . . . . 28 3.2. Strukturelle und chemische Charakterisierung . . . . . . . . . . . . . 29 3.2.1. Röntgendiffraktometrie . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 29 3.2.2. Rasterkraftmikroskopie . . . . . . . . .. . . . . . . . . . . . . . . . . . . . . . 31 3.2.3. Transmissionselektronenmikroskopie . . . . . . . . . . . . . . . . . . . 33 3.2.4. Energiedispersive Röntgenspektroskopie . . . . . . . . . . . . . . . . 33 3.2.5. Rutherford-Rückstreuspektrometrie und Partikel-induzierte Röntgenemission . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 34 3.2.6. Röntgenphotoelektronenspektroskopie . . . . . . . . . . . . . . . . . . 34 3.3. Optische Charakterisierung . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 35 3.3.1. Transmissionsmessungen . . . . . . . . . . . . . . . . . . . . . . . . . . . . 35 3.3.2. Lumineszenzmessungen . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 36 3.3.3. Spektroskopische Ellipsometrie . . . . . . . . . . . . . . . . . . . . . . . . 37 3.3.4. Raman-Streuung . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 37 3.4. Magnetische Charakterisierung . . . . . . . . . . . . . . . . . . . . . . . . . 39 3.4.1. Messungen der Magnetisierung mit einem SQUID-Magnetometer . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .. . . . . . . 39 3.4.2. Elektronenspinresonanz . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 40 3.5. Elektrische Charakterisierung . . . . . . . . . . . . . . . . . . . . . . . . . . 41 3.5.1. Strom-Spannungs-Messungen . . . . . . . . . . . . . . . . . . . . . . . . 41 3.5.2. Seebeck Effekt Messungen . . . . . . . . . . . . . . . . . . . . . . . . . . . . 41 4. Die Herstellung und Charakterisierung von BaTiO3/SrTiO3-Bragg-Spiegeln mittels PLD . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 43 4.1. Einführung . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 43 4.2. Bragg-Spiegel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 44 4.3. Die Materialien Strontiumtitanat und Bariumtitanat . . . . . . . . . . 45 4.3.1. Kristallstruktur . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 45 4.3.2. Substrateigenschaften . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 46 4.4. Epitaktische BaTiO3-Dünnfilme . . . . . . . . . . . . . . . . . . . . . . . . . . 47 4.4.1. Heteroepitaktische BaTiO3-Dünnfilme auf SrTiO3 (001)-Substraten . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 47 4.4.2. Initiale Wachstumsphasen von BaTiO3-Dünnfilmen auf SrTiO3 (001)-Substraten . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 53 4.4.3. Auswirkung der PLD-Abscheideparameter auf epitaktische BaTiO3-Dünnfilme . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .60 4.4.4. Veränderung der optischen Konstanten durch die Modifikation der PLD-Abscheideparameter . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 69 4.5. Epitaktische SrTiO3-Dünnfilmen . . . . . . . . . . . . . . . . . . . . . . . . . . 70 4.6. Abscheidung von BaTiO3/SrTiO3-Bragg-Spiegel . . . . . . . . . . . . . 73 4.6.1. BaTiO3/SrTiO3-Einfach–Heterostrukturen . . . . . . . . . . . . . . . . 73 4.6.2. BaTiO3/SrTiO3-Mehrfach–Heterostrukturen . . . . . . . . . . . . . . . 78 4.6.3. BaTiO3/SrTiO3-Bragg-Spiegel . . . . . . . . . . . . . . . . . . . . . . . . . . 80 4.6.4. Abschlussbemerkungen . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 85 5. Die Herstellung und Charakterisierung von ZnO/MgxZn1−xO-Quantengräben mittels PLD . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 87 5.1. Einführung . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 87 5.2. Die Materialien ZnO und MgxZn1−xO . . . . . . . . . . . . . . . . . . . . . 88 5.2.1. ZnO . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 88 5.2.2. MgxZn1−xO . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 88 5.3. Quantengrabenstrukturen . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 89 5.3.1. Exzitonen im Zinkoxid . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 91 5.3.2. Quantum-Confined Stark Effect . . . . . . . . . . . . . . . . . . . . . . . . 91 5.4. Die Abscheidung von ZnO- und MgxZn1−xO-Dünnfilmen mittels PLD . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 92 5.4.1. Heteroepitaktische Abscheidung von ZnO- und MgxZn1−xO-Dünnfilmen auf a-Saphir-Substraten . . . . . . . . . . . . . . . . . . . . . . . . . 93 5.4.2. Homoepitaktische Abscheidung von ZnO- und MgxZn1−xO-Dünnfilmen auf verschiedenen ZnO-Substraten . . . . . . . . . . . . . . . . 106 5.5. Die Herstellung von ZnO/MgxZn1−xO-Quantengrabenstrukturen auf verschiedenen Substraten . . . . . . . . . . . . . . . . . . . . . . . . . . . . 129 5.5.1. Heteroepitaktische Quantengrabenstrukturen auf a-Saphir-Substraten . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 130 5.5.2. Anmerkungen zu homoepitaktischen Quantengrabenstrukturen abgeschieden auf c-ZnO-Substraten . . . . . . . . . . . . . . . . . . . . . . . . 143 5.5.3. Homoepitaktischen Quantengrabenstrukturen abgeschieden auf nicht-polaren ZnO-Substraten . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 144 5.5.4. Abschlussbemerkungen . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 152 6. Die Herstellung und Charakterisierung von Mangan stabilisierten Zirkondioxid als potentieller verdünnter magnetischer Halbleiter mittels PLD . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 155 6.1. Einführung . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 155 6.2. Theoretische Grundlagen . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 156 6.2.1. Spintronik . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 156 6.2.2. Verdünnte magnetische Halbleiter . . . . . . . . . . . . . . . . . . . . . 158 6.2.3. Ferromagnetische Kopplung in verdünnten magnetische Halbleitern . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 159 6.3. Mangan stabilisiertes Zirkondioxid als möglicher DMS . . . . . . . . 162 6.4. Das Material Zirkondioxid . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 164 6.4.1. Die Phasen des Zirkondioxids . . . . . . . . . . . . . . . . . . . . . . . . . 164 6.5. Substrateigenschaften von (001) und (111) orientiertem Yttrium stabilisierten Zirkondioxid . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 166 6.6. Untersuchungen an Mangan stabilisierten Zirkondioxid Dünnfilmen . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .176 6.6.1. Strukturelle und chemische Charakterisierung . . . . . . . . . . . . 177 6.6.2. Analyse der unterschiedlichen Phasen im Mangan stabilisierten Zirkondioxid . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .190 6.6.3. Elektrische und optische Charakterisierung . . . . . . . . . . . . . . 203 6.6.4. Magnetische Charakterisierung von Mangan stabilisiertem Zirkondioxid . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .210 6.6.5. Magnetische Charakterisierung von nominell undotiertem Zirkondioxid . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .221 6.6.6. MnSZ-Mehrfach-Heterostrukturen . . . . . . . . . . . . . . . . . . . . . 224 6.6.7. Einfluss einer thermischen Behandlung auf die magnetischen Eigenschaften . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .227 6.6.8. Zusammenfassung der Messergebnisse . . . . . . . . . . . . . . . . 232 6.7. Abschlussbemerkung . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 234 7. Zusammenfassung und Ausblick . . . . . . . . . . . . . . . . . . . . . . . 237 8. Literaturverzeichnis . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 245 A. Symbole und Abkürzungen . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 275 B. Liste der Veröffentlichungen . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 281 C. Danksagung . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 283 D. Curriculum Vitae . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .286 E. Selbstständigkeitserklärung . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 287