Thesis (M.S.)--Virginia Polytechnic Institute and State University, 1992. / Vita. "x̳", "1̳-x", and "3̳" are subscripts. Abstract. Includes bibliographical references (leaves 120-128). Also available via the Internet.

In this work, ordered all-binary short-period strained InAs/GaAs superlattice quantum wells were studied as an alternative to strained ternary alloy InGaAs/GaAs quantum wells. InGaAs quantum wells QWs have been of great interest in recent years due to the great potential applications of these materials in future generations of electronic and optoelectronic devices. The all binary structures are expected to have all the advantages of their ternary counterparts, plus several additional benefits related to growth, to the elimination of alloy disorder scattering and to the presence of a higher average indium content.

Undoped and doped Pb(Zr_xTi_1-x)O₃, i. e. PZT, ferroelectric thin films were prepared by chemical solution deposition and spin-coating method. The precursors for making the undoped PZT films were derived from lead acetate, zirconium n-propoxide, and titanium iso-propoxide. In addition, lanthanum acetylacetonate, neodymium acetate, and niobium ethoxide were introduced into the precursor solution to accomplish doping of the corresponding elements. Both doped and undoped PZT films were coated onto Pt/Ti/SiO₂/Si, RuO_x and single-crystal sapphire substrates of various thickness and annealed at a range of temperatures and times. The effects of dopants were studied in terms of the Curie temperature, crystal distortion, transformation temperature, microstructure, optical properties, and electrical properties. In addition to the dopant effect, the effects of substrates were also investigated with regard to crystallization and preferred orientation. The Curie temperature of the doped and undoped PZT films was determined by in-situ hot-stage transmission electron microscope (TEM) and compared with those of bulk ceramics. Lattice distortion and phase transformation were determined by x-ray diffraction (XRD). Microstructure of the films was characterized by using optical microscopy, scanning electron microscopy (SEM), and scanning transmission electron microscopy (STEM). Optical properties were characterized by a UV-VIS-NIR scanning spectrophotometer and electrical properties and fatigue testing were measured on a standardized RT66A using a Virtual-Ground circuit. It was observed that the addition of Nd and La dopants tends to enhance perovskite phase formation and improve electrical properties of PZT films. Higher refractive indices in La and Nd-doped PZT films imply that packing densities of PZT films are improved by adding dopants. Furthermore, the lower leakage currents and improved fatigue properties in PZT films were also observed by the addition of Nb dopants. / Master of Science

Thesis (Ph. D.)--University of Canterbury, 2009. / Typescript (photocopy). Includes bibliographical references. Also available via the World Wide Web.

In this work tunability, implantation damage and recovery of GaAs doping superlattices implanted with hydrogen ions were studied. The applicability of two models of the optical properties of semiconductors was also investigated. GaAs doping superlattices were implanted with 0.5 MeV hydrogen ions at doses of 1012 cm-2, 1014 cm-2 and 1016 cm-2. This gradually modifies their optical characteristics from superlattice behaviour to something resembling the bulk material and beyond. Such a processing technique therefore provides a convenient way of tuning the optical properties of a superlattice semi-permanently. A combined result of ellipsometry and near infrared reflectance measurements showed that a single effective oscillator as well as a more advanced three-parameter model could be applied to the virgin and ion-implanted doping superlattices. This allowed us to determine the dose dependent effective band gap as well as other model parameters. Photoluminescence as well as normal and resonance Raman techniques were applied to study hydrogen ion implantation damage and its recovery. These techniques showed that implantation damage could be reversed to a large extent by a simple thermal annealing step. / Dissertation (MSc)--University of Pretoria, 2006. / Physics / unrestricted

Thesis (Ph.D.)--McMaster University (Canada), 1993. / Source: Dissertation Abstracts International, Volume: 55-06, Section: B, page: 2345. Adviser: G. C. Weatherly.