Este estudo se propôs a analisar as características morfológicas da dentina humana irradiada com laser de Er:YAG utilizando diferentes larguras temporal de pulso nos protocolos de preparo cavitário e pré-tratamento da dentina. Foram utilizados 18 molares humanos que foram seccionados no sentido mésio-distal e amelocementário obtendo-se um disco plano de dentina. Em seguida foram lixados com uma sequência decrescentes de lixas para padronizar os espécimes em 2mm de espessura. Os grupos experimentais foram compostos a partir de 2 fatores de variação: 1) indicação clínica - preparo cavitário (E=200mJ/20Hz), e pré-tratamento (E=80mJ/2Hz); e 2) largura temporal de pulso - 50, 300 e 600µs. Assim formaram-se 6 grupos experimentais com (n=3): G1(E=200mJ/20Hz/50µs); G2(E=200mJ/20Hz/300µs); G3(E=200mJ/20Hz/600µs); G4(E=80mJ/2Hz/50µs); G5(E=80mJ/2Hz/300µs); G6(E=80mJ/2Hz/600µs). Os espécimes foram irradiados com o laser de Er:YAG com comprimento de onda de 2,94µm, de modo não contato, com um distância de 7mm do feixe de saída, sob irrigação de 60ml/min de água e 40ml/min de ar. Após a irradiação, os espécimes foram processados e destinados à avaliação descritiva das imagens obtidas em Microscopia Eletrônica de Varredura (MEV), nos diferentes grupos experimentais. A análise morfológica dos grupos irradiados revelou uma superfície irregular, ausência de smear layer que expõe a abertura dos túbulos dentinários, dentina peritubular evidente e, sem indícios de carbonização e derretimento para todos os protocolos utilizados. Os resultados deste estudo in vitro mostraram que a irradiação com o laser de Er:YAG promoveram um padrão morfológico microrretentivo característico de ablação para todos os grupos testados e os grupos G1 e G4, que utilizaram a menor largura temporal de pulso (50 ?s), apresentaram uma superfície mais rugosa quando comparados aos demais grupos. Por fim, podemos concluir que a largura temporal de pulso influência nas características morfológicas da dentina irradiada nas diferentes indicações clínicas testadas, preparo cavitário e pré-tratamento. A menor largura de pulso (50 µs) produz uma morfologia mais irregular quando comparada as maiores larguras de pulsos (300 e 600 µs). / This study evaluated the morphological characteristics of Er:YAG laser irradiated dentin using different temporal pulses width on the protocols of cavity preparation and dentin pretreatment. Eighteen human molars were cut longitudinally in a mesiodistal direction and amelocemental junction providing dentin disks. Samples were polished in a decreasing silicon carbide paper to obtain standard 2mm thick disks. The experimental groups were divided by two variables: 1) clinical protocol - cavity preparation (E=200mJ/20Hz) and pretreatment (E=80mJ/2Hz); and 2) temporal pulse width - 50, 300 and 600µs. Therefore, six experimental groups were (n=3): G1(E=200mJ/20Hz/50µs); G2(E=200mJ/20Hz/300µs); G3(E=200mJ/20Hz/600µs); G4(E=80mJ/2Hz/50µs); G5(E=80mJ/2Hz/300µs); and G6(E=80mJ/2Hz/600µs). The samples were irradiated with the Er.YAG laser using wave-length of 2.94µm, in a non contact mode at a focal distance of 7mm from the target point under continuous water spray of 60-40ml/min. After the irradiation, the samples were processed and evaluated by scanning electron microscopic evaluation (SEM). The morphological analysis on the irradiated groups showed an irregular dentin surface, without smear layer, exposed dentinal tubules apertures, evidenced peritubular dentin, without carbonization and melting signs for all groups. A microretentive morphological pattern, characteristic of the ablation process could be observed in all groups. However, groups G1 and G4, that used 50?s of temporal pulse width, presented a greater irregularity when compared to other groups. In conclusion, the temporal pulse width interfere on the morphological characteristic of the irradiated dentin, regardless of clinical protocol, cavity preparation and pretreatment. The shorter the pulse width (50µs), the greater the surface irregularity.

Este estudo se propôs a analisar os efeitos das diferentes larguras temporais de pulso do laser de Er:YAG na rugosidade superficial, na perda de volume do material e na altura do degrau formado em uma Y-TZP (Yttrium-stabilized Tetragonal Zirconia Polycrystal) pré-sinterizada. Foram utilizados 5 blocos de Y-TZP pré-sinterizados destinados ao uso CAD/CAM que foram seccionados, obtendo-se 63 espécimes padronizados. Em seguida, esses espécimes foram lixados com uma sequência decrescente de lixas para padronização da superfície. Os grupos experimentais foram compostos a partir de 1 fator de variação - o tratamento de superfície. Os espécimes foram irradiados com o laser de Er:YAG (Fidelis III Fotona, Eslovênia) - 2,94 ?m, 100 mJ, 15,87J/cm2, 10 Hz, 1W, 7 mm, 60% água/40% ar. Assim formaram-se 7 grupos experimentais (n=9): G1 (50 ?s); G2 (100 ?s); G3 (300 ?s); G4 (600 ?s); G5 (1000 ?s); G6 (Abrasão triboquímica com partículas de 30 ?m); G7 (Sem tratamento). Após os tratamentos de superfície, os espécimes foram sinterizados em forno específico, de acordo com as recomendações do fabricante. Foram capturadas imagens em Microscópio Confocal a Laser 3D de cada espécime e avaliadas por meio de um software. A análise dos grupos irradiados revelou um aumento da rugosidade nos grupos G1, G2, G3 e G4 quando comparados aos grupos G6 e G7. O grupo G5 apresentou superfície totalmente plana e desfavorável para retenção. No que se refere à perda de volume e formação de degrau, os grupos G1, G2 e G3 demonstraram grande perda de volume e grande altura de degrau formado, o que pode levar a uma desadaptação da peça protética. No grupo G4 foram observados valores de rugosidade satisfatórios com pouca perda de volume e pequena altura de degrau formado, semelhante ao que foi notado para a abrasão trioboquímica (G6), podendo ser indicada para tratamento de superfície de Y-TZP pré-sinterizada. A irradiação com o laser de Er:YAG promoveu um padrão morfológico com muitas irregularidades, característico de ablação para os grupos G1, G2, G3 e G4 e, para todos os protocolos utilizados, não foi observada a presença de trincas ou carbonização. Sugere-se que a largura temporal de 600 ?s (G4) seja a mais indicada como alternativa para tratamento de superfície, objetivando a criação de micro-retenções superficiais, com pouca perda de volume de material e que, ao mesmo tempo, não provoque danos à estrutura da cerâmica policristalina. / This study evaluated the effects of different Er:YAG laser pulse width protocols on surface roughness, loss of volume of the material and the step height formed of pre-sintered Yttrium-stabilized tetragonal Zirconia Polycrystal (Y-TZP) by three-dimensional profilometric assessment. Blocks of pre-sintered Y-TZP were cut providing 63 standard 5mm thick samples which were divided by surface treatment, as follows (n=9): G1 (50?s); G2 (100?s); G3 (300?s); G4 (600?s); G5 (1000?s); G6 (tribochemical silica coating); G7 (Untreated). Laser settings: The Er:YAG laser (Fidelis III; Fotona, Ljubljana, Slovenia) 100mJ, 15,87J/cm2, 10Hz, 1W, (60%) and air (40%) cooling. After treated or not, samples were sintered according to the manufacturer\'s recommendations. Roughness, volume loss and step and were analyzed by 3D profilometric assessment with confocal laser microscopy. Irradiated groups showed an increased roughness in the groups G1, G2, G3 and G4 when compared to G6 and G7 groups. The G5 group showed a completely flat and unfavorable surface for retention. The groups G1, G2 and G3 shown great loss of volume and the step height formed, which can lead to a gap on the crowns. In G4 were observed satisfactory roughness with little loss of volume and the step height formed similar to G6. Irrespective of laser protocol, any of the specimens showed presence of cracks and carbonization. It is suggested that the pulse width 600?s (G4) is the most suitable pulse width protocol as an alternative surface treatment, promoting micro-retention, with little loss of volume of material, comparable to gold standard treatment.

O objetivo deste estudo foi o de avaliar os efeitos da irradiação laser de Er,Cr:YSGG em superfícies dentinárias no tratamento da hipersensibilidade dentinária cervical, em busca de um protocolo para ser aplicado clinicamente. Para o teste de permeabilidade, foram preparados 144 pré-molares, as coroas seccionadas e as raízes impermeabilizadas. Duas áreas de irradiação antagônicas foram delimitadas e livres da impermeabilização (controle e experimental). A seguir, os dentes foram subdivididos em dois sub-grupos, diferindo o condicionamento da superfície irradiada (EDTA 24% e ácido fosfórico 35%) e em grupos diferindo o protocolo:G1)Er:YAG, 60mJ/2Hz; G2)0,25W; G3)0,5W; G4)0,75W; G5)1W, G6)1,25W; G7)1,50W; G8)1,75W G9)2W. Após as irradiações, os espécimes foram imersos em azul de metileno 2% por 4 horas, e incluídos em resina epóxica para a realização dos cortes longitudinais. Estes tiveram suas imagens trabalhadas em computador para mensuração do nível de infiltração. Os dados foram submetidos à análise estatística. O Sub-grupo 1, condicionado com EDTA, apresentou diferenças entre os grupos sendo que as amostras irradiadas com Er:YAG demonstraram menor infiltração, diferindo estatisticamente dos grupos 3, 6 e 9. Os resultados do sub-grupo 2 mostraram que as médias das amostras irradiadas com Er:YAG tenderam a zero entretanto, não houve diferença entre os grupos. Na Fase B, fragmentos de dentina foram obtidos da região cervical de dentes humanos, preparados para análise em microscopia eletrônica de varredura. Morfologicamente, observou-se oclusão parcial dos túbulos dentinários após irradiação com Er:YAG e Er,Cr:YSGG nas condições de 0,25W e 0,50W. A partir de 0.75W, foi observado abertura dos túbulos e à medida que as energias aumentaram, foram observadas carbonização e fendas. De posse dos resultados dos trabalhos in vitro, foram selecionados os parâmetros para a aplicação e o acompanhamento clínico de 1 mês: G1)controle (placebo); G2)Er:YAG; G3)Er,Cr:YSGG 0,25W e G4)Er,Cr:YSGG 0,75W. Após a triagem, foram selecionados voluntários de acordo com critérios de exclusão e inclusão. O nível de sensibilidade de cada voluntário foi avaliado através da escala visual analógica de dor (VAS) com auxílio do ar da seringa tríplice 1 semana antes (Pré-1), 5 minutos anterior ao tratamento (Pré-2), após 5 minutos (Pós-1), 1 semana (Pós-2) e 1 mês após o tratamento (Pós-3). Os dados foram coletados e submetidos à análise estatística separadamente para os dois estímulos realizados: spray de ar e sonda exploradora. Tanto para o estímulo ar quanto para o estímulo sonda, não foram observadas diferenças estatisticamente significantes nas escalas Pré-1 e Pré-2, concluindo que os pacientes estavam padronizados e não houve efeito da profilaxia nos níveis de dor. Ao estímulo do spray de ar, nota-se uma redução nos níveis de dor na escala Pós-1, porém há uma estabilidade dos valores das escalas seguintes. O grupo 2 (Er:YAG) apresentou o menor nível de dor quando comparado aos outros grupos. Ao estímulo mecânico foi observado que o grupo 4 (Er,Cr:YSGG 0,50W) demonstrou o decréscimo de dor mais acentuado imediatamente após o tratamento, porém ao final do estudo, apresentou os maiores níveis de dor. Os grupos 1, 2 e 3 apresentam redução de dor, porém estatisticamente diferentes do grupo 4. Com base nos resultados apresentados e dentro dos limites e parâmetros estudados, pode-se concluir que nenhuma condição foi capaz de eliminar completamente a microinfiltração e diminuir a permeabilidade dentinária; porém o laser de Er:YAG e o laser de Er,Cr:YSGG 0,25W apresentaram resultados satisfatórios nos três estudos realizados. / The aim of the present study was to determine the correct parameters of the Er,Cr:YSGG laser in the treatment of cervical dentin hypersensitivity. This work was presented in 3 different stages. In the first one, it was evaluated the decrease in dentin permeability of dentinal tubules after Er,Cr:YSGG laser irradiation in radicular surfaces. Ninety premolars were prepared with its crows sectioned, and the roots completely impermeabilized. Two antagonist areas of irradiation were determined as control and experimental. Each surface was conditioned with EDTA 24% (sub-group1) and phosphoric acid 35% (sub-group2) and the selected parameters were: 1)Er:YAG, 60mJ, 2Hz, 4 irradiations of 20sec each, defocused mode; and groups 2 to 9 received irradiation with Er,Cr:YSGG laser, 20Hz, Z6 tip, 600µm diameter, defocus mode, 0% of air and water: 2)Er,Cr:YSGG 0,25W; 3) 0,5W; 4) 0,75W; 5) 1,0W; 6) 1,25W, 7) 1,50W, 8) 2W; 9) 2 W. After irradiation, samples were immersed in a solution of methylene blue for 4 hours, washed for 5 min and included in epoxy resin to allow longitudinal cuts. The images were digitalized and computed worked. Data was statistically analyzed. Although the samples irradiated with Er:YAG showed less microleakage, the sub-group 1 showed differences between the groups, statistically different from groups 3, 6 e 9. The results of the sub-group 2 showed that the mean values of the Er:YAG samples had a tendency to be negative, however, no differences were detected between the groups. In the second stage, cuts from the cervical area were obtained and prepared for scanning electron microscopy to evaluate the superficial morphology. It was observed the partial closure of dentinal tubules after the irradiation with Er:YAG and Er,Cr:YSGG laser in the 0.25 and 0.50W protocols. From the 0.75W until 2W, it was observed the dentinal tubules opened as the energy densities raised. With the results of the in vitro studies, the parameters were selected: G1)control; G2)Er:YAG; G3)Er,Cr:YSGG 0,25W e G4)Er,Cr:YSGG 0,75W. Thirty subjects, who met the entry criteria, were admitted into the study. The assessment method used to quantify sensitivity was the cold air syringe, recorded by the visual analogue scale (VAS), prior to treatment as baseline (Pre-1), immediately before (Pre-2) and immediately after (Post-1) the topical treatment, after 1 week (Post-2) and after 1 month (Post-3). Teeth were assigned to the 4 groups. After the follow-up, data was collected and submitted to statistical analysis for both kinds of stimulus: evaporative (air) and mechanical (probe). For both air and probe it was not observed differences among the Pre-1 and Pre-2 moments, for what it can be concluded that patients were standardized. Analyzing the evaporative stimulus, it can be observed the reduction in the pain level immediately after the treatment; however there was stability in the next values. Group 2 (Er:YAG) showed the least level of pain. Throughout the mechanical stimulus, it was observed that group 4 (Er,Cr:YSGG 0,50W) showed the most pronounced decrease of pain immediately after treatment, however, at the end of the study, the levels of pain increased. Groups 1, 2 e 3 showed reduction of pain, statistically different from the group 4. Based on the results and within the limits of this study, it can be concluded that none of the parameters and lasers studied were capable of eliminate the microleakage and decrease the dentin permeability, however, the Er:YAG and Er,Cr:YSGG 0,25W lasers showed satisfactory results in the three studies performed.

A erosão dental provoca alterações histológicas complexas na dentina e, apesar do aumento da ocorrência desta patologia na última década, a literatura apresenta poucos estudos sobre a adesão na dentina erodida. Com o aprimoramento da tecnologia e o conhecimento de que os lasers de érbio apresentam grande afinidade pela água e hidroxiapatita, sua utilização tem sido considerada um método alternativo para tratamento da superfície dentinária antes dos procedimentos adesivos. Assim, o objetivo deste trabalho in vitro foi avaliar o efeito de diferentes tratamentos de superfície (ponta diamantada, laser de Er:YAG 2,94 m, 60 mJ, 2 Hz, 0,2 W, 19,3 J/cm2 - e laser de Er,Cr:YSGG 2,78 m, 50 mJ, 30 Hz, 1,5 W, 4,5 J/cm2), prévios ao tratamento restaurador, tanto na dentina humana hígida quanto na dentina artificialmente erodida. Metade das amostras foi submetida à ciclagem erosiva, a qual foi realizada durante 5 dias por meio da imersão em solução de ácido cítrico 0,05 M (pH 2,3, 10 minutos, 6x/dia) e solução supersaturada (pH 7,0, 60 minutos entre os ataques ácidos). Na fase experimental 1, 32 fragmentos de dentina foram divididos aleatoriamente em 8 grupos (n = 4) e com o auxílio da Microscopia Eletrônica de Varredura (MEV), realizou-se a análise da morfologia da superfície da dentina hígida e da submetida à ciclagem erosiva, após os diferentes tratamentos de superfície. Na fase experimental 2, 192 terceiros molares humanos foram divididos aleatoriamente em 2 grupos (dentina hígida e dentina submetida à ciclagem erosiva) e 8 subgrupos (n = 12) para avaliação da resistência de união entre as superfícies tratadas e 2 sistemas adesivos (01 autocondicionante e 01 com condicionamento ácido prévio), por meio do ensaio de microtração e da análise do padrão de fratura. Para o ensaio de microtração, blocos de resina composta microhíbrida foram confeccionados na superfície de dentina e, após armazenados em água destilada-deionizada por 24h (37oC), palitos foram obtidos para serem tracionados na máquina de ensaio universal (0,5mm/min). A análise do padrão de fratura realizada em microscópio ótico (40x) e as avaliações das eletromicrografias foram feitas de forma descritiva. Os valores obtidos de resistência de união(MPa) foram submetidos aos testes de ANOVA (dois fatores) e de comparações múltiplas de Tukey (p<0,05). A análise morfológica de superfície mostrou alterações significativas da dentina hígida e da dentina artificialmente erodida, submetidas aos diferentes tratamentos de superfície. Quanto à resistência de união, na dentina hígida, o grupo controle, tanto do sistema autocondicionante (54,69 ± 7,80 MPa) quanto do condicionamento ácido total (47,36 ± 9,35 MPa), apresentou valores significativamente maiores que os outros grupos, sendo, porém, diferentes entre si. Na dentina erodida, a maior resistência de união foi alcançada com o grupo tratado com o laser de Er,Cr:YSGG associado ao adesivo autocondicionante (28,26 ± 9,22 MPa), o qual foi significativamente diferente de todos demais grupos. Com base nos parâmetros de irradiação utilizados neste estudo, pode-se concluir que em dentina hígida, os tratamentos de superfície com os lasers de Er:YAG e Er,Cr:YSGG apresentaram resultados de adesão inferiores, mas satisfatórios, em relação ao grupo controle. Já em substrato dentinário erodido, a irradiação com laser de Er,Cr:YSGG, associada ao uso de sistema adesivo autocondicionante, promoveu efeito positivo para a adesão à resina composta. / Dental erosion can cause complex histological changes in dentin and, despite the increase in its incidence during the last decade, limited information is available regarding adhesion to eroded dentin. With improvements in technology and due to the fact that the erbium lasers have high affinity to water and hydroxyapatite, the use of laser can consist on an alternative for the treatment of dentin surface before adhesive procedures. The aim of this in vitro study was to evaluate the effect of different surface treatments (diamond bur, Er:YAG laser 2.94 m, 60 mJ, 2 Hz, 0.2 W, 19.3 J/cm2 - and Er,Cr:YSGG laser 2.78 m, 50 mJ, 30 Hz, 1.5 W, 4.5 J/cm2) prior to restorative treatment, in sound and artificially eroded human dentin. Half of the samples was submitted to the erosive cycling, which was performed by immersion in 0.05 M citric acid (pH 2.3, 10 min, 6x/day) and in supersaturated solution (pH 7.0, 1h, between acid attacks), during 5 days. In phase 1, 32 dentin fragments were randomly divided into 8 groups (n = 4). The analysis of surface morphology of both sound and eroded dentin was performed by Scanning Electron Microscopy (SEM), after the different surface treatments. In phase 2, 192 human third molars were randomly divided into 2 groups (sound and eroded dentin) and 8 subgroups (n=12) to evaluate the bond strength between the treated surfaces and composite resin, with two adhesive systems (self-etching and total-etching) by means of the microtensile bond strength (TBS) test and fracture pattern analysis. For the microtensile bond strength test, blocks of composite resin were bonded to the samples and, after 24 h-storage in distilled/deionized water (37°C), stick-shapped samples were obtained and submitted to TBS test in a universal testing machine (0.5 mm/min). The fracture pattern was performed with an optical microscopy (40x) and the evaluations of the electromicrographs were made under a descriptive mode. The bond strength values (MPa) were analyzed by two-way ANOVA and Tukey tests ( = 0.05). In sound dentin, for the control group, both self-etching (54.69 ± 7.8 MPa) and total-etching adhesive system (47.36 ± 9.3 MPa) showed significantly higher values than all other groups (p<0.05), even though they differ from each other. However, in eroded dentin groups, the self-etching on the samples treated with the Er,Cr:YSGG laser presented the highest mean (28.3 ± 9.2 MPa), which was statistically significant higher than all the other treatments (p<0.05). Based on the irradiation parameters considered for this study, it can be concluded that in healthy dentin, the surface treatment with Er:YAG and Er,Cr:YSGG irradiation showed bonding values lower than the control group, but they presented satisfactory results. However, in eroded dentin, the use of Er,Cr:YSGG laser, associated with the self-etching adhesive system, promoted positive effect on adhesion to composite resin.

Made available in DSpace on 2014-06-11T19:24:08Z (GMT). No. of bitstreams: 0 Previous issue date: 2004-02-10Bitstream added on 2014-06-13T19:10:17Z : No. of bitstreams: 1 gois_am_me_arafo.pdf: 658823 bytes, checksum: 0abf0aa96e870eb9a4ad26842cbc521f (MD5) / Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) / Este estudo avaliou a resistência adesiva de microtração em reparos de resinas compostas, novas e envelhecidas, após tratamento da superfície usando irradiação a laser de Er: YAG, ponta diamantada e abrasão a ar. 36 blocos de resina composta híbrida Z100 (3M) com 5mm de comprimento e 6 mm de lado foram confeccionados com auxílio de uma matriz. Metade desses blocos foram reparados após 24 horas, e a outra metade foi reparada após envelhecimento artificial com luz ultravioleta. Cada grupo foi subdividido em 6 subgrupos e as superfícies experimentais foram submetidas a diferentes tratamentos: (G1) desgaste com ponta diamantada; (G2) jateamento com partículas de óxido de alumínio de 60 mm; (G3) ablação com laser de Er: YAG a um nível de energia de 100mJ; (G4) ablação com laser de Er:YAG a um nível de energia de 200mJ; (G5) ablação a laser de Er:YAG a um nível de energia de 300mJ; (G6) controle- ausência de tratamento de superfície. Após tratamento da superfície, o agente adesivo (Single Bond 3M) foi aplicado e os blocos foram reparados com a resina composta Point4 (KERR). Reparados, os blocos foram seccionados em espécimes de 1.0 mm2. A resistência adesiva de microtração foi medida em uma máquina de teste universal MTS. No grupo que foi reparado 24 horas após, não houve diferença estatisticamente significante na resistência adesiva interfacial entre os subgrupos. No grupo que foi envelhecido, os subgrupos G1 e G3 tiveram as maiores médias de resistência adesiva de reparo. Significantemente, os menores valores foram achados para os subgrupos G2 e G6. As médias da resistência adesiva de reparo foram estatisticamente similares para G3, G4 e G5. O exame em SEM indicou que a fratura adesiva foi o tipo predominante de falha. Os resultados desse estudo indicam que os maiores valores de resistência adesiva foram achados para o desgaste da superfície com... . / This study assessed the microtensile bond strengths of composite repairs, new and aged, after surface treatments, using Er:YAG laser irradiation, diamond bur and air abrasion. 36 blocks of hybrid composite resin Z100 (3M) with 5.0 mm length and 6.0 mm of side were made in mold. Half of these blocks were repaired after 24 hr and the other half was aged in an artificial aging chamber with exposure to a total ultraviolet irradiation. Each group was then divided into six subgroups and the experimental surface was exposed to a different treatment: (G1) grinding with diamond burs; (G2) air-abraded with 60mm aluminum oxide particles; (G3) ablation with an Er: YAG laser under the energy level of 100 mJ; (G4) ablation with an Er: YAG laser under the energy level of 200 mJ; (G5) ablation with an Er: YAG laser under the energy level of 300 mJ; (G6) controle - with no surface treatment. After the resin treatment on the surface, the bonding agent (Single bond, 3M) was applied and the blocks were repaired with the resin Point4 (Kerr) composite. Repaired, the blocks were sectioned into specimens (stick) of 1.0 mm2. Microtensile bond strength was measured in a universal testing machine MTS. The group repaired after 24 hours did not present statistically significant differences on interfacial bond strengths between the subgroups. On the aged group, the subgroups G1 and G3 presented the highest mean of repairing bond strenght. Significant lower values were found for subgroups G2 and G6 .The mean of repairing bond strenght was statistically similar for G3, G4 and G5. SEM examination indicated that adhesive failure was the predominant mode of failure. The results of this study indicate that the highest bond values were achieved by grinding the surface with diamond burs and ablating the surface with an Er: YAG laser under the energy level of 100mJ... (Complete abstract, click electronic address below).

Made available in DSpace on 2014-06-11T19:24:08Z (GMT). No. of bitstreams: 0 Previous issue date: 2004-07-26Bitstream added on 2014-06-13T19:10:19Z : No. of bitstreams: 1 rossato_dm_me_arafo.pdf: 1938222 bytes, checksum: fb0dee4a630e9b7c50ea8d084d2ad7cb (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste trabalho foi realizar avaliação da resistên - cia de união ao cisalhamento de reparos de resina compostas em restaurações com resina composta envelhecidas, em função de diferentes tratamentos superficiais. Foram confeccionados 60 corpos-de-prova de resina composta Z250 (3M) e levados a termociclagem para simular o envelhecimento da restauração, foram realizados 500 ciclos de 15 segundos cada, variando entre 5°e 55°C. Separados aleatoriamente em seis grupos que sofreram os seguintes tratamentos superficiais: nenhum tratamento (G1 - controle), desgaste com ponta diamantada (G2), jato de óxido de alumínio com partículas de 27,5æm (G3) por 10 segundos, laser de Er:YAG - 200mJ (G4), laser de Er:YAG - 300mJ (G4) e laser de Er:YAG - 400mJ (G6), os três últimos com freqüência de 10Hz por 10 segundo. Foi realizada microscopia eletrônica de varredura para observarmos o aspecto do material após os tratamentos terem sido executados. O reparo da restauração foi realizado utilizando-se a mesma resina. O teste de cisalhamento foi feito na Máquina de Ensaios Mecânicos MTS - 810. Analisando os resultados por ANOVA e pelo teste de Tukey não foram encontradas diferenças significativas (p-valor=0.5120). A análise dos valores medianos, mostrou que o tratamento superficial com jato de óxido de alumínio apresentou uma maior resistência da interface do reparo ao cisalhamento (8.91Mpa) enquanto que o laser de Er:YAG com 400mJ de potência, apresentou a menor (6.76Mpa). A análise dos tipos de fratura mostrou que 90% dos corpos-de-prova do grupo 3 (óxido de alumínio) sofreram fraturas coesivas. / The aim of this work was to perform the evaluation of the shear bond strength of the composite resin repairs in old composite restorations, modifying the superficial treatment of the samples. Sixty samples of the composite resin Z250 (3M) were prepared and thermocycled for 500 cycles at 5° and 55°C with a dwelling time of 15 seconds. Speciments were randomly divided into six groups and subjected to different surface treatments as follows: No surface treatment (G1 - control), grinding with a diamond bur (G2), sandblasting with a microetcher for 10 seconds with 27,5æm Al2O3 particles (G3), treated with Er:YAG laser with an energy intensity of 200mJ (G4), 300mJ (G5), 400mJ (G6), frequency of 10Hz for 10 seconds. The speciments after surface treatment were observed using the scanning electron microscope. The repair of the old resin was done with the same material. The shear bond strength test was performed in a Mechanic Testing MTS - 810. Statistical treatment by ANOVA and Tukey's test showed no significant differences between the groups tested (p=0.5120). The highest shear bond strength values were achieved by sandblasting the surface with a microetcher with Al2O3 (8,91Mpa), whereas the lowest values were obtained with Er:YAG laser with energy intensity of 400mJ (6.76Mpa). Observing the rupture surface, G3 presented 90% of cohesive failures.

Submitted by Fernanda Alves Feitosa null (fernanda.feitosa@fosjc.unesp.br) on 2016-06-07T14:46:57Z No. of bitstreams: 1 Tese ok - versão final com ficha catalografica certa.pdf: 3711607 bytes, checksum: d94558d40ddaabd3c84ddd7cdec2d8bb (MD5) / Approved for entry into archive by Ana Paula Grisoto (grisotoana@reitoria.unesp.br) on 2016-06-08T13:34:17Z (GMT) No. of bitstreams: 1 feitosa_fa_dr_sjc.pdf: 3711607 bytes, checksum: d94558d40ddaabd3c84ddd7cdec2d8bb (MD5) / Made available in DSpace on 2016-06-08T13:34:17Z (GMT). No. of bitstreams: 1 feitosa_fa_dr_sjc.pdf: 3711607 bytes, checksum: d94558d40ddaabd3c84ddd7cdec2d8bb (MD5) Previous issue date: 2016-06-02 / O objetivo desse estudo foi avaliar a eficiência da irradiação com lasers de alta potência e a influência da aplicação do silano previa ou posteriormente à irradiação com os lasers na resistência de união entre cerâmica vítrea de dissilicato de lítio, cimento resinoso e dentina humana. Foram confeccionados 50 espécimes tronco-cônicos de cerâmica (n=10), divididos aleatoriamente em 5 grupos: 1- Controle- Condicionamento com ácido hidrofluorídrico 10% por 1 min e aplicação do silano; 2- Er:YAG – irradiação com laser Er:YAG (200 mJ e 10 Hz), seguido do condicionamento com ácido hidrofluorídrico 10% por 1 min e aplicação do silano; 3- Silano + Er:YAG – Condicionamento com ácido hidrofluorídrico 10% por 1 min, aplicação do silano e irradiação com laser Er:YAG nos mesmo parâmetros do grupo anterior; 4- Nd:YAG – irradiação com laser Nd:YAG (120 mJ e 10 Hz), seguido de condicionamento com ácido hidrofluorídrico 10% por 1 min e aplicação do silano, 5- Silano + Nd:YAG - Condicionamento com ácido hidrofluorídrico 10% por 1 min, aplicação do silano e irradiação com laser Nd:YAG nos mesmo parâmetros do grupo anterior. Após os tratamentos os espécimes cerâmicos foram cimentados com cimento resinoso de presa dual à superfície de dentina de 50 molares humanos incluídos em resina acrílica ativada quimicamente. Após armazenamento por 24 h foi realizado o ensaio de tração em máquina de ensaios universais com célula de carga de 10 KgF e velocidade constante de 1mm/min. Os dados obtidos foram submetidos à ANOVA 2-fatores e teste de Dunnet (α=5%). A análise dos padrões de fratura foram analisadas em estereomicroscopio. Adicionalmente foram confeccionados 15 espécimes em cerâmica no formato cilíndrico, submetidos aos mesmo tratamentos dos grupos anteriores (n=3) e utilizados para análise do ângulo de contato e análise em microscópio eletrônico de varredura. O teste de Dunnet mostrou diferenças significativas entre o grupo controle (9,42 ± 2,27 MPa) e os grupos Er (19,25 ± 3,7 MPa) e Sil+Er (14,11 ± 4,11 MPa). A análise de variância (p<5%) para os fatores Tipo de Laser (p<0,0001) e Técnica de Silanização (p=0,0002) mostraram diferenças significativas para os dois fatores, porém não para sua interação. Assim, a irradiação com Er:YAG (16,68 MPa) mostrou-se mais eficiente que a irradiação com Nd:YAG (8,19 MPa). A técnica de silanização posterior à irradiação com laser (14,46 MPa) também se mostrou superior à silanização previa (10,41 MPa). Quanto à análise de fraturas, o grupo Controle teve prevalência de falhas adesivas em dentina e em cerâmica; os grupos Nd, Sil + Nd e Sil + Er tiveram prevalência de falhas adesivas em cerâmica, e o grupo Er apresentou predominância de falhas coesivas no cimento. A análise do ângulo de contato foi submetida aos testes ANOVA 1-fator e Tukey, apresentando diferenças significativas entre os grupos (p<0,0001). Os grupos com silanização prévia (Sil + Er = 45,60b graus; Sil + Nd = 52,10b graus) apresentaram ângulos de contato superiores aos demais, e semelhantes entre si. As imagens de Microscopia Eletrônica de Varredura mostram a presença da camada de silano sobre a superfície cerâmica no grupo Sil + Nd, e uma aparente fundição à superfície cerâmica no grupo Sil + Er. Para os Grupos Er e Nd foi possível verificar modificações no padrão normal da estrutura da cerâmica, entremeadas por áreas semelhantes ao padrão convencional do grupo Controle após condicionamento com ácido hidrofluorídrico. Conclui-se que o tratamento com laser de Érbio associado ao condicionamento com ácido hidrofluorídrico a 10% por 1 min apresenta os melhores resultados de resistência de união e ângulo de contato. O tratamento com silano previamente à irradiação melhorou a resistência de união em relação ao grupo Controle apenas quando associado ao laser de Érbio. / The aim of this study was to evaluate the efficiency of irradiation with high-power lasers and the influence of silane application before or after irradiation with lasers on the bond strength between lithium disilicate glass-ceramic, resin cement and human dentin. Fifty truncated-cones ceramic specimens (n=10) were randomly divided into 5 groups: Control- etching with hydrofluoric acid 10% for 1 min and application of silane; 2- Er - Er:YAG laser irradiation (200 mJ and 10 Hz), followed by etching with hydrofluoric acid 10% for 1 min and application of silane; 3- Sil + Er - etching with hydrofluoric acid 10% for 1 min, silane application and irradiation with Er: YAG laser in the same parameters as the previous group; 4- Nd:YAG laser - irradiation with Nd: YAG laser (120 mJ and 10 Hz), followed by etching with hydrofluoric acid 10% for 1 min and application of the silane, 5- Sil + Nd- Etching with hydrofluoric acid 10% for 1 min, silane application and irradiation with Nd: YAG laser on the same parameters as the previous group. After treatment, the ceramic specimens were cemented with dual cure resin cement to the dentin of 50 human molars included in acrylic resin. After storage for 24 h it was submitted to tensile test in a universal testing machine with 10 kgf load cell and constant speed of 1 mm/min. Data were submitted to ANOVA 2-way and Dunnet test (α = 5%). The analysis of fracture patterns were analyzed in stereomicroscope. In addition were made 15 ceramic specimens in cylindrical shape, subjected to the same treatment of the above groups (n = 3) and used for analysis of the contact angle analysis and scanning electron microscope. The Dunnet test showed significant differences between Control group (9.42 ± 2.27 MPa) and Er group (19.25 ± 3.7 MPa) and Sil + Er (14.11 ± 4.11 MPa). ANOVA 2-way (p <5%) for Laser Type (p <0.0001) and Technical of Silanization (p = 0.0002) showed significant differences for both factors, but not for their interaction. Thus, the irradiation with Er:YAG laser (16,68 MPa) was more effective than irradiation with Nd:YAG laser (8,19 MPa). The technique of silanization after laser irradiation was more effective (14,46 MPa) than the previous silanization (10,41 MPa). The analysis of fractures showed a prevalence of adhesive failures on dentin and ceramic for the Control group; Nd, Sil + Nd e Sil + Er had a prevalence of adhesive failures in ceramics, and Er group presented predominance of cohesive failures in cement. The analysis of contact angle was submitted to ANOVA 1-way and Tukey test, with significant differences between the groups (p <0.0001). Groups with silanization previous to laser irradiation (Sil + Er = 45,60b degrees; Sil + Nd = 52,10b degrees) had contact angles greater than the other groups. The Scanning Electron Microscopy images showed the presence of a silane layer on the ceramic surface in Sil + Nd group, and an apparent casting of the ceramic surface in Sil + Er group. For Er and Nd Groups was possible to see changes in the normal pattern of ceramic structure, interspersed with areas similar to conventional standard control group after etching with hydrofluoric acid. It is concluded that treatment with Er:YAG laser associated with etching with hydrofluoric acid at 10% for 1 min gives the highest bond strength results and the lower contact angle, resulting in a recommended treatment. Treatment with silane previously to laser irradiation improved bond strength only when associated with the Er:YAG laser, which probably occurred by the efficiency of Er: YAG laser irradiation, and not due to the silanization technique.

Orientador: Marcelo Ferrarezi de Andrade / Banca: Vanderlei Salvador Bagnato / Banca: José Eduardo Pelizon Pelino / Resumo: Este estudo avaliou a resistência adesiva de microtração em reparos de resinas compostas, novas e envelhecidas, após tratamento da superfície usando irradiação a laser de Er: YAG, ponta diamantada e abrasão a ar. 36 blocos de resina composta híbrida Z100 (3M) com 5mm de comprimento e 6 mm de lado foram confeccionados com auxílio de uma matriz. Metade desses blocos foram reparados após 24 horas, e a outra metade foi reparada após envelhecimento artificial com luz ultravioleta. Cada grupo foi subdividido em 6 subgrupos e as superfícies experimentais foram submetidas a diferentes tratamentos: (G1) desgaste com ponta diamantada; (G2) jateamento com partículas de óxido de alumínio de 60 mm; (G3) ablação com laser de Er: YAG a um nível de energia de 100mJ; (G4) ablação com laser de Er:YAG a um nível de energia de 200mJ; (G5) ablação a laser de Er:YAG a um nível de energia de 300mJ; (G6) controle- ausência de tratamento de superfície. Após tratamento da superfície, o agente adesivo (Single Bond 3M) foi aplicado e os blocos foram reparados com a resina composta Point4 (KERR). Reparados, os blocos foram seccionados em espécimes de 1.0 mm2. A resistência adesiva de microtração foi medida em uma máquina de teste universal MTS. No grupo que foi reparado 24 horas após, não houve diferença estatisticamente significante na resistência adesiva interfacial entre os subgrupos. No grupo que foi envelhecido, os subgrupos G1 e G3 tiveram as maiores médias de resistência adesiva de reparo. Significantemente, os menores valores foram achados para os subgrupos G2 e G6. As médias da resistência adesiva de reparo foram estatisticamente similares para G3, G4 e G5. O exame em SEM indicou que a fratura adesiva foi o tipo predominante de falha. Os resultados desse estudo indicam que os maiores valores de resistência adesiva foram achados para o desgaste da superfície com... (Resumo completo, clicar acesso eletrônico abaixo). / Abstract: This study assessed the microtensile bond strengths of composite repairs, new and aged, after surface treatments, using Er:YAG laser irradiation, diamond bur and air abrasion. 36 blocks of hybrid composite resin Z100 (3M) with 5.0 mm length and 6.0 mm of side were made in mold. Half of these blocks were repaired after 24 hr and the other half was aged in an artificial aging chamber with exposure to a total ultraviolet irradiation. Each group was then divided into six subgroups and the experimental surface was exposed to a different treatment: (G1) grinding with diamond burs; (G2) air-abraded with 60mm aluminum oxide particles; (G3) ablation with an Er: YAG laser under the energy level of 100 mJ; (G4) ablation with an Er: YAG laser under the energy level of 200 mJ; (G5) ablation with an Er: YAG laser under the energy level of 300 mJ; (G6) controle - with no surface treatment. After the resin treatment on the surface, the bonding agent (Single bond, 3M) was applied and the blocks were repaired with the resin Point4 (Kerr) composite. Repaired, the blocks were sectioned into specimens (stick) of 1.0 mm2. Microtensile bond strength was measured in a universal testing machine MTS. The group repaired after 24 hours did not present statistically significant differences on interfacial bond strengths between the subgroups. On the aged group, the subgroups G1 and G3 presented the highest mean of repairing bond strenght. Significant lower values were found for subgroups G2 and G6 .The mean of repairing bond strenght was statistically similar for G3, G4 and G5. SEM examination indicated that adhesive failure was the predominant mode of failure. The results of this study indicate that the highest bond values were achieved by grinding the surface with diamond burs and ablating the surface with an Er: YAG laser under the energy level of 100mJ... (Complete abstract, click electronic address below). / Mestre

Er: YAG laser is a new method of preparation that promises gentler and more accurate dental treatment. Its specific characteristics is large absorption of the beam in the water and a small absorption in the tissue without the thermal effect. Therefore the treatment is safer and effectiver. The research has the aim in its theoretical - cognitive part to assess its advantages in comparison with treaditional treatment method - drill. As an essential element will be evaluation of caries lesion in vitro and in vivo. The size of the cavity will be judged on, the shape of developing a smear layer and retention surface in relation to the filling and the . The extracted teeth will be scanned in electronic microscope to assess the formation of contact and non-contact preparation, focusing on the shape and size of the prepared lesion in relation to modern filling materials - low viscosity composites. Extensive research supported by the Ministry of Health (IGA : 9991-4 and 13351-4) that focuses on the the use of various therapeutic methods in the treatment of special needs patients. Dental treatment of a special needs patients is expensive and time-consuming than conventional dental treatment. Therefore, clinical application of theoretical cognitive part will create a electronical support system for the...

Este estudo longitudinal investigou a influência de tratamentos de superfície com o laser de Er:YAG com 50?s de largura de pulso sobre a adesão de dois sistemas adesivos autocondicionantes (SA) em dentina hígida (DH) e dentina afetada por cárie (DAC) através dos teste de resistência de união (RU) de microcisalhamento (?SBS), teste de ultramicrodureza da camada de adesivo (NdA) e da camada híbrida (NdCH), além de análise da interface adesiva com microscopia eletrônica de varredura (MEV). A análise qualitativa dos tratamentos de superfície realizados foi executada através de MEV e microscopia eletrônica de transmissão (MET). A dentina oclusal planificada de 215 molares humanos foi protegida com verniz ácido resistente, exceto em janela de 4x5mm para produção de DAC artificial após 7 dias de desafio cariogênico com biofilme de S. mutans, permitindo dados pareados por substrato. Os espécimes foram divididos nos grupos experimentais de acordo com: tratamento de superfície [controle-sem tratamento-(G1); Laser 80-80mJ, 2 Hz, 12.58J/cm2-(G2); Laser 50-50mJ, 10 Hz, 9.4J/cm2-(G3)]; sistema adesivo [Clearfil SE Bond(CF) e Single Bond Universal(SB)]; substrato [DH(h) ou DAC(a)] e tempo de armazenamento em saliva artificial [24 horas (24) ou 1 ano (1)], compondo 24 grupos experimentais: CFG1h24; CFG1h1; CFG1a24; CFG1a1; CFG2h24; CFG2h1; CFG2a24; CFG2a1; CFG3h24; CFG3h1; CFG3a24; CFG3a1; SBG1h24; SBG1h1; SBG1a24; SBG1a1; SBG2h24; SBG2h1; SBG2a24; SBG2a1; SBG3h24; SBG3h1; SBG3a24; SBG3a1. Nos grupos tratados com laser a largura temporal de pulso foi ajustada em 50?s. A resina composta Z350XT foi utilizada para a confecção dos corpos de prova. Os sistemas adesivos foram aplicados de acordo com as instruções do fabricante. As análises de MEV e MET de superfície avaliaram somente o efeito dos tratamentos em ambos os substratos testados. Os valores de RU e de nanodureza foram analisados através do teste de ANOVA (três fatores) e do teste de comparações múltiplas de Tukey (?=0,05). Para o teste de ?SBS, para ambos os SA, e todos tratamentos de superfície, a DAC apresentou valores de RU menores comparados à DH; a influência do armazenamento em saliva artificial foi substrato dependente: corpos de prova obtidos com DAC apresentaram queda nos valores de RU após 1 ano de armazenamento, enquanto nenhuma diferença entre os grupos experimentais foi observada em dentina hígida. NdA revelou que apenas os corpos de prova construídos com CF apresentaram redução dos valores após 1 ano. A NdCH obtida com CF e SB, resultou em menores valores em DAC comparada à DH, após 1 ano de armazenamento ambos os substratos apresentaram redução da NdCH, para todos tratamentos de superfície. A MEV revelou que todas as interfaces adesivas, especialmente aquelas obtidas em DAC, sofreram degradação intensa após 1 ano. Os tratamentos com Laser 80 e Laser 50 promovem alteração superficial característica de ablação em DAC e DH, conforme observado em MEV de superfície, e alterações de fibrilas colágenas observadas em MET. Independentemente dos SA, a adesão e nanodureza em DAC é menor que em DH. Todas as interfaces adesivas obtidas foram sensíveis ao armazenamento em saliva artificial por 1 ano. A adesão não foi influenciada pelo tratamento com o laser Er:YAG com 50?s de largura de pulso. / This longitudinal study investigated the influence of super short pulse Er:YAG laser treatment on microshear bond strength (?SBS), adhesive and hybrid layer nanohardness test and qualitative interface scanning electron microscopy (SEM) of two self-etch adhesive systems to sound (SD) and caries-affected like dentin (CAD). Additionally, qualitative investigation of surface treatments by SEM and transmission electron microscopy (TEM) were performed. CAD lesions (4x5mm) were produced by 7 days S. mutans biofilm cariogenic challenge in 215 human ground flat human dentin specimens, enabling paired data by substrate. Specimen were divided in groups according to surface treatment [control-no treatment-(G1); Laser 80-80mJ, 2Hz, 12.58J/cm2-(G2); Laser 50-50mJ, 10Hz, 9.4J/cm2-(G3)]; self-etching adhesive system [Clearfil SE Bond(CF) and Single Bond Universal(SB)]; substrate [SD(h) or CAD(a)] and artificial saliva storage [24 hours(24) or 1 year(1)]: CFG1h24; CFG1h1; CFG1a24; CFG1a1; CFG2h24; CFG2h1; CFG2a24; CFG2a1; CFG3h24; CFG3h1; CFG3a24; CFG3a1; SBG1h24; SBG1h1; SBG1a24; SBG1a1; SBG2h24; SBG2h1; SBG2a24; SBG2a1; SBG3h24; SBG3h1; SBG3a24; SBG3a1. Pulse duration was set in 50?s for laser groups. ?SBS, nanohardness and interface SEM specimen preparation was constructed with Z350XT composite resin. Adhesive systems were applied according to manufacturer\'s instructions. Surface SEM and TEM specimen only evaluated treatment effects on distinct substrates. The ?SBS and nanohardness means were analysed using three-way ANOVA and Tukey´s multiples comparisons test (?=0.05). For ?SBS test, for both adhesive systems, and all surface treatments, CAD revealed lower ?SBS values compared to SD; the influence of artificial saliva storage was substrate dependent. CAD specimens resulted in lower ?SBS values after 1 year, while no difference among experimental groups was observed in SD. The adhesive layer (AL) nanohardness statistical evaluation revealed that only CF specimens decreased the AL nanohardness after 1 year of storage. The hybrid layer (HL) produced with CF and SB, resulted in lower nanohardness values for CAD than SD, which reduces after 1 year storage, for all surface treatments. Interface SEM analysis revealed that all adhesive interfaces, especially those in CAD, have experienced degradation after 1 year of storage. Laser 80 and Laser 50 promotes surface ablation characteristics in CAD and SD, as noted in surface SEM and collagen fibrils alterations observed in TEM. Despite of adhesive systems, bonding and nanohardness to CAD is lower than to SD. All tested adhesive interfaces were sensitive to saliva storage. Surface treatment with 50?s Er:YAG laser did not influence on bonding.