Submitted by (edna.saturno@ufrpe.br) on 2016-11-04T12:11:59Z No. of bitstreams: 1 Roberto Romulo Ferreira da Silva.pdf: 3155721 bytes, checksum: 3e1007b29d728c7b43b0e1cf83f48040 (MD5) / Made available in DSpace on 2016-11-04T12:11:59Z (GMT). No. of bitstreams: 1 Roberto Romulo Ferreira da Silva.pdf: 3155721 bytes, checksum: 3e1007b29d728c7b43b0e1cf83f48040 (MD5) Previous issue date: 2008-02-29 / The aim of this study was to evaluate the effects of 0.5% sodium hypochlorite (NaClO) in the healing of open wounds in the skin, induced experimentally in 24 rats(Rattus norvegicus albinus), 4 months of age, male, weighing approximately 250g. Two surgically injuries were performed in the right and left lateral sides of the chest. The wound located into the right antimere was treated with 0.5% NaClO and the contralateral wound received 0.9 %. sodium chloride (NaCl) solution. To measure the wounds contraction, morphometric analysis were accomplished at the beginning of the experiment (time zero) and post-surgery at times 3, 7 and 14 days. The data were statistically analyzed by the Uniformity KS test, and the groups were compared by ANOVA and TUKEY tests. The histopathological analysis of the post-surgical injuries’ fragment showed that the wounds treated with 0.5% NaClO presented greater contraction at day 14 compared to those treated with 0.9% NaCl. In addition an expressive decrease in the neovascularization at day 14 and a greater tendency to the organization of fibrous tissue at day 21 were observed in the lesions treated with 0.5 % NaClO. However, no statistical difference (p ≤ 0.05) was observed for each time trial in both treatments. Nevertheless, it was observed that 0.5% NaClO caused greater reduction in the treated wounds and therefore this antiseptic could be suggested as an alternate treatment for open wounds in the Veterinary Medicine. / Este trabalho objetivou avaliar os efeitos do hipoclorito de sódio (NaClO) 0,5% na cicatrização de feridas cutâneas abertas, induzidas experimentalmente em 24 ratos (Rattus norvegicus albinus), com 4 meses de idade, machos,pesando aproximadamente 250g. Foram realizadas cirurgicamente duas feridas nas faces laterais direita e esquerda do tórax, sendo que na ferida do antímero direito foi utilizado borrifamento com solução de hipoclorito de sódio 0,5% e na ferida contralateral, empregou-se solução de cloreto de sódio (NaCl) 0,9%. Realizaram-se avaliações morfométricas para avaliar a contração das feridas no início do experimento (tempo zero) e nos tempos experimentais 3, 7 e 14 dias pósoperatório (PO), sendo submetidas à análise estatística pelo teste de Homogeneidade K-S, e em seguida os grupos foram comparados através dos testes ANOVA e pós-teste de TUKEY. Fragmentos das lesões nos tempos experimentais 3, 7, 14 e 21 dias pós-operatórios foram submetidos a exames histopatológicos. A análise da evolução das feridas considerando-se cada tratamento isoladamente, demonstrou que as feridas tratadas com NaClO 0,5% apresentaram maior contração com 14 dias PO quando comparadas àquelas tratadas com NaCl 0,9%. A histopatologia demonstrou expressiva regressão da neovascularização aos 14 dias PO e maior tendência à organização do tecido fibroso aos 21 dias, nas lesões tratadas com NaClO 0,5%. Entretanto, não se observou diferença estatística significante para p ≤ 0,05 quando se comparou os dois tratamentos, a cada tempo experimental. Apesar disso, observou-se que o NaClO 0,5% provocou maior redução nas feridas tratadas e portanto sugere-se que este antisséptico possa ser utilizado como tratamento alternativo de feridas abertas em Medicina Veterinária.

Orientador: Caio Cezar Randi Ferraz / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-16T22:03:38Z (GMT). No. of bitstreams: 1 Kawagoe_ShaianaTashy_M.pdf: 2714587 bytes, checksum: deecc48f9db412f90441b3916f405a0e (MD5) Previous issue date: 2010 / Resumo: O prognóstico do tratamento endodôntico é favorecido quando se sela corretamente o acesso coronário logo após a conclusão da terapia endodôntica, evitando, desta forma, a recontaminação do sistema de canais radiculares e minimizando o risco de fratura. Devido às suas excelentes propriedades mecânicas e de selamento, os sistemas adesivos são considerados materiais de escolha para a restauração definitiva e imediata desses dentes. No entanto, os efeitos adversos relacionados ao tipo de substância química auxiliar endodôntica utilizada, assim como sua influência na resistência e na longevidade adesiva, carecem de maiores esclarecimentos. O presente estudo teve por objetivo analisar a resistência e a longevidade adesiva de 2 sistemas (Scotchbond Multi Purpose e Clearfil SE Bond), aplicados em dentina radicular bovina tratada com diferentes substâncias químicas auxiliares (clorexidina gel 2%, EDTA a 17% e hipoclorito de sódio (NaOCl) 5,25% associado ou não ao ascorbato de sódio 10%), além de avaliar a importância das fibrilas colágenas na adesão. As amostras foram submetidas a ensaios mecânicos de cisalhamento por extrusão, após imersão em água, nos intervalos de 1 dia e 1 ano. Como controle de longevidade, parte da amostragem permaneceu imersa em óleo mineral também por 1 ano. Posteriormente, o padrão de fratura foi analisado em uma lupa estereoscópica (25X), e classificado em: adesivo (interface dentina resina), coesivo (em dentina, em camada híbrida, em resina ou no pino) ou misto (envolvendo 2 ou mais substratos). Após a análise dos resultados foi possível concluir que: O sistema Scotchbond Multi Purpose apresentou os melhores resultados. O NaOCl reduziu os valores de resistência adesiva imediata, quando utilizado como substância química auxiliar ou quando empregado na desproteinização. O uso do ascorbato de sódio após a utilização do NaOCl restabeleceu os valores de adesão. A desproteinização e a aplicação de clorexidina conservaram os valores de resistência adesiva inalterados após 1 ano. / Abstract: The prognosis of the endodontic treatment is improved by a correct sealing of the coronal access soon after the root canal obturation, preventing the root canal system recontamination and minimizing the risk of fracture. Due to their excellent mechanical properties and sealing ability, the adhesive systems are considered choice material for teeth restoration. However, the adverse effects related to the type of auxiliary chemical substances used during the endodontic treatment, as well as its influence on the adhesive strength and longevity need greater clarification. The objective of the present study was to examine the adhesive strength and longevity 2 adhesive systems (Scotchbond Multi Purpose and Clearfil SE Bond), applied in radicular dentin treated with different auxiliary chemical substances (2% chlorhexidine gel, EDTA 17% and 5.25% sodium hypochlorite (NaOCl) associated or not to sodium ascorbate 10%), and evaluate the importance of the collagen fibers in adhesion process. The shear bond strength was assessed after 1 day or 1 year in water immersion. As longevity control, part of the sample was kept submerged in mineral oil for 1 year. Subsequently, the fracture pattern was analyzed using a stereomicroscope (25 X), and classified as: adhesive (dentin/resin interface), cohesive (in dentin, layer hybrid resin or post) or mixed (involving 2 or more substrates). After the data analysis it was concluded that: the Scotchbond Multi Purpose presented the best results. The NaOCl reduced the immediate adhesive resistance when used as an endodontic auxiliary chemical substance or when employed in deproteinization. The use of sodium ascorbate after using the NaOCl re-established the adhesion values. The deproteinization and chlorhexidine use kept the adhesive strength values unchanged after 1 year. / Mestrado / Endodontia / Mestre em Clínica Odontológica

Orientador: Brenda Paula Figueiredo de Almeida Gomes / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-12T19:24:46Z (GMT). No. of bitstreams: 1 Sena_NeyllaTeixeira_D.pdf: 3038730 bytes, checksum: 1cacde1c32eceda5813f7908699bd2f9 (MD5) Previous issue date: 2009 / Resumo: Este estudo investigou: a) a atividade antimicrobiana de cimentos endodônticos (AH Plus e Epiphany) frente a microrganismos encontrados na microbiota intracanal (Enterococcus faecalis, Staphylococcus aureus, Actinomyces naeslundii e Candida albicans); b) a microinfiltração coronária de dentes obturados com AH Plus/ guta-percha e Epiphany/ Resilon; c) os possíveis efeitos antimicrobianos residuais destas substâncias nos cones quando em contato com E. faecalis e Porphyromonas gingivalis, d) as alterações na superfície dos cones de guta-percha e Resilon expostos à desinfecção com clorexidina gel 2% e hipoclorito de sódio 5,25%. A ação antimicrobiana dos cimentos foi testada através de dois métodos: o de contato direto nos tempos: imediato, 24 h, 48 h, 7 e 14 dias após a espatulação, e através do teste de difusão em Agar. A avaliação da microinfiltração coronária de dentes obturados endodonticamente foi acompanhada diariamente por 90 dias após a contaminação. A ação residual dos agentes desinfetantes sobre a superfície dos cones foi observada através do método de difusão em Agar (nos períodos de 1, 5, 10, 20 e 30 min), e as alterações estruturais na superfície dos cones foram testadas através de análise em Microscópio Eletrônico de Varredura (MEV). Quanto ao método de contato direto os resultados foram: O cimento AH Plus teve maior atividade antimicrobiana que o Epiphany, o Epiphany apresentou grande dissolução em todos os tempos testados (p<0.05), A. naeslundii foi o microrganismo mais suscetível e E. faecalis o mais resistente a todos os cimentos testados. Quanto ao método de difusão em Agar a maior atividade antimicrobiana foi a do Primer, seguida do AH Plus e do Epiphany. C. albicans foi o microrganismo mais suscetível e o S. aureus o mais resistente. Quanto à prevenção da microinfiltração coronária, AH Plus/guta-percha foi superior ao sistema Epiphany (p<0.05). Os dentes obturados com o sistema Epiphany apresentaram clinicamente alterações de cor em suas raízes. Quanto à atividade antimicrobiana das substâncias químicas auxiliares sobre os cones, estas foram incapazes de se unirem aos componentes dos cones de guta-percha e de apresentarem efeito residual. Entretanto o cone de Resilon apresentou ação antibacteriana residual quando exposto a clorexidina gel. Quanto às alterações estruturais dos cones em MEV, não foi encontrada modificação nas características superficiais dos cones e nem presença de cristais de cloreto. Em conclusão, os resultados sugerem que o sistema Epiphany não demonstrou ser superior ao AH Plus quanto à ação antimicrobiana e à prevenção da microinfiltração coronária, e que as substâncias químicas auxiliares usadas na desinfecção dos cones de guta-percha e de Resilon não apresentaram ação residual nos cones de guta-percha e nem alteraram a superfície dos dois tipos de cones testados. Entretanto o cone de Resilon apresentou ação antibacteriana residual quando exposto à clorexidina gel. / Abstract: The aims of the present study were to investigate: a) the antimicrobial property of endodontic sealers (AH Plus and Epiphany) against the following microorganisms: Enterococcus faecalis, Staphylococcus aureus, Actinomyces naeslundii and Candida albicans; b) the coronal microleakage of teeth obturated with AH Plus/ gutta-percha and Epiphany/ Resilon; c) to evaluate the alterations on the surface of the gutta-percha and Resilon cones disinfected with 2% CHX-gel and 5.25% NaOCl; d) the possible residual antimicrobial properties of these substances on the cones when in contact with E. faecalis and Porphyromonas gingivalis. The antimicrobial properties of endodontic sealers were tested by two methods: the direct contact at different times (immediately, 24/ 48 hours and after 7/14 days) and the Agar diffusion method. The coronal microleakage was followed daily during 90 days after contamination. The residual property of the disinfectant agents on the cones was tested by the Agar diffusion method (at 1, 5, 10, 20 and 30 min) and the alterations on the surface structure of the cones were observed by the Scanning Electron Microscopy (SEM) analysis. Regarding the direct contact method, the results are: the AH Plus sealer showed greater antimicrobial than the Epiphany; Epiphany presented greater dissolution during all tested times (p< 0.05). A. naeslundii was the most susceptible microorganism and S. aureus the most resistant against all tested sealers. Regarding the Agar diffusion method, the greatest antimicrobial activity was achieved by the primer, followed by AH Plus and Epiphany. C. albicans was the most susceptible microorganism, while S. aureus was the most resistant. Regarding the prevention of the coronal microleakage, AH Plus/ gutta-percha presented better results than the Epiphany system (p<0.05). All teeth filled with Epiphany system presented color alteration on the root surface. Regarding the antimicrobial property of the auxiliary chemical substances on the cones, both chemical agents were unable to bind to the gutta-percha cone components and to release themselves into the Agar medium during all the periods of time tested. Nevertheless, when disinfected with 2% CHX gel, the Resilon cone demonstrated a residual action. Regarding the residual property of the disinfectants on the surface of the cones, SEM analysis showed no alteration on their superficial features. In conclusion, the results suggest that the Epiphany system was not superior to the AH Plus regarding the antimicrobial action and the prevention of the coronal microleakage, and the auxiliary chemical substances used in the disinfection of gutta-percha and Resilon cones did not show any residual action on the gutta-percha cones and did not cause any damage on the surface of both types of cones. However, the Resilon cones showed a residual antibacterial action when exposed to the chlorhexidine gel. / Doutorado / Endodontia / Doutor em Clínica Odontológica

Orientadores: Yoon Kil Chang, Manuel Salvador Vicente Plata Oviedo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia de Alimentos / Made available in DSpace on 2018-08-13T03:16:39Z (GMT). No. of bitstreams: 1 Conto_LeilaneCostade_M.pdf: 2123146 bytes, checksum: 3aa7f490a9b5357b74bc04129c3d30a7 (MD5) Previous issue date: 2009 / Resumo: O pinhão, semente da Araucaria angustifolia (Betortoloni, Otto Kuntze), possui alto teor de carboidratos, principalmente amido. A literatura escassa e contraditória, em alguns pontos, indica a necessidade de um conhecimento aprofundado sobre as características do amido de pinhão, principalmente voltado ao método de extração e à modificação química para a obtenção de características específicas para sua aplicação. O presente trabalho procurou: estudar a extração de amido de pinhão por três metodologias distintas (Wosiacki e Cereda, Bello-Pérez et al. E Teixeira et al .- modificada) com e sem estocagem prévia dos pinhões; estudar as propriedades químicas, físicas e reológicas do amido nativo de pinhão extraído de sementes armazenadas por longos períodos e estudar o efeito da temperatura de processo e da concentração de cloro ativo na modificação química por oxidação nas principais propriedades do amido de pinhão. Todos os dados obtidos foram avaliados estatisticamente por análise de variância e teste de médias de Tukey (p < 0,05). Das três metodologias de extração utilizadas para pinhões in natura com 0 e 12 meses de estocagem, o método proposto por Bello-Pérez et al. (2006) foi considerado o mais apropriado a ser utilizado na extração do amido devido ao maior rendimento observado após a constatação de que o tempo de estocagem influencia nas características de rendimento e coloração do amido de pinhão. O amido de pinhão obtido por este método apresentou 14,37% de umidade, 0,06% de proteínas, 0,29% de fibra bruta, 0,06% de matéria mineral, 1,34% de lipídios e 27,25% de amilose (b.s). Os grânulos do amido de pinhão foram de tamanhos e formatos irregulares, predominando as formas arredondadas e ovais, com presença marcante da cruz de Malta. Na oxidação do amido do pinhão, amostras foram tratadas com hipoclorito de sódio nas concentrações de 0,5 g, 1,0 g, 2,25 g, 3,5 g e 4 g de cloro ativo por 100 g de amido nas temperaturas de 20 ºC, 23 ºC, 32 ºC, 41 ºC e 45 ºC. O efeito das variáveis independentes foi avaliado através do Método de Superfície de Resposta, seguindo um Delineamento Composto Central Rotacional 22, com 4 pontos centrais e 4 pontos axiais. A aplicação de hipoclorito de sódio no amido de pinhão obtido de matéria-prima estocada, extraído segundo Bello-Pérez et al., proporcionou modificações nas suas principais propriedades tecnológicas. A concentração de cloro ativo exerceu efeito significativo sobre o índice de solubilidade em água, o teor de carboxilas e carbonilas, o teor de amilose e o percentual de transmitância de luz (650 nm) do amido de pinhão. O efeito da temperatura como variável independente foi observado apenas no índice de solubilidade em água, no teor de carbonilas e no percentual de transmitância de luz (650 nm) do amido de pinhão. A oxidação foi mais intensa quando o amido foi tratado com 3,5% de cloro ativo, seguido do tratamento com 4% de cloro ativo, onde foram observados o aumento no teor de carboxilas e carbonilas e a redução do teor de amilose / Abstract: The Brazilian pine, seed of Araucaria angustifólia (Betortoloni, Otto Kuntze), has a high carbohydrate content, principally starch. The literature is scarce and contradictory in some points, indicating the need for a profound understanding of the characteristics of the starch of this pine, mainly with respect to extraction methods and to chemical modification to obtain specific characteristics for defined applications. The present study aimed at the following: to study the extraction of starch from Brazilian pine seeds by three distinct methodologies (Wosiacki & Cereda, Bello-Pérez et al. and Teixeira et al. - modified) with and without storage of the seeds; to study the chemical, physical and rheological properties of the native starch extracted from seeds stored for long periods, and to study the effect of the process temperature and active chlorine concentration on the chemical modification by oxidation of the main properties of the Brazilian pine starch. All the data obtained were statistically evaluated using the variance analysis and Tukey¿s means test (p = 0.05). Of the three extraction methodologies used on in natura Brazilian pine seeds stored from 0 to 12 months, the method proposed by Bello- Pérez et al. (2006) was considered to be the best for the extraction of starch, after showing that the storage time influences the characteristics of yield and color of the pine starch. The Brazilian pine starch obtained presented 14.37% moisture content, 0.06% proteins, 0.29% crude fiber, 0.06% mineral matter, 1.34% lipids and 27.25% amylose (d.w.b.). The starch granules showed irregular sizes and forms, oval and rounded forms predominating, with a marked presence of the Maltese cross. In the oxidation of the pine starch, the following concentrations of sodium hypochlorite were used: 0.5 g, 1.0 g, 2.25 g, 3.5 g and 4 g of active chlorine per 100 g starch, at temperatures of 20 ºC, 23 ºC, 32 ºC, 41 ºC and 45 ºC. The effect of the independent variables was evaluated using response surface methodology with a complete compound rotational design (22 with 4 central points and 4 axial points). The application of sodium hypochlorite to pine starch extracted from the stored raw material, extracted according to Bello-Pérez et al. (2006), resulted in modifications of the principle technological properties. The active chlorine concentration exerted a significant effect on the water solubility index, the carbonyl and carboxyl contents, the amylase content and the percentage of light transmittance (650 nm) of the Brazilian pine starch. The effect of temperature as an independent variable was only observed on the water solubility index, the carbonyl content and the percentage of light transmittance (650 nm) of the Brazilian pine starch. Oxidation was more intense when the starch was treated with 3.5% active chlorine, followed by the treatment with 4% active chlorine, where increases in the carboxyl and carbonyl contents and reductions in the amylase content were observed / Mestrado / Mestre em Tecnologia de Alimentos

Orientador: Regina Maria Puppin-Rontani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-09T19:32:12Z (GMT). No. of bitstreams: 1 Borges_AnaFlaviaSanches_D.pdf: 9249860 bytes, checksum: 185c997bcd0228668822df9171b2e4c2 (MD5) Previous issue date: 2007 / Resumo: Teoricamente, o suposto menor grau de mineralização da dentina decídua comparado à permanente, produziria comportamento diferente deste substrato após contato com soluções desproteinizantes/desmineralizantes, seguido de restaurações com materiais resinosos. O objetivo deste estudo foi fornecer novas informações científicas nos campos químicos, mecânico e morfológico em relação à qualidade do conteúdo mineral e orgânico da dentina decídua em comparação ao conteúdo da dentina permanente, após a ação de soluções desmineralizante/desproteinizante. No intuito de facilitar a apresentação desta tese, a mesma foi dividida em dois estudos, como descrito nas proposições seguintes. Estudo 1: Identificar a dentina decídua em comparação à permanente, na região de dentina média, após condicionamento com ácido fosfórico 35%. As análises foram: Espectroscopia Raman Transformada de Fourier (FT-Raman), Microscopia Eletrônica de Varredura/Espectroscopia de Energia Dispersiva (MEV/EED) e microdureza Knoop. Dez molares humanos, 5 decíduos e 5 permanentes, foram desgastados com fresa carbide até a dentina média e seccionados no sentido mesio-distal e vestíbulo-lingual, longitudinalmente. Metade da amostra foi destinada à espectroscopia FT-Raman e metade ao teste de dureza Knoop. Os grupos estudados foram (n=10): G1 (smear layer decídua); G2 (dentina decídua + ácido fosfórico 35%); G3 (smear layer permanente); G4 (dentina permanente + ácido fosfórico 35%). Espectros resultantes da análise química foram submetidos à análise de Cluster, com base nos componentes principais identificados. Análise MEV/EED foi realizada para complementar os dados obtidos pelo FT-Raman. O ensaio micromecânico de dureza foi realizado para cada grupo (n=5). Cinco impressões foram feitas em cada espécime com 100 µm de distância entre cada impressão. A média de cada grupo foi calculada e os valores foram submetidos à ANOVA e teste de Tukey (p<0,05). A análise FT-Raman revelou diferença entre os grupos. Conteúdo inorgânico: G3 foi o mais diferente, seguido pelo G4, enquanto G1 e G2 foram os mais similares entre si. MEV/EDS identificou os elementos químicos C, O, P, Ca e Zn. Conteúdo orgânico: G2 mostrou ser o mais diferente de todos os grupos, seguido pelo G4, enquanto G1 e G3 foram os mais similares entre si. O teste de dureza revelou não haver diferença significativa entre G1 vs G3 e G2 vs G4 (p>0,05), porém houve diferença significativa entre G1 vs G2 e G3 vs G4 (p<0,05). Estudo 2: Avaliar por meio da FT-Raman e MEV, a dentina coronária das paredes laterais da câmara pulpar, decídua e permanente, após ação da solução NaOCl 1% seguido de condicionamento com ácido fosfórico a 35%, simulando as alterações que podem ocorrer em dentes tratados endodonticamente, os quais apresentam cavidade tipo classe I restaurada com compósito cujo sistema de união requer condicionamento ácido total. Vinte molares humanos, 10 decíduos e 10 permanentes, foram seccionados no sentido mesio-distal, longitudinalmente. As secções dentinárias foram distribuídas entre os grupos (n = 5): Dentes decíduos (Grupos 1, 2, 3 e 4); dentes permanentes (grupos 5, 6, 7 e 8) : G1 e G5 ¿ dentina; G2 e G6 ¿ dentina irrigada com NaOCl 1% (30 min); G3 e G7 - dentina irrigada com NaOCl 1% (30 min) e condicionada com ácido fosfórico 35%; G4 e G8 - dentina condicionada com ácido fosfórico 35%. Após a análise FT-Raman, todos os espécimes foram preparados e avaliados em MEV. As alterações morfológicas foram classificadas de acordo com score pré-estabelecido. Resultados: Conteúdo inorgânico: Houve nítida diferença entre a dentina que compõe a câmara pulpar decídua e permanente. G1 e G4 mostraram ser muito similares entre si, seguido do G2 que foi intermediário entre eles e G3. G6 e G7 também foram altamente similares entre si, seguido do G8 que foi intermediário entre eles e G5. Conteúdo orgânico: G7 e G8 foram muito similares entre si; G2 foi intermediário; G4 e G6 foram altamente similares entre si, bem como G3 e G5, os quais foram similares ao G1. As fotomicrografias demonstraram haver diferença morfológica entre os grupos não tratados, tratados com NaOCl e tratados com NaOCl seguido de condicionamento ácido, sendo que os grupos apenas condicionados não diferiram daqueles tratados e condicionados. Conclusão Geral: O arranjo molecular do conteúdo inorgânico dos dentes decíduos é qualitativamente diferente do arranjo molecular do conteúdo inorgânico dos dentes permanentes, tanto na dentina da região média coronária quanto da câmara pulpar, sendo o NaOCl um agente capaz de alterar o conteúdo inorgânico quimicamente, tanto na dentina decídua quanto na permanente, porém não morfologicamente caso seja tratado com NaOCl e seguido pelo condicionamento com ácido fosfórico / Abstract: Theoretically, it is supposed to have lower degree of mineralization for primary dentin compared with permanent one could lead different behavior of this substrate after contact with deproteinizating/demineralizating solutions, followed by composite restorations. The aim of this study was provide scientific informations at chemical, mechanical and morphological levels regarding the quality of inorganic and organic content of primary dentin compared to permanent one, as well as after deproteinizating/demineralizating solutions action. In order to facilitate the accomplishment of this thesis, it was divided into two phases, as described on the following descriptions: Study 1: To recognize the primary dentin compared to permanent dentin in the middle of crown, with or without 35% phosphoric acid total etching. The analyses were: Fourier Transformed Raman Spectroscopy (FT-Raman); Scanning Electron Microscopy/Energy-Dispersive Spectroscopy (EDS/SEM) and Hardness Micromechanical Test, related to molecular and micro-mechanical areas. Ten human molars, 5 primary and 5 permanent, were abrading with carbide bur until reach the middle dentin simultaneously to smear layer production. Four parts per tooth were obtained, half designed to FT-Raman spectroscopy and half to hardness test. The studied groups were (n=10): G1 (primary dentin smear layer); G2 (35% phosphoric acid etched primary dentin); G3 (permanent dentin smear layer); G4 (35% phosphoric acid etched permanent dentin). Result spectros from chemical analysis were subject to Cluster analysis based on identified principal components. The EDS/SEM analysis was done in order to add the FT-Raman data. To hardness test, 5 specimens were included, polished, cleaned, and etching (G2, G4) before the test. Five indentations were recorded to each specimen under middle dentin surface with 100 µm of distance each others beginning with 50 µm apart from JAD. A mean was calculated by each group and these values were recorded. The results were subjected to ANOVA and Tukey test. FT-Raman analysis showed difference among groups. Inorganic content: G3 was the most different, followed by G4, while G1 and G2 were the most similar to each other. EDS/SEM identified the C, O, P, Ca and Zn chemical elements in dentin. Organic content: G2 was the most different of all groups, followed by G4, while G1 and G3 were the most similar. There were no difference of hardness between G1 vs G3 and G2 vs G4 (p>0.05), however, there were difference between G1 vs G2 and G3 vs G4 (p<0.05). Study 2: FT-Raman and SEM were used to evaluate chemically and morphologically the coronary dentin of pulp chamber laterals walls after 1% NaOCl action followed by 35% phosphoric acid total etching. The aim of this study was to simulate the changes that can occur in endodontically treated teeth with type class I cavity restored with composite and total etching adhesive systems. Twenty human molars, 10 primary and 10 permanent, were sectioned mesio-distally paralleled to long axis of teeth. Two parts of dentin pulp chamber, buccal and lingual lateral walls, were obtained from each tooth, providing 20 parts to primary as well as to permanent teeth, followed by division into groups (n = 5): Primary teeth (Groups 1, 2, 3 and 4); permanent teeth (groups 5, 6, 7 and 8) : G1 and G5 ¿ pulp chamber dentin ; G2 and G6 ¿ pulp chamber dentin irrigated with 1% NaOCl (30 min); G3 e G7 - pulp chamber dentin irrigated with 1% NaOCl (30 min) and etched by 35% phosphoric acid; G4 e G8 - pulp chamber dentin etched by 35% phosphoric acid. After FT-Raman analysis, all specimens were prepared and evaluated by SEM. The morphological changes were classified according a score. Results: Inorganic content: There was a clear difference between primary and permanent dentin pulp chamber. Within this division, G1 and G4 showed very similar profile between them, followed by G2 that was intermediated between them and G3. G6 and G7 showed are very similar between them, followed by G8 that was intermediated between them and G5. Organic content: G7 and G8 were very similar between them; G2 showed be intermediate; G4 and G6 were very similar between them as well as G3 and G5 that, in turn, were quite similar to G1. The photomicrographs showed difference among non-treated groups, NaOCl treated groups and NaOCl treated followed by phosphoric acid etched groups. The groups only acid etched not differ from NaOCl treated followed by acid etched groups. Therefore, the inorganic content of primary teeth is qualitatively different from inorganic content of permanent ones, both in middle dentin of crown as well as in pulp chamber dentin, but not morphologically in case of NaOCl treatment followed by phosphoric acid treatment / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

Orientador: Rafael Leonardo Xediek Consani / Tese (doutorado) - Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-15T21:51:08Z (GMT). No. of bitstreams: 1 Lira_AndreaFabianade_D.pdf: 1753774 bytes, checksum: f60f5f6c197cc4eaf156bebf1bdc75a1 (MD5) Previous issue date: 2010 / Resumo: Este trabalho avaliou o efeito da termociclagem, escovação mecânica e desinfecção química na dureza e rugosidade de resinas com diferentes ciclos de polimerização. Foram confeccionadas 480 amostras (25 mm x 14 mm x 3 mm) e distribuídas aleatoriamente em 3 grupos de acordo com as resinas: Onda Cryl (G1), QC-20 (G2) e Clássico (G3). Metade das amostras foi submetida a ensaio de rugosidade e a outra metade a ensaio de dureza, antes e após os tratamentos: controle, escovação mecânica ou desinfecção química (hipoclorito e Efferdent) com e sem termociclagem. Amostras G1 foram confeccionadas, polimerizadas em micro-ondas com potência de 900 W; G2 foram polimerizadas a 100°C por 20 minutos e G3 foram polimerizadas a 74°C por 9h. As amostras foram desincluídas e acabadas em politriz com refrigeração à água, em ordem decrescente de granulação. A desinfecção química foi realizada com: 1) Hipoclorito de sódio a 0,5% a 37 ± 1ºC, durante 20 minutos; 2) Peróxido de Hidrogênio, a 37 ± 1ºC, durante 15 minutos. Após as desinfecções, as amostras foram lavadas e imersas em água destilada a 37 ± 1ºC, pelo período restante das 24 h. O processo foi repetido 8 vezes por dia, durante 90 dias (720 ciclos). A escovação mecânica foi conduzida em máquina MSEt à taxa de 5 movimentos por segundo (20.000 ciclos) e as amostras foram avaliadas sem e com envelhecimento térmico com imersões de 60 segundos a 5 ± 1ºC e 55 ± 1ºC, simulando 2 anos. Rugosidade média de superfície foi verificada pela leituras realizadas transversalmente à direção de movimentos lineares de escovação. A dureza Knoop foi verificada, sob carga de 25g/Força de penetração por 5 segundos, em cinco mensurações, antes e após a aplicação dos tratamentos. Foi realizado teste de Kruskal-Wallis e Dunn, Mann-Whitney e Wilcoxon, com 5% de significância. Resultados: Onda-Cryl apresentou dureza (KHN) antes e após os métodos, sem termociclagem, diferença estatisticamente significante (p = 0,013), enquanto entre as resinas com termociclagem, Onda-Cryl (p = 0,001) e QC 20 (p = 0,002) apresentaram diferenças estatisticamente significantes. QC 20 apresentou rugosidade média antes e após os métodos, sem termociclagem, diferença estatisticamente significante (p = 0,003), enquanto entre as resinas com termociclagem, Onda-Cryl (p = 0,046) e QC 20 (p = 0,010) apresentaram diferenças estatisticamente significantes. Entre os métodos sem termociclagem: O peróxido revelou diferença estatisticamente significante na dureza, apenas para Onda-Cryl e na rugosidade, apenas para QC 20 em relação aos métodos peróxido e o hipoclorito. Entre os métodos com termociclagem: Os grupos controle, escovação e peróxido revelaram diferença estatisticamente significante na dureza para Onda-Cryl; o método controle para resina QC 20 e os métodos peróxido e Hipoclorito para Clássico, enquanto a rugosidade revelou diferenças estatisticamente significantes para Onda Cryl em relação ao método peróxido e QC 20 para os métodos peróxido e hipoclorito. Conclusão: houve diferença estatisticamente significante relativa à Dureza apenas para o método controle nas resinas Onda-Cryl e QC 20 independentemente da termociclagem. Não houve diferença estatisticamente significante relativa à rugosidade independentemente da associação entre termociclagem, resinas e métodos / Abstract: This study evaluated the effect of thermocycling, mechanical brushing and chemical disinfection on the hardness and roughness of resins with different polymerization cycles. 480 samples were prepared (25 mm x 14 mm x 3 mm) and distributed randomly into three groups according to the resins: Onda-Cryl (G1), QC-20 (G2) and Classic (G3). Half of the samples were tested as roughness and the other half for testing the hardness, before and after treatments: control, mechanical brushing or chemical disinfection (hypochlorite and Peroxide) with and without thermocycling. G1 samples were fabricated, cured in the microwave with power of 900 W, G2 were polymerized at 100° C for 20 minutes and G3 were polymerized at 74° C for 9h. The samples were deflasked polishing and finished in water-cooled, in decreasing order of grain. The chemical disinfection was carried out with: 1) Sodium hypochlorite 0.5% at 37 ± 1º C for 20 minutes, 2) Hydrogen Peroxide at 37 ± 1º C for 15 minutes. After disinfection, the samples were washed and immersed in distilled water at 37 ± 1º C, for the remainder of 24 h. The process was repeated eight times daily for 90 days (720 cycles). The mechanical brushing was conducted in machine MSET at 5 moves per second (20,000 cycles) and the samples were evaluated with and without thermal aging with dips of 60 seconds to 5 ± 1º C and 55 ± 1º C simulating 2 years. Average surface roughness was determined by readings taken transversely to the direction of linear motion of brushing. Knoop hardness was observed under load 25g/Power penetration for 5 seconds, five measurements before and after treatments. Was performed using the Kruskal-Wallis and Dunn, Mann-Whitney and Wilcoxon, with 5% significance level. Results: Onda-Cryl presented hardness (KHN) before and after methods, without thermocycling, a statistically significant difference (p = 0.013), while among the resins with thermocycling, Onda-Cryl (p = 0.001) and QC 20 (p = 0.002) showed statistically significant differences. QC 20 had average roughness before and after methods, without thermocycling, a statistically significant difference (p = 0.003), while among the resins with thermocycling, Onda-Cryl (p = 0.046) and QC 20 (p = 0.010) were statistically different. Among the methods without thermocycling: The peroxide showed a statistically significant difference in hardness only to Onda-Cryl and roughness, only QC 20 in relation to methods peroxide and hypochlorite. Among the methods thermocycling: Control groups, mechanical brushing and peroxide showed statistically significant difference in hardness for Onda-Cryl; the control method for QC 20 resin and methods for peroxide and hypochlorite Classic, while the roughness, showed statistically significant differences for Onda-Cryl in relation to the peroxide method and 20 for QC methods peroxide and hypochlorite. Conclusion: statistically significant difference on hardness only to the control method in the resins Onda-Cryl and QC 20 regardless of thermocycling. There was no statistically significant difference on the association between roughness regardless of thermocycling, resins and methods / Doutorado / Protese Dental / Doutor em Clínica Odontológica

Com os sistemas adesivos autocondicionantes, o uso prévio do ácido fosfórico passou a ser dispensado em dentina. Assim, outras soluções foram propostas a fim de se promover uma limpeza da cavidade e otimizar um melhor embricamento do adesivo ao substrato. O objetivo deste estudo foi avaliar a influência de soluções químicas à adesão à dentina bovina, por meio da resistência ao microcisalhamento, de três sistemas adesivos autocondicionantes em função do tempo. Duzentos e quarenta incisivos bovinos foram incluídos, desgastados e polidos em série com lixas de carbeto de silício, obtendo uma superfície planificada de dentina de 10 mm de diâmetro. Os espécimes foram divididos aleatoriamente em 4 grupos, de acordo com a solução aplicada: SF- aplicação de soro fisiológico com 0,9% NaCl (grupo controle); HS- desproteinização com hipoclorito de sódio a 5%, por 2 minuto e HSAA- hipoclorito de sódio a 5%, por 2 minuto seguida da aplicação de ácido ascórbico (ascorbato) a 10%, por 1 minuto; CHX- aplicação de solução clorexidina a (2% por 1 minuto). Às superfícies preparadas foram aplicados três sistemas adesivos autocondicionantes, por grupo - Optibond All-in-One (KERR), Filtek P90-System Adhesive (3M-ESPE) e Adper SE (3M-ESPE), todas seguidas da inserção de resina composta (Filtek Z250 ou Filtek P90). Metade dos espécimes de cada grupo foram armazenados por 24 horas e metade por 6 meses. Após esses períodos, os espécimes foram submetidos ao teste de microcisalhamento, em uma máquina de ensaios universal (Emic, na velocidade de 0,5mm/min). Os dados foram avaliados estatisticamente através de análise de variância (ANOVA) a três critérios e testes de comparações múltiplas de Tukey ambos considerando a=0,05. O adesivo Filtek P90-System Adhesive foi o único que manteve a resistência adesiva após o envelhecimento, porém, os dois tratamentos de superfície contendo hipoclorito de sódio influenciaram negativamente. Já com a clorexidina não houve diferença estatisticamente significante comparada ao grupo controle. O adesivo OptiBond All- In-One (Kerr) foi influenciado positivamente pelo hipoclorito de sódio e hipoclorito de sódio mais ascorbato, no tempo de 24 horas. Sendo de iqual resultado com o envelhecimento em solução aquosa. Adper SE (3M-ESPE) sofreu influência dos tratamentos à base de hipoclorito de sódio. O melhor resultado, comparando dois tratamentos com hipoclorito, após o envelhecimento, foi obtido pelo tratamento com o hipoclorito de sódio mais ascorbato sendo estatisticamente idêntico ao grupo controle. Foi concluído que os tratamentos de superficie influenciam na resistência adesiva dos adesivos testados. A clorexidina possibilitou os melhores resultados em quase todos os testes. / With the Self-etching adhesives, acid-etching with phosphoric acid has to be dispensed in dentin. Than, other solutions have been proposed in order to promote the cavity cleaner and improvement in bonding effectiveness. The aim of this study was to investigate the microshear bond strength, with the influence of chemical solutions and time, in three adhesive systems used on bovine dentin. Two hundred and forty bovine incisors were included, and the surface was polished in series with silicon carbide paper, getting flattened dentin surface of 10 mm in diameter. The specimens were randomly divided into four groups, according to the applied solution: SF- saline solution with 0.9% NaCl (control group), HS-deproteinization with sodium hypochlorite at 5%, for 2 minutes and HSAA- sodium hypochlorite 5% for 2 minutes followed by the application of ascorbic acid (ascorbate) and 10% for 1 minute;CHXapplication of chlorhexidine solution (2% for 1 minute). Were applied to surfaces prepared three adhesive systems, per group - Optibond All-in-One (Kerr), Filtek-P90 System Adhesive (3M-ESPE) and Adper SE (3M-ESPE), all followed by the insertion of composite resin ( Filtek Z250 and Filtek P90). Half of the specimens of each group / treatment were stored for 24 hours and half for six months. After these periods were tested using the microshear in a universal testing machine (Emic, the speed of 0.5 mm / min). Results were submitted to three way ANOVA and TUKEY test multiple comparison both considering a = 0.05. The adhesive Filtek P90 System Adhesive was the one who kept the bond strength after aging, however, the two surface treatments containing sodium hypochlorite influenced negatively. With chlorhexidine, there was no statistically significant difference compared to the control group. The adhesive OptiBond All-in-One (Kerr) was affected by the sodium hypochlorite, sodium hypochlorite more ascorbate, at 24 hours. As a result of iqual with aging in aqueous solution. Adper SE (3M-ESPE) was influenced by the treatments using sodium hypochlorite. The best result, comparing two treatments with hypochlorite, after aging, was obtained by treatment with sodium hypochlorite more ascorbate was statistically identical to the control group. It was concluded that the influence of surface treatments on bond strength of adhesives tested. The chlorhexidine resulted in better results in almost every test.

O objetivo deste trabalho foi avaliar a perda de massa e a alteração da rugosidade superficial causadas pela associação dos métodos mecânico (escovação) e químico (imersão) de higiene de próteses totais. Foram utilizados 72 corpos de prova (90 x 30 x 3 mm) de Plexiglass. O ensaio de escovação (método mecânico) foi realizado em máquina de escovação (Mavtec), em frequência de 356 rpm, curso da escova (Tek Macia) de 3,8 centímetros, peso da sapata de 200 gramas e tempo de 50 minutos (simulação de 01 ano de escovação). Como suspensões, foram utilizadas água destilada e 04 dentifrícios (02 convencionais: Sorriso e Colgate; e 02 específicos para próteses totais: Polident e Corega). Após a escovação, os corpos de prova foram imersos (hipoclorito de sódio 0,5% - NaClO) por 121,6 horas (simulação de 01 ano de imersão, por 20 minutos diários). Foram obtidos 06 grupos, sendo 01 controle (C - escovação e imersão em água) e 05 experimentais (Ex1 - água; Ex2 - Sorriso; Ex3 - Colgate; Ex4 - Polident; Ex5 - Corega; todos imersos em NaClO). A perda de massa foi avaliada pelo método Gravimétrico, sendo as pesagens realizadas em balança (Metler Toledo GMbH) antes dos procedimentos de higiene (M1), após a escovação (M2) e após a imersão (M3). A alteração da rugosidade superficial (m) foi avaliada por rugosímetro (Surftest SJ-201P), por meio da obtenção de média de três leituras (4,0 mm de comprimento e valor de &Prime;cut-off&Prime; de 0,8 mm, a 0,5 mm/s) antes dos procedimentos de higiene (R1), após a escovação (R2) e após a imersão (R3). Os resultados foram submetidos a ANOVA (dois fatores) e teste de Bonferroni. Para a perda de massa, após o ensaio mecânico, entre os dentifrícios, os maiores valores foram registrados para Ex2 (-0,0137±0,0085), Ex3 (- 0,0123±0,0038) e Ex5 (-0,0121±0,0032), e menores para Ex4 (-0,0072±0,0017); após o método combinado, os maiores valores foram obtidos para os grupos Ex2 (-0,0184±0,0040) e Ex3 (- 0,0155±0,0034), e os menores para Ex4 (-0,0108±0,0023); o método combinado resultou em maior perda de massa que o método mecânico, exceto para o grupo Ex5. Para a alteração da rugosidade superficial, após o ensaio mecânico, os menores valores foram registrados para Ex1 (-0,007±0,016) e Ex4 (0,402±0,378) e maiores para os demais; após o método combinado, os maiores valores foram obtidos para Ex2 (1,617±1,190) e Ex5 (1,634±1,082), e os menores para Ex1 (-0,063±0,013); não houve diferença entre os tratamentos. Conclui-se que: 1. A escovação com dentifrícios acarretou maior perda de massa e alteração da rugosidade que a escovação com água; 2. A imersão em NaClO 0,5% associada à escovação com dentifrícios, acarretou maior perda de massa e alteração da rugosidade, quando comparada à imersão em água; 3. O dentifrício Polident (específico) apresentou os menores valores de perda de massa e de rugosidade superficial para ambos os métodos (mecânico e combinado); 4. O método combinado não resultou em alteração da rugosidade superficial, mas acarretou maior perda de massa que o método mecânico, exceto para o dentifrício Corega (específico). / The aim of this study was evaluate the weight loss and changes in surface roughness when mechanical and chemical methods of denture cleanser were associated. Seventy-two Plexiglass specimens (90x30x3 mm) were used. The brushing test was carried out using a toothbrushing machine (Mavtec), with a frequency of 356 rpm, course covered by brush corresponds to 3.8 cm, the load was standardized at 200 g, and length of 50 minutes (01 year of brushing). Like suspension, were utilized distilled water and 04 dentifrices (02 conventional: Sorriso and Colgate; and 02 indicated for denture cleanser: Polident and Corega). After brushing, the specimens were immersed in sodium hypochlorite (NaClO) 0,5% for 121,6 hours (01 year of immersion). Six groups were obtained, 01 control (C - brushing and immersion with water) and 05 experimental (Ex1: water; Ex2: Sorriso; Ex3: Colgate; Ex4: Polident; Ex5: Corega- all immersed in NaClO). The specimens were weighed before the tests (M1), after the brushing test (M2) and after the immersion test (M3) in a precision balance (Metler Toledo GMbH). The surface roughness (m) was evaluated by rugosimeter (Surftest SJ-201P) before the tests (R1), after the brushing test (R2) and after the immersion test (R3). The weight loss and roughness dates were subjected to ANOVA and Bonferroni tests (p < 0.05). After the brushing test, between the dentifrices, the greater values was registered for Ex2 (-0,0137±0,0085), Ex3 (-0,0123±0,0038) e Ex5 (-0,0121±0,0032), and the lowest for Ex4 (-0,0072±0,0017); after the association of the two methods, the grater values was obtained for Ex2 (-0,0184±0,0040) e Ex3 (-0,0155±0,0034), and the lowest for Ex4 (- 0,0108±0,0023); the association of the methods resulted in greater weight loss than the mechanical method, except for Ex5. For the surface roughness, after the mechanical test, the lowest values were registered for Ex1 (-0,007±0,016) and Ex4 (0,402±0,378), and the grater for the others; after the association of the methods, the greater values were obtained for Ex2 (1,617±1,190) and Ex5 (1,634±1,082), and the lowest for Ex1 (-0,063±0,013); there was no difference for the treatments. We conclude that: 1. Brushing with toothpaste resulted in greater weight loss and change in roughness that brushing with water. 2. The immersion in NaClO 0.5% associated with tooth brushing caused greater weight loss and change of roughness, when compared to immersion in water. 3. The toothpaste Polident (specific) had the lowest mass loss and surface roughness for both methods (mechanical and combined) 4. The association of the two methods resulted in no change in surface roughness, but in greater weight loss than the mechanical method, except for the Corega (specific).

O objetivo do presente estudo foi avaliar o efeito antibacteriano do laser diodo com diferentes comprimentos de onda em blocos de dentina infectados com Enterococcus faecalis, por meio de análise microbiológica com espectrofotometria e alterações ultraestruturais por meio de microscópio eletrônico de varredura. Treze dentes unirradiculares foram seccionados de forma a obter 100 blocos de dentina intrarradicular. Inicialmente, os blocos foram imersos por 5 minutos em EDTA 17% e em seguida lavados por 5 minutos com água destilada, e então autoclavados por 30 minutos a 120&deg;C. As amostras de dentina foram inoculadas com 1mL de suspensão de E. faecalis em 5mL de BHI (Brain Heart Infusion) e incubadas a 37&deg;C por cinco dias. Após a contaminação, os espécimes foram distribuídos em dez grupos (n=10) de acordo com tratamento de superfície: GI - 5 mL NaOCl 2,5%, GII - 5 mL NaOCl 2,5% + diodo 808nm, GIII - 5 mL NaOCl 2,5% + diodo 970nm, GIV - diodo 808nm, GV - diodo 970nm, GVI - CHX 2%, GVII - CHX 2% + diodo 808nm, GVIII - CHX 2% + diodo 970nm, GIX - controle positivo e GX controle negativo. O crescimento bacteriano foi analisado pela turbidez e densidade óptica do meio de cultura por espectrofotometria (nm). Em seguida, os espécimes foram preparados para análise das alterações ultraestruturais da superfície dentinária em MEV. Os dados foram submetidos ao teste ANOVA um fator e evidenciaram que o GI (77,5 ± 12,1), GII (72,5 ± 12,2), GIII (68,7 ± 8,7), GV (68,3 ± 8,7), GVI (62,0 ± 5,5) e GVII (67,5 ± 3,3) foram semelhantes entre si e diferente estatisticamente dos grupos GIV (58,8 ± 25,0), GVIII (59,2 ± 4,0) e grupos controles (p<0,05). A análise em MEV evidenciou uma matriz orgânica amorfa e derretimento da dentina intertubular quando submetidos à irradiação do laser diodo 970nm, e erosão da dentina intertubular quando irradiada com laser 808nm, sendo que ao associar NaOCl 2,5% ao laser com diferentes comprimentos de onda, observou-se maior erosão intertubular. Conclui-se que todos os protocolos terapêuticos foram capazes de reduzir o contingente bacteriano dos blocos de dentina e ao associar o laser diodo e soluções não houve melhora significativa na redução do contingente bacteriano. / The objective of this study was to evaluate the disinfection degree of dentin blocks contaminated by Enterococcus faecalis caused by different diode laser wavelengths through microbiological analysis with spectrophotometry and ultrastructural alterations by scanning electron microscope. Thirteen uniradicular teeth were sectioned into 100 dentin Intraradicular blocks. Initially, the blocks were immersed for 5 minutes in 17% EDTA and then washed for 5 minutes with distilled water, and then esterilized for 30 minutes at 120&deg;C. The dentin samples were inoculated with 1mL of E. faecalis suspension in 5mL BHI (Brain Heart Infusion) and incubated at 37&deg;C for five days. After contamination, the specimens were distributed into ten groups (n = 10) according to surface treatment: GI - 5 mL NaOCl 2.5%, GII - 5 mL NaOCl 2.5% + diode 808nm, GIII - 5 mL NaOCl 2.5% + diode 970nm, GIV - diode 808nm, GV - diode 970nm, GVI - CHX 2%, GVII - CHX 2% + diode 808nm, GVIII - CHX 2% + diode 970nm, GIX - positive control and GX - Negative control. Bacterial growth was analyzed by turbidity and optical density of the culture medium by spectrophotometry (nm). Afterwards, the specimens were processed for analysis of the ultrastructural changes of the dentin surface in SEM. The data was subject to the One-way ANOVA test and showed that GI (77,5 ± 12,1), GII (72,5 ± 12,2), GIII (68,7 ± 8,7), GV (68,3 ± 8,7) and GVII (67,5 ± 3,3) were statistically similar and statistically different from GIV (58,8 ± 25,0), GVIII (59,2 ± 4,0) and control groups (p <0.05). SEM analysis showed a modified organic matrix layer with an amorphous, intertubular dentin melting when dentin samples were irradiated with 970nm diode laser, erosion of the intertubular dentin in blocks submitted to 808nm diode laser, and a increased erosion of the intertubular dentin when associating NaOCl 2,5% to the laser with different wavelengths. All the therapeutic protocols were able to reduce the bacterial contingent in dentin blocks with the association of laser diode and solutions did not significantly improve the reduction of the bacterial contingent.

Orientador: Caio Cezar Randi Ferraz / Texto em português e inglês / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-25T07:03:00Z (GMT). No. of bitstreams: 1 Miyagaki_DanielaCristina_D.pdf: 1888182 bytes, checksum: c2a3adf7e320c1e55bd3e32e5b42ebb9 (MD5) Previous issue date: 2014 / Resumo: Este estudo teve como objetivo analisar in vitro a influência de diferentes protocolos de irrigação endodônticos na resistência de união e longevidade adesiva de pinos de fibra de vidro modelados utilizando um cimento autoadesivo (capítulo único). Para isso, canais de 96 raízes bovinas foram preparados com auxílio de broca de largo n°6 e, divididos aleatoriamente em 8 grupos (n=12) de acordo com os diferentes tratamentos na superfície da dentina intrarradicular: G1(controle)- soro fisiológico 0,9% (NaCl); G2- hipoclorito de sódio 5,25% (NaOCl) + EDTA 17%+NaOCl; G3- NaOCl + EDTA 17% + NaOCl + ascorbato de sódio 10% (ASC); G4- gluconato de clorexidina gel 2% (CLX) + NaCl + EDTA 17%; G5- NaOCl ; G6- EDTA 17%; G7- ASC e G8- CLX. Logo após a irrigação e secagem dos canais, os pinos de fibra de vidro foram modelados com resina composta e então cimentados com o cimento autoadesivo RelyX U100®. Cada grupo foi dividido em dois subgrupos: 24h de armazenamento em água e 1 ano de armazenamento em água. Após os períodos, 4 secções de 2mm de espessura foram preparadas para cada espécime a fim de serem submetidos ao ensaio mecânico de cisalhamento por extrusão (push out). Os dados coletados em Newton foram convertidos em Megapascal, e então analisados estatisticamente com Shapiro-Wilk, Anova e Tukey (P=0,05). Posteriormente, o modo de fratura de cada amostra foi analisado por meio de microscopia eletrônica de varredura, e classificado em: (1) adesiva na interface dentina/cimento, (2) adesiva na interface cimento/resina, (3) adesiva na interface resina/pino ou (4) mistas (envolvendo 2 ou mais substratos). Os resultados mostraram que após 24 h, o EDTA sozinho ou associado à CLX diminuíram significativamente os valores de resistência de união quando comparados ao grupo controle. O ascorbato de sódio sozinho ou associado ao NaOCl obteve a maior média de resistência de união quando comparado ao controle (P>0,05). Os demais grupos obtiveram valores similares ao grupo controle, sem diferença estatisticamente. Após 1 ano, os grupos do NaOCl, associado ou não ao EDTA obtiveram significativa redução dos valores (P<0,05). O padrão de fratura foi predominante mista, independente do período de armazenagem ou protocolo de irrigação. Foi possível concluir que o hipoclorito de sódio sozinho ou associado ao EDTA prejudica significativamente a resistência adesiva a longo-prazo. O ascorbato de sódio sozinho ou em associação foi capaz de melhorar e preservar os valores de resistência de união após 1 ano / Abstract: The present study aimed to analyze in vitro the influence of different irrigation protocols in the adhesive strength and longevity of relined fiberglass posts cemented with self-adhesive resin cement (single chapter). Ninety-six bovine root canals were instrumented with the aid of #6 largo drills, and were randomly divided into 8 groups (n=12) according to the different treatments in radicular dentin: G1 (control)-0.9% saline solution (NaCl); G2- 5.25% sodium hypochlorite (NaOCl) + 17% EDTA + NaOCl; G3- NaOCl + 17% EDTA + NaOCl+ 10% sodium ascorbate (SA); G4- 2% chlorhexidine gluconate gel (CHX) + NaCl + 17% EDTA; G5-NaOCl; G6- 17% EDTA; G7- SA and G8-CHX. After irrigation protocols, the root canals were dried and the fiberglass posts were modeled with resin composite and cemented with RelyX U100 ®. Each group was divided into two subgroups: 24 hours and 12 months of water storage. After storage periods, all roots were sectioned transversely producing 4 slices of 2-mm-thick in order to be subjected to the push-out test. The data obtained in Newton were converted in Megapascal, afterwards the results were analyzed by Shapiro-Wilk, Anova and Tukey's test (P=0.05). Subsequently, the failure pattern was classified using a scanning electron microscopy as: (1) adhesive between resin cement/dentin, (2) adhesive between resin cement/resin composite, (3) adhesive between resin composite/post or (4) mixed (involving 2 or more substrates). The results showed that after 24 hours, EDTA alone or associated with CHX significantly decreased the bond strength values when compared to control group. Sodium ascorbate alone or associated with NaOCl had the highest mean values of bond strength when compared to control group (P>0.05). The other groups showed values similar to control group but without statistical difference. After one year, only NaOCl groups, associated or not to EDTA, showed significant reduction of the bond strength values (P<0.05). Failure pattern was predominantly mixed, irrespective of storage period and irrigation protocol used. It was possible to conclude that sodium hypochlorite alone or in association with EDTA significantly jeopardizes the long-term bond. Sodium ascorbate alone or in association, was capable of improve and preserve the adhesion values after one year / Doutorado / Endodontia / Doutora em Clínica Odontológica