Submitted by Bruna Corrêa Lucatto null (brulucatto@hotmail.com) on 2018-01-25T00:26:13Z No. of bitstreams: 1 merged (2).pdf: 2609941 bytes, checksum: 81898d81b1fe7413008b3e7b4b083151 (MD5) / Approved for entry into archive by Silvana Alvarez null (silvana@ict.unesp.br) on 2018-02-01T19:05:03Z (GMT) No. of bitstreams: 1 merged (2).pdf: 2609941 bytes, checksum: 81898d81b1fe7413008b3e7b4b083151 (MD5) / Made available in DSpace on 2018-02-01T19:05:03Z (GMT). No. of bitstreams: 1 merged (2).pdf: 2609941 bytes, checksum: 81898d81b1fe7413008b3e7b4b083151 (MD5) Previous issue date: 2017-12-06 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste trabalho foi sintetizar e caracterizar nanopartículas de sílica recobertas por prata, e avaliar a influência quando incorporadas à resina acrílica quimicamente ativada, ao reembasador macio, e a um glaze, em suas características microbiológicas, microestruturais e mecânicas. Foi confeccionada, pelo método de hidrólise e condensação controlada (método de Stober), uma solução contendo nanopartículas de sílica revestidas por nanopartículas de prata em duas proporções, 10 milimols e 30 milimols, onde as mesmas foram caracterizadas. As nanopartículas de sílica incorporadas com a prata foram analisadas por energia dispersiva de raios-X integrado (EDS), microscopia eletrônica de varredura (MEV), e espalhamento de luz dinâmico (DLS). Para análise microbiológica foram confeccionadas 10 amostras cilíndricas (2mmx10mm), em resina acrílica quimicamente ativada onde as partículas foram incorporadas em duas concentrações: 2.5% e 5% com as duas molaridades diferentes 10 mM e 30 mM. Em outra situação foram confeccionadas 10 amostras cilíndricas (2mmx10mm) de reembasador macio, com concentrações de 2,5% e 5% com as duas molaridades diferentes 10 mM e 30 mM, no terceiro caso as partículas foram acrescentadas a um glaze nas duas concentrações e molaridades e aplicada sob uma amostra de reembasador macio. Uma suspensão de Candida albicans e Estreptococos mutans foi utilizada para análise de concentração inibitória mínima. Amostras retangulares em resina acrílica (n=6) de 30x10x3mm, foram confeccionadas para realização do teste de resistência a flexão de três pontos de ensaios mecânicos EMIC (Modelo DL-1000, EMIC Equipamentos e Sistemas LTDA., São José dos Pinhais - PR – Brasil), com velocidade de 1mm/min. Amostras sem a presença de nanopartículas foram confeccionadas como grupo controle. A sílica inicialmente apresentava-se como um pó de coloração branca e fina, após a sua caracterização com as partículas de Nitrato de Prata, houve alteração da coloração para um tom amarelado, aumento da sua densidade e do tamanho de suas nanopartículas. Os resultados de ação antimicrobiana foram positivos para as amostras de reembasador macio e glaze com 5% e 30 mMol de nanopartículas, já no ensaio mecânico não houve diferença significante estatisticamente entre os grupos. / The aim of this work was to synthesize and characterize silver - coated silica nanoparticles, and to evaluate the influence when incorporated into chemically activated acrylic resin, soft reliner, and glaze, in their microbiological, microstructural and mechanical characteristics. A solution containing silica nanoparticles coated by silver nanoparticles in two proportions, 10 millimols and 30 millimols, where they were characterized, was prepared by the hydrolysis and controlled condensation method (Stober method). Silica nanoparticles incorporated with silver were analyzed by integrated X-ray dispersive energy (EDS), scanning electron microscopy (SEM), and dynamic light scattering (DLS).For the microbiological analysis, 10 cylindrical samples (2mmx10mm) were made in chemically activated acrylic resin where the particles were incorporated in two concentrations: 2.5% and 5% with two different molarities of 10 mM and 30 mM. In another situation, 10 cylindrical samples (2mmx10mm) of soft reliner were made, with concentrations of 2.5% and 5% with the two different molarities 10 mM and 30 mM, in the third case the particles were added to a glaze in the two concentrations and molarities and applied under a sample of soft reliner. A suspension of Candida albicans and Streptococcus mutans was used for analysis of minimal inhibitory concentration. The samples were made in acrylic resin (n = 6) of 30x10x3mm and were made to perform the three-point flexural strength test of EMIC (Model DL-1000, EMIC Equipamentos e Sistemas Ltda., São José dos Pinhais - PR - Brazil), with a speed of 1mm / min. Samples without the presence of nanoparticles were made as a control group. The silica initially presented as a fine white powder after its characterization with the Silver Nitrate particles, there was a change of coloration to a yellowish tone, increase of its density and the size of its nanoparticles. The results of antimicrobial action were positive for the soft reliner and glaze samples with 5% and 30 mMol of nanoparticles, whereas in the mechanical assay there was no statistically significant difference between the groups.

As tintas em pó estão ganhando espaço no mercado, por serem ecologicamente corretas, sem solventes e com componentes sólidos. A proteção é uma de suas principais funcionalidades para evitar a ação direta de agentes agressivos. Por serem compostas de polímeros elas correm o risco em situações adversas de entrarem em combustão. O presente estudo sobre retardadores de chama tem a finalidade de avaliar a utilização de uma resina acrílica com a adição de argilas Montmorilonita (MMT) na classificação 15A , 30B, e Mica moscovita. A adição das argilas foi na proporção de 2% e 4%(m/m) e a incorporação das argilas na tinta em pó ocorreu no estado fundido através da extrusão. A mistura da tinta em pó base acrílica(TA) com as argilas ,antes da cura, foram analisadas por diferentes técnicas de caracterização, tais como, análise termogravimétrica (TGA), microscopia eletrônica de varredura (MEV), difração de raios X (DRX) e espectroscopia de infravermelho por transformada de Fourier (FTIR). A aplicação das tintas em pó sobre painéis de aço carbono AISI 1006 ocorreu por pulverização eletrostática. O efeito da incorporação de diferentes teores de argila nas propriedades físicas, proteção à corrosão e à combustão das tintas foram avaliadas por ensaios de medida de brilho, flexibilidade, resistência ao impacto, aderência, exposição à névoa salina e a chama (norma DIN 4102 B2). As tintas em pó com MMT e Mica moscovita apresentaram um comportamento térmico semelhante a amostra de tinta acrílica pura, sendo a perda de massa das amostras acima de 300ºC relacionadas à degradação da matriz polimérica. Pelo MEV constatou-se que as argilas MMT-15A e MMT- 30B apresentaram aglomerados irregulares e a Mica moscovita apresentou uma morfologia constituída por conjunto de placas paralelas sobrepostas. Através do DRX, a resina acrílica com argilas MMT-15A ou MMT-30B demonstraram o aparecimento de picos, sugerindo uma estrutura intercalada. A difração de raios-X da tinta acrílica com Mica moscovita 2% e 4% demonstraram perfil característico da argila, com picos agudos. Quanto as propriedades de retardamento de chama nos tempos de combustão de 60s e principalmente de 40s nas tintas acrílicas com Mica moscovita 2% e 4% apresentaram maior estabilidade térmica perante as demais formulações. O ensaio de flexibilidade mostrou que as amostras sem argila e com a Mica moscovita em 2% e 4% não apresentaram desplacamento. O ensaio de resistência ao impacto mostrou uma excelente resposta da resina acrílica pura. No teste de aderência constatou-se a inexistência de áreas desplacadas. O teste de dureza a lápis o filme mais resistente para o sistema foi da tinta acrílica MMT-30B em 4%. Nos ensaios de névoa salina todas as amostras apresentaram produtos de corrosão próximo à incisão. A tinta acrílica com Mica moscovita demonstrou inúmeras qualidades, principalmente o retardamento de chama. / Submitted by Ana Guimarães Pereira (agpereir@ucs.br) on 2015-12-08T13:16:26Z No. of bitstreams: 1 Dissertacao Gilmar Antonio Santa Catarina.pdf: 401910 bytes, checksum: d9ce54a7c1f445abe5dd7919193f11df (MD5) / Made available in DSpace on 2015-12-08T13:16:26Z (GMT). No. of bitstreams: 1 Dissertacao Gilmar Antonio Santa Catarina.pdf: 401910 bytes, checksum: d9ce54a7c1f445abe5dd7919193f11df (MD5) / The powder coatings are gaining market share because they are environmentally friendly, solvent-free and solid components. Protection is one of its main features to avoid direct action of aggressive agents. Because they are composed of polymers they risk in adverse situations come into combustion. This study of flame retardants is intended to evaluate the use of an acrylic resin with the addition of Montmorillonite clays (MMT) in rank 15A, 30B, and muscovite mica. The addition of clay has a proportion of 2% and 4% (m / m) and the incorporation of clays in powder paint was in the molten state by extrusion. The mixture ink in acrylic-based powder (TA) with the clay, prior to curing, analyzed by various characterization techniques such as Thermogravimetric Analysis (TGA), scanning electron microscopy (SEM), X-ray diffraction (XRD ) spectroscopy and Fourier transform infrared (FTIR). The application of powder coatings on carbon AISI 1006 steel panels by electrostatic spraying occurred. The effect of incorporating different clay in physical properties, corrosion protection and combustion of the inks were evaluated by brightness measurement tests, flexibility, impact resistance, adhesion, exposure to salt spray and flame (DIN 4102 B2 ). Powder paints with MMT and Mica Muscovite had a similar thermal behavior pure acrylic paint sample, and the mass loss of the samples above 300 °C related to the degradation of the polymeric matrix. By SEM it was found that the MMT-clay and MMT 15A-30B show irregular agglomerates and Muscovite mica showed a morphology constituted by overlapping set of parallel plates. By XRD, acrylic resin MMT-clay or MMT 15A-30B show the appearance of peaks, suggesting an interleaved structure. The X-ray diffraction of acrylic paint with Muscovite Mica 2% and 4% clay showed a characteristic profile with sharp peaks. As the flame retardant properties in combustion times of 60 s and 40 s mainly in acrylic inks Muscovite Mica 2% and 4% had greater thermal stability towards other formulations. The flexibility test showed that the samples without clay and with the Muscovite Mica 2% and 4% showed no peeling. The impact resistance test showed an excellent response of pure acrylic resin. In the adhesion test it was found that no desplacadas areas. The pencil hardness test the tougher the film to the acrylic paint system was MMT-30B in 4%. In the salt spray test all samples showed corrosion products close to the incision. Acrylic paint with Muscovite Mica demonstrated many qualities, especially flame retardancy.

Resumo: A proposta do presente estudo foi avaliar, por meio do teste quantitativo de incorporação de 3H-timidina, o efeito do tratamento térmico em microondas sobre a citotoxicidade de três resinas termopolimerizáveis indicadas para confecção de bases de próteses, em função do tempo de armazenamento em água, e de três resinas autopolimerizáveis indicadas para reembasamento. A hipótese de que o tratamento térmico em microondas poderia diminuir a citotoxicidade de resinas acrílicas foi avaliada. Os materiais testados foram Lucitone 550 (a mufla foi imersa em água à temperatura de 730C permanecendo por 90 minutos, em seguida, à temperatura foi elevada para 1000C e a mufla mantida por mais 30 minutos), QC 20 (a mufla foi imersa em água em ebulição, o aquecimento foi mantido e a mufla permaneceu no recipiente por um período de 20 minutos contados a partir do momento em que a água atingiu novamente à temperatura de ebulição e Acron MC (a mufla foi levada ao forno de microondas durante 3 minutos à potência de 500 W) e os reembasadores Tokuyama Rebase II, Kooliner e New Truliner. Foram confeccionados, em condições assépticas, corpos-de-prova de cada resina em forma de discos medindo 10 mm de diâmetro e 1 mm de espessura. As amostras das resinas termopolimerizáveis foram armazenadas em água destilada por 0, 24 ou 48 horas a 37ºC. Para avaliar o efeito do tratamento térmico em microondas, os corpos-de-prova de todas as resinas foram divididos em dois grupos: 1) sem tratamento térmico e 2) com tratamento térmico em microondas, com as amostras imersas em água, irradiadas durante 3 minutos à 500 W. Os extratos das resinas foram preparados colocando-se três corpos-de-prova de cada grupo experimental, após terem recebido o tratamento térmico, em tubos de ensaio com 9 ml de meio de cultura Eagle e incubados a 37ºC por 24 horas. Um tubo de ensaio, contendo apenas 9 ml de meio... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of the current study was to evaluate the effect of microwave post-polymerization heat-treatments and water storage time on the cytotoxicity of denture base and reline acrylic resins. The hypothesis that post-polymerization treatment could decrease the cytotoxicity of acrylic base resins was tested in this study. The materials tested were Lucitone 550 (water-bath at a temperature of 73ºC for 90 minutes, followed by 30 minutes of heating at 100ºC), QC 20 (boil water, insert flask, return to boil, boil for 20 minutes) and Acron MC (microwave-polymerized, irradiated for 3 minutes at 500 W) and the hard chair-side reline resin Tokuyama Rebase II, Kooliner and New Truliner. Sample disks of the denture base resins were fabricated under aseptic conditions in mold 10 mm in diameter by 1 mm thick. The samples of the denture base acrylic resins were stored in distilled water for 0, 24 and 48 hours at 37ºC. To assess the biologic effect of the heat-treatment on the denture resins, samples fabricated were further divided into two groups: 1) samples without heat-treatment; and 2) sample were treated in microwave, immersed in water, irradiated for 3 minutes at 500 W. Eluates of the materials were prepared by placing three disks into a sterile glass vial with 9 ml of Eagle's medium supplemented with antibiotics and fetal bovine serum. These were incubated for 24 hours at 37ºC. Medium without disks was also incubated and diluted as above to serve as the control. L929 mouse fibroblasts (1 x 104 cell/ml) were cultivated in Eagle's medium supplemented with antibiotics and fetal bovine serum in 96 well culture plates and incubated for 24 hours at 37ºC in an air atmosphere containing 5% CO2. After 24 hours of incubation, the culture medium was replaced by 50 ml of eluate and 50 ml of fresh medium were added to each well of the 96-well culture plate and incubated for more... (Complete abstract, click electronic address below) / Orientador: Eunice Teresinha Giampaolo / Coorientadora: Iracilde Zeppone Carlos / Banca: Ana Cláudia Pavarina / Banca: Carlos Eduardo Vergani / Banca: Ricardo Faria Ribeiro / Banca: Wellington Cardoso Bonachela / Doutor

Orientadora: Daniela Micheline dos Santos / Coorientador: Marcelo Coelho Goiato / Banca: Marcela Fillié Haddad / Banca: Sandra Helena Penha de Oliveira / Resumo: A prótese bucomaxilofacial implantorretida pode ser suportada por pele ou por mucosa. Subprodutos dos materiais utilizados na confecção destas próteses podem atuar como irritantes ou causadores de reações alérgicas a tais tecidos. A proposta do presente estudo foi avaliar a citotoxicidade de primers e adesivo utilizados na confecção de próteses maxilofaciais retidas por implantes, por meio da análise da proliferação celular e da produção de citocinas pró-inflamatórias e de proteínas de matriz extracelular por queratinócitos humanos. Foram confeccionadas 28 amostras de resina e silicone, em forma de discos (10 x 1 mm), unidas ou não pela aplicação de primer e/ou adesivo. Estas amostras foram distribuídas em 7 grupos: Resina (R), Silicone (S), Resina + Silastic Medhical Adhesive Type A + Silicone (RAS), Resina + DC 1205 primer + Silicone (RDCpS), Resina + Sofreliner primer + Silicone (RSpS), Resina + DC 1205 primer + Silastic Medhical Adhesive Type A + Silicone (RDCpAS) e Resina + Sofreliner primer + Silastic Medhical Adhesive Type A + Silicone (RSpAS). Os extratos dos materiais testados foram preparados colocando-se quatro amostras de cada grupo experimental em tubos de ensaio contendo 9 mL de meio de cultura DMEM (Dulbecco's Modified Eagle's) e incubados a 37°C por 24 horas. Após o período de incubação, a citotoxicidade dos extratos foi avaliada pelo ensaio de MTT em cultura de queratinócitos humanos (HaCaT). Foi avaliada, também, a produção das citocinas IL-1, IL-6 e TNF-α e a quimiocina MIP-1α por meio do ensaio ELISA (Ensaio Imunoabsorbente de Ligação Enzimática). Também foi avaliada a expressão de RNAm para MMP-9, TGF-β e COL-IV por meio da técnica de RT-PCR em tempo real (Reação em Cadeia da Polimerase em Tempo Real). Os dados obtidos foram submetidos à Análise de Variância (ANOVA), seguido... / Abstract: The implant-retained maxillofacial prosthesis can be supported by skin and mucosa. The sub-products produced by the materials used to fabricate these prostheses may act as an irritant factor and cause allergy in these tissues. The aim of this study was to evaluate the cytotoxic effect of primers and adhesive used to bond the acrylic resin and the facial silicone during implant-retained maxillofacial prosthesis fabrication, through the analysis of the cell proliferation, and the production of proinflammatory cytokines and extracellular matrix proteins by keratinocytes. A total of 28 round shape samples (10 x 1 mm) made of resin and silicone bonded or not with primer and adhesive was fabricated. Samples were divided into 7 groups: Resin (R), Silicone (S), Resin + Silastic Medical Adhesive Type A + Silicone (RAS), Resin + DC 1205 primer + Silicone (RDCpS), Resin + Sofreliner primer + Silicone (RSpS), Resin + DC 1205 primer + Silastic Medical Adhesive Type A + Silicone (RDCpAS), and Resin + Sofreliner primer + Silastic Medical Adhesive Type A + Silicone (RSpAS). Extracts of tested materials were prepared setting four samples of each experimental group in Falcon tube with 9mL of medium (Bulbecco's Modified Eagle's) and incubated at 37°C for 24 hours. After incubation period, the extract cytotoxicity was evaluated by an assay of cell survival/proliferation (MTT test) in cultures of human keratinocytes (HaCaT). The levels of IL-1, IL-6 and TNF-α and the chemokine MIP-1α were evaluated by ELISA (Enzyme-Linked Immunoabsorbent Assay). The mRNA expression for MMP-9, TGF-β and collagen type IV were analyzed by the RT-PCR (Real time polymerase chain reaction). Data were submitted to the analysis of variance with Bonferroni post-tests (p<0.05). The results showed increased cell proliferation for the RAS group. The RDCpS group showed the highest... / Mestre

Orientador: João Neudenir Arioli Filho / Banca: Francisco de Assis Mollo Junior / Banca: Maximiliano Piero Neisser / Resumo: O objetivo deste estudo foi avaliar a resistência de união à tração e dureza Shore A de dois materiais reembasadores macios (Eversoft e Molloplast-B), processados juntamente com três resinas acrílicas de base de dentadura (SR Triplex, Lucitone 550 e Acron MC), polimerizadas com diferentes ciclos de polimerização. As amostras para o ensaio de tração eram divididas em dois segmentos de resina acrílica, cada um com 60 x 10 x 10 mm, e um segmento central de material reembasador macio, com 3 x 10 x 10 mm. Dez espécimes foram confeccionados para cada combinação resina acrílica/material reembasador, polimerizados por três ciclos diferentes de polimerização, como segue: SR Triplex - 2 horas a 100ºC; Lucitone 550 - 90 minutos a 73ºC, seguido de 2 horas a 100ºC, e Acron MC - energia por microondas por 10 minutos a 850W. As amostras foram testadas em uma máquina de ensaios universais MTS-810, a uma velocidade de 5 mm/min. Os valores médios de resistência de união foram calculados e expressos em megapascals (MPa), e o tipo de falha foi avaliado e anotado como coesiva, adesiva ou mista. As amostras para a avaliação da dureza Shore A consistiam de corpos-de-prova com dimensões de 36 x 7 x 6 mm preparados com os dois materiais macios de reembasamento. Dez amostras de cada material também foram polimerizadas pelos ciclos de polimerização já apresentados e a dureza foi determinada em um durômetro Shore A, de acordo com as normas D-2240 da ASTM. Os dados de ambos os testes foram analisados pela análise de variância e teste de Tukey permitindo concluir que: a) o maior valor de resistência de união foi apresentado pelo material Molloplast-B, quando processado com as resinas acrílicas Lucitone 550 (1,41 +0,15 MPa) e SR Triplex (1,40 + 0,10 MPa),... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The purpose of this study was to evaluate the tensile bond strength and Shore A hardness of two soft denture liners (Eversoft and Molloplast-B), processed against three heat-cured denture base acrylic resins (SR Triplex, Lucitone 550 and Acron MC), and polymerized by different curing cycles (water bath and microwave energy). Tensile specimens consisted of two segments of acrylic resin, each 60 x 10 x 10 mm, and a central segment of soft liner, 3 x 10 x 10 mm. Ten specimens were prepared by each liner/resin combination, and were cured by three different curing cycles, as follows: SR Triplex - boiling water for 2 hours; Lucitone 550 - 73ºC for 90 minutes, plus 2 hours at 100ºC; and Acron MC - microwave activation at 850W for 10 minutes. Specimens were tested in an MTS-810 Universal Testing Machine, at a crosshead speed of 5 mm/min. Mean bond strength was calculated and expressed in megapascals (MPa), and the type of failure was assessed and recorded as being cohesive, adhesive, or mixed. Shore A specimens consisted of 36 x 7 x 6 mm samples prepared with the two soft liners. Ten samples of each liner were polymerized by the curing cycles early presented. Hardness was determined in a Shore A durometer, according the ASTM D-2240 specification. Data from both tests were analyzed by ANOVA and Tukey test, showing that: a) the highest bond strength was presented by Molloplast-B, when processed against Lucitone 550 (1.41 +0.15 MPa) and SR Triplex (1.40 + 0.10 MPa) acrylic resins, and the lowest values were observed for Eversoft, when processed against Acron MC resin (0.38 + 0.06 MPa), b) when polymerized by microwave energy, both Molloplast-B and Eversoft presented their lowest bond strength values, when compared with the groups cured in water bath (p< .05), and c)...(Complete abstract, click electronic access below) / Mestre

Orientador: Carlos Eduardo Vergani / Banca: Ana Lucia Machado / Banca: Renata da Cunha Matheus Rodrigues Garcia / Resumo: O procedimento de reembasamento da prótese é normalmente utilizado para restabelecer a adaptação entre a prótese e o tecido bucal. As resinas autopolimerizáveis são um dos materiais indicados para o reembasamento. No entanto, tem sido demonstrado que, após a polimerização das resinas autopolimerizáveis, nem todo o monômero é convertido em polímero e esse monômero residual pode afetar as propriedades mecânicas desses materiais. Estudos têm sugerido que o conteúdo de monômero residual pode ser reduzido pela irradiação em microondas ou tratamento em banho de água. Esse estudo avaliou o efeito dos tratamentos térmicos sobre a resistência à flexão e dureza Vickers de quatro resinas autopolimerizáveis para reembasamento (Duraliner II - D, Kooliner-K, Tokuso Rebase Fast - TR e Ufi Gel Hard - UGH) e uma resina termopolimerizável (Lucitone 550 - L). Para cada material, trinta corpos-de-prova foram confeccionados e igualmente divididos em três grupos. No grupo controle, os corpos-de-prova foram submetidos ao teste de resistência à flexão imediatamente após sua polimerização. Previamente ao teste, os grupos 2 e 3 foram submetidos ao tratamentos complementares em banho de água e irradiação por microondas, respectivamente. Os corpos-de-prova do material para base de prótese foram armazenados em água por 48 horas a 37o l 1oC previamente ao teste. As medidas de força foram realizadas em máquina de ensaio universal MTS 810 com uma velocidade de 5 mm/min, utilizando o teste em três pontos a uma distância de 50 mm entre os apoios. Em seguida, um dos fragmentos do corpo-de-prova foi submetido ao teste de dureza Vickers. Os valores de dureza foram determinados utilizando-se uma carga de 25 gf (resinas K, TR, L e UGH) e 10 gf para a resina D, após 30 segundos de contato. Doze mensurações de dureza foram realizadas em cada corpo-de-prova e ...(Resumo completo, clicar acesso eletrônico abaixo) / Abstract: To maintain the prosthesis-tissue relationship, denture base reline procedure is commonly required. Autopolymerizing resins are one of the materials indicated for relining. It has been shown that, after polymerization, not all the monomer is converted to polymer in autopolymerizing resins and this residual monomer could detrimentally affect the mechanical properties of the materials. It has been suggested that the residual monomer could be decreased by microwave irradiation or water bath heat-treatments. This study investigated the effect of heat treatments on the flexural strength and Vickers hardness of four autopolymerizing reline resins (Duraliner II - D, Kooliner-K, Tokuso Rebase Fast-TR and Ufi Gel Hard-UGH) and one heat-polymerized resin (Lucitone 550-L). For each material, 30 specimens were made and equally divided into three groups. In control group, the specimens were submitted to the flexural strength test immediately after polymerization. Before testing, groups 2 and 3 were submitted to water bath and microwave post-cure treatments, respectively. The denture base material specimens were stored in water for 48 h at 37o l 1oC before they were bend-tested. Force measurements were made with a testing machine MTS 810 at a crosshead speed of 5 mm/min using a three-point bending fixture with a span of 50 mm. Thereafter, one fragment of specimen was submitted to Vickers microhardness test. The values were determined by using a 25 gf load (resins K, TR, UGH and L) and 10 gf for resin D, after 30 s contact. Twelve hardness measurements were taken on each specimen and the average was then calculated. Kruskal-Wallis non-parametric test was used for determination of statistical significance (p<0.01). The results demonstrated that: compared to the control groups, the flexural strength of TR and...(Complete abstract, click electronic access below) / Mestre

Resumo: O objetivo deste estudo foi estabelecer, inicialmente, um método analítico em CLAE, para comparar o conteúdo de monômero residual de uma resina autopolimerizável para reembasamento imediato (Duraliner II - D) e uma resina termopolimerizável utilizada na confecção de bases de próteses (Lucitone 550 - L). Além disso, foi avaliado o efeito de dois tratamentos térmicos sobre esse conteúdo. Os monômeros utilizados como padrões foram o MMA (resina L) e o BMA (resina D). As condições cromatográficas para a análise foram: coluna ODS (15,0 x 0,46 cm), com 5 mm de tamanho de partícular e 100 Å de tamanho de poro, fase móvel ACN : H2O (55%: 45%) + 0,01% TEA, fluxo 0,8 mL/min, l 230 nm, volume de injeção 100 mL. As resinas foram proporcionadas e polimerizadas de acordo com as instruções dos fabricantes. Os corpos-de-prova (n = 18) dos dois materiais foram divididos em 3 grupos, com 6 corpos-de-prova cada. O grupo I (GI) não foi submetido a nenhum tratamento (controle). Para o grupo II (GII), os corpos-de-prova foram irradiados com microondas, a 550 W por 3 min para o material L e a 650 W por 4 min para o material D. Para o grupo III (GIII), os corpos-de-prova dos materiais L e D foram submetidos ao tratamento térmico por imersão em água a 55oC por 60 min e 10 min, respectivamente. Cada corpo-de-prova foi, então, fragmentado e submetido ao procedimento de extração em MeOH por 2 horas. Os valores de conteúdo de monômero residual foram transformados em porcentagem e analisados pelo teste de Kruskall-Wallis, ao nível de confiança de 99%. Em todos os grupos avaliados, o material D apresentou valores médios de monômero residual (GI - 0,87%; GII - 0,71%; GIII - 0,52%) significativamente maiores (p<0,01) que o material L (GI - 0,09%; GII - 0,06%; GIII - 0,05%). De acordo com a metodologia utilizada neste estudo, foram obtidas as seguintes conclusões: 1) O método ...(Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of this study was to firstly establish an analytical method, which was the most satisfactory with reference to optimization of chromatographic conditions for HPLC. The method was then used to compare the residual monomer content in one hard chair-side reline resin (Duraliner II - D) and one heat-polymerized denture base resin (Lucitone 550 - L). Also, it was investigated the effect of two after polymerization heat-treatments on this residual monomer content. The HPLC operating conditions established were column ODS (15.0 x 0.46 cm), with 5 mm particles, mobile phase - 55% ACN : 45% deionized distilled water, flow injection rate - 0.8 mL/min., wave length detection - UV 230 nm, amount of sample solution injection 100 mL. Calibration curves were produced using standard solutions containing known amounts of each monomer evaluated (MMA - L; BMA - D) in mobile phase. The materials (D and L) were mixed and polymerized according to the manufacturer's instructions. Specimens (n = 18) of both materials were then divided into three groups, of six specimens each. Group I specimens were left untreated (GI - control). Specimens of group II (GII) were given heat treatment by microwave irradiation with 550 W for 3 min for material L and 650 W for 4 min for material D. For group III (GIII), L and D specimens were submitted to a heat-treatment by immersion in water at 55oC for 60 min and 10 min, respectively. Each specimen were cut into small pieces and subjected to an extraction procedure in methanol for 2 hours. The residual monomer content was then expressed as a percentage of residual monomer in the specimen. The percentage residual monomer data were analyzed by non-parametric Kruskall-Wallis test, at 99% level of confidence. In all groups evaluated, material D showed significantly higher (p<0.01) residual monomer mean values (GI - 0.87%; GII - 0.71%; ...(Complete abstract, click electronic access below) / Orientador: Ana Lucia Machado / Coorientador: Quezia Bezerra Cass / Banca: Carlos Eduardo Vergani / Banca: Neila Maria Cassiano / Mestre

Orientador: Marco Antonio Compagnoni / Banca: Helena de Freitas Oliveira Paranhos / Banca: Ana Carolina Pero / Resumo: Muitas tentativas de incorporar agentes antimicrobianos a resinas acrilicas para base protetica tem sido realizadas visando prevenir inflamacoes nos tecidos orais de usuarios de proteses. Entretanto, essas substancias podem ser liberadas da resina acrilica e afetar suas propriedades mecanicas. O metacrilato 2-ter-butilaminoetilo (TBAEMA) e uma substancia policationica que pode apresentar atividade antimicrobiana a partir de grupos amina presentes em sua composicao. Objetivos: 1) investigar uma possivel uniao quimica entre o TBAEMA e a matriz de uma resina acrilica e avaliar a presenca de grupos amina na superficie dos especimes; 2) verificar os efeitos causados pela incorporacao de TBAEMA sobre a resistencia flexural e a temperatura de transicao vitrea (Tg) da resina acrilica. Material e Método: Foram confeccionados especimes a partir de uma resina acrilica termopolimerizavel (Lucitone 550) contendo diferentes concentracoes de TBAEMA (0%, 0,5%, 1%, 1,50%, 1,75% e 2%) e posteriormente foram submetidos a avaliacoes em Espectroscopia de Infravermelho por Transformada de Fourier (FTIR), Espalhamento Superficial de Eletrons com Analise Quimica (ESCA) e Calorimetria Diferencial de Varredura (DSC). A avaliacao de resistencia a flexao foi realizada de acordo com as normas ISO/FDIS 1567. Resultados: Atraves de FTIR, observou-se bandas de absorcao na regiao 1300-1320 cm-1 do espectro dos grupos de resina acrilica modificada. Diferentes indices de Nitrogenio foram observados na superficie dos especimes atraves de analises em ESCA. A Tg diminuiu de acordo com a incorporacao de TBAEMA. A resistencia a flexao foi avaliada por meio de analise de variancia a um fator (ANOVA) seguida pelo teste de Tukey (α= 0,05). Observou-se que a resistencia a flexao diminuiu significativamente apos a adicao de TBAEMA em concentracoes de 1%, 1,5%, 1,75% e 2% (p<0,05). Conclusão: Pode ser concluido que: 1) Houve evidencias... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Several attempts to incorporate antimicrobials agents into denture base resins have been reported in order to prevent inflammation of oral tissues in denture wearers. However, these substances may be released from acrylic resins and affect their mechanical properties. The 2-tertbutylaminoethyl methacrylate (TBAEMA) is a polycationic substance that may displays antimicrobial activity from pendant amino groups. Objectives: 1) to investigate the possible chemical bound of TBAEMA to the matrix of acrylic resin and to analyze the presence of amino groups on the specimen surface; 2) to evaluate the effect of the incorporation of TBAEMA on flexural strength and glass transition temperature (Tg) of an acrylic resin. Material and Methods: Specimens were prepared from a heat-polymerized acrylic resin (Lucitone 550) mixed to different concentrations of TBAEMA (0%, 0.5%, 1%, 1.50%, 1.75% and 2%) and were submitted to Fourier Transform Infrared (FTIR) Spectroscopy, Electron Spectroscopy for Chemical Analysis (ESCA) and Differential Scanning Calorimetry (DSC) analyses. Flexural strength tests were performed according to ISO/FDIS 1567 specifications. Results: FTIR analysis showed absorbance bands at 1300-1320 cm-1 in the spectrum of TBAEMA-modified acrylic resin groups. Different nitrogen ratios were observed on specimens surfaces by ESCA measurements. The Tg decreased with incorporation of TBAEMA. Flexural strength data were analyzed by one-way ANOVA followed by Tukey's test (α= .05). The flexural strength decreased with the addition of 1%, 1.5%, 1.75% e 2% of TBAEMA (p<0.05). Conclusion: Within the limitations of this study, it may be concluded that: 1) There was an evidence of copolymerization between acrylic resin and TBAEMA and the presence of nitrogen indicate that amine groups were found on the specimens surfaces; 2) Flexural strength and glass transition temperature were affected after... (Complete abstract click electronic access below) / Mestre

Orientador: João Vieira de Moraes / Banca: José Eduardo Junho de Araújo / Banca: Rogério Lacaz Netto / A BFO possui a versão preliminar da tese, com alterações, sob o título: Estudo comparativo in vitro do comportamento, quanto à força necessária à remoção, de grampos circunferenciais de Prótese Parcial Removível com regimes de trabalho sobre esmalte e sobre um tipo de resina composta. / Resumo : Foi realizado um estudo experimental in vitro para investigar o comportamento da força necessária para o deslocamento de grampos circunferenciais de P.P.R. em dois grupos de corpos de prova: 1 com regime de trabalho do terminal retentivo sobre esmalte 2 com regime de trabalho do terminal retentivo sobre resina composta Para tal finalidade foi idealizado um dispositivo, construído a partir de uma máquina de costura de marca Elgin que tinha por objetivo simular repetidamente o movimento de introdução e remoção de grampos circunferenciais sobre os corpos de prova. O dispositivo contava ainda com uma plataforma para fixar os corpos de prova e permitir aferições, um contador de ciclos e um dinamometro. Os corpos de prova foram obtidos a partir da inclusão em gesso de dentes naturais extraídos, íntegros, do grupo dos molares, cujas áreas retentivas eram em esmalte natural ou construídas artificialmente, por adição de resina composta. Os grampos foram obtidos a partir de esculturas com resina acrílica e cera e fundidos em liga de cobalto cromo. A resina composta usada foi de última geração, do tipo monomodal, fotopolimerizável e retida no esmalte através de ataque ácido. Os testes foram realizados em meio aquoso, estabelecendo-se para cada corpo de prova cinco mil ciclos. Foram feitas verificações a cada cem ciclos até dois mil e a cada duzentos ciclos até o total de cinco mil. Os resultados mostraram que as variações na quantidade de força necessária para remover os grampos dos corpos de prova durante todo o período dos ensaios foi desprezível, sem significância, tanto para aqueles com áreas retentivas em esmalte como naqueles com áreas retentívas artificialmente feitas com resina composta / Abstract: An experimental study was undertaken in arder to find out lhe behavior of the required force to yield dislodgement of circumierential clasps of removable partial dentures ou two groups of samples. 1 with retentive terminais engaging and acting ou enamel 2 with retentive terminais engaging on enamel and acting on composite resm With this aim a device was designed based on a sewing machine (brand name Elgin) that could repeatedly simulate lhe introduction-removal movement of circunferencial clasps ou the samples. ln addiction the device had a platform to sustain the samples and permit measurements, a cycle counter and a dynamometer. The samples were constructed by inclusion in dental stone of extracted natural molar teeth whose retentive areas were ou natural enamel or composite resin addictions.The clasps were fabricated from wax ups of resin and wax and were cast with chromium cobalt alloy. The composite resin used was one of the last generation, monomodal type, photopolymerized and binded to the enamel by the acid etching technique. Tests were carried out in aqueous enviroment. Is was established a maximum of 5.000 cycles for each of the samples. Observatins were made from 100 to 100 cycles until 2.000 and from 200 to 200 cycles to 5.000. Results showed that variations in the amount of the required force for dislodgement of the clasps from the samples during the test periods had no significancy eather to those with retentive areas on the enamel or to those with retentive fabricated with addictions of composite resin / Mestre

Orientador: Humberto Gennari Filho / Banca: Alcides Gonini Júnior / Banca: Marcos Frossard / Banca: Marcelo Coelho Goiato / Banca: Eduardo Piza Pellizzer / Resumo: Foi investigada a alteração da posição dos dentes artificiais durante o processamento de próteses totais desde a fase de enceramento até o polimento, utilizando as resinas de marcas comerciais QC 20 (Dentsply) e Onda Cryl (Clássico - específico para microondas), com inclusão em gesso tipo II e com muralha de silicone, polimerizadas tanto pelo método de banho em água quente, quanto pela polimerização por energia de microondas. Foram utilizadas 40 amostras, obtidas de um modelo padrão e divididas em 4 grupos de 10, que receberam os seguintes tipos de processamento. a) grupo 1: incluídos em muflas metálicas com muralha de gesso pedra e polimerização por banho de água quente. b) grupo 2: incluídos em muflas de fibra de vidro com muralha de gesso pedra e polimerização por microondas. c) grupo 3: incluídos em muflas metálicas com muralha de silicone e polimerização por banho em água quente. d) grupo 4: incluídos em muflas de fibra de vidro com muralha de silicone e polimerização por energia de microondas. Para detecção dos deslocamentos dentais utilizou-se um guia de resina acrílica com 5 pontos pré-determinados nas cúspides dos dentes que proporcionaram pontos de referência nas réplicas permitindo mensurar tais deslocamentos através da digitalização das superfícies oclusais dos dentes e analisados por um programa de computador "AutoCad". Baseados nos resultados obtidos, de acordo com os materiais e metodologia empregados, concluimos que: 1. Em todas as técnicas de processamento de prótese total estudadas houve alteração da posição dos dentes após o processamento. 2. A técnica de inclusão com muralha de silicone e polimerização por microondas (grupo 4) apresentou os menores valores de alterações na posição dos dentes durante toda a fase de processamento... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Artificial teeth position changes were investigated during the upper complete denture processing, resins QC 20 (Dentsply) and Onda Cryl (Clássico - specific for microwave energy) were used and flasked in type II gypsum stone mould or silicone mould, polymerized in hot water bath as well in microwave polymerization. Forty specimens were used, which were obtained from one standard cast, and divided into four groups of ten that were processed as the following: a) group I (control): flasked in metallic muffles with gypsum stone barrier and conventional polymerization. b) group II: flasked in glass fiber muffles with gypsum stone barrier and polymerization by microwave energy. c) group III: flasked in metallic muffles with silicone barrier and conventional polymerization. d) group IV: flasked in glass fiber muffles with silicone barrier and microwave polymerization. An acrylic resin guide was used to detect teeth displacements, this guide was marked with 5 predetermined points in teeth cuspids that has proportionate reference points in the replicas. These points were used to measure, by AutoCad software, teeth displacements by digitized occlusal surface of the teeth. Based upon the results, according to the employed material and method, the following can be concluded: 1. It was observed teeth position changes after denture processing in all experimental groups. 2. The technique of flasking with silicone mould and microwave polymerization (group 4) presented minor degree of teeth position changes during all the processing. 3. The segments that constitute the smaller triangle represented by the points of teeth 15, 21 and 25 showed more homogeneity and linearity than the bigger triangle represented by the cuspids of 17, 21 and 27. 4. These dimensional changes of shrinkage and expansion in both triangles followed a uniform sequence for all the segments, that is, as one segment changes, the others follow it, thus, they don’t occur randomly. / Doutor