Luminescence investigation of zinc oxide nanoparticles doped with rare earth ionsKabongo, Guy Leba 11 1900 (has links)
Un-doped, Tb3+ as well as Yb3+ doped ZnO nanocrystals with different concentrations of RE3+ (Tb3+, Yb3+) ions were successfully synthesized via sol-gel method to produce rare earth activated zinc oxide nanophosphors. The phosphor powders were produced by drying the precursor gels at 200˚C in ambient air.
Based on the X-ray diffraction results, it was found that the pure and RE3+ doped ZnO nanophosphors were highly polycrystalline in nature regardless of the incorporation of Tb3+ or Yb3+ ions. Moreover, the diffraction patterns were all indexed to the ZnO Hexagonal wurtzite structure and belong to P63mc symmetry group. The Raman spectroscopy confirmed the wurtzitic structure of the prepared samples.
Elemental mapping conducted on the as prepared samples using Scanning electron microscope (SEM) equipped with energy dispersive X-ray spectrometer (EDX) revealed homogeneous distribution of Zn, O, and RE3+ ions. The high resolution transmission electron microscope (HR-TEM) analyses indicated that the un-doped and RE3+ doped samples were composed of hexagonal homogeneously dispersed particles of high crystallinity with an average size ranging from 4 to 7 nm in diameter, which was in agreement with X-ray diffraction (XRD) analyses.
ZnO:Tb3+ PL study showed that among different Tb3+ concentrations, 0.5 mol% Tb3+ doped ZnO nanoparticles showed clear emission from the dopant originating from the 4f-4f intra-ionic transitions of Tb3+ while the broad defects emission was dominating in the 0.15 and 1 mol% Tb3+doped ZnO. Optical band-gap was extrapolated from the Ultraviolet Visible spectroscopy (UV-Vis) absorption spectra using TAUC‟s method and the widening of the optical band-gap for the doped samples as compared to the un-doped sample was observed. The PL study of ZnO:Yb3+ samples was studied using a 325 nm He-Cd laser line. It was observed that the ZnO exciton peak was enhanced as Yb3+ions were incorporated in ZnO matrix. Furthermore, UV-VIS absorption spectroscopic study revealed the widening of the band-gap in Tb3+ doped ZnO and a narrowing in the case of Yb3+ doped ZnO system.
X-ray photoelectron spectroscopy demonstrated that the dopant was present in the doped samples and the result was found to be consistent with PL data from which an energy transfer was evidenced. Energy transfer mechanism was evidenced between RE3+ and ZnO nanocrystals and was discussed in detail. / Physics / M.Sc. (Physics)
|
12 |
Luminescence investigation of zinc oxide nanoparticles doped with rare earth ionsKabongo, Guy Leba 11 1900 (has links)
Un-doped, Tb3+ as well as Yb3+ doped ZnO nanocrystals with different concentrations of RE3+ (Tb3+, Yb3+) ions were successfully synthesized via sol-gel method to produce rare earth activated zinc oxide nanophosphors. The phosphor powders were produced by drying the precursor gels at 200˚C in ambient air.
Based on the X-ray diffraction results, it was found that the pure and RE3+ doped ZnO nanophosphors were highly polycrystalline in nature regardless of the incorporation of Tb3+ or Yb3+ ions. Moreover, the diffraction patterns were all indexed to the ZnO Hexagonal wurtzite structure and belong to P63mc symmetry group. The Raman spectroscopy confirmed the wurtzitic structure of the prepared samples.
Elemental mapping conducted on the as prepared samples using Scanning electron microscope (SEM) equipped with energy dispersive X-ray spectrometer (EDX) revealed homogeneous distribution of Zn, O, and RE3+ ions. The high resolution transmission electron microscope (HR-TEM) analyses indicated that the un-doped and RE3+ doped samples were composed of hexagonal homogeneously dispersed particles of high crystallinity with an average size ranging from 4 to 7 nm in diameter, which was in agreement with X-ray diffraction (XRD) analyses.
ZnO:Tb3+ PL study showed that among different Tb3+ concentrations, 0.5 mol% Tb3+ doped ZnO nanoparticles showed clear emission from the dopant originating from the 4f-4f intra-ionic transitions of Tb3+ while the broad defects emission was dominating in the 0.15 and 1 mol% Tb3+doped ZnO. Optical band-gap was extrapolated from the Ultraviolet Visible spectroscopy (UV-Vis) absorption spectra using TAUC‟s method and the widening of the optical band-gap for the doped samples as compared to the un-doped sample was observed. The PL study of ZnO:Yb3+ samples was studied using a 325 nm He-Cd laser line. It was observed that the ZnO exciton peak was enhanced as Yb3+ions were incorporated in ZnO matrix. Furthermore, UV-VIS absorption spectroscopic study revealed the widening of the band-gap in Tb3+ doped ZnO and a narrowing in the case of Yb3+ doped ZnO system.
X-ray photoelectron spectroscopy demonstrated that the dopant was present in the doped samples and the result was found to be consistent with PL data from which an energy transfer was evidenced. Energy transfer mechanism was evidenced between RE3+ and ZnO nanocrystals and was discussed in detail. / Physics / M.Sc. (Physics)
|
13 |
Préparation et caractérisation de nouveaux éléments pour la conception de nanohybrides organiques /inorganiquesRivoal, Morgane 07 December 2012 (has links)
Actuellement, l'élaboration de matériaux nanohybrides organiques/inorganiques suscite l'engouement de nombreux chercheurs du fait de leurs diverses applications potentielles. Le but de ce projet de thèse a été de préparer et caractériser de nouveaux éléments inorganiques et organiques permettant la conception de nanohybrides multi-fonctionnels possédant des propriétés répondant aux problématiques actuelles. Dans cet objectif, nous avons préparé des nanoparticules d'oxyde de zinc (ZnO) en tant que composant inorganique par ablation laser. La surface de ces NPs peut être modifiée par des composés organiques possédant un groupe d'ancrage acide carboxylique. Nous avonssynthétisé et caractérisé des dérivés viologènes, bien connu comme de forts accepteurs d'électron, possédant le groupe d'ancrage. Les nanohybrides de ZnO/viologènes ont été préparés et caractérisés par diverses techniques de spectroscopie. Nous avons développé des voies de synthèse efficaces permettant d'obtenir une série de nouveaux hétérocycles possédant des propriétés de donneur d'électron : dérivés de dibenzo[2,3:5,6]pyrrolizino[1,7-bc]indolo[1,2,3-lm]carbazole. Ces nouvelles molécules présentent une forte stabilité thermique et une forte fluorescence dans le domaine du visible. Leurs propriétés d'absorption à un et deux photons (Proche-infrarouge) ainsi que leur habilité de donneur d'électron ont été étudiés expérimentalement et à l'aide de calculs de mécanique quantique. Les éléments organiques et inorganiques étudiés sont des motifs de choix pour l'élaboration future de nanohybrides utilisables pour diverses applications comme dans le domaine de l'énergie photovoltaïque ou encore l'imagerie médicale. / Currently, the development of organic/inorganic nanohybrid materials arouses the enthusiasm of many researchers owing to their potential applications. The aim of this thesis was to prepare and characterize new inorganic and organic components for the future design of new multi-functional nanohybrids with properties responding to the current challenges. For this purpose, we have prepared nanoparticles of zinc oxide (ZnO) as the inorganic component by laser ablation. The surface of these nanoparticles can be modified by an organic component bearing the carboxylic group as an anchor. We synthesized and characterized a number of viologen derivatives, well known as strong electron acceptors, involving the anchoring groups. The nanohybrids of ZnO/viologens were prepared and characterized by various spectroscopic techniques. We have developed efficient synthetic routes toward a series of new heterocycles possessing the electron donating properties: derivatives of dibenzo[2,3:5,6]pyrrolizino[1,7-bc]indolo[1,2,3-lm]carbazole. These new molecules exhibit high thermal stability and strong fluorescence in the visible range. Their one- and two-photon (Near-infrared) absorption properties and electron donor ability were investigated experimentally and by means of quantum mechanical calculations. The studied organic and inorganic components can serve as promising building blocks of choice for the future development of nanohybrids used in various application domains such as in the fields of photovoltaics and medical imaging.
|
14 |
Nanostructured Thin Films Prepared by Planetary Ball Milling: Fabrication, Characterization and ApplicationsSapkota, Raju 05 May 2022 (has links)
Planetary ball milling (PBM) is a well-known technique for efficient size reduction and homogenization of materials that has been used for many decades in various engineering and industrial processes. More recently, it has emerged as a unique top-down nanofabrication approach for nanomaterials based on nanoscale grinding. However, its potential application in nanostructured thin film fabrication has not been fully explored, as only a limited number of studies have been carried out. In this work, the effects of different grinding parameters (speed, time and solvents) were used to create previously unstudied nanoscale grinding conditions for nanostructured thin film materials via PBM with distinct and novel properties: Nanoparticles of silicon, titanium disilicide (TiSi2) and zinc oxide (ZnO) ground in different solvents (deionized (DI) water/ ethylene glycol (EG)/isopropyl alcohol) resulted in colloidal suspensions (or nanoinks) that could be used to coat various substrates (wafers, glass, flexible substrates, etc.) via drop casting, doctor blading or dip coating. Thin film properties such as wettability, electrical conductivity and gas sensing behavior are studied. The fabricated thin film coating properties could be tuned depending on the combination of starting powder materials, grinding parameters and resulting nanoparticle size/geometry: The influence of surface chemistry, solvent type, particle geometry, surface roughness and defects was shown to alter the conductivity and surface wettability of the resultant films. Thus, thin films formed using PBM nanoinks allow varied and tunable properties for advanced multi-functional coatings and devices.
To demonstrate the feasibility of PBM nanoinks for thin film device applications, ZnO nanoinks were used to create chemiresistive gas sensors that operate at room temperature. By varying grinding parameters (speed, time and solvent) thin film sensors with differing particle sizes and porosity were produced and tested with air/oxygen against hydrogen, argon and methane target gas species, in addition to relative humidity. Grinding speeds of up to 1000 rpm produced particle sizes and RMS thin film roughness below 100 nm, as measured by atomic force microscopy and scanning electron microscopy. Raman spectroscopy, photoluminescence and x-ray analysis confirmed the purity and structure of resulting films. The peak gas sensor response was found for grinding parameters of 400 rpm (average particle size 275 nm) and 30 minutes (average particle size 225 nm) in EG and DI water, respectively, which could be correlated to an increased film porosity and an enhanced electron concentration resulting from adsorption/desorption of oxygen ions on the surface of ZnO nanoparticles. Similarly, gas response and dynamic behavior were found to improve as the operating temperature was increased between 100 and 150 °C. These results demonstrate the use of low-cost PBM nanoinks to optimize the active materials for solution-processed thin film gas/humidity sensors that can operate at room temperature for use in environmental, medical, food packaging, laboratory, and industrial applications.
Overall, the nanogrinding technique can produce large amounts of nanoparticle suspension with variable particle sizes for creating thin films with tunable properties. By adjusting grinding parameters, the nanoparticle shape/size and properties can be varied resulting in nanoparticle inks for inexpensive coatings on various substrates and for use in different applications. / Graduate
|
15 |
Electron Filed Emission Studies of Nanostructured Carbon MaterialsIvaturi, Sameera January 2012 (has links) (PDF)
Field emission is the emission of electrons from a solid under an intense electric field, of the order of 109 V/m. Emission occurs by the quantum mechanical tunneling of electrons through a potential barrier to vacuum. Field emission sources offer several attractive features such as instantaneous response to field variation, resistance to temperature fluctuation and radiation, a high degree of focusing ability in electron optics, good on/off ratio, ballistic transport, and a nonlinear current-voltage relationship.
Carbon nanotubes (CNTs) are potential candidates as field emitters since they possess high aspect ratio and are chemically inert to poisoning, and physically inert to sputtering during field emission. They can carry a very high current density and do not suffer field-induced tip sharpening like metallic tips. In addition, the CNT field emitters have the advantage of charge transport through 1D channels and electron emission at the sharp tips due to large enhancement. But the injection of electrons from the back contact remains a technical challenge which requires binding of CNT emitters to metallic substrate. Also, detachment of the CNT from the substrate tends to occur with time. The electrically conducting mixtures of CNTs and polymer can provide an alternative route to address these issues in the field emission of CNTs. The composites can be casted on any substrate in desired shape and the polymer matrix provides necessary support.
The research work reported in this thesis includes the preparation of high quality multiwall carbon nanotubes (MWCNTs), MWCNT-polystyrene (PS) composites, and experimental investigation on field emission properties of MWCNT¬PS composites in two different configurations. Electrical conductivity and percolation threshold of the MWCNT-PS composites are also investigated to ensure their high quality prior to the field emission studies. The study has been further extended to reduced graphene oxide (rGO) coated on polymer substrate. The main results obtained in present work are briefly summarized below.
This thesis contains eight chapters.
Chapter 1 provides an overview of basics of field emission, and the potential of CNT and CNT-polymer composites as field emitters.
Chapter 2 deals with the concise introduction of various structural characterization tools and experimental techniques employed in this study.
Chapter 3 describes the synthesis of MWCNTs and characterization by using electron microscopy and Raman spectroscopy.
MWCNTs are synthesized by chemical vapor deposition (CVD) of toluene [(C6H5) CH3] and ferrocene [(C5H5)2 Fe] mixture at 980 °C. Here toluene acts as carbon source material and ferrocene provides catalytic iron (Fe) particles. The MWCNT formation is based on the thermal decomposition of the precursor mixture. Scanning electron microscopy (SEM) characterization shows that the MWCNTs are closely packed and quite aligned in one direction. The average length of MWCNTs is about 200 μm and outer diameter lies in the range of 50-80 nm. The high quality of as-prepared MWCNT sample is confirmed by Raman spectroscopy. The as-grown MWCNTs are encapsulated with catalytic Fe nanoparticles, revealed by transmission electron microscopy. The Fe nanoparticles trapped within the MWCNT serve as fantastic system for studying the magnetic properties. Three types of MWCNT samples filled with Fe nanoparticles of different aspect ratio (~10, 5 and 2) are synthesized by varying the amount of ferrocene in the precursor material, and their magnetic properties are investigated. Enhanced values of coercivity (Hc) are observed for all samples, Hc being maximum (~2.6 kOe) at 10 K. The enhancement in Hc values is attributed to the strong shape anisotropy of Fe nanoparticles and significant dipolar interactions between Fe nanoparticles.
Chapter 4 deals with the field emission studies of MWCNT-PS composites in the parallel configuration.
By incorporating as-prepared MWCNTs in PS matrix in a specific ratio, composites with varying loading from 0.01-0.45 weight (wt.) fraction are prepared using solution mixing and casting. High degree of dispersion of MWCNTs in PS matrix without employing any surfactant is achieved by ultrasonication. Low percolation threshold (~0.0025 wt. fraction) in the MWCNT-PS composites ensures the good connectivity of filler in the fabricated samples. Field emission of MWCNT¬PS composites is studied in two different configurations: along the top surface of the film (parallel configuration) and along the cross section of the sample (perpendicular configuration). In this chapter field emission results of the MWCNT-PS composites in parallel configuration are presented. The effect of charge transport in limiting the field emission of MWCNT-PS composite is discussed. Field emission results of MWCNT-PS composites in parallel configuration indicate that the emission performance can be maximized at moderate wt. fraction of MWCNT (0.15). The obtained current densities are ~10 µA/cm2 in the parallel configuration.
Chapter 5 presents the study of field emission characteristics of MWCNT¬PS composites of various wt. fractions in the perpendicular configuration. Till date most studies using nanotube composites tend to have the nanotubes lying in two dimensional plane, perpendicular to the applied electric field. In the perpendicular configuration, the nanotubes are nearly aligned parallel to the direction of the applied electric field which results in high field enhancement, and electron emission at lower applied fields.
SEM micrographs in cross-sectional view reveal that MWCNTs are homogeneously distributed across the thickness and the density of protruding tubes can be scaled with wt. fraction of the composite film. Field emission from composites has been observed to vary considerably with density of MWCNTs in the polymer matrix. High emission current density of 100 mA/cm2 is achieved at a field of 2.2 V/µm for 0.15 wt. fraction. The field emission is observed to follow the Fowler– Nordheim tunneling mechanism, however, electrostatic screening plays a role in limiting the current density at higher wt. fractions.
Chapter 6 highlights the field emission response of rGO coated on a flexible PS film.
Field emission of rGO coated PS film along the cross section of the sample is studied in addition to the top film surface of the film. The effect of geometry on the improved field emission efficiency of rGO coated polymer film is demonstrated. The emission characteristics are analyzed by Fowler–Nordheim tunneling for field emission. Low turn-on field (~0.6 V/µm) and high emission current (~200 mA/cm2) in the perpendicular configuration ensure that rGO can be a potential field emitter.
Furthermore, stability and repeatability of the field emission characteristics are also presented.
Chapter 7 deals with the synthesis, characterization, and field emission of two different kinds of hybrid materials: (1) MWCNT coated with zinc oxide (ZnO) nanoparticles (2) ZnO/graphitic carbon (g-C) core-shell nanowires. The field emission from the bucky paper is improved by anchoring ZnO nanoparticles on the surface of MWCNT. A shift in turn on field from 3.5 V/µm (bucky paper) to 1.0 V/µm is observed by increasing the ZnO nanoparticle loading on the surface of MWCNT with an increase in enhancement factor from 1921 to 4894.
Field emission properties of a new type of field emitter ZnO/g-C core-shell nanowires are also presented in this chapter. ZnO/g-C core/shell nanowires are synthesized by CVD of zinc acetate at 1300 °C. Overcoming the problems of ZnO nanowire field emitters, which in general possess high turn on fields and low current densities, the core-shell nanowires exhibit excellent field emission performance with low turn on field of 2.75 V/µm and high current density of 1 mA/cm2.
Chapter 8 presents a brief summary of the important results and future perspectives of the work reported in the thesis.
|
16 |
Low Temperature Charge Transport And Magnetic Properties Of MWNTs/MWNT-Polystyrene CompositesBhatia, Ravi 12 1900 (has links) (PDF)
Carbon nanotubes (CNTs) have been recognized as potential candidates for mainstream device fabrication and technologies. CNTs have become a topic of interest worldwide due to their unique mechanical and electrical properties. In addition, CNTs possess high aspect ratio and low density that make them an important material for various technological applications. The field of carbon nanotube devices is rapidly evolving and attempts have been made to use CNTs in the fabrication of devices like field emitters, gas sensors, flow meters, batteries, CNT-field effect transistors etc. These molecular nanostructures are proposed to be an efficient hydrogen storage material. CNT cylindrical membranes are reported to be used as filters for the elimination of multiple components of heavy hydrocarbons from petroleum and for the filtration of bacterial contaminants of size less than 25 nm from water. Recently, CNT bundles have been proposed to be a good material for low-temperature sensing.
CNTs have also been considered as promising filler materials due to extraordinary characteristics mentioned above. Fabrication of nanocomposites using CNTs as reinforcing material has completely renewed the research interest in polymer composites. The conductive and absorptive properties of insulating polymer doped with conducting filler are sensitive to the exposure to gas vapors and hence they can be used in monitoring various gases. The application of fiibre reinforced polymer composites in aeronautic industry are well known due to their high mechanical strength and light weight. Also, the conductive composite materials can be used for electromagnetic shielding. Desired properties in CNT-composites can be attained by adding small amount of CNTs in comparison to traditional filler materials. Due to high aspect ratio and low density of CNTs, percolation threshold in CNT-polymer composites can be achieved at 0.1 vol % as compared to ~16 vol. % in case of carbon particles. The research work 0.1 vol. %, as compared to reported in this thesis includes the preparation of multiwall carbon nanotube (MWNTs) and MWNT-polystyrene composites, experimental investigations on low temperature charge transport, and magnetic properties in these systems.
This thesis contains 7 chapters.
Chapter 1 provides an overview of CNTs and CNT-polymer composites. This chapter briefly describes the methods for synthesizing CNTs and fabricating CNT-polymer composites, charge transport mechanisms in CNTs and composites, and their magnetic properties as well.
Chapter 2 deals with the concise introduction of various structural characterization tools and experimental techniques employed in the present work. An adequate knowledge of the strengths and limitations of experimental equipment can help in gathering necessary information about the sample, which helps in studying and interpreting its physical properties correctly.
Chapter 3 describes the synthesis of MWNTs and their use as filler material for the fabrication of composites with polystyrene (PS). The characterization results of as-prepared MWNT and composites show that MWNTs possess high aspect ratio (~4000), and are well dispersed in the composite samples (thickness ~50-70 µm). The composite samples are prepared by varying the MWNT concentration from 0.1 to 15 wt %. The as¬fabricated composites are electrically conductive and expected to display novel magnetic properties since MWNTs are embedded with iron (Fe) nanoparticles.
Chapter 4 presents the study of charge transport properties of aligned and random MWNTs in the temperature range 300-1.4 K. The low temperature electrical conductivity follows the weak localization (WL) and electron-electron (e-e) interaction model in both samples. The dominance of WL and e-e interaction is further verified by magneto-conductance (MC) measurements in the perpendicular magnetic field up to 11 T at low temperatures. The MC data of these samples consists of both positive and negative contributions, which originates from WL (at lower fields and higher temperatures) and e-e interaction (at higher fields and lower temperatures).
Chapter 5 contains the results of charge transport studies in MWNT-PS composite near the percolation threshold (~0.4 wt %) at low temperatures down to 1.4 K. Metallic-like transport behavior is observed in composite sample of 0.4 wt %, which is quite unusual. In general, the usual activated transport is observed for systems near the percolation threshold. The unusual weak temperature dependence of conductivity in MWNT-PS sample at percolation threshold is further verified from the negligible frequency dependence of conductivity, in the temperature range from 300 to 5 K.
Chapter 6 accounts on the experimental results of magnetization studies of MWNTs and MWNT-PS composites. The observation of maxima in coercivity and squareness ratio at 1 wt % of Fe-MWNT in a polymer matrix show the dominance of dipolar interactions among the encapsulated Fe-nanorods within MWNTs. The hysteresis loop of 0.1 wt % sample shows anomalous narrowing at low temperatures, which is due to significant contribution from shape anisotropy of Fe-nanorods.
Chapter 7 presents brief summary and future perspectives of the research work reported in the thesis.
|