MORAIS, N. W. S. Estudo comparativo da conformabilidade mecânica dos aços MAR 350 e MAR 300. 2013. 60 f. Dissertação (Mestrado em Engenharia e Ciência de Materiais) - Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2013. / Submitted by Marlene Sousa (mmarlene@ufc.br) on 2015-02-23T18:06:18Z No. of bitstreams: 1 2014_dis_nwsmorais.pdf: 3693374 bytes, checksum: d24baecda8d0e8df5362d32c78aca251 (MD5) / Approved for entry into archive by Marlene Sousa(mmarlene@ufc.br) on 2015-02-24T17:08:03Z (GMT) No. of bitstreams: 1 2014_dis_nwsmorais.pdf: 3693374 bytes, checksum: d24baecda8d0e8df5362d32c78aca251 (MD5) / Made available in DSpace on 2015-02-24T17:08:03Z (GMT). No. of bitstreams: 1 2014_dis_nwsmorais.pdf: 3693374 bytes, checksum: d24baecda8d0e8df5362d32c78aca251 (MD5) Previous issue date: 2013-12-18 / The maraging steels are ultra - high strength materials that has great technological importance due its application in military and nuclear sectors . Because its applications, it is necessary to understand how the plastic properties of these materials behave, because the literature lacks information on the mechanical behavior of steel the Mar350 and alloy redeveloped Mar300 . This study investigated how different levels of cold deformation influence the properties of plastic anisotropy of both materials . Cold deformation were carried out on levels of 50, 70 and 80% by rolling and after was made annealing were the materials carried out at 900 ° C for 1h varying the rate of cooling, the samples were cooled in water , air and the furnace until the room temperature. The results of metallographic analysis showed that the materials do not undergo morphological changes in the grains by varying the cooling rate, but some coarsening undergo a deformation in 50 and 70%. The samples of cold rolled steel Mar350 80% showed an ultra- grain refinement and precipitation of an intermetallic phase while the samples of steel Mar350* showed grain refining compared to the other conditions for the same steel, but without undergoes a significant hardening. The texture measurements showed the evolution of the cold deformation there is a tendency to cleanup texture appears more intense γ fiber . The measurements show that some microtexture for most conditions studied the presence of other components less intense outside the fiber γ , these components that could be the reason for the displacement of ΔR zero. / Os aços maraging são materiais de ultra-alta resistência que tem grande importância tecnológica devida sua aplicação nos setores nuclear e bélico. Devido suas aplicações de responsabilidade, é necessário compreender como se comportam as propriedades plásticas desses materiais, pois a literatura carece de informações sobre o comportamento mecânico dos aços Mar350 e de liga desenvolvida Mar350*. Esse trabalho investigou como a diferentes níveis de deformação à frio influenciam as propriedades de anisotropia plástica de ambos materiais. Foram realizadas deformações a frio nos níveis de 50, 70 e 80% por laminação e após foram realizados recozimentos a 900°C por 1h variando-se a taxa de resfriamento, resfriado-se as amostras em água, ao ar e ao forno até a temperatura ambiente. Os resultados das análises metalográficas mostraram que os materiais não sofrem alterações morfológicas nos grãos com a variação de taxa de resfriamento, mas sofrem um coalescimento nas deformações de 50 e 70%. As amostras do aço Mar350 laminadas a frio em 80% mostraram um ultra-refino de grão e a precipitação de uma fase intermetálica enquanto as amostras do aço Mar350* mostraram um refino grão quando comparado às demais condições para o mesmo aço, mas sem sofre um endurecimento significativo. As medições de textura mostraram com o evoluir da deformação à frio há uma tendência de ‘limpeza’ da textura apresentado mais intensa a fibra γ. As medições de microtextura mostram que algumas para a maioria das condições estudadas a presença da componente cubo girado menos intensa γ, componentes estas que poderiam ser a justificativa para o afastamento de ΔR de zero e os menores valores de Rm.

BARROS NETO. J. R. Evolução da microestrutura e da textura cristalográfica durante a etapa de aquecimento do recozimento de um aço IF. 2013. 88 f. Dissertação (Mestrado em Engenharia e Ciência de Materiais) - Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2013. / Submitted by Marlene Sousa (mmarlene@ufc.br) on 2015-02-23T18:59:08Z No. of bitstreams: 1 2014_dis_jrbarrosneto.pdf: 4555176 bytes, checksum: 7286949e68fd6fdd519ee07a51dbfea0 (MD5) / Approved for entry into archive by Marlene Sousa(mmarlene@ufc.br) on 2015-02-24T17:17:13Z (GMT) No. of bitstreams: 1 2014_dis_jrbarrosneto.pdf: 4555176 bytes, checksum: 7286949e68fd6fdd519ee07a51dbfea0 (MD5) / Made available in DSpace on 2015-02-24T17:17:13Z (GMT). No. of bitstreams: 1 2014_dis_jrbarrosneto.pdf: 4555176 bytes, checksum: 7286949e68fd6fdd519ee07a51dbfea0 (MD5) Previous issue date: 2013-08-28 / The Interstitial Free (IF) steels were developed in the 70s aiming to obtain materials of good formability and good mechanical strength for application in the automotive industry. The crystallographic texture after the annealing process of the IF steel sheet has good formability role in these steels. In this work were studied the evolution of the microstructure and crystallographic texture of a stabilized IF steel to titanium (Ti) during the heating step in annealing. The samples were hot rolled, cold rolled (75% reduction in thickness) and annealed, respectively. During the heating step in the annealed the samples were removed for temperatures of 730, 740, 750, 760, 770, 780, 790, 800, 810, 820 ° C for analysis. It was evaluated the evolution of the microstructure of each sample removed from the oven by optical microscopy. The evaluation of the evolution of texture was made using the techniques of X-ray diffraction and EBSD (Electron Back Scatter Diffraction). The results show the development of recrystallization grain size and grain microstructure with increasing temperature. The evolution of texture shows that in cooler temperatures it is observed the stronger presence of fibers DL component and the cube spun than the DN fiber. With the rise of temperature occurs elimination of component spun cube and elimination of DL fiber increasing the intensity of DN fiber, but with the advent of preferred directions (components). The EBSD technique confirmed this behavior and allowed us to observe the evolution of texture and recrystallization temperature. / Os aços IF (Interstitial Free) foram desenvolvidos nos anos 70 objetivando obter materiais de boa conformabilidade e boa resistência mecânica para aplicação na indústria automobilística. A textura cristalográfica após o processo de recozimento das chapas de aço IF tem papel determinante na boa conformabilidade destes aços. Neste trabalho são estudadas as evoluções da microestrutura e da textura cristalográfica de um aço IF estabilizado ao titânio (Ti) durante a etapa de aquecimento no recozimento. As amostras analisadas foram laminadas à quente, laminadas a frio (75% de redução na espessura) e recozidas, respectivamente. Durante a etapa de aquecimento no recozimento foram retiradas amostras nas temperaturas de 730, 740, 750, 760, 770, 780, 790, 800, 810, 820 ºC para análise. Foi avaliada a evolução da microestrutura de cada uma das amostras retiradas do forno por microscopia ótica. A avaliação da evolução da textura foi feita utilizando as técnicas e difração de raios-X e EBSD (Electron Back Scatter Diffraction). Os resultados mostraram a evolução da recristalização dos grãos e o tamanho de grão na microestrutura com o aumenta da temperatura. A evolução da textura mostrou que em temperaturas mais baixas observa-se a presença mais intensa das fibras DL e da componente Cubo Girado do que a fibra DN. Com a elevação da temperatura ocorre a eliminação da componente Cubo Girado e da fibra DL aumentando a intensidade da fibra DN, mas com aparecimento de direções (componentes) preferenciais. A técnica de EBSD confirmou este comportamento e permitiu observar a evolução da textura e da recristalização com a temperatura.

PIMENTA, P. V. C. L. Simulação termomecânica do processo de lingotamento contínuo utilizando o método de volumes finitos baseado em elementos. 2014. 67 f. Dissertação (Mestrado em Ciências de Materiais) – Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2014. / Submitted by Marlene Sousa (mmarlene@ufc.br) on 2015-03-24T12:16:03Z No. of bitstreams: 1 2014_dis_pvclpimenta.pdf: 7933536 bytes, checksum: 59f63398e101f4083f7863690b47b92e (MD5) / Approved for entry into archive by Marlene Sousa(mmarlene@ufc.br) on 2015-03-24T15:25:17Z (GMT) No. of bitstreams: 1 2014_dis_pvclpimenta.pdf: 7933536 bytes, checksum: 59f63398e101f4083f7863690b47b92e (MD5) / Made available in DSpace on 2015-03-24T15:25:17Z (GMT). No. of bitstreams: 1 2014_dis_pvclpimenta.pdf: 7933536 bytes, checksum: 59f63398e101f4083f7863690b47b92e (MD5) Previous issue date: 2014-11-24 / The continuous casting technique in the last four decades has been large used for to production of semi-finished steel. The heat transfer is major mechanism and it occurs in various steps during the continuous casting. The quality of steel is directly related to the way the heat transfer occur because the thermal variations produce mechanical loads as well as contact forces which are generated through the rollers and shake of the mold. Such factors may cause defects such as fractures or cracks in the final product if the resulting stresses and strains exceed critical values. The technique must be improved in order to reduce the appearance of defects and the production time. For this a good understanding of physical phenomena involved during the solidification process is critical. The focus of this work is to apply the EbFVM (Element based Finite-Volume Method) approach to study the effects of linear tensions unidirectionally coupled with the temperature applied to continuous casting of the steel 1013D (0,3% of carbon) In the simulations we adopted some simplifications such as the Plane Strain and isotropic material. We also neglected the body forces contact with the rollers the liquid pressure on the walls of the steel ingot (ferrostatic pressure) and the convective effect. However despite of the simplifications adopted this work provides quantitative informations on the linear tensions accumulation that point out to areas of possible of cracks formations / A técnica de lingotamento contínuo nas últimas quatro décadas é cada vez mais utilizada na produção de aço semiacabado. A transferência de calor é o principal mecanismo dominante e ocorre em todas as etapas do processo. A qualidade do aço no lingotamento está diretamente relacionada à forma que ocorrem as trocas de calor pois as variações térmicas produzem carregamentos mecânicos assim como as forças de contato as quais são geradas por intermédio dos rolos e da oscilação do molde. Tais fatores podem causar defeitos como fraturas ou trincas no produto final caso as tensões e deformações resultantes excedam valores críticos. O aprimoramento da técnica tem a finalidade de evitar o surgimento de defeitos e reduzir o tempo de produção. Para isso é fundamental uma boa compreensão dos fenômenos físicos envolvidos ao longo do processo de solidificação. O foco deste trabalho é aplicar a abordagem do EbFVM (Element based Finite-Volume Method) no estudo dos efeitos das tensões lineares acopladas unidirecionalmente com a temperatura aplicado ao lingotamento contínuo do aço 1013D (0,3% de carbono) Nas simulações adotou-se algumas simplificações com o estado plano de tensões e isotropia do material. Descartando-se as forças de corpo o contato com os rolos a pressão do aço líquido nas paredes do lingote (pressão ferrostática) e o efeito convectivo. Contudo apesar das simplificações adotadas este trabalho traz informações quantitativas quanto a formação do acúmulo das tensões lineares que apontam para regiões de possíveis formações de trincas

PENNAFORT JUNIOR, L. C. G. Aplicação da mecânica da danificação na análise do comportamento de materiais compósitos poliméricos reciclados reforçados por fibras de coco. 2015. 112 f. Tese (Doutorado em Ciências de Materiais) – Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2015. / Submitted by Marlene Sousa (mmarlene@ufc.br) on 2015-04-30T16:16:16Z No. of bitstreams: 1 2015_tese_lcgpennafortjunior.pdf: 7709926 bytes, checksum: c55121a4bddba28059f966f77d35b30a (MD5) / Approved for entry into archive by Marlene Sousa(mmarlene@ufc.br) on 2015-05-04T10:27:04Z (GMT) No. of bitstreams: 1 2015_tese_lcgpennafortjunior.pdf: 7709926 bytes, checksum: c55121a4bddba28059f966f77d35b30a (MD5) / Made available in DSpace on 2015-05-04T10:27:04Z (GMT). No. of bitstreams: 1 2015_tese_lcgpennafortjunior.pdf: 7709926 bytes, checksum: c55121a4bddba28059f966f77d35b30a (MD5) Previous issue date: 2015-03-27 / With increasing the ecological movements around the world, whose the main objective aims to raise awareness and encourage the world's population to save natural resources, coupled with the need to divert grounded waste (sanitary or industrial) in order to reduce environmental problems and public health, arising f rom the improper disposal of solid waste, emerge incentives for recy cling, and the development of biodegradable materials. Given this context, the composites reinforced with natural fibers began to be highlighted in the scientific community. However, its utilization is still seen with suspicion due to little or no knowledge of these pr omising materials. Faced with this problem, arose the proposal of this investigative character work, in with it was researched and devel oped a fully recycled composite, of thermoplastic matrix (recycled PVC) reinforced with fibers obtained from the bark of green coconut s discarded. For this objective were used various tools of physical, chemical, thermal and mechanical characterization, whose amounts of d eformation fields were obtained by Digital Image Correlation (DIC), c omparing the image of the body not deformed with images of the deforme d body. Finally, we assessed the processes of damage of the composite, through experimental characterization of the evolution of t he isotropic damage by the methods of varying the effective elastic mod ulus (tensile test with loading and unloading) and by Tsai-Wu index wi th the parameters constitutive of hyperbolic tangent function, where the values found, in both methods, were within the expected range for composite, from 0.20 to 0.50. / Com os crescentes movimentos ecológicos em todo o mundo, onde o objetivo principal visa conscientizar e estimular a população mundial a poupar os recursos naturais, aliado a necessidade de se desviar os resíduos aterrados (sanitários ou industriais), de forma a reduzir os problemas ambientais e de saúde pública, decorrentes da disposição inadequada de resíduos sólidos, surgem os incentivos a reciclagem de materiais, bem como o desenvolvimento de materiais biodegradáveis. Diante deste contexto, os materiais compósitos reforçados com fibras naturais ganham destaque no meio científico. No entanto, seu uso ainda é tido com desconfiança, devido ao pouco ou nenhum conhecimento desses promissores materiais. Perante essa problemática, surgiu a proposta deste trabalho de caráter investigativo, em que foi pesquisado e desenvolvido um compósito totalmente reciclado, de matriz termoplástica (PVC reciclado) reforçado, com fibras obtidas da casca de cocos verdes descartados. Para esse objetivo foram utilizadas diversas ferramentas de caracterização física, química, térmica e mecânica, sendo os valores dos campos de deformação obtidos pela Correlação de Imagem Digital (CID), comparando a imagem do corpo não deformado com imagens do corpo deformado. E finalmente, avaliou-se os processos de danificação do compósito, através da caracterização experimental da evolução do dano isotrópico pelos métodosda variação do Módulo de Elasticidade efetivo (ensaio de tração com carga e descarga) e pelo índice de Tsai-Wu com os parâmetros constitutivos da função tangente hiperbólica, onde os valores encontrados, em ambos os métodos, mantiveram-se dentro da faixa esperada para compósitos, 0,20 – 0,50.

SILVA, Y. C. Envelhecimento térmico de metais de solda dissimilares da liga AWS ER NiCrMo-14 (Inconel 686). 2015. 95 f. Dissertação (Mestrado em Ciências de Materiais) – Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2015. / Submitted by Marlene Sousa (mmarlene@ufc.br) on 2015-06-08T13:20:44Z No. of bitstreams: 1 2015_dis_ycsilva.pdf: 7857852 bytes, checksum: 3d0a303891c3f3b5720af807c129b145 (MD5) / Approved for entry into archive by Marlene Sousa(mmarlene@ufc.br) on 2015-06-10T17:54:05Z (GMT) No. of bitstreams: 1 2015_dis_ycsilva.pdf: 7857852 bytes, checksum: 3d0a303891c3f3b5720af807c129b145 (MD5) / Made available in DSpace on 2015-06-10T17:54:05Z (GMT). No. of bitstreams: 1 2015_dis_ycsilva.pdf: 7857852 bytes, checksum: 3d0a303891c3f3b5720af807c129b145 (MD5) Previous issue date: 2015-02-06 / Nickel based alloys are highly recommended to oil industry due to its mechanical properties and corrosion resistance. The Inconel 686 alloy as-welded had its microstructure and mechanical properties studied in several works in Welding Engineering Laboratory of the UFC (Federal University Ceará). However, there is no known scientific studies regarding to the effects of thermal aging on the microstructure of this given alloy and its corrosion resistance. This study examines the AWS ER NiCrMo-14 (Inconel 686) alloy in a way that it was TIG welded using cold wire feed and aged at temperatures of 650 ° C and 950 ° C for 10, 50, 100 and 200 hours, with the objective to analyze the microstructure formed after aging treatment and its consequences in corrosion resistance. The ageing treatments caused a significant precipitation at both temperatures. In the treatment at 650 ° C there was a needled precipitation, of P or µ phases rich in molybdenum, around larger precipitates. In the sample of 950 ° C it was not observed the same precipitation as cited above, however, also presented an intense precipitation up to 13.82%. The precipitates were characterized by X-Ray diffraction (XRD) and Scanning Electronic Microscopic (SEM), Transmission Electronic Microscope (TEM), selected area electrons diffraction (SAD) and Energy Dispersive Spectroscopy (EDS). At the 650°C samples, it could be possible to identify, by using X-Ray diffraction, both M3C2 and M7C3 type carbides, μ and P phase. By using electron diffraction P phase was identified. At the 950°C treated samples, it could be possible to identify, by using X-ray diffraction and electron, the same stages that has been told above, except for the carbide M23C6 type. At this type, plaques were formed close to the interface with the base metal due to carbon migration from base metal (ASTM A36 Steel) to the nickel alloy and to the high temperature, which favors its formation. The precipitation had a great influence on the corrosion resistance of the samples. The alloy has been subjected to the immersion corrosion test according to ASTM G48 C method and anything samples had fail in temperature of 40 °C / As ligas de níquel são de fundamental importância para a indústria do Petróleo devido a suas propriedades mecânicas e a resistência a corrosão. A liga Inconel 686 como soldada teve sua microestrutura e suas propriedades mecânicas estudadas em diversos trabalhos realizados no laboratório de Engenharia de Soldagem da UFC (Universidade Federal do Ceará), porém não existe na literatura estudos sobre os efeitos do envelhecimento térmico na microestrutura desta liga e na sua resistência a corrosão. No presente estudo a liga AWS ER NiCrMo-14 (Inconel 686) foi soldada utilizando o processo TIG com alimentação de arame frio e envelhecida em temperaturas de 650 °C e 950 °C por 10, 50, 100 e 200 horas, com o objetivo de analisar a microestrutura formada após o envelhecimento térmico e as suas consequências na resistência a corrosão. Os tratamentos de envelhecimento causaram uma intensa precipitação em ambas as temperaturas. No tratamento a 650 °C ocorreu uma precipitação agulhada, de fase P ou µ ricas em molibdênio, em torno de precipitados maiores de fase P. Na amostra de 950 °C não foi observada a precipitação fina em torno da precipitação maior, mas também apresentou-se uma intensa precipitação, de até 13,82 %. Os precipitados foram caracterizados por meio de difração de raios X (DRX), análises de microscopia eletrônica de varredura (MEV), microscopia eletrônica de transmissão (MET), difração de elétrons de área selecionada (SAD), espectroscopia de energia dispersiva (EDS). Nas amostras de 650 °C foram identificados por difração de raios X carbonetos do tipo M3C2, M7C3 e fase µ e P e por difração de elétrons foram identificadas fase P. Nas amostras tratadas a 950 °C foram identificadas por difração de raios X e de elétrons as mesmas fases, com exceção do carboneto do tipo M23C6. Este formou-se em placas próximo a interface com o metal de base devido a migração de carbono do metal de base (aço ASTM A36) para a liga de níquel e da alta temperatura que favoreceu sua formação. A precipitação teve uma grande influência sobre a resistência a corrosão das amostras. A liga foi submetida ao ensaio de corrosão por imersão seguindo a norma ASTM G48 método C e algumas amostras apresentaram falhas a temperatura de 40 °C

PESSOA, A. R. P. Soldagem em chapas de aços inoxidáveis superduplex UNS S32750 utilizando o processo arame tubular. 2015. 271 f. Tese (Doutorado em Ciências de Materiais) – Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2015. / Submitted by Marlene Sousa (mmarlene@ufc.br) on 2015-06-15T18:45:20Z No. of bitstreams: 1 2015_tese_arppessoa.pdf: 25693307 bytes, checksum: 1dae9f6f74676e0a0e2068e11cf5e983 (MD5) / Approved for entry into archive by Marlene Sousa(mmarlene@ufc.br) on 2015-06-16T17:26:39Z (GMT) No. of bitstreams: 1 2015_tese_arppessoa.pdf: 25693307 bytes, checksum: 1dae9f6f74676e0a0e2068e11cf5e983 (MD5) / Made available in DSpace on 2015-06-16T17:26:39Z (GMT). No. of bitstreams: 1 2015_tese_arppessoa.pdf: 25693307 bytes, checksum: 1dae9f6f74676e0a0e2068e11cf5e983 (MD5) Previous issue date: 2015-04-17 / Superduplex stainless steels (SDSS) may be defined as a family of steels having a two-phase ferritic-austenitic microstructure and the good mechanical properties and high corrosion resistance of this alloy are attributed to this microestrutural balance. These excellent qualities attribute to SDSS great employability in the oil sector, where manufacturing and equipment maintenance are performed by welding, which if not executed properly, can have a negative effect on the metallurgical properties and this problem becomes more critical in multipass welding due to repeated thermal cycles. Among the several welding processes employed in the welding of SDSS, fell to this work was to evaluate the FCAW process in multipass welding joints of SDSS UNS S32750, regarding the selection of appropriate welding parameters and the influence of these parameters on microstructural transformations, mechanical properties and corrosion resistance of welded joints. Then, this work was divided into three steps: Stage 1 was the characterization of the base metal in as-received condition. In Stage 2, weldings were accomplished using a bead on plate (BOP) technique to determine the control factors and their levels to be used in the subsequent stage, in which an experimental design was conducted by Taguchi method with Alloy, Stick out, Shielding gas, welding gun orientation, Arc oscillation, Energy technique and Heat input used as control factors and quality characteristics were evaluated the ratio R/L, bead penetration, ferrite content and inclusions content and microhardness. Finally, in Stage 3 were performed multipass welding in joints and afterwards was executed: A microstructural characterization in three regions of Fusion Zone (Root, Filler and Cap) and Heat Affected Zone by Optical Microscopy (OM) and Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectroscopy (EDS) and were also performed a measurement of the ferrite content; measurement of inclusions content; microhardness tests and Critical Temperature Pitting (CPT) tests according to ASTM G150. The results showed, ferrite contents ranging from 44% and 54.9% and their highest values were observed when employed the alloy 2507, heat input of 1.6 kJ/mm and pulsed current. The lowest inclusions contents were obtained by using of shielding gas with the mixture of 96%Ar + 4%CO2 (Stage 2) and heat input of 1,6kJ/mm (Stage 3). The microhardness values in FZ of joints were not affected significantly by any of the control factors. Already, the results of CPT tests showed that pits nucleated preferentially within α, at α/γ grain boundaries and at interfaces areas between large diameter inclusions and the metallic matrix and propagated predominantly into α phase. The CPT values ranging from 47 °C to 78 °C, with highest were obtained for the alloy 2507, heat input of 1.6 kJ/mm and continuous current into Root region and for the alloy 2507, heat input of 1.6 kJ/mm and the pulsed current in Filler and Cap regions. From the three regions of FZs, the Root showed the best results with no defects, satisfactory ferrite contents, lowest inclusions contents and highest CPT values / Os aços inoxidáveis superduplex (AISDs) possuem uma microestrutura bifásica constituída por ferrita (α) e austenita (γ) e quando devidamente balanceadas conferem ao material, boas propriedades mecânicas e elevada resistência à corrosão. Qualidades que atribuem aos AISDs grande empregabilidade no setor petrolífero, onde a fabricação e manutenção de equipamentos são realizadas por soldagem e se executada inadequadamente, pode afetar negativamente as propriedades destes aços, o que se torna mais crítico quando há a imposição de inúmeros ciclos térmicos durante uma soldagem multipasse. Dentre os inúmeros processos de soldagem utilizados na soldagem dos AISDS, coube a este trabalho avaliar o processo arame tubular na soldagem multipasse em juntas do AISD UNS S32750, levando em consideração a seleção dos parâmetros de soldagem adequados, bem como a influência destes parâmetros nas alterações microestruturais, microdureza e resistência à corrosão das juntas soldadas. Desta forma, dividiu-se este trabalho em três etapas: A Etapa 1 consistiu na caracterização do metal de base na condição como recebido. Já na Etapa 2 foram realizadas soldagens por simples deposição para selecionar os fatores de controle e seus níveis a serem utilizados na etapa posterior, e o planejamento experimental foi realizado pelo método Taguchi com a Liga, Gás, DBCP, Técnica da Tocha, Tecimento, Técnica de Energia e Energia foram utilizados como fatores de controle e como variáveis de resposta escolheu-se a razão R/L, a penetração, a fração de ferrita, a fração das inclusões e a microdureza. E por fim, na Etapa 3 foram realizadas soldagens multipasse em juntas e posteriormente efetuou-se: uma caracterização microestrutural em três regiões da Zona Fundida (Raiz, Enchimento e Acabamento) e Zona Afetada pelo Calor através de Microscopia Ótica (MO) e Microscopia Eletrônica de Varredura (MEV) e Espectroscopia de Energia Dispersiva de Raios X (EDS); quantificação da fração de ferrita; quantificação da fração das inclusões; ensaios de microdureza e uma avaliação da resistência à corrosão por pites através dos ensaios de temperatura crítica de pite (CPT) seguindo a norma ASTM G150. Como resultados, obteve-se frações de ferrita entre 44% e 54,9% com seus maiores valores observados quando utilizou-se a liga 2507, a energia de 1,6 kJ/mm e a corrente contínua pulsada. As menores frações das inclusões foram obtidas pela utilização do gás de proteção com 96%Ar + 4%CO2 (Etapa 2) e da energia de 1,6kJ/mm (Etapa 3). As microdurezas na ZF das juntas não apresentaram diferenças significativas. Já os ensaios de CPT revelaram que os pites nuclearam preferencialmente no interior da α, nos contornos α/γ e nas interfaces entre inclusões de grande diâmetro e a matriz metálica, propagando-se exclusivamente através da α. Os valores de CPT apresentaram uma faixa de 47°C à 78°C, com os maiores valores obtidos para a liga 2507, a energia de 1,6 kJ/mm e a corrente contínua constante na região da Raiz e nas regiões do Enchimento e Acabamento ao utilizar-se a liga 2507, a energia de 1,6 kJ/mm e a corrente contínua pulsada. Dentre as três regiões das ZFs, a Raiz apresentou os melhores resultados com ausência de defeitos, frações de ferrita satisfatórias, menores frações das inclusões e maiores valores de CPT

LOPES, Rogério Mendes. A concepção do ensino de clonagem nos livros didáticos de biologia do ensino médio numa perspectiva histórica. 2015. 122 f. Dissertação (mestrado) - Universidade Federal do Ceará, Centro de Ciências, Programa de Pós-Graduação em Ensino de Ciências e Matemática, Fortaleza-Ce, 2015 / Submitted by Erivan Almeida (eneiro@bol.com.br) on 2015-06-26T19:28:33Z No. of bitstreams: 1 2015_dis_rmlopes.pdf: 6503003 bytes, checksum: af3e16a95436dd0a8f3cf46da0dfd965 (MD5) / Approved for entry into archive by Rocilda Sales(rocilda@ufc.br) on 2015-06-29T12:03:24Z (GMT) No. of bitstreams: 1 2015_dis_rmlopes.pdf: 6503003 bytes, checksum: af3e16a95436dd0a8f3cf46da0dfd965 (MD5) / Made available in DSpace on 2015-06-29T12:03:24Z (GMT). No. of bitstreams: 1 2015_dis_rmlopes.pdf: 6503003 bytes, checksum: af3e16a95436dd0a8f3cf46da0dfd965 (MD5) Previous issue date: 2015 / This research had as main purpose the science history analysis present in the secondary school biology textbooks, taking as focus the cloning theme. The choice of this theme happened due to many scientific, religious and ethical discussions, especially since the advent of Dolly the sheep in the mid 1990s. A second purpose of this research is providing to teachers a supporting material that talks historically about cloning and its social implications to be used during the classes about the theme. This research presented a deductive approach as method, founded in formal logical principles of bibliographic materials analysis that were chosen to the study, chasing an analysis founded in the rational logic of the arguments present on the selected material of the research. As to the research level, is characterized as an exploratory research, having as purpose to measure identifiable hypotheses to subsidize further studies. In this case the hypothesis that the use of the history of science applied to biology teaching in the cloning theme enhances the improved understanding of the subject by high school students, promoting the improvement of their learning. Still is outlined as a bibliographic research, constructed by search in books, dissertations and thesis related to the study of the history of science, besides the high school textbooks. The approach of history of science had as function to show that the science is not linear, nor the discoveries happen without the connection with other researches and social and historical events. It was tried to work through a historical analysis which took aspects that were analyzed on the historical narratives, such as: idea of continuity, accumulation of knowledge, linearity and presentation of positive results in researches. The results obtained in the research showed that the high school textbooks present only some aspects of history of science, being more evident the presence of biographies and the most important achievements of the scientists. / Esta pesquisa teve como objetivo central a análise da História da Ciência presente nos livros didáticos de Biologia do ensino médio, tomando como foco o tema Clonagem. A escolha desse tema se deu em virtude de ter gerado muitas discussões científicas, religiosas e éticas, especialmente desde o advento da ovelha Dolly, em meados da década de 1990. Um segundo objetivo da pesquisa é o de fornecer ao professor um material de apoio que aborde historicamente a Clonagem e suas implicações sociais para ser utilizado durante as aulas sobre o tema. Esta pesquisa apresentou, quanto ao método, a abordagem dedutiva, fundada em princípios lógicos formais de análise dos materiais bibliográficos selecionados para estudo, perseguindo uma análise fundada na lógica racional dos argumentos presentes nos materiais selecionados para a pesquisa. Quanto ao nível da pesquisa, caracteriza-se como uma pesquisa exploratória, tendo como objetivo mensurar hipóteses identificáveis para subsidiar estudos posteriores. Neste caso, a hipótese de que o uso da História das Ciências aplicada ao ensino de Biologia no tema clonagem potencializa a melhoria da compreensão do tema por parte dos alunos do ensino médio, promovendo a melhoria de sua aprendizagem. Ademais, delineia-se como uma pesquisa bibliográfica, constituída por consultas a livros, teses e dissertações relacionados ao estudo da História da Ciência, além dos livros didáticos do ensino médio. A abordagem da História da Ciência teve como função evidenciar que a Ciência não é linear, nem as descobertas acontecem sem ligação com outras pesquisas e eventos sociais e históricos. Buscou-se trabalhar, portanto, mediante uma análise de cunho histórico que levou aspectos que foram analisados nas narrativas históricas, a saber: a ideia de continuidade, de acumulação de conhecimento, de linearidade e da apresentação de resultados positivos nas pesquisas. Os resultados obtidos na pesquisa evidenciaram que os livros didáticos do ensino médio apresentam apenas alguns aspectos da História da Ciência, sendo mais evidente a presença de biografias e as principais realizações dos cientistas.

NUNES, E. B. Revestimentos de aços inoxidáveis duplex e superduplex pelo processo plasma pó. 2015. 305 f. Tese (Doutorado em Ciência de Materiais) – Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2015. / Submitted by Marlene Sousa (mmarlene@ufc.br) on 2015-07-06T16:57:23Z No. of bitstreams: 1 2015_tese_ebnunes.pdf: 22476533 bytes, checksum: 2ef39bc69a86e2ecad2fa58c580d892b (MD5) / Approved for entry into archive by Marlene Sousa(mmarlene@ufc.br) on 2015-07-22T15:57:30Z (GMT) No. of bitstreams: 1 2015_tese_ebnunes.pdf: 22476533 bytes, checksum: 2ef39bc69a86e2ecad2fa58c580d892b (MD5) / Made available in DSpace on 2015-07-22T15:57:30Z (GMT). No. of bitstreams: 1 2015_tese_ebnunes.pdf: 22476533 bytes, checksum: 2ef39bc69a86e2ecad2fa58c580d892b (MD5) Previous issue date: 2015-02-26 / The weld overlay of duplex (DSS) and superduplex (SDSS) stainless steels is an interesting alternative used in oil and gas industry, allowing to reach the desirable characteristics, such as corrosion resistance and good mechanical properties. The main objective of the present work was to develop and evaluate the operational and metallurgical characteristics of DSS/SDSS alloys weld overlays deposited by PTA-P on pipes. Initially, the welds were performed in single weld bead for evaluation of geometric characteristics and cost reduction and later in multipass to produce the coating, changing several operational parameters with deposition of DSS DIN 1.4462 and SSS UNS S32760. The microstructure was investigated using light microscopy, scanning electron microscopy (SEM), energy dispersive of X-ray spectroscopy (EDS) and X-ray diffraction (XRD). Critical Pitting Temperature (CPT) - ASTM G 150 and microhardness tests were carried out to evaluate the corrosion resistance and determining the microhardness over coating. The results showed that deposition of DSS and SSS demonstrated to be an interesting option for the weld overlay. It could to deposited in just one layer, coatings with low levels of dilution, important characteristics to assure a good performance of the coatings. The microstructure in weld metal of the coatings deposited with SDSS alloy was constituted by nitrides, however the DSS alloy was constituted by secondary austenite precipitation and a good balance between ferrite and austenite. The results of microhardness test showed that the coating is more resistance than the API 5L X65 and it was not observed higher levels in the coating near the interface coating/substrate. The CPT test showed that the first weld bead is less resistant in relation to the last bead deposited and the DSS alloy showed greater pitting corrosion resistance in relation to the SdSS alloy / A soldagem de revestimento com aços inoxidáveis duplex (AID) e superduplex (AISD) é uma boa opção que pode ser utilizada no setor de petróleo e gás natural, permitindo alcançar características desejadas, como resistência à corrosão e boas propriedades mecânicas. O objetivo do presente trabalho foi desenvolver e avaliar as características operacionais e metalúrgicas em soldagens de revestimento de dutos com deposição de AID/AISD pelo processo Plasma pó. Inicialmente, as soldagens foram realizadas em simples depósito para avaliação das características geométricas e redução de custos e, posteriormente, aplicados os revestimentos, variando diversos parâmetros do processo Plasma pó com deposição de AID DIN 1.4462 e AISD UNS S32760. A caracterização microestrutural consistiu de análises de microscopia ótica, microscopia eletrônica de varredura (MEV), espectroscopia de raio-x dispersivo em energia (EDS) e difração de raios-X (DRX). Ensaios de Temperatura Crítica de Pites (ASTM G 150) e ensaios de microdureza foram realizados para avaliar a resistência à corrosão do metal de solda e determinação da microdureza ao longo do revestimento. Os resultados mostraram que a deposição de AID/AISD pode ser uma boa opção para soldagem de revestimento, com deposição em apenas uma camada, com baixos níveis de diluição e com características favoráveis para garantir boas propriedades aos revestimentos. Em relação à microestrutura, os revestimentos depositados com a liga AISD UNS S32760 proporcionou uma quantidade considerável de nitretos no metal de solda, porém os revestimentos com deposição de AID DIN 1.4462 obtiveram maior quantidade de austenita secundária em relação aos nitretos, ambos com bom balanço de fases ferrita e austenita. Os resultados de microdureza dos revestimentos mostraram maior resistência do metal de solda em relação ao API 5L X65 com ausência de elevados picos de microdureza na interface. O ensaio de TCP mostrou que o primeiro cordão de solda é menos resistente em relação ao último cordão depositado e que a liga AID mostrou ter maior resistência à corrosão por pites em relação à liga AISD

CAMPOS, C. V. F. Suscetibilidade à corrosão sob tensão dos aços AISI 321 e 347 em meio de H2SO4 + CuSO4. 2003. 68 f. Dissertação (Mestrado em Engenharia e Ciência de Materiais) - Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2003. / Submitted by Marlene Sousa (mmarlene@ufc.br) on 2012-04-24T19:03:28Z No. of bitstreams: 1 2003_dis_cvfcampos.pdf: 6614687 bytes, checksum: 8f5a00275c03fe34c56319ae8c6080e8 (MD5) / Approved for entry into archive by Marlene Sousa(mmarlene@ufc.br) on 2012-04-24T19:10:57Z (GMT) No. of bitstreams: 1 2003_dis_cvfcampos.pdf: 6614687 bytes, checksum: 8f5a00275c03fe34c56319ae8c6080e8 (MD5) / Made available in DSpace on 2012-04-24T19:10:57Z (GMT). No. of bitstreams: 1 2003_dis_cvfcampos.pdf: 6614687 bytes, checksum: 8f5a00275c03fe34c56319ae8c6080e8 (MD5) Previous issue date: 2003-08 / Because of their resistance to high temperature corrosion by hydrogen sulfide, austenitic stanless steels are commonly used for equipment in desulfurization process. However, these materials are subject to sensitization (chromium carbide precipitation) from exposure in the temperature range 425 to 815ºC during fabrication or operation. Sensitization makes the equipment susceptible to failure from intergranular stress corrosion cracking caused by polythionic acid. Polythionic acid is formed by sulfur compounds, moisture, and air at ambient temperature. The main goal of the present work is to investigate the stress corrosion cracking susceptibility of stainless steels AISI 321 and 347 in polythionic acids using an alternative process that is to submit the samples to cooper-cooper sulfate-16% sulfuric acid test (ASTM A262 Pr.E). After the stabilization heat treatment at 900ºC for 75 minutes, samples were heat treated at 600ºC during 20, 40, 80, 120 and 140 hours and then exposed to boiling acidified copper sulfate solution for 72 hours. After exposure, the specimens were bent. The appearance of fissures or cracks was not observed in AISI 321 and 347 samples. The effectiveness of the solution has been made by submitting AISI 304L samples to the same environment . The AISI 304L samples with higher finishing have been cracked. The ones with fine-ground finishing have not been attacked. / Os aços inoxidáveis austeníticos têm sido bastante utilizados em equipamentos de unidades de dessulfurização de petróleo devido à sua boa resistência à corrosão em temperatura elevada. Contudo, este materiais estão sujeitos à sensitização (deficiência em cromo na região vizinha ao contorno de grão) quando expostos a temperaturas de 425 a 815°C, durante a operação ou processos de fabricação. A sensitização torna o equipamento suscetível à corrosão sob tensão na presença de tensões de tração e de ácidos politiônicos, formados pela interação de compostos sulfurosos, umidade e ar em temperatura ambiente. A resistência à corrosão sob tensão de amostras de aço inoxidável austenítico AISI 321 e 347, removidas de um tubo, foi investigada através do procedimento ASTM 262 Pr. E - ensaio alternativo e de execução mais fácil do que a simulação dos ácidos politiônicos. Os corpos de prova foram submetidos aos tratamentos térmicos de estabilização (900°C, durante 75 minutos) e de sensitização (600°C, durante 20, 40, 80, 120 e 140 horas), após o que foram expostos ao meio corrosivo de CuSO4 + H2SO4 durante 72 horas e depois submetidos ao ensaio de dobramento, não apresentando trincamento. A agressividade do meio utilizado no ensaio foi verificada através da utilização de amostras de aço AISI 304L sensitizadas durante 08, 14, 24 e 48 horas a 600°C e 24, 48 e 72 horas a 677°C. Verificou-se que somente as amostras com acabamento superficial feito com lixa n° 100 sofreram um intenso processo corrosivo.

TESSER, J. A. Caracterização de defeitos de soldagem por análise fractal utilizando emissão acústica em ensaios de tração. 2004. 110 f. Dissertação (Mestrado em Engenharia e Ciência de Materiais) - Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2004. / Submitted by Marlene Sousa (mmarlene@ufc.br) on 2012-04-25T14:34:44Z No. of bitstreams: 1 2004_dis_jatesser.pdf: 4788817 bytes, checksum: 0fa39e94c4b91b9c080ac89743aaa7ed (MD5) / Approved for entry into archive by Marlene Sousa(mmarlene@ufc.br) on 2012-04-25T14:35:48Z (GMT) No. of bitstreams: 1 2004_dis_jatesser.pdf: 4788817 bytes, checksum: 0fa39e94c4b91b9c080ac89743aaa7ed (MD5) / Made available in DSpace on 2012-04-25T14:35:48Z (GMT). No. of bitstreams: 1 2004_dis_jatesser.pdf: 4788817 bytes, checksum: 0fa39e94c4b91b9c080ac89743aaa7ed (MD5) Previous issue date: 2004-02 / The present work aims at characterizing and correlating waveforms of acoustic emission signals from welded test samples, with defects, of ASTM 516 - Grade 60 steel used in pressure vessels, pipes, storage spheres, etc., by us-ing fractal analysis and spectral analysis, in order to evaluate their structural integrity. The signals were generated by submitting the samples to tensile tests, and were analyzed in the time domain by using the box counting method, which gives the fractal dimension, and the rescaled range Hurst technique, and, in the frequency domain, the spectral method of Fourier. From the relations predicted by the scaling laws, it can be concluded that the exponents obtained from the spectral analysis and rescaled range Hurst analysis are correlated between themselves and to the fractal dimension obtained by the box counting method. It was also shown that there are two distinct regions which characterize the transi-tion between the elastic and plastic regimes for the samples submitted to the tensile loading. It has also been verified that this behaviour was characteristic of the welded materials as well as of the base metal. / O presente trabalho tem como objetivo caracterizar e correlacionar for-mas de onda de sinais de emissão acústica, utilizando métodos de análise es-pectral e fractal, em corpos de prova previamente soldados com seus respecti-vos defeitos, avaliando assim a integridade estrutural do material aço carbono ASTM 516 Grau 60, utilizado em vasos de pressão, tubulações, esferas de ar-mazenamento, etc. Os sinais de emissão acústica foram gerados submetendo os corpos de prova a ensaios de tração. Para análise dos sinais no domínio dos tempos, foram utilizados o método de contagem de caixas, que fornece a dimensão fractal, e o de intervalo re-escalado de Hurst, e no domínio das fre-qüências o método espectral de Fourier. Através das relações previstas pelas leis de escala, concluiu-se que os expoentes calculados pelos métodos espec-tral de Fourier e re-escalado de Hurst, correlacionam-se entre si, bem como com a dimensão fractal obtida pelo método de contagem de caixas. Mostrou-se também a existência de duas regiões de escala distintas que caracterizam a mudança do regime elástico para o regime plástico quando as amostras foram submetidas ao carregamento de tração. Verificou-se ainda que este comporta-mento foi característico tanto para os materiais soldados como para o metal de base.