Orientador: Jose Roberto Lovadino / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-21T22:42:33Z (GMT). No. of bitstreams: 1 Boscarioli_AnaPaulaTeixeira_D.pdf: 5232084 bytes, checksum: 382e181fcc8fa853165baa7ddc8e9507 (MD5) Previous issue date: 1996 / Resumo: O cimento de ionômero de vidro, dado às suas propriedades preventivas, vem se desenvolvendo muito, surgindo novos tipos, em busca de melhores propriedades mecânicas, estéticas e de manipulação. O propósito deste estudo foi verificar a alteração de cor por manchamento, de vários tipos de cimentos ionoméricos, em função da proteção e acabamento superficial, através de espectrofotometria, quantificando a concentração de corante depositado sobre o cimento...Observação: O resumo, na íntegra, poderá ser visualizado no texto completo da tese digital / Abstract: The glass ionomer cement, like a preventive material, comes evolving very much, appearing new kinds, to get better mechanic, aesthetic and manipulation properties. The purpose of this study was t evaluate color alteration from staining of the several cements kinds, due to surface protection and finishing, through spectrophometric study quantifying the dye concentration deposited over the cement ...Note: The complete abstract is available with the full electronic digital thesis or dissertations / Doutorado / Materiais Dentarios / Doutor em Ciências

Orientadores: Monica Campos Serra, Luis Alexandre Maffei Sartini Paulillo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-22T17:29:58Z (GMT). No. of bitstreams: 1 Ribeiro_AnaPaulaGranato_M.pdf: 3102293 bytes, checksum: 2bd01622329d42556f7464c5ff73d82d (MD5) Previous issue date: 1997 / Resumo: o objetivo deste estudo foi avaliar, espectrofotometricamente, a efetividade de diferentes protetores superficiais para três ionômeros de vidro modificados por resina. Os corpos de prova de cada material foram confeccionados, de acordo com as recomendações dos fabricantes, e submetidos às diferentes condições experimentais de tratamento superficial. Em seguida cada corpo de prova foi imerso, individualmente, em uma solução corante de azul de metileno a 0,05%, na qual permaneceram por 24 horas. Após este período, eles foram lavados, retirados das matrizes,' triturados e imersos em ácido nítrico a 65%, durante 24 horas. Posteriormente, as soluções foram centrifugadas e os sobrenadantes utilizados para as análises espectrofotométricas. Através das leituras de absorbância, foi possível inferir a quantidade de corante presente em cada corpo de prova. Não houve diferença quanto à penetração de corante entre os trê~ materiais restauradores, porém, todos necessitaram de proteção superficial. A resina fluida fotopolimerizável (Heliobond) apresentou os melhores resultados para os três ionômeros de vidro modificados por resina avaliados / Abstract: o objetivo deste estudo foi avaliar, espectrofotometricamente, a efetividade de diferentes protetores superficiais para três ionômeros de vidro modificados por resina. Os corpos de prova de cada material foram confeccionados, de acordo com as recomendações dos fabricantes, e submetidos às diferentes condições experimentais de tratamento superficial. Em seguida cada corpo de prova foi imerso, individualmente, em uma solução corante de azul de metileno a 0,05%, na qual permaneceram por 24 horas. Após este período, eles foram lavados, retirados das matrizes,' triturados e imersos em ácido nítrico a 65%, durante 24 horas. Posteriormente, as soluções foram centrifugadas e os sobrenadantes utilizados para as análises espectrofotométricas. Através das leituras de absorbância, foi possível inferir a quantidade de corante presente em cada corpo de prova. Não houve diferença quanto à penetração de corante entre os trê~ materiais restauradores, porém, todos necessitaram de proteção superficial. A resina fluida fotopolimerizável (Heliobond) apresentou os melhores resultados para os três ionômeros de vidro modificados por resina avaliados / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientador: Mário Fernando de Góes / Dissertação (mestrado profissional) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-22T14:40:39Z (GMT). No. of bitstreams: 1 Arita_CarlaHarueMartins_M.pdf: 3875036 bytes, checksum: a7eb7c2f429f80e13807b4154f6963ae (MD5) Previous issue date: 2013 / Resumo: O objetivo do estudo foi avaliar a união de cimentos à base de metacrilato à superfície de um compósito à base de silorano, com ou sem prétratamento de superfície, em teste de microtração. No total, 84 discos de resina à base de silorano (3mmX10mm) foram confeccionados, 42 discos tiveram a superfície tratada (ST) com jatos de óxido de alumínio (50?m) e os demais (42) não tiveram a ST. Os discos foram divididos em 6 grupos e foram cimentados aos pares (n=5) conforme descrição: G1 (SAM+CD)-discos sem ST com aplicação do sistema adesivo à base de metacrilato (SAM) e cimentados com cimento resinoso dual (CD); G2 (JSAM+CD)-discos com ST com aplicação do SAM e cimentados com CD; G3 (CA)-discos sem ST cimentados com cimento resinoso autoadesivo (CA); G4 (JCA)-discos com ST cimentados com CA; G5 (SAS+CD)-discos sem ST com aplicação do sistema adesivo da resina à base de silorano (SAS), foi feita a aplicação do adesivo hidrófobo seguido da aplicação do primer, e cimentação com CD; G6 (JSAS+CD)-discos com ST com aplicação do SAS e cimentados CD. Os conjuntos (disco/cimento/disco) foram armazenados em água deionizada por 24 horas. Os conjuntos foram seccionados para a obtenção de amostras em forma de palitos de (0,7 ± 0,1mm). O teste de microtração (?TBS) foi realizado à velocidade de 0,5mm/min até a fratura. Foram calculadas as médias, desvios-padrão e análise estatística (?=0,05). Foram analisados os modos de fratura. Quatro discos, de cada grupo, foram tratados, cimentados aos pares e seccionados ao meio para análise da interface de união. As médias e desvios-padrão dos grupos foram: G1=0(0); G2=47,96(9,12); G3=50,37(8,63); G4=57,07(12,01); G5=70,74(9,18); G6=59,24(9,91). A média do G1 foi inferior e estatisticamente diferente dos demais grupos, que não apresentaram diferenças estatísticas entre eles (p>0,05). A união dos materiais à base de metacrilato à superfície da resina composta à base de silorano é influenciada pelo tratamento de superfície. Em contra partida, a união de materiais à base de metacrilato fosfatado parece não ser influenciada pelo tratamento de superfície / Abstract: The aim of this in vitro study was the investigation of microtensile bond strength of low-shrinkage silorane-based composite discs (with or without pretreatment) cemented with methacylate based-cements. In total, 84 discs of silorane-based composite (3mmX10mm) were fabricated, 42 were pretreated (PT) and 42 were not (sandblasting with oxide aluminium of 50?m) and cemented in pairs. They were divided in 6 groups (n=5) as described: G1 - no PT discs with methacrylate based adhesive applied (MA) and cemented with a methacrylate based dual cure cement (DC); G2 - PT discs with MA applied and cementes with DC; G3 - no PT discs cemented with self-adhesive cement (SA); G4 - PT discs cemented with SA; G5 - no PT discs with the adhesive of silorane based composite (ASC) applied, in this group the bond was applied first followed by the primer, and cemented with DC; G6 - PT discs with ASC cemented with DC. After 24h of deionized water storage, the sets were serially sectioned into sticks (0,7 ± 0,1mm). The microtensile bond strength test (?TBS) was performed at a crosshead speed of 0,5mm/min until failure. The means were calculated and statistically analyzed (?=0,05). Modes of falure were also determined. Four discs, for each group, were PT, cemented in pairs and cut in half to interface analysis. The means and standard deviations for all groups were: G1=0(0); G2=47,96(9,12); G3=50,37(8,63); G4=57,07(12,01); G5=70,74(9,18); G6=59,24(9,91). The mean presented by group 1 was the lowest and statistically different comparing with the others, wich did not differ statistically among each other(p>0,05). The ?TBS strength of methacylated materiais was significantly influenced by the surface pretreatment. On the other hand, the ?TBS strength of methacrylate materials with phosphate groups does not seem to be influenced by surface pretreatment / Mestrado / Materiais Dentarios / Mestra em Materiais Dentários

Orientador: Francisco Jose de Souza Filho / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-25T18:57:55Z (GMT). No. of bitstreams: 1 GomesFilho_JoaoEduardo_M.pdf: 4077224 bytes, checksum: a5fbeb8c5cf9bbd8b59192bc1d6cc054 (MD5) Previous issue date: 1999 / Resumo: Um dos métodos mais práticos e usados para o estudo da biocompatibilidade dos cimentos endodônticos é a implantação de tubos de polietileno contendo esses materiais no tecido subcutâneo de ratos. A ação irritante desses cimentos é, então, avaliada pelo exame histopatológico da resposta tecidual ao redor do material. No entanto, o processamento histológico das peças contendo o tecido e o tubo, geralmente incluídos em parafina, apresenta dificuldades técnicas que podem influir na imagem final e consequentemente na avaliação dos resultados. O objetivo deste trabalho foi estudar a eficiência do glicol metacrilato como material de inclusão de tecido subcutâneo de ratos implantados com tubos de polietileno contendo cimento endodôntico. Para o experimento foram utilizados tubos de polietileno termicamente selados em uma das extremidades preenchidos com cimento endodôntico (Endométhasone), os quais foram implantados em tecido sUb,cutâneo de ratos. Após 30 dias, os ratos foram sacrificados e peças contendo tecido epitelial, tubo preenchido por cimento, tecido conjuntivo e tecido mscular foram removidos e fixados em Bouin por 24 horas e em seguida deixados em solução de formol tamponado até o momento do processamento histológico. Os tubos foram localizados no interior das peças e seccionados transversalmente, sendo que o segmento que continha a extremidade selada foi descartado e o outro dividido longitudinalmente ao meio para que fossem obtidas duas hemi-metades muito semelhantes. Uma hemi-metade foi processada histologicamente pelo método da parafina e a outra pelo método do glicol metacrilato, Os resultados obtidos com a inclusão em glicol metacrilato foram superiores aos da parafina, mostrando uma boa qualidade histológica, que permitiu uma melhor análise das células e dos tecidos com a microscopia óptica. Desta maneira pode-se concluir que a inclusão em glicol metacrilato é um método alternativo e eficiente para avaliar a biocompatibilidade de cimentos endodônticos em tecido subcutâneo de ratos / Abstract: One of the most practical and widely used methods to assess the biocompatibility of endodontic sealers is the implantation of polyethylene tubes filled with the sealer into the subcutaneous connective tissue of rats. The irritant effect of the sealers is then evaluated by the histological process of the tubes with surrounding tissue, usually using paraffin embedding, presents several technical difficulties wich can influence in the analysis of the results. The aim of this work was to study the efficence of glycol methacrylate as embedding material of rat subcutaneous tissue wich received implants of tubes filled with endodontic sealer. Polyethylene tubes hot sealed in one end and were filled with endodontic sealer (Endomethasone) were implanted into subcutaneous tissue of rats. After the 30 days, the animais were killed and blocks with epithelium tissue, tube and sealer, connective tissue and muscular tissue were removed and fixed in Bouin to 24 hours and in 10% buffered formalin until being processed. The tubes were then transversally cut to higher axis, the sealed part was despised ando the other one cut in the midle of the higher axis, this way we had two similar halves. One of the halves was process~d by paraffin embedding method and the other one by glycol methacrylate methad. The results acheived when the glycol methacrylate was used were highly superior than the ones with paraffin, showing a good histologic quality wich allowed an improved analysis of cell an tissues biology with ligth microscopy. Therefore, it is concluded that the glycol methacrylate is as alternative and efficent method to assess the biocompatibility of endodontic sealers into subcutaneous tissue of rats / Mestrado / Endodontia / Mestre em Clínica Odontológica

Orientador: Luiz Antonio Ruhnke / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-13T23:24:09Z (GMT). No. of bitstreams: 1 Cardoso_LuizAntonioMorais_M.pdf: 1019863 bytes, checksum: dc4008e8c8b82b38774422bea80439c6 (MD5) Previous issue date: 1990 / Resumo: O objetivo deste trabalho foi avaliar o efeito de um condicionamento ácido sobre cimentos de ionômeros de vidro após a presa clínica. Foram confeccionados trinta e dois corpos de prova cilíndricos (20mm de diâmetro e 1,5 mm de altura) para cada cimento avaliado e posteriormente divididos em grupos de oito que sofreram condicionamento ou não. Os tempos de imersão em água distilada foram de 24 horas ou 7 dias. Para a quantificação da solubilidade foi utilizado o teste gravimétrico. Os resultados obtidos comprovam que o condicionamento ácido nos moldes aqui empregado promove um aumento significativo na solubilidade dos materiais / Abstract: It was the object of this paper evalluate the effect of acid etchant on solubility of two glass ionomer cements set. Thyrty two cilindrics test samples (20mm of diameter and 1,5mm long) were prepared from each material and divided in groups of 8 that were etched or no. The imersion times in distiled water were 24 hour or 7 days. To determine the solubility was utilized the gravimetric test. The results obtained demonstrated that the etching here employed produce a significant rise in solubility of the materials / Mestrado / Materiais Dentarios / Mestre em Ciências

Orientador : Lourenço Correr Sobrinho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T15:08:52Z (GMT). No. of bitstreams: 1 Borges_GilbertoAntonio_D.pdf: 6983339 bytes, checksum: 31e20358d57bb9c3f1b76abb4e370566 (MD5) Previous issue date: 2003 / Resumo: o objetivo deste estudo foi avaliar o desajuste cervical antes e após a fixação de coroas totais IPS Empress 2, Cergogold e In Ceram, em preparos sobre dentes bovinos, utilizando 2 tipos de cimento. Noventa incisivos bovinos foram embutidos em resina e as porções coronárias foram preparadas para receber coroas totais completas, usando pontas diamantadas nO 4103 com paredes axiais com expulsividade de 8° e término cervical em ombro reto. Trinta coroas com 8,0 mm de diâmetro por 8,5 mm de altura foram confeccionadas para cada tipo de cerâmica. Após, as coroas foram adaptadas sobre os preparos com carga de 9 kgf por 1 minuto e a discrepância marginal foi medida com microscópio de mensuração (STM). Em seguida, as coroas foram removidas e 15 amostras de cada tipo de cerâmica foram cimentadas sobre os dentes com cimento resinoso (Variolink 11) e 15 com ionômero de vidro modificado por resina (Vitremer) e novamente a discrepância marginal foi medida. Os resultados foram submetidos à Análise de Variância e ao teste de Tukey (5%) e indicaram que os três sistemas cerâmicos apresentaram desajuste cervical após a cimentação estatisticamente superiores ao desajuste cervical antes da cimentação, para os dois cimentos. O sistema IPS Empress 2 apresentou valores de desajuste cervical estatisticamente superior ao Cergogold antes e após a cimentação. Nenhuma diferença estatística foi observada entre o sistema IPS Empress 2 e In Ceram e In Ceram e Cegogold. Para os três sistemas cerâmicos, nenhuma diferença estatistica foi observada para o desajuste cervical quando cimentadas com cimento resinoso e ionomero de vidro / Abstract: The purpose of this study was to evaluate the cervical fit before and after cementation of IPS Empress 2, Cergogold and In Ceram ali crowns, on bovine teeth preparation utilizing two kinds of the cement. Ninety bovin incisors were embedded in resin and the coronal portions of the teeth were prepared to receive complete crowns using a 4103 diamond bur under refrigeration with 10° of tapering and right shoulder. Thirty crowns with 8.0mm in diameter and 8.5mm height were fabricated for each ceramic system. After, the crowns were seated on the teeth with 9 kgf load for 1 minute and the marginal discrepancy was measured using a mensuration microscopic (STM). Afterwards, the crowns were removed and fifteen samples of each ceramic system were luted on the teeth with resin cement (Variolink 11) and glass ionomer cement (Vitremer) and the marginal discrepancy was measured again. The results were submitted to analysis of variance and Tukey's test (5%) and indicated that the three ceramics systems showed cervical fits after cementation statistically superior than cervical fits before cementation, for the two cements. The IPS Empress 2 showed values of the cervical fits statistically superior than Cergogold before and after cementation. No statistically significant difference was found between IPS Empress 2 and In Ceram and In Ceram and Cergogold. For the three ceramics systems, no statistically significant difference was found for the cervical fit cemented with resin cement and glass ionomer cement / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

Orientador: Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-23T23:10:32Z (GMT). No. of bitstreams: 1 Martins_Fabio_D.pdf: 4457611 bytes, checksum: 86f57f3d95c884d43b768399a95e8c73 (MD5) Previous issue date: 1998 / Resumo: Oobjetivo deste estudo foi verificar a resistência à tração de coroas totais e restaurações de classe II MOD, cimentadas em preparos efetuados em 64 dentes molares humanos hígidos, recém-extraídos, e armazenados em soro fisiológico por 3 meses, utilizando cimento de ionômero de vidro convencional Shofu Glaslonomer e modificado por resina Vitremer 3M. Após a profilaxia, as raízes de cada dente foram incluídas em resina acrílica. A coroa foi preparada inicialmente em tomo mecânico e a fmalização do preparo foi feita com ponta diamantada em alta rotação refrigerada à água, até a obtenção de um preparo cônico para coroa total ou um preparo estilizado tipo classe II, para restaurações MOD. Em seguida, as restaurações metálicas foram obtidas com liga à base de Ni-Cr através da técnica de fundição pelo método da cera perdida. Os corpos-de-prova foram divididos em oito grupos de 8 unidades ada, sendo quatro grupos para os preparos de coroa total e quatro para os preparos de restaurações de classe II MOD, ficando metade dos grupos cimentados com cada tipo de cimento ionomérico, com e sem ciclagem térmica. A cimentação foi realizada sob carga estática compressiva de 5 kgf durante 10 minutos e os ensaios de tração numa máquina de ensaio universal Otto Wolpert-Werke (Alemanha), nuína velocidade de 6 mm/min., após 24 horas de armazenagem. Os resultados foram submetidos à análise de variância e teste de Tukey a 5% de probabilidade. Os autores concluíram que o cimento de ionômero de vidro modificado por resina Vitremer-3M obteve os maiores valores de resistência à tração em relação ao cimento de ionômero de vidro convencional Shofu Glaslonomer, em todas as situações estudadas, exceto quando as restaurações MOD sofreram tratamento térmico / Abstract: The object of this study was to verify the resistance to tension strength of total and inlays MOD metalic crowns, cemented to human teeth with glass ionomer Iutins cement Shofu GIaslonomer and resin-modified glass ionomer Iuting cement Vitremer-3M. Sixty-four sound, recently-extracted human molars were used. The dental crown of each tooth was machined initially in a mechanicalIathe until the form adequate for the preparation for a total and inlays MOD crown was obtained, Iather, "the handpiece was used to frnishthe preparation. The total and inlays MOD crowns were obtained by the 10st-waX dental casting method, using a Ni-Cr based alIoy. The prepared teeth, with their respective cast croWllS, were separed into eight groups of 8 teeth each, cemented with the two cements, with and without termical cycle. Analysis of the variations recorded, in reference to the Tukey test, showed that the average - values obtained for the eight groups did show a statistically significant diferences in the comparison of the two rpaterials, and with the two preparation, with and without tennical cyc1e. Analysing the resuIts the autours conc1uded that the resin-modified glass ionomer Iuting cement Vitremer-3M have the most resistence of tension strength in alI cases, except with inlay MOD metalic Ni-Cr crowns with termica) cycle / Doutorado / Materiais Dentarios / Doutor em Ciências

Orientador: Luiz Antonio Ruknke / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-15T15:18:45Z (GMT). No. of bitstreams: 1 Sampaio_TeresadeJesusSousa_M.pdf: 1450218 bytes, checksum: e46b72e00131866b723b445769656c66 (MD5) Previous issue date: 1984 / Resumo: o objetivo deste trabalho foi verificar a inf1uência exercida pelas soluções antissipticas da cavidade oral sobre a solubilidade e desintegração do cimento de silicato Porcelana Melhorada da S.S.White comparando-a com a desintegração em água destilada que é o meio solvente recomendado pela especificação n. 9 da American Dental Association. Em virtude da dificuldade de separar o resíduo seco do próprio meio daquele deixado pelos corpos de prova do cimento, a desintegração nas soluções :antissépticas foi calculada a partir da porcentagem de fosfato liberado nos referidos meios. Os resultados analisados permitiram concluir que: 1) a desintegração foi maior no grupo constituído pelas soluções antissépticas "Flororal" e "Ma1vatricin", seguidas em ordem decrescente por ãgua destilada, "Malvona" e finalmente pelo grupo constituído pelas soluções de "Anapyon" e "Cepacol"; 2) a porcentagem de desintegração em água destilada, apresentada pelo cimento utilizado, está de acordo com o índice estabelecido pela especificação n. 9 da American Dental Association / Abstract: The present study was carried out to evaluate the influence of antisseptical solutions upon the solubility and disintegration of one brand of silicate cement, in comparison with the amount of disintegration in distilled water, according to American Dental Association Specification n. 9. Due to the fact that the application of the A.D.A. method may distort the results and cause difficult in interpretation, the disintegration was calculated indirectly from the phosphate percentage evaluated from the specimens. The results have shown that: 1) the disintegration level was bigger in the media M3 (Flogoral) and M4 (Malvatricin) followed by Ml (water distilled), M2 (Malvona) and finally by the group that presented the lowest disintegration, M5 (Anapyon) and M6 (Cepacol); 2) the disintegration percentage presented by the brand of silicate cement is in accordance with the level established by American Dental Association Specification n. 9 / Mestrado / Materiais Dentarios / Mestre em Odontologia

Orientador: Mario Fernando de Goes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-18T18:37:20Z (GMT). No. of bitstreams: 1 Boscarioli_AnaPaulaTeixeira_M.pdf: 2954229 bytes, checksum: ec4a71ee104cfdf7942dcfad7b811a94 (MD5) Previous issue date: 1993 / Resumo: O propósito deste estudo foi avaliar a resistência à compressão de dois cimentos de ionomero de vidro restauradores (Chelon-Fil e Vidrion R) com e sem proteção superficial e manipulados sob diferentes condições de temperatura e umidade relativa do ar, nos períodos de 1 hora e 24 horas de armazenamento. A especificação n° 09 da A. D .A. foi utilizada para adequar a proporção póníquido a uma consistência padrão para cada condição ambiental de trabalho. Foram confeccionadas 80 amostras para cada material e divididas em 08 grupos experimentais com 1° corpos de prova cada, sendo manipulados em ambiente "controlado" (T=23'+ ou -'1°C e 50'+ ou -'10 UR) e "não controlado" (T=25'+ ou -'1°C e 75'+ ou -'5 UR) e mantido com e sem proteção nos períodos de armazenamento. Os resultados demonstraram que não há diferença estatisticamente significante entre os materiais Chelon Fil e Vidrion R com relação a resistência à compressão, sendo que somente quando manipulado em ambiente controlado e armazenado no período de 24 horas sem proteção superficial houve diferença estatisticamente significante (p < 0,05) entre os materiais. Com relação à manipulação em ambiente de trabalho controlado e não controlado os grupos onde o Chelon Fil foi mantido com ou sem proteção superficial e armazenado durante 24 horas e o material Vidrion R protegido superficialmente e armazenado também em 24 horas apresentaram diferença estatisticamente significante (p < 0,05) para valor de resistência à compressão. 0s demais grupos não se diferiram quanto à manipulação nos diferentes ambientes de trabalho. A proteção superficial produziu valores de resistência à compressão reduzidos e estatisticamente significante '(p < 0,05) para o material Chelon Fil, exceto para o grupo manipulado em ambiente nAo controlado e armazenado por 1 hora. Já para o material Vidrion R somente o grupo manipulado em ambiente controlado e armazenado por 24 horas apresentou diferença estatisticamente significante com relação à proteção superficial (p < 0,05). Os demais grupos não se diferiram estatisticamente. O tempo de armazenamento de 24 horas apresentou valores de resistência à compressão superiores e estatisticamente significantes (p < 0,05) quando comparados ao período de 1 hora de armazenamento, com exceção do grupo manipulado em ambiente controlado e mantido com proteção superficial para o material Vidrion R / Abstract: The purpose of this study was to evaluate the compressive strength of two filling glass ionomer cements (Chelon Fil anel Vldrion R) with an without surface protection an manipulated under different conditions of temperature and relative humidity of the atmosphere, in 1 and 24 hours of storage. The specification number 9 of the A.D.A. was used to suit the powder/liquid ratio to a standarel consistency for each environmental work condition. Eighty samples of each material were mede and divided into eight experimental groups, each of them with ten samples, manipulated in "controlled" (T=23'+ ou -'1°C e 5O%'+ ou -'10% HR) and "non-controlled" (T=25'+ ou -'1°C e 75'+ ou -'5% HR) environmental and kept with and without protection in the storage periods. The results showed that statistically there is no significant difference between Chelon Fi! and Vidrion R conceming to their compressive strength. Statistically significant differences (p<O,05) between the material took peace only when the samples were manipulated in controlled environment and stored for 24 hours without surface protection. Conceming to the manipulation in controlled and non-controlled work environment, the groups in which Chelon Fil was kept with or without surface protection stored for 24 hours and VlDRION R with surface protection ,'and also stored for 24 hours presented statistically significant diferences (P<O,05) for compressive strength value. No difference was noted for the other groups conceming to the manipulation in different work environments. The surface protection produçed decrease and statistically significant (p<O,05) compressive strength values for Chelon Fil, except for the groups manipulated in non controlled environment anel stored for 1 hour. For Vidrion R, only the group manipulated environment and stored for 24 hours presented statistically significant difference related to surface protection, no statistic difference was noted between the other groups. For the 24 hours storage, superior and statistically significant compressive strength values were obtained when comapred with the 1 hour storage períod, except for the Vidrion R group manipulated in controlled environment and kept with surface protection / Mestrado / Materiais Dentarios / Mestre em Odontologia

Orientador: Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-18T20:18:38Z (GMT). No. of bitstreams: 1 Conceicao_EwertonNocchi_D.pdf: 6008838 bytes, checksum: cec5182119fc20eba397e1e94e18f007 (MD5) Previous issue date: 1993 / Resumo: O objetivo deste trabalho foi avaliar o condicionamento químico sobre a resistência ao cisalhamento da interface cimento resinoso ¿ liga metálica. Foram confeccionados 6 amostras metálicas medindo 10 mm de diâmetro por 2 mm de altura com a liga Resistal P. Após acabamento e limpeza das peças metálicas, foi realizado aquecimento a 960 o C durante 5 minutos em um forno à vácuo. Logo após, foram efetuados jateamentos com óxido de alumínio e novo procedimento de limpeza em ultrasom com água destilada por 10 minutos. Três amostras foram consideradas controle e as demais foram submetidas ao condicionamento químico com a solução "CG-ETCH" em 100 ml da solução condicionadora durante uma hora e mantidos armazenados a 70° C. A análise e a documentação topográfica foram realizadas com um microscópio eletrônico de varredura. Para realização dos ensaios de resistência ao cisalhamento 20 amostras metálicas medindo 6 mm de diâmetro por 3 mm de altura foram obtidas para cada um dos três agentes de cimentação: Comspan Opaque, Panavia Ex e Ali Bond 2. Destas, 10 amostras foram condicionadas quimicamente com a solução "CG-ET em 100" e as demais foram consideradas controle. Uma área de 4 mm de diâmetro por 5 mm de altura era deixada exposta para inserção dos agentes de cimentação manipulados conforme instruções dos fabricantes. A seguir, três porções de resina composta APH eram inseridos e adaptados nesta região e fotopolimerizados por 40 segundos cada uma. Logo após a confecção, os corpos de prova foram armazenados em estufa a 37 o C com umidade relativa de 100% por 24 horas e então, ensaiados em uma máquina de ensaio universal a uma velocidade de 13 mm/minuto. Com base nos resultados verificamos que: a) o condicionamento químico com a solução "CG-ETCH" alterou a morfologia da superfície da liga Resital P, propiciando microrretenções de aspecto alveolar uniforme; b) a liga Resistal P condicionada com a solução "CG-ETCH" apresentou valores numericamente maiores e estatisticamente diferentes (p < 0,05) de resistência ao cisalhamento, independentemente do tipo de agente de cimentação utilizado para fixação, quando comparado com os respectivos grupos controle; e c) independentemente do tratamento superficial da liga metálica, os agentes de cimentação Paanavia Ex e Ali Bond 2 apresentaram os maiores valores de resistência ao cisalhamento, sendo estatisticamente diferentes do cimento Comspan Opaque / Abstract: The purpose of this study was to evaluate chemical etching on shear bond strength of the resin luting-agent/metal interface. Six specimens measuring 2 mm in heigth and 10 mm in diameter were cast with Resistal P alloy. After cleaned and polished procedures the alloy specimens were fired to 960 o C for five minutes, and polished byair¬ abrasion with alumina particles. Then, they were cleaned with water in a ultrasonic system for ten minutes and dried. Three diskform specimens were considered contrai and the others were positioned separetely in bottles with 100 ml of "CG-ETCH" etchant and heated to 70 o C for 60 minutes. The examination and photogr,aphic documentation were made with a scanning electron microscope. For shear bond strength tests 20 diskform specimens measuring 3 mm in heigth and 6 mm in diameter were cast for each resin luting agent used in this study: Comspan Opaque, Panavia Ex and Ali Bond 2. Ten specimens were chemically etching with "CG-ETCH" etchant and the others were considered contrai groups. A metallic matrix and perforáted adhesive tape were used to bond composite to metal. The metallic matrix was 4 mm in diameter and 5 mm in heigth was positioned on the alloy surface. Then, the resin luting-agents were applied on the alloys surface according to the manufacturer's instructions and APH was loaded and ligth cured for 40 seconds in three increments. Ali the bonded specimens were stored in 100% humidity at 37 o C for 24 hours. The shear bond tests were made with Universal Testing Machine at a cross-head speed of 13 mm/minute. The analysis of the results indicated that a) the chemical etching with "CG-ETCH" etchant on the Resistal P alloy surface produced suitable and uniform microretention; b) High shear bond strengths were obtained with chemical etching by "CG-ETCH" etchant in ali test goups, being statistically significant different (p < 0.05) when compared to the contrai groups and c) the shear bond strengths obtained with Panavia Ex and Ali Bond 2 resin luting age'nts were not statistically different, but were statistically significant (p < 0.05) when compared with Comspari Opaque / Doutorado / Materiais Dentarios / Doutor em Ciências