Orientador: Marcelo Ferrarezi de Andrade / Banca: José Roberto Cury Saad / Banca: Osmir Batista de Oliveira Júnior / Banca: Luis Henrique Borges / Banca: Fernando Carlos Hueb de Menezes / Resumo: O objetivo deste trabalho foi avaliar a infiltração marginal da resina Flow Filtek™ e do cimento resinoso dual RelyX™ na fixação de inlays de cerômeros fotoativados com LEDs e Luz "Halógena". Foram selecionados 32 dentes íntegros recém-extraídos armazenados em solução de soro fisiológico no freezer, divididos em quatro grupos: Grupo I - aparelho Elipar™ FreeLight e resina Flow Filtek™; Grupo II - aparelho Ultralux® e Resina Flow Filtek™; Grupo III - aparelho Elipar™FreeLight e cimento resinoso RelyX™ e Grupo IV - aparelho Ultralux® e cimento resinoso RelyX™. Foram feitos 64 preparos cavitários com término em esmalte e cemento a 1 mm acima e abaixo da junção amelo-cementária respectivamente. As inlays foram jateadas internamente com óxido de alumínio de 100 æm com 40 Bar de pressão e, posteriormente foi feito o condicionamento das superfícies das inlays com ácido fosfórico a 37% durante 60 segundos, as quais foram lavadas e silanizadas. Após o condicionamento das inlays, foi feito o preparo da superfície dental com ácido fosfórico a 37% durante 15 segundos, as quais foram lavadas, secas com papel absorvente, tendo sido aplicado o adesivo dentinário Single Bond™ (3m/Espe), e fixadas com seus respectivos cimentos. Posteriormente à fixação, foram fotoativadas pelos aparelhos em íntimo contato com sua superfície por 60 segundos, termociclados com 1.000 ciclos variando-se a temperatura de 5ºC a 55ºC, em seguida imersas em solução de fucsina básica a 5% durante 24 horas, lavadas e seccionadas no centro da restauração para que fosse feita a medida da infiltração em um Software Image Tool calibrado em milímetros, pelo qual foram selecionados os resultados que apresentavam maiores infiltrações em medidas lineares para aplicação dos testes estatísticos...(Resumo completo, clicar no acesso eletrônico abaixo). / Abstract: The objective of this work was to evaluate the microleakage of the Flow Filtek™resin and dual luting RelyX™ in the fixation of composite resin inlays cured with LEDs and Halogenic Light units. 32 recently extracted complete teeth were selected stored in solution of physiologic serum in freezer, divided in four groups: I Group I- Elipar™ FreeLight unit and Flow Filtek™ resin; Group II- Ultralux® unit Flow Filtek™resin; Group III- Elipar™FreeLight unit and RelyX™ luting and Group IV- Ultralux® unit RelyX™luting. They were made 64 cavitary preparations with end in enamel and dentine with 1 mm above and below enamel-dentin junction respectively, the inlays were sandblasted internally with 100æm/40 pressure Bar and later made the conditioning of the surfaces of the inlays with phosphoric acid to 37% goes 60 seconds, washed and silanizadas. After the conditioning of the inlays they were made the preparation of the dental surface with phosphoric acid to 37% for 15 seconds, washed, dried with absorbent and applied paper the dentinal sticker Single Bond™ (3m/Espe) and fastened with their respective luting. Later the fixation, these were cured for the units in intimate contact with its surface for 60 seconds. The samples were then thermocycled with 1000 cycles varying the temperature of 5ºC and 55ºC, soon afterwards immersed in solution of basic fucsina to 5% for 24 hours, washed and split up in the center of the restoration so that it was made the measure of the microleakage in a Software Image Tool gaged in millimeters, where they were selected the results that presented larger leakage in lineal measures for application of the statistical tests... (Complete abstract, click electronic address below). / Doutor

O objetivo do presente estudo foi desenvolver e avaliar um Objeto Virtual de Aprendizagem (OVA) sobre agentes de cimentação com ênfase no Cimento de Fosfato de Zinco (CFZ) e verificar a sua influência no conhecimento teórico e habilidade prática em estudantes de graduação em Odontologia. Foram descritas a metodologia e as ferramentas necessárias para o desenvolvimento do OVA. Foi criado um questionário de avaliação pedagógica e técnica do OVA utilizando a escala Likert (0 nunca e 4 sempre). O OVA foi aplicado em 46 estudantes de graduação em odontologia que foram randomizada em 4 grupos: OVA Imediato (GIOVA n=9), OVA longitudinal (GLOVA n=15) e dois grupos controles sem OVA (GIC n=9 and GLC n=13). Os grupos imediatos tiveram acesso ao OVA ou livro por 20 minutos antes do teste de habilidade, enquanto os grupos longitudinais tiveram acesso por 15 dias. O desenvolvimento do objeto permitiu a criação de uma simulação virtual da manipulação do CFZ. O questionário de avaliação mostrou que aproximadamente 65% dos alunos deram 4 pontos e 14,85% deram 3 pontos. O software utilizado foi capaz de reunir as mídias em um OVA, sendo que esse objeto com simulação virtual sobre o CFZ possui alta taxa de aprovação entre os alunos de odontologia. Um pré e pós-teste de conhecimento teórico e dois testes laboratoriais foram realizados por todos os grupos e avaliados por examinadores cegos. Os estudantes que utilizaram o OVA obtiveram melhores resultados nos testes de habilidade do que seus controles. O pós-teste de conhecimento mostrou diferença estatística nos grupos longitudinais GLC (6.0±1.15) e GLOVA (7.33±1.43). Menor espessura de película foi encontrada com diferença estatística nos grupos que utilizaram o OVA: (GIC 25±9,3) e GIOVA (16,24±5,17); GLC (50±27,08) e GLOVA (22,5±9,65). Os grupos que utilizaram o OVA obtiveram maior tempo de presa do que seus controles, e o grupo imediato mostrou diferença estatística GIC (896±218,90) e GIOVA (1138,5±177,95). O OVA com simulação virtual sobre o CFZ possui alta taxa de aprovação entre os alunos de odontologia. O CFZ manipulado por estudantes que utilizaram o OVA tiveram melhores propriedades mecânicas nos testes laboratoriais. Portanto, os grupos que utilizaram o OVA obtiveram melhor habilidade clínica que seus controles e maior retenção de conhecimento após 15 dias. / The aim of this study was to develop and evaluate a Virtual Learning Object (VLO) on cementing agents with emphasis on Zinc Phosphate Cement (ZPC), verifying its influence in theoretical knowledge and practical ability of dentistry undergraduates. The methodology and tools needed to develop the VLO were described and a pedagogical and technique assessment using the Likert Scale (0 never and 4 always) about the object was created. The VLO was applied to 46 dentistry undergraduates randomized into 4 groups: immediate VLO (GIOVA n=9), longitudinal VLO (GLOVA n=15) and two control groups without VLO (GIC n=9 and GLC n=13). Immediate groups had access to VLO or book for 20 minutes before the skill test, while the longitudinal groups had access to VLO or book for 15 days. The development of the object allowed the creation of a virtual simulation of ZPC manipulation. The questionnaire indicates that, approximately, 65% of students gave 4 points to VLO and 14.85% gave 3 points to it. The software used to construct the VLO enables to gather all media in one object, including the virtual simulation on the ZPC, that has a high approval rating among dentistry undergraduates. Pre and post test theoretical knowledge and two laboratory skill tests were performed by all groups and evaluated by blinded examiners. Students who used the VLO obtained better results in skill tests than their controls. Theoretical knowledge showed statistically significant differences in post-test of longitudinal groups: GLC (6.0 ± 1.15) and GLOVA(7:33 ± 1.43). VLO groups achieved a smaller film thickness in the skill test with statistical difference: (GIC 25 ± 9.3) and GIOVA (16.24 ± 5.17); GLC (50 ± 27.08) and GLOVA (22.5 ± 9.65). The higher setting time occurred in the VLO groups, and the immediate group showed a significant difference: GIC (896 ± 218.90) and GIOVA (1138.5 ± 177.95). The VLO with virtual simulation on ZPC has high approval rating among dentistry undergraduates. The ZPC manipulated by students who used the VLO had better mechanical properties in laboratory tests. Therefore, the groups that used the VLO had better clinical skills than their controls and greater retention of knowledge after 15 days.

Objetivos: O objetivo desse estudo foi avaliar a influência da presença do cimento endodôntico e agente cimentante na retenção de pinos de fibra. Metodologia: Cento e oitenta dentes extraídos foram divididos em dois grupos (n=90) de acordo com a forma de obturação: condensação lateral ou obturação apenas do terço apical. Cada um destes grupos foi subdividido em três grupos (n=10) de acordo com o cimento utilizado para a obturação (AH Plus, Endofil e MTAFillapex). Os cimentos foram manipulados e acrescidos de corante Rodamina B na proporção de 0,1% para possibilitar visualização através da microscopia confocal a laser. Quinze dias após a obturação, estes dentes foram preparados para a cimentação do pino de fibra (Reforpost Angelus) com os cimentos RelyX ARC (ARC), U200 e Gold Label Cement Lining (GL). Os dentes foram seccionados transversalmente para obtenção de fatias com 1mm de espessura e submetidos à microscopia confocal a laser para verificar a penetração do cimento endodôntico nos túbulos dentinários, posteriormente ao teste de push-out. O padrão de falha foi analisado em esteromicroscópio e imagens representativas foram feitas em microscopia eletrônica de varredura. Os valores de resistência de união em MPa de acordo com a técnica de obturação foram analisados pelo teste de Mann-Whitney. Os valores de resistência de união dos grupos experimentais foram analisados pelo teste de Kruskal-Wallis e post hoc de Dunn, com nível de significância de 5%. Resultados: Não houve diferença significativa entre as formas de obturação (P>0,05). O tipo de cimento obturador influenciou a resistência de união, e o cimento MTA-Fillapex apresentou valores de resistência de união significativamente inferiores ao AH Plus (P<0,05). Os grupos que utilizaram GL para cimentação dos pinos de fibra de vidro apresentaram valores para o teste de push-out superiores aos cimentos resinosos (P < 0,05). Não houve diferença significativa entre o ARC e o U200 (P > 0,05). Conclusões: Valores de resistência de união mais altos foram observados quando os pinos de fibra foram cimentados com cimento GL . Os padrões de falha mistas foram predominantes e ocorreram em todos os grupos experimentais. / Aim: Evaluate the influence of the endodontic sealer and luting cements on the fiber post bond strength. Methodology: One hundred and eighty extracted teeth were assigned to two groups, considering the root filling technique: lateral condensation or root filling of the apical portion only. Each group were divided into three groups (n=10) according the sealer applied (AH Plus, Endofill or MTA-Fillapex). Rhodamine B was mixed to the sealer in a ratio of 0,1% in order to provide adequate fluorescence assessed by confocal microscopy. Fifty days after root canal filling, post-space preparation were performed with luting cements: RelyX ARC (ARC), U200 and Gold Label Cement Lining (GL). One thick slices were produced and submitted to confocal miscroscopy to assessed sealer penetration into dentinal tubules, and than submitted to push-out test. The failure modes were analysed in stereomicroscope and representative images were obtained in a scanning electron microscope. Push-out strength values of the root filling technique were analyzed using Mann-Whitney test. Push-out strength values of experimental groups were analysed using Kruskal-Wallis and Dunn´s post hoc test at significance level 5%. Results: No significant difference was observed (P>0.05) between the root filling technique. The type of endodontic sealer influenced the push-out bond strength, and MTA-Fillapex sealers presents lower bond strength values than AH Plus (P<0.05). Fiber posts cemented with GL presented higher push-out bond strength than resin cements (P<0.05). There was no significant difference between ARC and U200 (P>0.05). Conclusions: Fiber posts showed higher bond strength values when cemented with GL. Mixed failures were predominant and occurred in all the experimental groups.

O objetivo do presente estudo foi desenvolver e avaliar um Objeto Virtual de Aprendizagem (OVA) sobre agentes de cimentação com ênfase no Cimento de Fosfato de Zinco (CFZ) e verificar a sua influência no conhecimento teórico e habilidade prática em estudantes de graduação em Odontologia. Foram descritas a metodologia e as ferramentas necessárias para o desenvolvimento do OVA. Foi criado um questionário de avaliação pedagógica e técnica do OVA utilizando a escala Likert (0 nunca e 4 sempre). O OVA foi aplicado em 46 estudantes de graduação em odontologia que foram randomizada em 4 grupos: OVA Imediato (GIOVA n=9), OVA longitudinal (GLOVA n=15) e dois grupos controles sem OVA (GIC n=9 and GLC n=13). Os grupos imediatos tiveram acesso ao OVA ou livro por 20 minutos antes do teste de habilidade, enquanto os grupos longitudinais tiveram acesso por 15 dias. O desenvolvimento do objeto permitiu a criação de uma simulação virtual da manipulação do CFZ. O questionário de avaliação mostrou que aproximadamente 65% dos alunos deram 4 pontos e 14,85% deram 3 pontos. O software utilizado foi capaz de reunir as mídias em um OVA, sendo que esse objeto com simulação virtual sobre o CFZ possui alta taxa de aprovação entre os alunos de odontologia. Um pré e pós-teste de conhecimento teórico e dois testes laboratoriais foram realizados por todos os grupos e avaliados por examinadores cegos. Os estudantes que utilizaram o OVA obtiveram melhores resultados nos testes de habilidade do que seus controles. O pós-teste de conhecimento mostrou diferença estatística nos grupos longitudinais GLC (6.0±1.15) e GLOVA (7.33±1.43). Menor espessura de película foi encontrada com diferença estatística nos grupos que utilizaram o OVA: (GIC 25±9,3) e GIOVA (16,24±5,17); GLC (50±27,08) e GLOVA (22,5±9,65). Os grupos que utilizaram o OVA obtiveram maior tempo de presa do que seus controles, e o grupo imediato mostrou diferença estatística GIC (896±218,90) e GIOVA (1138,5±177,95). O OVA com simulação virtual sobre o CFZ possui alta taxa de aprovação entre os alunos de odontologia. O CFZ manipulado por estudantes que utilizaram o OVA tiveram melhores propriedades mecânicas nos testes laboratoriais. Portanto, os grupos que utilizaram o OVA obtiveram melhor habilidade clínica que seus controles e maior retenção de conhecimento após 15 dias. / The aim of this study was to develop and evaluate a Virtual Learning Object (VLO) on cementing agents with emphasis on Zinc Phosphate Cement (ZPC), verifying its influence in theoretical knowledge and practical ability of dentistry undergraduates. The methodology and tools needed to develop the VLO were described and a pedagogical and technique assessment using the Likert Scale (0 never and 4 always) about the object was created. The VLO was applied to 46 dentistry undergraduates randomized into 4 groups: immediate VLO (GIOVA n=9), longitudinal VLO (GLOVA n=15) and two control groups without VLO (GIC n=9 and GLC n=13). Immediate groups had access to VLO or book for 20 minutes before the skill test, while the longitudinal groups had access to VLO or book for 15 days. The development of the object allowed the creation of a virtual simulation of ZPC manipulation. The questionnaire indicates that, approximately, 65% of students gave 4 points to VLO and 14.85% gave 3 points to it. The software used to construct the VLO enables to gather all media in one object, including the virtual simulation on the ZPC, that has a high approval rating among dentistry undergraduates. Pre and post test theoretical knowledge and two laboratory skill tests were performed by all groups and evaluated by blinded examiners. Students who used the VLO obtained better results in skill tests than their controls. Theoretical knowledge showed statistically significant differences in post-test of longitudinal groups: GLC (6.0 ± 1.15) and GLOVA(7:33 ± 1.43). VLO groups achieved a smaller film thickness in the skill test with statistical difference: (GIC 25 ± 9.3) and GIOVA (16.24 ± 5.17); GLC (50 ± 27.08) and GLOVA (22.5 ± 9.65). The higher setting time occurred in the VLO groups, and the immediate group showed a significant difference: GIC (896 ± 218.90) and GIOVA (1138.5 ± 177.95). The VLO with virtual simulation on ZPC has high approval rating among dentistry undergraduates. The ZPC manipulated by students who used the VLO had better mechanical properties in laboratory tests. Therefore, the groups that used the VLO had better clinical skills than their controls and greater retention of knowledge after 15 days.

Objetivos: O objetivo desse estudo foi avaliar a influência da presença do cimento endodôntico e agente cimentante na retenção de pinos de fibra. Metodologia: Cento e oitenta dentes extraídos foram divididos em dois grupos (n=90) de acordo com a forma de obturação: condensação lateral ou obturação apenas do terço apical. Cada um destes grupos foi subdividido em três grupos (n=10) de acordo com o cimento utilizado para a obturação (AH Plus, Endofil e MTAFillapex). Os cimentos foram manipulados e acrescidos de corante Rodamina B na proporção de 0,1% para possibilitar visualização através da microscopia confocal a laser. Quinze dias após a obturação, estes dentes foram preparados para a cimentação do pino de fibra (Reforpost Angelus) com os cimentos RelyX ARC (ARC), U200 e Gold Label Cement Lining (GL). Os dentes foram seccionados transversalmente para obtenção de fatias com 1mm de espessura e submetidos à microscopia confocal a laser para verificar a penetração do cimento endodôntico nos túbulos dentinários, posteriormente ao teste de push-out. O padrão de falha foi analisado em esteromicroscópio e imagens representativas foram feitas em microscopia eletrônica de varredura. Os valores de resistência de união em MPa de acordo com a técnica de obturação foram analisados pelo teste de Mann-Whitney. Os valores de resistência de união dos grupos experimentais foram analisados pelo teste de Kruskal-Wallis e post hoc de Dunn, com nível de significância de 5%. Resultados: Não houve diferença significativa entre as formas de obturação (P>0,05). O tipo de cimento obturador influenciou a resistência de união, e o cimento MTA-Fillapex apresentou valores de resistência de união significativamente inferiores ao AH Plus (P<0,05). Os grupos que utilizaram GL para cimentação dos pinos de fibra de vidro apresentaram valores para o teste de push-out superiores aos cimentos resinosos (P < 0,05). Não houve diferença significativa entre o ARC e o U200 (P > 0,05). Conclusões: Valores de resistência de união mais altos foram observados quando os pinos de fibra foram cimentados com cimento GL . Os padrões de falha mistas foram predominantes e ocorreram em todos os grupos experimentais. / Aim: Evaluate the influence of the endodontic sealer and luting cements on the fiber post bond strength. Methodology: One hundred and eighty extracted teeth were assigned to two groups, considering the root filling technique: lateral condensation or root filling of the apical portion only. Each group were divided into three groups (n=10) according the sealer applied (AH Plus, Endofill or MTA-Fillapex). Rhodamine B was mixed to the sealer in a ratio of 0,1% in order to provide adequate fluorescence assessed by confocal microscopy. Fifty days after root canal filling, post-space preparation were performed with luting cements: RelyX ARC (ARC), U200 and Gold Label Cement Lining (GL). One thick slices were produced and submitted to confocal miscroscopy to assessed sealer penetration into dentinal tubules, and than submitted to push-out test. The failure modes were analysed in stereomicroscope and representative images were obtained in a scanning electron microscope. Push-out strength values of the root filling technique were analyzed using Mann-Whitney test. Push-out strength values of experimental groups were analysed using Kruskal-Wallis and Dunn´s post hoc test at significance level 5%. Results: No significant difference was observed (P>0.05) between the root filling technique. The type of endodontic sealer influenced the push-out bond strength, and MTA-Fillapex sealers presents lower bond strength values than AH Plus (P<0.05). Fiber posts cemented with GL presented higher push-out bond strength than resin cements (P<0.05). There was no significant difference between ARC and U200 (P>0.05). Conclusions: Fiber posts showed higher bond strength values when cemented with GL. Mixed failures were predominant and occurred in all the experimental groups.

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / The reduction of shrinkage stress of resin cements, without loss of their mechanical properties, is essential to longevity of adhesive luting procedures. It has been demonstrated that the delayed light-curing of dual-cured resin cements reduces the shrinkage stress. However, the effects of this postponement on mechanical properties showed are dependent form material composition. Thus, the aim of this study was to evaluate the effect of filler content on properties of dual-cured resin cements light-cured immediately or 5 minutes after their mixing. Two light-curing protocols were additionally evaluated, using a single or 3-point of light-activation. For this purpose, only the cement with 65% of filler was used. Experimental dual-cured resin cements were formulated using a monomeric matrix BisGMA/TEGDMA (1:3 in weight) and filled with 60, 65 or 68% of silanated barium borosilicate glass. The viscosity of experimental cements was measured using a digital viscometer. Bar-shaped specimens (25 x 2 x 2 mm) were confectioned, while the light-curing was performed immediately or 5 minutes after the insertion of cements into the mold (n = 7). Three-point bending test was performed and the values of flexural strength and elastic modulus were measured. The fractured specimens (n = 5) were included into epoxy resin cylinders, polished and the Vickers hardness measurement was performed. Data from viscosity were submitted to one-way ANOVA, while the data from mechanical properties were analyzed by two-way ANOVA. All pair-wise comparison were performed using Tukey’s test (α = 0.05). Specimens that were light-cured at 3 points showed the highest values of flexural strength. Only for light-activation at 1 point, the moment of light-activation affected the elastic modulus (higher for delayed). Cements with 68% of filler showed highest viscosity and those with 60% presented the lowest one. Irrespective of light-curing moment, the cement with 65% of filler presented the highest values of flexural strength and elastic modulus. Addition of 60% of filler resulted in the lowest elastic modulus, while 68% of filler resulted in lowest flexural strength. Regarding the hardness, the cement with 68% of filler showed the highest values, while there was no difference between 60 and 65% of filler. In conclusion, the filler content affects the mechanical properties of cements and this effect is independent form moment of light-curing. / A redução da tensão de contração de cimentos resinosos, sem perdas nas suas propriedades mecânicas, é essencial para a longevidade das cimentações adesivas. Tem sido demonstrado que a fotoativação tardia dos cimentos resinosos duais reduz as tensões de contração. Entretanto, a influência desta postergação da fotoativação sobre as propriedades mecânicas mostrou ser dependente da composição do material. Assim, o objetivo deste estudo foi avaliar o efeito da concentração de carga nas propriedades de cimentos resinosos de dupla ativação fotoativados imediatamente ou após 5 minutos de sua manipulação. Cimentos experimentais duais foram manipulados com matriz monomérica BisGMA/TEGDMA (1:3 em massa) com 60, 65 ou 68% de carga (em massa) de partículas silanizadas de bório-alumínio-silicato. A viscosidade dos cimentos experimentais foi avaliada em viscosímetro digital. Dois protocolos de fotoativação foram adicionalmente avaliados, usando um ponto de fotoativação ou 3 pontos, para isto, usou-se apenas o cimento com 65% de carga. Corpos-de-prova em forma de barra (25 x 2 x 2 mm) foram confeccionados, sendo a fotoativação realizada imediatamente ou 5 minutos após a inserção dos cimentos na matriz (n = 7). Ensaio de flexão de três pontos foi realizado e os valores de resistência flexural e módulo de elasticidade foram mensurados. Os corpos-de-prova fraturados foram embutidos (n = 5) em cilindros de resina acrílica, polidos e a leitura de dureza Vickers foi realizada. Os dados de viscosidade foram submetidos à ANOVA de uma via, enquanto que os dados das propriedades mecânicas avaliadas foram analisados por ANOVA de duas vias. Todas as comparações múltiplas foram realizadas com o teste de Tukey (α = 0,05). Amostras fotoativadas em 3 pontos apresentaram maiores valores de resistência flexural. Apenas para a fotoativação em 1 ponto, o momento de fotoativação afetou o módulo de elasticidade (maior para tardia). Os cimentos com 68% de cargas mostraram a maior viscosidade e os com 60% a menor. Independentemente do momento da fotoativação, o cimento com 65% de carga apresentou os maiores valores de resistência flexural e módulo de elasticidade, enquanto que adição de 68% de carga resultou nos menores valores. Já para dureza, o cimento com 68% de carga apresentou os maiores valores, não havendo diferença entre 60 e 65% de carga. Como conclusão, a concentração de carga afeta as propriedades mecânicas dos cimentos e este efeito independente do momento da fotoativação.

O presente estudo teve como objetivo avaliar comparativamente in vitro a resistência à fratura radicular de dentes tratados endodonticamente usando diferentes materiais obturadores: AH Plus (Dentsply/De Trey, Alemanha), Real Seal (Sybron Endo, EUA), GuttaFlow (Coltène/Whaledent, Suíça) , ActiV GP (Brasseler, EUA) e Thermafil (Dentsply-Tulsa Dental, EUA). Sessenta e quatro pré-molares inferiores foram divididos em Grupo Controle (n=4), onde as raízes não foram nem instrumentadas nem obturadas e outros 5 grupos de acordo com os materiais obturadores empregados: Grupo AH Plus (n=12); Grupo Real Seal (n=12); Grupo GuttaFlow (n=12); Grupo ActiV GP (n=12); Grupo Thermafil (n=12). As raízes foram instrumentadas com o sistema Protaper Universal (Dentsply-Maillefer, Suíça), e em seguida foram obturadas com os respectivos materiais. Após a obturação, todos os espécimes foram armazenados à 37º C com 100% de umidade por 72 horas e incluídos em resina acrílica. O ligamento periodontal foi simulado com Impregum, que formou uma fina camada entre a raiz e a resina acrílica. Os espécimes foram submetidos ao teste de resistência à fratura em uma máquina de ensaios triaxiais (1,0mm/min). Os valores médios obtidos e o desvio padrão (em Newtons) em ordem decrescente foram: Grupo controle 394,25 ± 56,17 N; Grupo ActiV GP 263 ± 89,32 N; Grupo Thermafil 198,17 ± 61,65 N; Grupo AH Plus 158,08 ± 31,56 N; Grupo Real Seal 154,92 ± 42,64 N e Grupo GuttaFlow 107,92 ± 20,72 N. Os dados foram submetidos aos testes ANOVA e Dunett (5%). Dentre os grupos experimentais, as raízes obturadas com ActiV GP mostraram-se mais resistentes à força vertical aplicada, porém similares aos grupos controle e Thermafil. Os grupos AH Plus, Real Seal e Thermafil mostraram-se similares estatisticamente quanto à resistência à fratura. O grupo GuttaFlow apresentou menores valores médios de resistência à fratura. / The aim of this study was to evaluate the in vitro vertical fracture resistance of endodontically treated teeth using different root filling materials: AH Plus (Dentsply/De Trey, Alemanha), Real Seal (Sybron Endo, EUA), GuttaFlow (Coltène/Whaledent, Suíça) , ActiV GP (Brasseler, EUA) and Thermafil (Dentsply- Tulsa Dental, EUA). Sixty four single-rooted human lower premolar were assigned into a Control Group (n=4), where the roots were not prepared or filled, and five experimental groups (n=12) according to the root filling materials: Group AH Plus; Group Real Seal; Group GuttaFlow; Group ActiV GP; Group Thermafil. The roots were prepared using Protaper Universal system (Dentsply-Maillefer, Suíça) and filled using one of the root filling materials. Then, the specimens were stored at 37º C at 100% humidity for 72 hours and included in acrylic resin. The periodontal ligament was simulated by the use of Impregum, which made a thin layer between the root and acrylic resin. The specimens were submitted to a vertical fracture resistance using a testing machine triaxiais (1,0mm/min). The values (Newton) and standard deviations obtained were: Control Group 394,25 ± 56,17N; Group ActiV GP 263 ± 89,32N; Group Thermafil 198,17 ± 61,65N; Group AH Plus 158,08 ± 31,56N; Group Real Seal 154,92 ± 42,64N and Group GuttaFlow 107,92 ± 20,72N. The data were submitted to ANOVA e Dunett tests (5%). Among the experimental groups, roots filled with ActiV GP showed the highest values of resistance of load vertical was applied, and were similar to Control Group and Thermafil. AH Plus, Real Seal and Thermafil groups showed statistical similar fracture resistance. GuttaFlow Group showed the lowest values of fracture resistance.

Submitted by isabela.moljf@hotmail.com (isabela.moljf@hotmail.com) on 2017-05-17T14:10:56Z No. of bitstreams: 1 deborapintoantunes.pdf: 1198844 bytes, checksum: d0dff20dab0cbefb8d4929858b0c3302 (MD5) / Approved for entry into archive by Adriana Oliveira (adriana.oliveira@ufjf.edu.br) on 2017-05-17T16:26:16Z (GMT) No. of bitstreams: 1 deborapintoantunes.pdf: 1198844 bytes, checksum: d0dff20dab0cbefb8d4929858b0c3302 (MD5) / Made available in DSpace on 2017-05-17T16:26:16Z (GMT). No. of bitstreams: 1 deborapintoantunes.pdf: 1198844 bytes, checksum: d0dff20dab0cbefb8d4929858b0c3302 (MD5) Previous issue date: 2012-01-01 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Avaliou-se a liberação de íon fluoreto de 2 cimentos de ionômero de vidro (CIV) anidro e 2 CIVs modificados por resina composta antes e após recarga com fluoreto de sódio neutro a 2% por 4min. e a proteção da superfície do CIV Maxxion R com um adesivo odontológico, um verniz cavitário e um esmalte incolor para unhas. Com uma matriz de aço inox com 2mm x 6mm, confeccionou-se 5 corpos de prova de cada material, os quais foram imersos em 5mL de água deionizada, trocada a cada 24h. Foram realizadas leituras em um potenciômetro calibrado acoplado a um eletrodo sensível a íons fluoreto nos dias 1, 2, 9 e 17 na 1ª e 2ª etapas, e as amostras foram tamponadas com solução TISAB III. Na 2ª etapa, as amostras foram submetidas à recarga e em seguida lavadas, secas e novamente imersas em 5mL de água deionizada. Na 3ª etapa foi realizada a proteção da superfície dos CIVs e feitas leituras nos 5min., 24h, 48h e 72h. Os dados foram submetidos aos testes estatísticos Post Hoc de Tukey e t Student (p<0,05). Concluiu-se que os CIVs anidros tiveram maior efetividade na liberação de íon fluoreto em comparação com os CIVs modificados por resina composta e o Maxxion R apresentou um comportamento homogêneo e estatisticamente significante nas duas etapas. Os CIVs possuem a capacidade de recarregar, especialmente os anidros. Todos os materiais protetores testados foram eficazes, e o esmalte incolor para unhas apresentou o melhor comportamento. / Was evaluated the fluoride ion release of 2 glass ionomer cements (GIC) and anhydrous 2 resin-modified GICs made before and after charge neutral sodium fluoride to 2% for 4 minutes. and protecting the surface of the IVC Maxxion R with a dental adhesive, a cavity varnish and a colorless nail polish. With an array of stainless steel with 6mm x 2mm, it was made five specimens of each material, which were immersed in 5 mL of deionized water, changed every 24 hours. Readings were taken in a calibrated potentiometer coupled to an electrode sensitive to fluoride ions on days 1, 2, 9 and 17 in the 1st and 2nd stages, and the samples were buffered with TISAB III solution. In Step 2, the samples were submitted to recharge and then washed, dried and again immersed in 5 mL of deionized water. In Step 3 was done to protect the surface of GICs and readings made in 5min., 24h, 48h and 72h. The data were subjected to statistical tests post hoc Tukey et Student (p <0.05). It was concluded that the GICs were more effective in anhydrous fluoride ion release compared to composite resin modified GICs and Maxxion R had a homogeneous behavior and statistically significant in two steps. The GICs have the ability to recharge, especially anhydrous. All protective materials tested were effective, and nail incolor enamel showed the best behavior.

Orientador: Lourenço Correr Sobrinho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-04T13:43:16Z (GMT). No. of bitstreams: 1 Reges_RogerioVieira_D.pdf: 465516 bytes, checksum: 5fc0375c76e29f88888b24dc2e9af545 (MD5) Previous issue date: 2005 / Resumo: O objetivo deste estudo foi avaliar a influência de duas fontes de luz sobre a dureza Knoop dos cimentos resinosos Variolink II, nas cores XL transparente ¿ (A1), A3, A2 e Opaco e Enforce B1, A2 e Branco Opaco, nos período imediato e 24 horas após a polimerização. Corpos-de-prova com 5mm de diâmetro por 1mm de espessura dos cimentos resinosos Variolink II (Ivoclar-Vivadent) e Enforce (Denstisply) foram preparados num molde de teflon, cobertos com uma tira de poliéster e disco de cerâmica feldspática Duceram na espessura de 2,0 mm e fotoativados por 40 segundos com aparelho XL 2500 (3M), com 615 mW/cm2 e 40 segundos com o aparelho LED ¿ Ultrablue Is (D.M.C.) com 610 mW/cm2 . A dureza Knoop foi efetuada no aparelho HMV-2, com carga de 50 gramas por 15 segundos, imediatamente e após armazenagem por 24 horas a 37o C. Doze penetrações foram feitas em cada corpo-de-prova para o cimento resinoso Enforce, sendo que cinco corpos-de-prova foram confeccionados para cada cor do cimento e cinco para o grupo controle (sem cerâmica) em cada tempo de armazenagem, totalizando 60 corpos-de-prova. Para o cimento Variolink II, quatro penetrações foram feitas em cada corpo-de-prova, sendo que cinco corpos-de-prova foram confeccionados para cada cor do cimento em cada condição experimental, totalizando 80 corpos-de-prova. Os dados foram submetidos à análise de variância e ao teste de Tukey (5%) e mostraram que o cimento resinoso Variolink II opaco apresentou o menor valor de dureza Knoop em relação as outras cores do cimento, para as duas fontes de luz e dois períodos de ativação (mediato e 24 horas). O aparelho fotoativador de lâmpada halógena apresentou valores de dureza Knoop estatisticamente superior em relação ao aparelho LED para as cores do cimento A2, A3 e opaco para a condição mediato e XL, A2 e A3 após 24 horas. Quando os dois métodos de fotoativação foram comparados para a mesma cor do cimento, os aparelhos fotoativadores com lâmpada halógena e LED (24 horas) apresentaram valores de dureza Knoop estatisticamente superiores aos valores fotoativados na condição mediato. A regressão linear positiva da dureza Knoop foi estabelecida em função da profundidade de fotoativação da amostra do cimento resinoso (Enforce) pela fotoativação direta e indireta pela interposição da cerâmica. O cimento resinoso Enforce na cor opaca mostrou valores de dureza Knoop estatisticamente inferior às outras cores do cimento. A dureza Knoop mediata mostrou valores de dureza Knoop na região de topo (100 µm) estatisticamente superior em relação a dureza na região de fundo (700 µm) / Abstract: The aim of this study was to evaluate the influence of two light sources in Knoop hardness values of resin cement Variolink II in the shade XL transparent (A1), A3, A2, and Opaque and Enforce B1, A2 and Opaque White, in the immediate time and 24 hours after polymerization. The specimens with 5.0 mm in diameter and 1.0 mm in thickness of resin cements Variolink II (Ivoclar-Vivadent) and Enforce (Dentisply) were made in the Teflon mould, covered with a Mylar strip and fledspatic ceramic Duceram Plus (DeguDent) disc 2.0 mm thick and photoactivated for 40 seconds with halogen light unit XL 2500 (3M), with intensity of 615 mW/cm2 and 40 seconds with LED ¿Ultrablue Is (D.M.C.) with power density of 610 mW/cm2. Knoop hardness was measured using HMV-2 (Shimadzu), with a 50g load for 15 seconds, immediately stored at 37o C for 24 hours. Twelve indentations were made in each specimen for the resin cement (Enforce). Five specimens were made for each color and five specimens for the control group (without ceramic) in each stored time, totaling sixty specimens. For the resin cement Variolink II, four indentations were made in each specimen, and five specimens were made for each one in each stored time, totaling eighty specimens. The data were submitted to variance analysis and Tukey¿s test (5%) and showed that the opaque shade of the resin cement had lower Knoop hardness value in relation to the other shades for both light sources and both activation periods (mediate and 24 hours). The halogen units showed Knoop hardness values higher than LED¿s for A2, A3 and opaque for mediate and XL, A2 and A3 after 24 hours. When the photoactivation methods were compared for the same shade halogen and LED (24 hours) showed higher Knoop hardness values than mediate photoactivation. Knoop hardness positive linear regression is a function of depth of specimen of resin cement direct and indirectly photoactivated. Opaque shade showed KHN statistically inferior to the others resin cement groups. Mediate KHN reading showed that Knoop hardness near top (100 µm) is statistically different from bottom surface (700 µm) / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

A cimentação de próteses e/ou de outros elementos protéticos constituem-se em uma preocupação permanente, já que uma das grandes aplicações do cimento de fosfato de zinco é como agente cimentante. No entanto, a reação de presa do cimento de fosfato de zinco, assim como o tempo de sua presa final, não estão ainda completamente esclarecidos. O presente estudo visa analisar, microestruturalmente, a evolução da reação de presa do cimento de fosfato de zinco. Mais especificamente, buscou-se mensurar, baseado no fenômeno conhecido como speckle dinâmico, o tempo de duração da reação de presa do cimento de fosfato de zinco, desde o momento do término da espatulação até a sua presa completa, em ambiente com temperatura e umidade relativa do ar controlada. A metodologia utilizada consiste na análise do speckle dinâmico obtido através da luz laser, em um ensaio não-destrutivo. A partir dos dados coletados pela técnica óptica de speckle, usando algoritmos computacionais, foi possível estabelecer os coeficientes de correlação temporal e momentos de intensidade. O tratamento estatístico permitiu relacionar e comparar com outros parâmetros tradicionais, químicos e mecânicos macroestruturais já existentes e estudados por outros autores. Pode-se concluir que os resultados alcançados pela nova técnica e pelos métodos convencionais são convergentes. / The prosthesis cementation and/or other prosthetic elements, consists in permanent concern, since one of the major applications of zinc phosphate cement is as lutting agent. This study aims at the microstructural analyze to the evolution of the zinc phosphate cement´s setting reaction. More specifically, searched to verify, based on the known phenomenon as dynamic speckle, how long takes the setting reaction of zinc phosphate cement, since the moment of the ending of the mix until your complete setting, in environment with air relative humidity and temperature controlled. The used methodology consist in the analysis of dynamic speckle gotten through the laser, in a non-destructive assay. From the data supplied by the laser speckle, it was possible to establish the temporal correlation coefficients and intensity moments. The statistical treatment, allowed to compare and relate with other traditional, chemical and mechanical macrostructural parameters, already existing and studied by other authors. It can be conclude that outcomes achieved by the new technique and with the conventional methods are convergent.