Made available in DSpace on 2014-06-11T19:35:03Z (GMT). No. of bitstreams: 0 Previous issue date: 2007-08-03Bitstream added on 2014-06-13T19:24:20Z : No. of bitstreams: 1 barbosa_sh_dr_sjc.pdf: 825696 bytes, checksum: 7d5f2983aadcc457cc4f6a75eeb2c368 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Este estudo analisou o efeito de 2 diferentes tratamentos de superfície na resistência de união de resinas nanoparticuladas antes e após envelhecimento. Blocos (N=128) das resinas Tetric EvoCeram (TE) (Ivoclar) ou Filtek Supreme (FS) (3M ESPE) foram preparados e divididos em 2 grupos: a) controle (sem envelhecimento); b) termociclagem (TC) (x5000, 5-55°C). Os blocos foram novamente divididos em dois grupos, de acordo com o tratamento de superfície: (1) jateamento com óxido de alumínio modificado pro sílica (CoJet, 3M ESPE)+silano (ESPE-Sil)+ Visiobond, (2) adesivo (A). Para o reparo, a mesma resina usada no substrato (FS ou TE) ou resina microhíbrida (Quadrant Anterior Shine, Cavex-QA) foi utilizada. Os espécimes foram submetidos ao teste de cisalhamento ou microtração (1mm/min). Os dados (MPa'mais ou menos'DP) foram analisados com os testes t-Student, ANOVA dois fatores e Tukey. Ensaio de microtração revelou efeito significante no tipo de resina de substrato (p<0.001) e no envelhecimento (p<0.001). Após TC, resina TE (37,6'mais ou menos'12,0) apresentou resistência a microtração significantemente inferior (p<0.05) a FS (45,7'mais ou menos'12,8). TC diminuiu a resistência de união para TE e FS quando comparado com os grupos controle (49,4'mais ou menos'15,6 e 52,2'mais ou menos'17,1, respectivamente). A resina composta usada para o reparo (TE, FS, QA) não afetou significantemente os resultados (p>0,05). Quando o teste de cisalhamento foi aplicado após TC, espécimes tratados com Cojet associado ao silano aumentaram significativamente a resistência de união para FS (21,5) quando comparado com o adesivo (14,8) (p<0,001), mas para TE o adesivo (22,29) foi mais mais efetivo que o Cojet (13,35) (p>0,05). / This study evaluated the effect of 2 different surface conditioning methods on the bond strength of nanofilled composites before and after aging conditions. Blocks (N=160) were prepared from composites namely, Tetric EvoCeram (TE) (Ivoclar) or Filtek Supreme (FS) (3M ESPE) and randomly divided into 2 groups: a) control (no aging); b) thermocycling (TC) (x5000, 5-55°C). The specimens were further assigned to two surface-conditioning methods: (1) Silica-coating (CoJet, 3M ESPE)+silane (ESPE-Sil), (2) Adhesive resin (A). As repair composites either the same material was used as the substrate (FS or TE) or a microhybrid one (Quadrant Anterior Shine, Cavex-QA). The specimens were submitted to either microtensile or shear bond test (1mm/min). Data (MPa'mais ou menos'SD) were analyzed using Student t-test, two-way ANOVA and Tukey's test. Microtensile test showed significant effect of the composite type (p<0.001) and the aging condition (p<0.001). After TC aging, TE composite (37.6'mais ou menos'12) showed significantly lower (p<0.05) microtensile bond strength results than FS (45.7'mais ou menos'12.8). TC decreased the bond strength results both for TE and FS when compared to the non-aged control group (49.4'mais ou menos'15.6 and 52.2'mais ou menos'17.1, respectively). The choice of repair composite (TE, FS, QA) did not significantly affect the results (p>0.05). When shear test was employed on TC aged, repaired specimens, silica coating and silanization significantly increased the bond strength for FS (21.5) when compared to adhesive resin application (14.8) (p<0.001) but for TE, adhesive resin (22.29) was more effective than silica coating (13.35) (p>0.05).

Orientador: Marco Antonio Bottino / Banca: Maria Fidela de Lima Navarro / Banca: Marcos Koiti Itinochi / Banca: Luiz Felipe Valandro Soares / Banca: Clóvis Pagani / Resumo: Este estudo analisou o efeito de 2 diferentes tratamentos de superfície na resistência de união de resinas nanoparticuladas antes e após envelhecimento. Blocos (N=128) das resinas Tetric EvoCeram (TE) (Ivoclar) ou Filtek Supreme (FS) (3M ESPE) foram preparados e divididos em 2 grupos: a) controle (sem envelhecimento); b) termociclagem (TC) (x5000, 5-55°C). Os blocos foram novamente divididos em dois grupos, de acordo com o tratamento de superfície: (1) jateamento com óxido de alumínio modificado pro sílica (CoJet, 3M ESPE)+silano (ESPE-Sil)+ Visiobond, (2) adesivo (A). Para o reparo, a mesma resina usada no substrato (FS ou TE) ou resina microhíbrida (Quadrant Anterior Shine, Cavex-QA) foi utilizada. Os espécimes foram submetidos ao teste de cisalhamento ou microtração (1mm/min). Os dados (MPa'mais ou menos'DP) foram analisados com os testes t-Student, ANOVA dois fatores e Tukey. Ensaio de microtração revelou efeito significante no tipo de resina de substrato (p<0.001) e no envelhecimento (p<0.001). Após TC, resina TE (37,6'mais ou menos'12,0) apresentou resistência a microtração significantemente inferior (p<0.05) a FS (45,7'mais ou menos'12,8). TC diminuiu a resistência de união para TE e FS quando comparado com os grupos controle (49,4'mais ou menos'15,6 e 52,2'mais ou menos'17,1, respectivamente). A resina composta usada para o reparo (TE, FS, QA) não afetou significantemente os resultados (p>0,05). Quando o teste de cisalhamento foi aplicado após TC, espécimes tratados com Cojet associado ao silano aumentaram significativamente a resistência de união para FS (21,5) quando comparado com o adesivo (14,8) (p<0,001), mas para TE o adesivo (22,29) foi mais mais efetivo que o Cojet (13,35) (p>0,05). / Abstract: This study evaluated the effect of 2 different surface conditioning methods on the bond strength of nanofilled composites before and after aging conditions. Blocks (N=160) were prepared from composites namely, Tetric EvoCeram (TE) (Ivoclar) or Filtek Supreme (FS) (3M ESPE) and randomly divided into 2 groups: a) control (no aging); b) thermocycling (TC) (x5000, 5-55°C). The specimens were further assigned to two surface-conditioning methods: (1) Silica-coating (CoJet, 3M ESPE)+silane (ESPE-Sil), (2) Adhesive resin (A). As repair composites either the same material was used as the substrate (FS or TE) or a microhybrid one (Quadrant Anterior Shine, Cavex-QA). The specimens were submitted to either microtensile or shear bond test (1mm/min). Data (MPa'mais ou menos'SD) were analyzed using Student t-test, two-way ANOVA and Tukey's test. Microtensile test showed significant effect of the composite type (p<0.001) and the aging condition (p<0.001). After TC aging, TE composite (37.6'mais ou menos'12) showed significantly lower (p<0.05) microtensile bond strength results than FS (45.7'mais ou menos'12.8). TC decreased the bond strength results both for TE and FS when compared to the non-aged control group (49.4'mais ou menos'15.6 and 52.2'mais ou menos'17.1, respectively). The choice of repair composite (TE, FS, QA) did not significantly affect the results (p>0.05). When shear test was employed on TC aged, repaired specimens, silica coating and silanization significantly increased the bond strength for FS (21.5) when compared to adhesive resin application (14.8) (p<0.001) but for TE, adhesive resin (22.29) was more effective than silica coating (13.35) (p>0.05). / Doutor

Objetivo: Este estudo avaliou a influência de bebidas e escovação na estabilidade de cor, rugosidade superficial e microdureza em profundidade de uma resina composta. Materiais e Método: 120 discos (10mm de diâmetro X 2mm de espessura) de resina composta (Filtek- Z250) foram preparados e polidos após 24 horas. A cor inicial e a rugosidade superficial inicial foram mensuradas e os espécimes foram divididos aleatoriamente em quatro grupos (vinho tinto, refrigerante, aguardente, ou saliva artificial controle) e três subgrupos (sem escovação; escovação com Colgate, ou escovação com Close Up Whitening). Os espécimes foram imersos na sua respectiva solução, 5x ao dia, por 5 minutos, durante 30 dias, sendo dois subgrupos escovados ao final de cada dia (120 movimentos/dia). A cor foi mensurada no 15º e no 30º dia de imersão; a rugosidade superficial final foi medida no 30º dia. Após o período de imersão, os espécimes foram armazenados em saliva artificial por 7 dias, quando a superfície dos mesmos foi polida e imediatamente realizou-se uma mensuração de cor. A alteração de cor foi mensurada com um espectrocolorímetro e analisada pelos valores de &Delta;E, &Delta;L, &Delta;a, e &Delta;b. Os valores de rugosidade (Ra-&mu;m) foram medidos com um rugosímetro. Com relação à microdureza, os espécimes primeiramente foram incluídos em resina de poliéster e seccionados no sentido transversal. Após o polimento destas superfícies, foram realizadas mensurações nas profundidades de 30&mu;m, 60&mu;m, 90&mu;m, 120&mu;m e 250&mu;m, empregando os parâmetros 25gf/40s de microdureza Knoop. Os dados foram submetidos à ANOVA e teste de Fisher\'s (&alpha;=5%). Resultados: Os valores de alteração de cor foram estatisticamente diferentes após a imersão nas bebidas; o vinho tinto promoveu a maior alteração, seguido pelo refrigerante e aguardente, que foram similares entre si e diferentes da saliva artificial. Nenhuma diferença foi observada com ou sem escovação, independentemente do dentifrício utilizado. Ao 30º dia, os espécimes apresentaram uma mudança de cor mais intensa do que ao 15º dia, após o repolimento, a cor dos espécimes foi similar à cor do 15º dia. As bebidas e a escovação influenciaram negativamente na rugosidade da superfície. Em relação à microdureza, não houve diferença significativa entre os grupos, independentemente da profundidade analisada. Conclusões: A mudança de cor da resina composta foi influenciada apenas pelas bebidas; a escovação não afetou a propriedade analisada. O repolimento não foi suficiente para promover o retorno da cor dos espécimes aos valores iniciais. A rugosidade superficial foi influenciada negativamente tanto pelas bebidas quanto pela escovação. Para a microdureza, a resina composta apresentou resultados similares independentemente das bebidas utilizadas e da presença ou ausência de escovação nos espécimes avaliados. / Objective: This study evaluated the influence of beverages and brushing on the color change, surface roughness and microhardness in depth of a composite resin. Methods: 120 composite resin disks (10mm-øX2mm-thickness; Filtek-Z250) were prepared and polished after 24h. Initials color and surface roughness were measured and specimens were randomly assigned into four groups (red wine, soft drink, sugar cane spirit, or artificial saliva control) and three subgroups (without brushing; brushing with Colgate, or brushing with Close Up Xtra Whitening). Specimens were immersed in the beverage 5x/day, for 5 minutes, over 30 days, being two subgroups brushed at the end of every day (120 moving/day). Color was measured at the 15th and 30th days of immersion; final surface roughness was measured at the 30th day. After the immersion period, specimens were stored in artificial saliva for 7 days, when their surfaces were repolished and immediately assessed by color. Color change was measured with a spectrocolorimeter and analyzed by &Delta;E, &Delta;L, &Delta;a, and &Delta;b values. The values of roughness (Ra - &mu;m) were measured with a rugosimeter. As regard microhardness, the specimens were firstly included in polyester resin and sectioned in the transverse direction. After polishing these surfaces, measurements were realized at depths of 30&mu;m, 60&mu;m, 90&mu;m, 120&mu;m and 250&mu;m, employing the parameters 25gf/40s of microhardness Knoop. Data were submitted to ANOVA and Fisher\'s tests (&alpha;=5%). Results: Color change values were statistically different after immersion in the beverages; red wine promoted the highest alteration, followed by soft drink and sugar cane spirit, which presented similar results among them and different from saliva. No difference was observed with or without brushing independently of the toothpaste used. At 30th day, specimens exhibited a color change higher than 15th day; after repolishing, the color of the specimens was similar to 15th day. Beverages and brushing negatively influenced the surface roughness. In relation to microhardness, there was no significant difference among groups, regardless of the depth examined. Conclusions: Color change of the composite resin was influenced only by the beverages and brushing did not affect the analyzed property. The repolishing was not sufficient to promote the return of the specimens color to their initial values. The surface roughness was negatively influenced both by the beverage as brushing. For microhardness, the composite resin showed similar results regardless of the beverages used and the presence or absence of brushing in the specimens tested.

O presente trabalho tem por objetivo avaliar os efeitos do clareamento caseiro, com peróxido de carbamida 10%, e clínico, com peróxido de carbamida 37%, na microdureza e alteração de cor de duas resinas compostas (Z250 e Supreme). Foram confeccionados 100 espécimes, 60 para microdureza e 40 para alteração de cor, com 6mm de diâmetro e 2mm de espessura, em resina composta. A matriz foi preenchida em um único incremento e polimerizada por 20s. Na seqüência os espécimes foram polidos com lixas #1200 e com pasta diamantada. Realizou-se então a primeira medição de dureza e cor dos espécimes. A seguir, para o estudo de cor foi realizada o manchamento com café durante 7 dias e então realizado uma segunda medição da cor. Os espécimes foram divididos aleatoriamente em 3 grupos para microdureza e 2 grupos para cor (n=10) de acordo com o tratamento clareador. Para o clareamento clínico foram realizadas três sessões com intervalo de 7 dias entre elas. Para o clareamento caseiro foram feitas 4h de aplicações diárias durante 14 dias. Nos intervalos entre os procedimentos de clareamentos os espécimes foram armazenados em saliva artificial a 37ºC. Após o final do clareamento nova medição de microdureza e cor foram realizadas. Os dados obtidos foram submetidos ANOVA e Fisher (p<0,05). Para a microdureza os dados revelaram que a Z250, o tratamento clínico e antes do tratamento apresentaram valores estatisticamente superiores aos demais. Na análise da cor pode-se observar que &Delta;E e &Delta;b apresentaram diferenças significativas para os fatores material, tratamento e entre os grupos, para o &Delta;L a Z250 apresentou-se mais escura que a Supreme. Na comparação do clareamento como o padrão observou-se não haver diferenças significativas entre o &Delta;E e &Delta;L para nenhum fator, porém diferenças significativas apresentaram-se para o &Delta;a e &Delta;b para os fatores material e tratamento. Pode-se concluir que os dois métodos de clareamento foram eficientes em clarear os espécimes a valores próximos ao padrão, sendo mais efetivo o clareamento clínico sem alterar a dureza dos materiais e tendo a Supreme apresentado melhor comportamento que a Z250 no retorno da coloração inicial. / The aim of this study was to evaluate the effects of home bleaching (10% carbamide peroxide) and in office bleaching (37% carbamide peroxide) on the color alteration and microhardness of two composite resins (Z250 and Supreme). For this purpose, it was prepared 100 specimens of resin, 60 for microhardness and 40 for color alteration, with 6mm diameter X 2mm thickness. The matrix was filled in a single increment and the resin was light cured for 20s. Specimens were polished after 24 hours with sandpaper #1200 and diamond paste. In this moment, the first color measurements (standard) and also microhardness measurements were realized. After, in the color study specimens were immersed in coffee for a seven days period, subsequently, a second color measurement was realized. Specimens were randomly divided in three groups for microhardness and two groups for color alteration (n=10) according to bleaching treatment. For the office bleaching were realized in 3 sessions with interval of 7 days among them, and every session were realized 3 applications of the bleach agent for 20 min. For the home bleaching, it was done daily applications with 4h duration by 14 days. Specimens were kept in artificial saliva at 37ºC ± 1ºC during intervals between the bleaching proceedings. A new microhardness and color measurements were realized in the end of the bleaching cycle. Data were submitted to ANOVA and Fisher test (p<0.05) and in relation to microhardness showed that Z250 (material), in office bleaching (treatment) and before bleaching (time) presented higher statistically significant values comparing to the others results. For color alteration showed that &Delta;E and &Delta;b were statistically significant differences for the following factors: material, treatment and interactions, for &Delta;L values, Z250 presented darker than Supreme. In the comparison of bleaching with the standard values, it was not observed statistically significant difference between &Delta;E e &Delta;L for all factors; however, it was observed significant difference to &Delta;a and &Delta;b for the factors material and treatment. It can be concluded that both methods of bleaching were efficient in brightness specimens to values near from standard. Furthermore, in office bleaching was more effective without change materials micro hardness and Supreme presented better behavior than Z250 in relation to return to initial color.

Made available in DSpace on 2014-06-11T19:24:08Z (GMT). No. of bitstreams: 0 Previous issue date: 2004-02-10Bitstream added on 2014-06-13T19:10:17Z : No. of bitstreams: 1 gois_am_me_arafo.pdf: 658823 bytes, checksum: 0abf0aa96e870eb9a4ad26842cbc521f (MD5) / Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) / Este estudo avaliou a resistência adesiva de microtração em reparos de resinas compostas, novas e envelhecidas, após tratamento da superfície usando irradiação a laser de Er: YAG, ponta diamantada e abrasão a ar. 36 blocos de resina composta híbrida Z100 (3M) com 5mm de comprimento e 6 mm de lado foram confeccionados com auxílio de uma matriz. Metade desses blocos foram reparados após 24 horas, e a outra metade foi reparada após envelhecimento artificial com luz ultravioleta. Cada grupo foi subdividido em 6 subgrupos e as superfícies experimentais foram submetidas a diferentes tratamentos: (G1) desgaste com ponta diamantada; (G2) jateamento com partículas de óxido de alumínio de 60 mm; (G3) ablação com laser de Er: YAG a um nível de energia de 100mJ; (G4) ablação com laser de Er:YAG a um nível de energia de 200mJ; (G5) ablação a laser de Er:YAG a um nível de energia de 300mJ; (G6) controle- ausência de tratamento de superfície. Após tratamento da superfície, o agente adesivo (Single Bond 3M) foi aplicado e os blocos foram reparados com a resina composta Point4 (KERR). Reparados, os blocos foram seccionados em espécimes de 1.0 mm2. A resistência adesiva de microtração foi medida em uma máquina de teste universal MTS. No grupo que foi reparado 24 horas após, não houve diferença estatisticamente significante na resistência adesiva interfacial entre os subgrupos. No grupo que foi envelhecido, os subgrupos G1 e G3 tiveram as maiores médias de resistência adesiva de reparo. Significantemente, os menores valores foram achados para os subgrupos G2 e G6. As médias da resistência adesiva de reparo foram estatisticamente similares para G3, G4 e G5. O exame em SEM indicou que a fratura adesiva foi o tipo predominante de falha. Os resultados desse estudo indicam que os maiores valores de resistência adesiva foram achados para o desgaste da superfície com... . / This study assessed the microtensile bond strengths of composite repairs, new and aged, after surface treatments, using Er:YAG laser irradiation, diamond bur and air abrasion. 36 blocks of hybrid composite resin Z100 (3M) with 5.0 mm length and 6.0 mm of side were made in mold. Half of these blocks were repaired after 24 hr and the other half was aged in an artificial aging chamber with exposure to a total ultraviolet irradiation. Each group was then divided into six subgroups and the experimental surface was exposed to a different treatment: (G1) grinding with diamond burs; (G2) air-abraded with 60mm aluminum oxide particles; (G3) ablation with an Er: YAG laser under the energy level of 100 mJ; (G4) ablation with an Er: YAG laser under the energy level of 200 mJ; (G5) ablation with an Er: YAG laser under the energy level of 300 mJ; (G6) controle - with no surface treatment. After the resin treatment on the surface, the bonding agent (Single bond, 3M) was applied and the blocks were repaired with the resin Point4 (Kerr) composite. Repaired, the blocks were sectioned into specimens (stick) of 1.0 mm2. Microtensile bond strength was measured in a universal testing machine MTS. The group repaired after 24 hours did not present statistically significant differences on interfacial bond strengths between the subgroups. On the aged group, the subgroups G1 and G3 presented the highest mean of repairing bond strenght. Significant lower values were found for subgroups G2 and G6 .The mean of repairing bond strenght was statistically similar for G3, G4 and G5. SEM examination indicated that adhesive failure was the predominant mode of failure. The results of this study indicate that the highest bond values were achieved by grinding the surface with diamond burs and ablating the surface with an Er: YAG laser under the energy level of 100mJ... (Complete abstract, click electronic address below).

Made available in DSpace on 2014-06-11T19:24:08Z (GMT). No. of bitstreams: 0 Previous issue date: 2009-02-18Bitstream added on 2014-06-13T20:12:01Z : No. of bitstreams: 1 saade_eg_me_arafo.pdf: 674732 bytes, checksum: 3bfed6ac99e5345683bc3cdd8c9e6925 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo desse trabalho foi investigar a influência do pré-aquecimento da resina composta anterior à fotopolimerização, sobre suas propriedades físicas e mecânicas como: o grau de conversão e dureza. As amostras foram fotopolimerizadas com uma unidade de luz halógena de quartzo-tungstênio (QTH) e uma unidade diodos emissores de luz azul (LED) por 40 s. Os compules de resina composta híbrida foram pré-aquecidos no dispositivo denominado Calset. A conversão dos monômeros a polímeros foi determinada através do FTIR-ATR. A propriedade de dureza foi avaliada no Microdurômetro MMT-3 Microhardness Tester equipado com o diamante Vickers. Para o teste de dureza Vickers cinco amostras para cada grupo (4 mm de diâmetro e 2 mm de espessura) foram confeccionadas com a resina composta pré-aquecida nas seguintes temperaturas: 37ºC, 54ºC e 60ºC (n=5). As amostras foram submetidas ao teste de dureza Vickers imediatamente após a sua confecção. Foram efetuadas 4 medidas no topo e 4 na base de cada amostra. De acordo com a interação entre as duas unidades de luz e o aumento de temperatura da resina composta, os resultados indicam que somente a unidade de luz influenciou nas médias dos valores de dureza Vickers. A unidade LED apresentou valores de dureza mais homogêneos entre o topo e a base da resina composta, evidenciando uma polimerização mais uniforme. O preaquecimento da resina composta não apresentou diferenças estatisticamente significativas nos valores de dureza. Para a avaliação do grau de conversão foram confeccionadas 5 amostras (4 mm de diâmetro e 2 mm de espessura) para cada grupo, utilizando a unidade QTH e LED, e a resina composta nas seguintes temperaturas: 25ºC (temperatura ambiente), 37ºC, 54ºC e 60ºC (n=40). Após a confecção as amostras foram preparadas para a análise do grau de conversão através do FTIR-ATR. Segundo os resultados conclui-se que não houve diferenças estatisticamente significativas. / The aim of this study was to evaluate the physics and mechanical properties of the pre-heating of the composite resin photo-activated. The samples were photo-activated with a light-curing unit QTH and LED for 40 s. The compules of hybrid composite resin for anterior restorations were pre-heated in the device called “Calset”. The monomer conversion was analyzed using the FTIR-ATR. The hardness property was evaluated with microdurometer MMT-3 equipped with diamond Vickers. Five samples were made for each group (4 mm in diameter and 2 mm in thickness) which the composite resin were pre-heated at temperatures three: 37°, 54° and 60°C. Immediately were submitted to hardness test, which the top and bottom surfaces of the samples took, place an impression for quadrant. According to the interaction between both light-curing units and the increase of the temperature of composite resin, the results showed that only lightcuring unit influenced the hardness average values. The LED light showed a cure homogeneous across the surface of the composite resin and good values of Vickers hardness. The pre-heating of composite resins prior to cure did not show statistically significant differences in the hardness values. For to evaluate the degree of conversion, five samples were made (4 mm in diameter and 2 mm in thickness) for each group using light-curing unit QTH and LED, with the composite resin pre-heated at temperatures of 25ºC (room temperature), 37ºC, 54ºC and 60ºC and analyzed in the spectrophotometer. No significant differences were found in the degree of conversion of the composite resin cured with QTH or LED and to different pre-heating of the composite resin. In this study, any evidence was found that type of light-curing unit used and pre-heating of composite resin could improve the degree of conversion.

Resumo: O objetivo desse trabalho foi avaliar a capacidade de polimerização, através da estrutura dental, de três diferentes fontes de luz (Halógena, Laser de Argônio e LEDs), por meio do teste de microdureza. Para isto, foram confeccionados corpos-de-prova em uma matriz metálica circular contendo um orifício na porção central com 4 mm de diâmetro e 2 mm de profundidade. Utilizou-se a resina composta microhibrida Charisma (Heraeus-Kulzer), na cor A2, para a confecção dos corpos-de-prova. Cinco corpos-de-prova foram confeccionados para cada situação diferente, perfazendo um total de 140 corpos-de-prova, distribuídos em 3 grupos da seguinte maneira: GRUPO I - fonte de luz halógena utilizada pelos tempos de exposição de 20 e 40 segundos, para as espessuras de 0 (grupo controle); 1,2 mm; 1,5 mm e 2,0 mm de faceta de estrutura dental; GRUPO II - fonte de luz de laser de argônio utilizada pelos tempos de exposição de 20 e 40 segundos, para as espessuras de 0 (grupo controle); 1,2 mm; 1,5 mm e 2,0 mm de faceta de estrutura dental e GRUPO III - fonte de luz à base de LEDs utilizada pelos tempos de 20, 40 e 60 segundos, para as espessuras de 0 (grupo controle); 1,2 mm; 1,5 mm e 2,0 mm de faceta de estrutura dental. Após a confecção dos corpos-de-prova, estes foram armazenados em estufa a 37ºC durante 24 horas. Após o período de armazenamento, procedeu-se o teste de microdureza Vickers, realizando-se 12 impressões para a superfície de topo (voltada à fonte de luz) e 12 para a superfície de base (oposta à fonte de luz). Os dados foram submetidos à Análise Estatística de Variância (P<0,05). Os valores dos desvios padrão das medidas de microdureza foram menores do que 1% da média, indicando diferença estatisticamente significante entre quase todos os grupos. Baseados nos resultados encontrados, pudemos concluir que... (Resumo completo, clicar acesso eletrônico abaixo). / Abstract: The objective of this study was evaluate the light-curing capacity, throught dental structure, of three differents light-curing device (Halogen, Argon Laser and LEDs), by microhardness testing. The specimes were made in a circular metallic mold with a of orifice in the cental portion measuring 4 mm in diameter and 2 mm in thickness. The composite resin was used the Charisma (Heraeus-Kulzer) at collor A2. Five samples was made by situation analyzed, adding up one hundred and forty samples: GROUP I - halogen light-curing device by exposure times of 20 and 40 seconds for the thickness 0 (control group); 1,2 mm; 1,5 mm and 2,0 mm of the structure dental facet; GROUP II - argon laser light-curing device by exposure times of 20 and 40 seconds for the thickness 0 (control group); 1,2 mm; 1,5 mm and 2,0 mm of the structure dental facet and GROUP III - LEDs light-curing device by exposure times of 20, 40 and 60 seconds for the thickness 0 (control group); 1,2 mm; 1,5 mm and 2,0 mm of the dental structure facet. After the polymerization procedures the specimes were stored at room temperature of 37ºC for 24 hours. After the storing, the microhardness testing was made, take effecting 12 impressions for the top surface and 12 for the botton surface. The hardness values means obtained were calculed and the statistically analised using Anova (P<0,05). According to the results, it was conclude that: 1) highest the thickness of the dental estructure face, have been a decreasing of the means values of microhardness, independent of the light-cured device utilized; 2) highest exposure times provided higher values means of the microhardness, independent of the light-cured device utilized; 3) the top surface showed the highest means values of hardness, independent of the light-cured device utilized; 4) the halogen light-cured device raised suitable... (Complete abstract, click electronic address below). / Orientador: Marcelo Ferrarezi de Andrade / Coorientador: Vanderlei Salvador Bagnato / Banca: Sillas Luiz Lordelo Duarte Júnior / Banca: João Carlos Gomes / Mestre

Orientador: Marcelo Ferrarezi de Andrade / Banca: José Roberto Cury Saad / Banca: Mânio de Carvalho Tibúrcio / Resumo: O objetivo desta pesquisa foi avaliar a influência da distância de uma fonte de luz halógena na microdureza superficial da resina composta, considerando as superfícies de topo e base dos corpos-de-prova. Foram utilizadas duas marcas comerciais de resina composta, Z250 de partículas pequenas e uma resina de micropartícula, A110, ambas da 3M do Brasil Ltda. O aparelho de ativação da resina composta foi K&M 220- R, cuja intensidade de luz possui um pulso que variava após os 5 primeiros segundos assim alcançando sua intensidade máxima que foi medida em 720 mW/cm2. Para a determinação da intensidade de luz emitida pelo aparelho fotoativador, utilizou-se um radiômetro (Medidor de irradiância 150- CMC , São Carlos - SP). Corpos-de-prova foram confeccionados utilizado-se matrizes metálicas que possuíam um orifício central de 4mm de diâmetro por 2mm de espessura. As resinas foram inseridas no orifício da matriz metálica, em um único incremento, por meio de uma espátula metálica e sobre elas foi sobreposta uma tira matriz transparente de poliéster e, após isto, um peso de 1 Kg foi posto em cima da tira para que houvesse uma melhor condensação da resina composta evitando a presença de bolhas de ar, no interior do corpo-de-prova. A fonte de luz halógena foi fixada em uma mesa de maneira que a saída da ponta de luz ficasse paralela à superfície do corpo-de-prova. Para provocar o distanciamento da fonte de luz, anéis metálicos confeccionados em latão, com espessuras que variavam de 2mm, 4mm e 8mm foram utilizados, os quais, após posicionados, eram removidos para não interferiem no dispersamento da luz. As distâncias imprimidas a fonte de luz na superfície da resina foram de 0mm(tocando a superfície), 2mm, 4mm e 8mm. Para cada uma destas distâncias, a intensidade de luz foi medida. Esta variou de intensidade de... (Resumo completo, clicar acesso eletrônico abaixo). / Abstract: The aim of this research was to evaluate the influence of the light tip distance in the superficial microhardness of the composite resin, considering the surfaces of top and base of the samples. Two commercial composite resin marks had been used, Z250 of small particles e a microparticle resin, A110, both of 3m of Brazil Ltda. The device of activation of the composite resin was K&M 220- R, whose intensity of light possess a pulse that varied the 5 first seconds after thus reaching its maximum intensity that was measured in 720 mW/cm2. For the determination of the intensity of light emitted for the fotoativador device, a radiometer (Measuring of irradiance 150- CMC was used, Is Carlos. SP). The samples had been confectioned used first metallic that had a central orifice of 4mm of diameter for 2mm of thickness. The resins had been inserted in the orifice of the metallic array, in an only increment, by means of a metallic spatula and on them a transparent first polyester strap was overlapped and, after this, one weight of 1 kg was rank in top of the strap so that it had one better condensation of the composite resin preventing the presence of air bubbles, in the inward of the body-of-test. The source of light was fixed in a table thus the output of the light tip was parallel to the surface of the body-of-test. To provoke distance from the light source, confectioned metallic rings in brass, with thickness that varied of 2mm, 4mm and 8mm had been used, which, after located, was removed to avoid concentration of light. The printed pitches the source of light in the surface of the resin had been of 0mm(on the surface), 2mm, 4mm and 8mm. For each one of these pitches, the light intensity was measured. This varied of intensity of 720 mW/cm2 for the tip touching the surface of the body-of-test, 650 mW/cm2 for in the distance of 2mm, 600 mW/cm2... (Complete abstract, click electronic address below). / Mestre

Orientador: Marcelo Ferrarezi de Andrade / Banca: Vanderlei Salvador Bagnato / Banca: José Eduardo Pelizon Pelino / Resumo: Este estudo avaliou a resistência adesiva de microtração em reparos de resinas compostas, novas e envelhecidas, após tratamento da superfície usando irradiação a laser de Er: YAG, ponta diamantada e abrasão a ar. 36 blocos de resina composta híbrida Z100 (3M) com 5mm de comprimento e 6 mm de lado foram confeccionados com auxílio de uma matriz. Metade desses blocos foram reparados após 24 horas, e a outra metade foi reparada após envelhecimento artificial com luz ultravioleta. Cada grupo foi subdividido em 6 subgrupos e as superfícies experimentais foram submetidas a diferentes tratamentos: (G1) desgaste com ponta diamantada; (G2) jateamento com partículas de óxido de alumínio de 60 mm; (G3) ablação com laser de Er: YAG a um nível de energia de 100mJ; (G4) ablação com laser de Er:YAG a um nível de energia de 200mJ; (G5) ablação a laser de Er:YAG a um nível de energia de 300mJ; (G6) controle- ausência de tratamento de superfície. Após tratamento da superfície, o agente adesivo (Single Bond 3M) foi aplicado e os blocos foram reparados com a resina composta Point4 (KERR). Reparados, os blocos foram seccionados em espécimes de 1.0 mm2. A resistência adesiva de microtração foi medida em uma máquina de teste universal MTS. No grupo que foi reparado 24 horas após, não houve diferença estatisticamente significante na resistência adesiva interfacial entre os subgrupos. No grupo que foi envelhecido, os subgrupos G1 e G3 tiveram as maiores médias de resistência adesiva de reparo. Significantemente, os menores valores foram achados para os subgrupos G2 e G6. As médias da resistência adesiva de reparo foram estatisticamente similares para G3, G4 e G5. O exame em SEM indicou que a fratura adesiva foi o tipo predominante de falha. Os resultados desse estudo indicam que os maiores valores de resistência adesiva foram achados para o desgaste da superfície com... (Resumo completo, clicar acesso eletrônico abaixo). / Abstract: This study assessed the microtensile bond strengths of composite repairs, new and aged, after surface treatments, using Er:YAG laser irradiation, diamond bur and air abrasion. 36 blocks of hybrid composite resin Z100 (3M) with 5.0 mm length and 6.0 mm of side were made in mold. Half of these blocks were repaired after 24 hr and the other half was aged in an artificial aging chamber with exposure to a total ultraviolet irradiation. Each group was then divided into six subgroups and the experimental surface was exposed to a different treatment: (G1) grinding with diamond burs; (G2) air-abraded with 60mm aluminum oxide particles; (G3) ablation with an Er: YAG laser under the energy level of 100 mJ; (G4) ablation with an Er: YAG laser under the energy level of 200 mJ; (G5) ablation with an Er: YAG laser under the energy level of 300 mJ; (G6) controle - with no surface treatment. After the resin treatment on the surface, the bonding agent (Single bond, 3M) was applied and the blocks were repaired with the resin Point4 (Kerr) composite. Repaired, the blocks were sectioned into specimens (stick) of 1.0 mm2. Microtensile bond strength was measured in a universal testing machine MTS. The group repaired after 24 hours did not present statistically significant differences on interfacial bond strengths between the subgroups. On the aged group, the subgroups G1 and G3 presented the highest mean of repairing bond strenght. Significant lower values were found for subgroups G2 and G6 .The mean of repairing bond strenght was statistically similar for G3, G4 and G5. SEM examination indicated that adhesive failure was the predominant mode of failure. The results of this study indicate that the highest bond values were achieved by grinding the surface with diamond burs and ablating the surface with an Er: YAG laser under the energy level of 100mJ... (Complete abstract, click electronic address below). / Mestre

Resumo: O objetivo desse trabalho foi investigar a influência do pré-aquecimento da resina composta anterior à fotopolimerização, sobre suas propriedades físicas e mecânicas como: o grau de conversão e dureza. As amostras foram fotopolimerizadas com uma unidade de luz halógena de quartzo-tungstênio (QTH) e uma unidade diodos emissores de luz azul (LED) por 40 s. Os compules de resina composta híbrida foram pré-aquecidos no dispositivo denominado Calset. A conversão dos monômeros a polímeros foi determinada através do FTIR-ATR. A propriedade de dureza foi avaliada no Microdurômetro MMT-3 Microhardness Tester equipado com o diamante Vickers. Para o teste de dureza Vickers cinco amostras para cada grupo (4 mm de diâmetro e 2 mm de espessura) foram confeccionadas com a resina composta pré-aquecida nas seguintes temperaturas: 37ºC, 54ºC e 60ºC (n=5). As amostras foram submetidas ao teste de dureza Vickers imediatamente após a sua confecção. Foram efetuadas 4 medidas no topo e 4 na base de cada amostra. De acordo com a interação entre as duas unidades de luz e o aumento de temperatura da resina composta, os resultados indicam que somente a unidade de luz influenciou nas médias dos valores de dureza Vickers. A unidade LED apresentou valores de dureza mais homogêneos entre o topo e a base da resina composta, evidenciando uma polimerização mais uniforme. O preaquecimento da resina composta não apresentou diferenças estatisticamente significativas nos valores de dureza. Para a avaliação do grau de conversão foram confeccionadas 5 amostras (4 mm de diâmetro e 2 mm de espessura) para cada grupo, utilizando a unidade QTH e LED, e a resina composta nas seguintes temperaturas: 25ºC (temperatura ambiente), 37ºC, 54ºC e 60ºC (n=40). Após a confecção as amostras foram preparadas para a análise do grau de conversão através do FTIR-ATR. Segundo os resultados conclui-se que não houve diferenças estatisticamente significativas. / Abstract: The aim of this study was to evaluate the physics and mechanical properties of the pre-heating of the composite resin photo-activated. The samples were photo-activated with a light-curing unit QTH and LED for 40 s. The compules of hybrid composite resin for anterior restorations were pre-heated in the device called "Calset". The monomer conversion was analyzed using the FTIR-ATR. The hardness property was evaluated with microdurometer MMT-3 equipped with diamond Vickers. Five samples were made for each group (4 mm in diameter and 2 mm in thickness) which the composite resin were pre-heated at temperatures three: 37°, 54° and 60°C. Immediately were submitted to hardness test, which the top and bottom surfaces of the samples took, place an impression for quadrant. According to the interaction between both light-curing units and the increase of the temperature of composite resin, the results showed that only lightcuring unit influenced the hardness average values. The LED light showed a cure homogeneous across the surface of the composite resin and good values of Vickers hardness. The pre-heating of composite resins prior to cure did not show statistically significant differences in the hardness values. For to evaluate the degree of conversion, five samples were made (4 mm in diameter and 2 mm in thickness) for each group using light-curing unit QTH and LED, with the composite resin pre-heated at temperatures of 25ºC (room temperature), 37ºC, 54ºC and 60ºC and analyzed in the spectrophotometer. No significant differences were found in the degree of conversion of the composite resin cured with QTH or LED and to different pre-heating of the composite resin. In this study, any evidence was found that type of light-curing unit used and pre-heating of composite resin could improve the degree of conversion. / Orientador: Sizenando de Toledo Porto Neto / Coorientador: Alessandra Nara de Souza Rastelli / Banca: Darlon Martins Lima / Banca: José Roberto Cury Saad / Mestre