Orientador : Mario Alexandre Coelho Sinhoreti / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T08:25:24Z (GMT). No. of bitstreams: 1 Alonso_RobertaCarolineBruschi_M.pdf: 8518395 bytes, checksum: b912abcdff33702d399af4a692a8efd0 (MD5) Previous issue date: 2003 / Resumo: O objetivo desse estudo foi avaliar o efeito dos métodos de fotoativação e de forradores resinosos na adaptação marginal de restaurações em compósito. Para isto, foram selecionados 200 incisivos bovinos, os quais tiveram a superficie vestibular desgastada de modo a expor uma área plana de pelo menos 6 mm de diâmetro de dentina, onde uma cavidade circular com 4 mm de diâmetro e 1,5 mm de profundidade foi confeccionada. A5 paredes cavitárias foram condicionadas com ácido fosfórico durante 15s e o sistema de união Scotchbond Multi-uso aplicado de acordo com as instruções do fabricante. Os dentes foram então separados em 5 grupos, segundo o método de fotoativação empregado: 1) Luz halógena contínua (800 mW/cm2 por 20s); 2) Dupla intensidade de luz (150 mW/cm2 por IOs, seguido por 800 mW/cm2 por 15s); 3) Luz pulsátil (600 mW/cm2 por 40s); 4) LED (370 mW/cm2 por 40s); 5) Arco de plasma de xenônio (1800 mW/cm2 por 3s). Cada grupo foi subdividido segundo a técnica restauradora utilizada: A) Controle - (1 camada de adesivo); B) Aplicação de 3 camadas de adesivo C) Aplicação do compósito Filtek Flow como forramento; D) Aplicação do compósito Protect Liner F como forramento. Após, todas as cavidades foram restauradas com o compósito Z250 e annazenadas em água destilada a 3T'C, durante 24h. A5 amostras foram então submetidas a acabamento e polimento em politriz reftigerada a água, utilizando lixas de granulação decrescente 400, 600 e 1200. Para análise dos resultados, as amostras foram coradas com solução de propileno glicol e ácido vermelho (Caries Detector - Kuraray Co. Japão), o que permitiu a evidenciação das fendas formadas. A5 fendas foram observadas em lupa estereoscópica e a imagem da restauração foi captada e transferida a um computador equipado com um programa de mensuração para determinar o comprimento da fenda. Tal valor foi convertido em porcentagem, pela razão entre o comprimento de fenda e o comprimento total da margem cavitária, multiplicada por 100. Os dados obtidos foram submetidos à análise de variância e as médias comparadas pelo teste de Tukey a 5% de significância. Os resultados demonstraram que as três técnicas restauradoras experimentais (3 camadas de adesivo, Filtek Flow e Protect Liner F) melhoraram significativamente a adaptação do compósito às margens cavitárias, em relação ao grupo controle (1 camada de adesivo), para o método de fotoativação por luz halógena contínua. Para os outros métodos de fotoativação não foram encontradas diferenças significativas entre as técnicas restauradoras. Com relação aos métodos de fotoativação, somente foram detectadas diferenças significativas no grupo controle (1 camada de adesivo), no qual o método pulsátil apresentou redução significativa no percentual de fendas formadas em relação aos métodos de luz halógena contínua e dupla intensidade de luz. Os grupos ativados por LEDs e lâmpada de arco de plasma de X~r;t9nio apresentaram resultados intermediários, não diferindo estatisticamente dos demais. Pôde-se concluir que, o método pulsátil melhorou efetivamente a qualidade marginal na técnica restauradora convencional (1 camada de adesivo) e que o uso de forradores resinosos reduziu a formação de fendas marginais quando a ativação do compósito foi feita com luz halógena convencional / Abstract: The purpose of this study was to evaluate the effect of the polymerization methods and the use of resin liners on marginal adaptation of eomposite restorations. Two hundred bovine ineisors were selected for the study. The bueeal surfaees ofthe teeth were grounded until a minimum of 6mm in diameter of dentin was exposed. A circular cavity (4mm in diameter x l.5mm in depth) was prepared in this area. The cavity walls were etehed and Seotehbond Multi Purpose system was applied aeeording to the manufacturer's instructions. These teeth were randomly assigned into tive groups, aeeording to the polymerization method: 1 Halogen eontinuous light (800mW/em2 for 20s); 2- Soft start polymerization (150mW/cm2 for lOs followed by 80OmW/cm2 for 15s); 3- Pulsating light (60OmW/em2 for 40s); 4- LED - light emitting diodes (37OmW/em2 for 40s); 5- Plasma are xenon (1800mW/em2 for 3s). Eaeh group was subdivided into four subgroups, according to the liner used: A- Control (1 adhesive layer); B- Application of three adhesive layers; C- pplieation of low viseosity eomposite Filtek Flow as a liner; D- Application of low viscosity composite Protect Liner F as a liner. All cavities were then restored with a single increment ofFiltek Z250 restorative composite and stored in distilled water at 3'PC for 24h. After storage, each restoration was polished with a sequence ofwet sand paper (400, 600, and 1200 grid). For the analysis of the results, a solution of red acid and propylene glycol (Caries Detector - Kuraray Co. Japan) was applied on eaeh specimen for 5s. This procedure allowed the verification of dyed margin length divided by the total cavity length, then multiplied by 100. Data were submitted to ANOV A and Tukey's test (p<0,05).Results showed that when the halogen continuous method was used, the three resin liner restorative tecbniques have significant1y increased marginal adaptation of the composite to the dentin margins when compared to control group (1 adhesive layer). When the other polymerization methods were used, no significant differences were detected among the restorative techniques. Regarding the polymerization methods, significant differences were only detected when the control restorative technique (1 adhesive layer) was used. Pulsating light showed better marginal quality than the other halogen methods (continuous and soft start polym~OIÜ. Within the limits of this study, it can be concluded that pulsating light and the use of resin liners with halogen continuous light significantly decrease marginal gap formation / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários

Orientadores : Giselle Maria Marchi Baron, Luiz Andre Freire Pimenta / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T08:26:44Z (GMT). No. of bitstreams: 1 Mitsui_FabioHiroyukiOgata_M.pdf: 2667244 bytes, checksum: e7bc18163fe746eb49916e8caa06b281 (MD5) Previous issue date: 2003 / Mestrado

Orientador : Mario Alexandre Coelho Sinhoreti / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T10:18:59Z (GMT). No. of bitstreams: 1 Cunha_LeonardoGoncalves_M.pdf: 4130905 bytes, checksum: 5859abb8a13bcbf680865f1fcf0cf958 (MD5) Previous issue date: 2003 / Resumo: O objetivo deste estudo foi avaliar o efeito de diferentes métodos de fotoativação e de materiais resinosos como forradores sobre a tensão gerada pela contração de polimerização do compósito odontológico Filtek Z250 (3MESPE). Os grupos avaliados quanto ao material de base foram: (G1) aplicação de uma camada de adesivo; (G2) aplicação de três camadas de adesivo e (G3) confecção de um forramento com o compósito de alto escoamento Protect Liner F. Os procedimentos de união foram realizados em dispositivos metálicos adaptados a uma máquina de ensaio universal (Instron, modelo 4411) através de sistema de rosca, presente na extremidade do dispositivo. As amostras de compósito foram confeccionadas através da utilização de condutos plásticos transparentes, com 5 mm de comprimento para G1 e G2 e 4,3 mm de comprimento para G3. Foram confeccionadas 50 amostras para cada grupo, sendo separadas em 5 subgrupos de 10 amostras cada, de acordo com o método de fotoativação do compósito: (1) Luz halógena contínua (40s a 800 mW/cm2); (2) Dupla intensidade de luz (10s a 150 mW/cm2 e 30s a 800 mW/cm2); (3) Luz halógena pulsátil (ciclos de 4s, com 2s de exposição à luz e 2s sem luz por 80s a 600 mW/cm2); (4) LED (40s a 170 mW/cm2); e, (5) Luz de arco de plasma de xenônio (1800 mW/cm2 por 3s). A fotoativação foi realizada utilizando dois aparelhos fotoativadores simultaneamente, posicionados em lados opostos do cilindro de compósito (face lateral). Após a fotoativação, um tempo de 5 minutos era aguardado antes do registro do valor máximo de tensão. Finalizado o experimento, realizou-se o teste de dureza Knoop nos cilindros de compósito através da utilização de um aparelho HMV-2000 (Shimadzu - Japão), com uma carga de 50 gramas por 15 segundos. Vinte e uma mensuraçóes foram realizadas em cada amostra e um total de 5 amostras foram escolhidas aleatoriamente de cada método de fotoativação. Os resultados foram submetidos à análise de variância e as médias comparadas pelo teste de Tukey (5%). Não foi verificada diferença estatística entre os métodos fotoativadores (p>0,05) quando foi realizada a aplicação de uma camada de adesivo, com exceção do método por arco de plasma de xenõnio, que apresentou resultados estatisticamente inferiores aos demais métodos. A utilização de materiais de base de baixo módulo de elasticidade foi eficiente na redução de tensões nos métodos por luz pulsátil e LED, nos quais a aplicação de três camadas de adesivo e confecção de forramento com compósito foram responsáveis pela diminuição significativa da tensão de contração. Para os outros três métodos de fotoativação não foi verificada diferença significativa na tensão máxima gerada entre os três grupos. Os valores de dureza obtidos com os métodos de luz halógena contínua e dupla intensidade de luz não diferiram entre si e foram superiores aos demais métodos / Abstract: The objeetive of this study was to evaluate the effeet of different photoaetivation methods and base materiais on the tension generated by polymerization shrinkage of eomposite resins. The restorative eomposite Filtek 2250 and the adhesive agent Seotehbond Multi-Purpose (3M-ESPE) were used in this study. The evaluated groups for the base material were: (G1) one eoat of adhesive agent; (G2) three eoat of adhesive agent, and (G3) flowable eomposite Proteet Liner F used as a liner. The bonding proeedures were made in metallie molds adapted to a universal testing maehine (Instron, model 4411) using a thread system in the extremity of the base. The eomposite samples were prepared using transparent plastie eonduits 5 mm in length for G1 and G2, and 4.3 mm in length for G3. Fifty samples were prepared for eaeh group. These were separated into 5 subgroups of 10 samples eaeh, aeeording to the photoaetivation method: (1) Continuous Light (40s at 800 mW/em2); (2) Stepped Light (10s at 150 mW/em2 and 30s at 800 mW/em2); (3) Intermittent light (eyeles of 4s, with 2s of exposure to light and 2s without light for 80s at 600 mW/em2); (4) LED (40s at 170 mW/em2); and (5) Xenon Plasma Are (1800 mW/em2 for 3s). The photoaetivation method was performed using simultaneously two units, whieh were positioned on eaeh si de of the eomposite eylinder. Following the photoaetivation method, an additional 5-minute period was awaited before the registration of maximum tension value. At the end of the experiment, Knoop hardness test was carried out with the use of the HMV-2000 equipment (Shimadzu - Japan), loaded with 50 grams for 15 seeonds. Twenty-one indentations were performed in eaeh sample and a total of 5 samples were randomly ehosen for each photoactivation method. The results were submitted to analysis of variance and mean values were compared by Tukey Test (5%). Statistically significant difference was not verified (p>O.O5) among the photoaetivation methods when. one coat of adhesive was applied, exeept for the Xenon plasma are method, whieh presented statistically the most inferior results in this study. The use of low elastic module base materiais was effieient in tension reduetion with Intermittent Light and LED methods. No significant differenee in the maximum tension generated among the three groups was verified for the other three photoaetivation methods. The hardness values between the eontinuous and stepped light were not statistically different (p>O.O5) and were superior to the other methods / Mestrado / Mestre em Materiais Dentários

Orientador: Luis Roberto Marcondes Martins / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T17:59:32Z (GMT). No. of bitstreams: 1 Soares_CarlosJose_D.pdf: 2703226 bytes, checksum: d7d768ba026761667d6f9ec930fb8cfc (MD5) Previous issue date: 2003 / Doutorado

Orientadores: Luis Alexandre M. S. Paulillo, Jaime Aparecido Cury / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T18:00:18Z (GMT). No. of bitstreams: 1 Mendonca_CarlotaCristinaLeite_D.pdf: 1552031 bytes, checksum: 27cf0ef67462150273284dc1c4caabbe (MD5) Previous issue date: 2002 / Resumo: O objetivo desta pesquisa foi avaliar a deposição superficial de placa bacteriana in situ sobre dois materiais estéticos indiretos, apresentando 2 texturas superficiais - lisa e rugosa - na presença ou não de sacarose. Assim, foram testadas a cerâmica Duceram LFC e a resina composta laboratorial Solidex. Para a avaliação do acúmulo de placa bacteriana foram selecionados 12 voluntários, para os quais foram confeccionados dispositivos palatinos em acrílico, onde foram fixados 4 corpos de prova correspondentes aos grupos experimentais: (1) Cerâmica lisa (glaze); (2) Cerâmica rugosa (desgaste com ponta diamamtada); (3) Resina composta indireta lisa (polimerizada em contato com a tira matriz) e (4) Resina composta rugosa (desgaste com ponta diamamtada). Os voluntários utilizaram a placa palatina 3 dias por semana, durante 8 semanas, divididas em 2 fases distintas: com sacarose e sem sacarose, 4 semanas para cada fase. Em uma etapa, metade dos voluntários realizou imersões do aparelho em sacarose a 20%, 8 vezes ao dia e a outra metade realizou as imersões em água. Na 2a etapa, esta situação foi invertida. No 4o dia, a placa formada sobre cada corpo de prova foi extraída em NaOH 1,0M e quantificada em espectrofotômetro. Os resultados obtidos apresentaram efeito estatístico significativo para os fatores material e superfície, e não significativo para o fator sacarose. Entre os materiais estudados, a cerâmica com superfície lisa, grupo (1) apresentou as menores médias em relação ao acúmulo de placa dental, sem diferença estatística para o grupo (2). As maiores médias foram obtidas pelo grupo (4), que apresentou diferença estatística significativa em relação aos demais grupos experimentais / Abstract: The aim of this study was to evaluate in situ the plaque retention on indirect aesthetic restorative materials presenting rough or smooth surfaces, after sucrose exposuring or not. Duceram LFC ceramic and Indirect composite resin Solidex were tested. Twelve subjects were request and asked to wear palatal appliances containing four samples corresponding the four experimental groups: (1) Ceramic (glaze); (2) Rough ceramic (finishing with diamond bur); (3) Indirect composite resin (polimerized in contact with Mylar Strips) and (4) Rough indirect composite resin (finishing with diamond bur). The experimental period was three days per week, divided into two distinct phases, during eight weeks: with or without sucrose exposuring. Each phase corresponds four weeks. Either the appliances were immersed eight times a day into 20% sucrose solution, to induce plaque formation or into water. The quantity of dental plaque formed on samples was extracted with Sodium Hidroxide solution 1,0 M and analysed by spectrophotometer. The results presented statistical main variances for the factors material and surface, and no significance for the fator sucrose. Among the studied samples, the ceramic blocks with smooth surface, group (1) showed the smalest mean considering plaque retention, no statistical diference was observed to group (2). In the other side, Group (4) presented larger amounts of dental plaque acumulation differing statistically from the other groups / Doutorado / Dentística / Doutor em Clínica Odontológica

Orientador: Simonides Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-17T16:31:27Z (GMT). No. of bitstreams: 1 Fugolin_AnaPaulaPiovezan_M.pdf: 7087256 bytes, checksum: 828f5aed76c8ac133d37deb6cf423e11 (MD5) Previous issue date: 2011 / Resumo: O objetivo neste estudo foi investigar a influência de diferentes irradiâncias e de energia emitida pelo fotoativador na dureza Knoop, grau de conversão e contração de polimerização de compósitos odontológicos com diferentes partículas de carga. Anéis de latão de 12 mm de diâmetro externo, 8 mm de diâmetro interno e 2 mm altura foram preenchidos com os compósitos Filtek Supreme XT® (ESPE 3M) e Charisma® (Heraeus Kulzer), ambos na cor A2. O aparelho utilizado foi o LED Bluephase G2 (Ivoclar-Vivadent), com tempo de fotoativação de 20 s e irradiância conforme o protocolo: grupos A e D- 300 mW/cm²; grupos B e E- 650 mW/cm² e grupos C e F- 1200mW/cm², sendo n = 5. Depois da polimerização, cada conjunto (matriz e amostra) foi submetido aos procedimentos de acabamento e polimento com lixas de carboneto de silício. A armazenagem foi em estufa a 37ºC por 24 horas, dispostos em recipiente a seco e no escuro. Após armazenagem, as superfícies de topo e base das amostras foram submetidas ao teste de dureza Knoop em durômetro, onde foram efetuadas 5 penetrações em cada região, com carga de 50 gf por 5 s. As amostras submetidas ao ensaio de dureza Knoop foram analisadas em microscopia eletrônica de varredura para verificar o nível de adaptação material-matriz. Por meio do programa UTHSCSA ImageTool foi mensurada a largura das fendas. Para avaliar o grau de conversão outras amostras foram confeccionadas, as quais foram avaliadas pelo FTIR com ATR. Os dados foram submetidos à ANOVA múltiplos fatores e teste de Tukey (5%). Os resultados mostraram que: A dureza Knoop do Filtek Supreme XT foi significativamente maior que do Charisma, independente do local e irradiância. Independente do material e local, as irradiâncias de 1200 mW/cm² e 650 mW/cm² mostraram valores de dureza estatisticamente similares, sendo ambas significativamente maiores aos de 300 mW/cm². Para Charisma houve diferença estatística significante entre topo e base nas irradiâncias de 300 mW/cm² e 650 mW/cm². No Filtek Supreme XT houve diferença estatística significante entre topo e base somente na irradiância de 300 mW/cm². Independente do local e irradiância, o grau de conversão do Charisma foi estatisticamente maior que do Filtek Supreme XT, exceto na irradiância de 650 mW/cm², onde os valores foram estatisticamente similares. No Charisma, a irradiância de 1200 mW/cm² proporcionou grau de conversão significativamente maior que 300 mW/cm² e 650 mW/cm², ambos similares entre si. No Filtek Supreme XT, a irradiância de 1200 mW/cm² proporcionou valor significativamente maior, 300 W/cm² menor e 650 mW/cm² valor intermediário. Independente da irradiância, para Filtek Supreme XT não houve diferença entre topo e base. Para Charisma, 300 mW/cm² e 650 mW/cm² apresentaram diferença estatística significante entre topo e base, sendo que em 1200 mW/cm² não houve diferença estatística significante. Independente da irradiância, a contração do Charisma foi significativamente maior que do Filtek Supreme XT. Independente do material, a contração promovida pelas irradiâncias foi similar. Os resultados deste estudo mostraram que a irradiância influenciou na dureza Knoop e no grau de conversão, não causando efeito na contração dos compósitos. / Abstract: The aim of this study was to investigate the influence of both energy and power density (of different levels) emitted by light curing unit in the Knoop hardness, conversion degree and polymerization shrinkage of dental composites with different types of filler particles. Brass rings of 12mm outside diameter, 8mm internal diameter and 2mm height were filled with the composites Filtek Supreme XT® (3M ESPE) and Charisma (Heraeus Kulzer), both color A2. The light curing unit Bluephase G2 LED (Ivoclar-Vivadent) was used for 20s with irradiance according to the protocol; groups A and D ¿ 300 mW/cm², groups B and E ¿ 650 mW/cm² and groups C and F ¿ 1200 mW/cm². After polymerization, the sets (matrix and sample) were finished and polished with silicon carbide sandpaper and stored for 24 hours at 37°C in dark and dry container. After his period the specimens were evaluated for their hardness in an indenter, where top and bottom surfaces were submitted to five penetrations, with a load of 50gf for 5 s. Scanning electron microscopy (SEM) of these samples was carried out to check the gap between composite and matrix and the extent of crack were measured using the program UTHSCSA ImageTool. FTIR with ATR techniques assessed the degree of conversion of new samples. The data were analyzed by multiple factors ANOVA and Tukey test (p ? 0.05). In the results Filtek Supreme XT showed hardness values significantly higher than those of Charisma, regardless the location and the irradiance. At irradiances of 1200 mW/cm² and 650 mW/cm² showed hardness values statistically similar and significantly higher at 300 mW/cm², regardless the material and the location. Charisma showed a statistically significant difference between top and bottom in the irradiances 300 mW/cm² and 650 mW/cm². Filtek Supreme XT showed significant difference between top and bottom only in the irradiance of 300 mW/cm². The results for degree of conversion showed that, regardless the location and irradiance, Charisma had statistically higher values than Filtek Supreme XT, except for the irradiance of 650 mW/cm², where the values of the composites were statistically similar. At the power density of 1200 mW/cm², Charisma achieved values significantly higher than 650 mW/cm² and 300 mW/cm². At the power density of 1200 mW/cm² Filtek Supreme XT showed the highest conversion values, while at 300 mW/cm² showed the lowest values, and at 650 mW/cm² intermediate values were found. Regardless the irradiance, Filtek Supreme XT showed no difference between top and bottom. Charisma, at 300 mW/cm² and at 650 mW/cm² showed statistically significant difference between top and bottom, and at 1200 mW/cm² the difference was not statistically significant. Charisma showed significantly higher values of contraction than Filtek Supreme XT, regardless the irradiance. Regardless the material, no statistical difference was found for values of contraction for the evaluated irradiances. The findings of this study showed that the power density influenced the hardness and the degree of conversion, but not the contraction. / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários

Propôs-se avaliar a influência de diferentes fontes de luz fotoativadoras na micromorfologia e na resistência de união adesiva de restaurações de resina composta. Selecionaram-se terceiros molares hígidos que receberam preparos cavitários classe I (6,0 mm x 4,5 mm; 2,5 mm profundidade). A resina composta (Filtek Z250 - RC) foi inserida em incremento único após a aplicação e polimerização do sistema adesivo (Adper Single Bond - SB). Os materiais restauradores foram fotoativados com os seguintes aparelhos: XL 3000 (QTH: 540 mW/cm2); Elipar FreeLight 2 (LED: 750 mW/cm2) e Arc Light IIM (PAC: 2.130 mW/cm2). Nove grupos experimentais foram avaliados de acordo com as combinações de fonte de luz para fotoativar SB/RC: QTH/QTH; QTH/LED; QTH/PAC; LED/LED; LED/QTH; LED/PAC; PAC/PAC; PAC/QTH; PAC/LED. Para a análise da micromorfologia foi utilizada microscopia de fluorescência (Laser de Fóton Duplo), sendo que um corante fluorescente vermelho (Rodamina B) foi adicionado ao sistema adesivo. Além disso, utilizou-se uma solução de corante fluorescente verde (Dextran- Fluoresceína), que foi aplicada na câmara pulpar durante 4 horas, para que se difundisse em direção à interface. Os dentes foram então lavados, incluídos, seccionados e analisados microscopicamente. Os parâmetros analisados foram: espessura da camada de adesivo, espessura e qualidade da camada híbrida, micropermeabilidade, qualidade e habilidade de selamento dos tags de resina e, ainda, localização e extensão de fendas. Para o teste de resistência adesiva, os dentes foram restaurados, de acordo com as combinações de fonte de luz, e armazenados por 24 horas a 37 °C. Em seguida os dentes foram seccionados e submetidos ao teste de microtração. Realizou-se ainda a análise dos parâmetros de cinética de conversão de monômeros (conversão total, taxa máxima de conversão, conversão na máxima taxa, tempo em que ocorreu a máxima taxa e relação conversão na máxima taxa/conversão total) em um espectrofotômetro de raios infravermelho, ao qual foram aplicados os mesmos materiais restauradores que foram polimerizados com as diferentes fontes de luz. Para as avaliações qualitativas foi realizado o teste estatístico Kruskal-Wallis e o teste de Dunnet para comparações múltiplas (&#945; = 0,05). Para as avaliações quantitativas foi realizada análise de variância e teste de Tukey para comparações múltiplas (&#945; = 0,05). Da análise dos resultados, observou-se que as fontes de luz utilizadas influenciaram nos parâmetros de cinética de conversão de monômeros. De forma geral, ocorreu uma relação inversa entre a conversão total e a densidade de potência quando se polimerizou o sistema adesivo. Na resina composta base, houve uma relação direta. Para ambos os materiais houve uma maior taxa máxima de conversão, em um menor tempo, proporcional à densidade de potência dos aparelhos. Quanto aos parâmetros de micromorfologia, não se observou diferença siginificante entre os grupos experimentais em relação à espessura e qualidade de camada híbrida. Em relação à espessura da camada de adesivo, observaram-se maiores espessuras quando o sistema adesivo foi polimerizado com o PAC. Para a micropermeabilidade, também não se observou diferença entre os grupos. Também, não se observou diferença siginificante em relação à qualidade e habilidade de selamento dos tags de resina. Em relação à presença de fendas, quando o PAC polimerizou o sistema adesivo, menores porcentagens de piores escores e menores extensões de fendas foram observadas. A combinação PAC/QTH apresentou valores significantemente maiores de resistência adesiva e LED/QTH, as menores. A espessura da camada de adesivo, localização de fendas e resistência adesiva foram significantemente influenciados pela fonte de luz que polimerizou o sistema adesivo, sendo que, quando o PAC foi utilizado, melhores resultados foram observados. As combinações de mesma fonte de luz apresentaram, de forma geral, resultados similares. As diferentes fontes de luz fotoativadoras influenciam na resistência de união adesiva e em alguns parâmetros da micromorfologia da interface de restaurações de resina composta. / The purpose of the present in vitro study was to evaluate the effect of different light-curing sources on interfacial micromorphology and on bond strength of resin composite restorations. Class I preparations (6.0 mm long, 4.5 mm wide, 2.5 mm deep) were made in extracted human third molars, after abrading cusps, following university approved HAC guidelines. Restorations were placed in bulk, using a dentin bonding agent (DBA) / resin composite (RC): Adper Single Bond / Filtek Z250. Restoratives were light-cured as follows: XL 3000 (QTH: 540 mW/cm2); Elipar FreeLight2 (LED: 750 mW/cm2); Arc Light II (PAC: 2,130 mW/cm2). Nine experimental groups were developed from the different light combinations with respect to curing the DBA/COMP: QTH/QTH; QTH/LED; QTH/PAC; LED/LED; LED/QTH; LED/PAC; PAC/PAC; PAC/QTH; PAC/LED. Fluorescing agent (Rhodamine B) was added to the DBA, highlighting the bonded interface and surrounding structures. A different colored dye (FTIC-Dextran) was placed in the pulp chamber for 3 hours, allowing time to diffuse toward the different-colored interface. The teeth were then embedded, sectioned, and microscopically analyzed using fluorescence microscopy (Two-Photon Laser) at 40x magnification. Micromorphology quantitative and qualitative evaluations were: quality and thickness of hybrid layer; micropermeability test, adhesive layer thickness; quality and sealing ability of resin tags; location and extension of gaps. For bond strength test, the same experimental groups were obtained. After restorative procedures, the teeth were stored in distilled water for 24 h at 37 °C. After this time period, resin layers were added to the restoration surface (providing same dentin/resin length), and then sectioned and subjected to microtensile test in a universal testing machine. Kinetics conversion parameters were also evaluated in an FT-IR spectrophotometer (total conversion, maximum rate of cure, time when maximum rate occurred, conversion at maximum rate, conversion at maximum rate/ total conversion ratio). The same restorative materials were applied to the ATR device, attached to the spectrophotometer, and then polymerized according to manufacturer’s instructions. Data was statistically analyzed as mentioned below. Statistical analyses revealed that different light sources influenced the kinetics conversion (one-way ANOVA, p< 0,05). It was found an inverse relation between power density and monomer conversion when polymerizing DBA. For resin composite (bottom), there was a positive relation between power density and total conversion. High intensity, broad banded PAC light produced higher maximum rate of cure (in %/s), in shorter times. In terms of micromorphology, no significant difference was found in terms of quality and thickness of hybrid layer (two-way ANOVA, p> 0.05). No significant difference was noted for in quality and in sealing ability of tags (Kruskal Wallis, p> 0.05). QTH/QTH presented higher percentages of best scores for both parameters. Adhesive layers were found to be significantly thicker when PAC light was used to polymerize DBA. Even thought it was also found no significance in micropermeability scores (Kruskal Wallis, p> 0.05), it was found higher percentage of best scores for control QTH/QTH. Photo-polymerizing DBA using PAC produced lower incidence of gap formation, irrespective of RC curing source. Combination PAC/QTH presented significantly higher bond strength and LED/QTH, the lower (two-way ANOVA, Dunnet’s pos-hoc test, p< 0.05). Part of interfacial micromorphology parameters and bond strength were more dependent on the photo-polymerization source used for dentin-bonding agent than for resin composite. Photo- polymerizing DBA using PAC produced best results for adhesive thickness, gap location, and bond strength. Although QTH/QTH, LED/LED, and PAC/PAC combinations produced similar general results, it was found inherent characteristics when analysing tested parameters. Different light curing units influence bond strength and some parameters of micromorphology.

Avaliou-se a resistência adesiva ao cisalhamento de uma resina composta contaminada por saliva, com adição de novo incremento do mesmo material. 40 corpos-de-prova de uma resina composta nano-híbrida, confeccionados em uma matriz de resina epóxica, foram divididos em quatro grupos, cada um recebendo um tratamento de superfície. Em um dos grupos, a superfície não foi contaminada (Grupo 1 - controle). Para a confecção do segundo segmento do corpo-de-prova, utilizou-se uma matriz de Teflon de 3,5mm de diâmetro por 3,0mm de altura. Nos demais grupos, a superfície da resina composta foi contaminada com saliva e seca com ar comprimido, sendo os tratamentos estabelecidos da seguinte forma: Grupo 2 - resina composta inserida e polimerizada sobre a superfície contaminada; Grupo 3 - condicionamento com ácido fosfórico a 35%, aplicação de adesivo e inserção de resina composta; Grupo 4 - asperização com ponta diamantada, condicionamento com ácido fosfórico a 35%, aplicação de adesivo e inserção de resina composta. Após a confecção, os espécimes foram armazenados em água a 37oC durante 24h, sendo em seguida montados em uma máquina universal de ensaios para realização dos testes de resistência ao cisalhamento. Os resultados foram submetidos à análise de variância a um critério e ao teste de Tukey para comparação entre os grupos. Não houve diferença entre os grupos 3, 4 e controle (p < 0,05). A contaminação da superfície da resina com saliva (Grupo 2) diminuiu significativamente a resistência de união (p < 0,05). A análise em MEV dos espécimes do grupo 2 demonstrou a ocorrência de fraturas na interface adesiva em quase todos os corpos-de-prova (80%). Fraturas coesivas da resina inserida na matriz de resina epóxica puderam ser observadas em todos os espécimes dos Grupos 3 e 4. O método que emprega limpeza superficial com ácido e aplicação de um sistema adesivo demonstrou ser efetivo na recuperação da resistência adesiva a valores semelhantes à resistência coesiva do material / Shear bond strength between the contaminated composite resin surface and a new increment of the same material was analysed. Forty specimens of a nanohybrid composite, were divided into four groups. Each group received a surface treatment. In one of the groups, there was no surface contamination (Group 1 - control). The new increment of composite resin was inserted by placing a Teflon matrix (3.5mm height, 3mm diameter) over the already polymerized composite surface. For the other groups, the polymerized composite surface was contaminated with saliva and dried with air. Surface treatments were performed in the following way: Group 2 - new increment was inserted and polymerized directly on the contaminated surface; Group 3 - contaminated surface was treated with 35% phosphoric acid etching and adhesive was applied prior to the insertion of the new increment; Group 4 - diamond bur roughening, 35% phosphoric acid etching, adhesive application and insertion of the new composite increment. Specimens were stored in water at 37oC for 24h. After this period, specimens were mounted in a universal testing machine for the shear bond strength tests. Results were submitted to one way anova and Tukey test multiple comparison. No significant differences were detected between Groups 3, 4 and control (p < 0.05). Saliva contamination of resin surface (Group 2) significantly reduced shear bond strength (p < 0.05). SEM analysis in Group 2 demonstrated fractures at the interface in 80% of the specimens. Cohesive fractures in first increment of resin composite was observed in all specimens in Groups 3 and 4. Decontamination of resin surface with phosphoric acid followed by adhesive application, was an effective method to improve shear strength, reaching similar numbers to the cohesive resistance of the material

Este estudo teve a finalidade de verificar influência de diferentes tipos de pinos intra-radiculares sobre a resistência à fratura de um material restaurador coronário, utilizando o teste de tração diametral. Foram confeccionados 70 corpos de prova divididos em 7 grupos: G1. Compósito (Tetric Ceram – Ivoclar/Vivadent) (Grupo Controle); G2. Compósito e pino VectrisPost (Ivoclar/Vivadent); G3. Compósito e pino Fiber-Post (Jeneric/Pentron); G4. Compósito e pino Æstheti-Plus (Bisco); G5. Compósito e pino Light-Post (Bisco); G6. Compósito e pino Dentorama (Svenska) e G7. Compósito e pino ParaPost (Còltene/Whaledent). Todos os grupos foram submetidos ao ensaio de tração diametral em uma máquina de ensaios Instron, modelo 8501, até a fratura. A média dos grupos em MPa foi: G 1- 49,64 (3,36); G 2- 29,77 (3,36); G 3- 31,9 (2,39); G 4- 28,92 (2,20); G 5- 34,26 (3,37); G 6-33,45 (2,46) e G 7- 27,90 (2,40). A análise estatística dos dados nos permitiu concluir que: os pinos utilizados não reforçaram a resina composta; os pinos Light-Post, Dentorama e Fiber-Post apresentaram os melhores valores de adesividade ao material de reconstrução coronária e que o pino metálico ParaPost apresentou o menor valor de adesão à resina de reconstrução coronal. / The purpose of this study was to determine the influence of different types of posts on the fracture strength of a resin composite core material using the diametral tensile strength test. Seven groups of specimens were prepared each with 10 cylindrical specimens made of one composite material (Tetric Ceram, IvoclarVivadent) as follows: Group 1- Control group of composite only specimens; Group 2-Composite and VectrisPost (IvoclarVivadent); Group 3- Composite and Fiber-Post (Jeneric/Pentron); Group 4- Composite and Æstheti-Plus post (Bisco); Group 5- Composite and Light-Post (Bisco); Group 6- Composite and Dentorama post (Svenska) and group 7- Composite and ParaPost (Coltene/Whaledent). Following storage specimens were subjected to compressive loading in an Instron testing machine (model 8501) until failure occurred. Means and standard deviations of diametral tensile strengths in MPa were: Group 1- 49,64 (3,36); Group 2- 29,77 (3,36); Group 3- 31,9 (2,39); Group 4- 28,92 (2,20); Group 5- 34,26 (3,37); Group 6- 33,45 (2,46) and Group 7- 27,90 (2,40). Statistical analysis revealed significant differences in mean diametral tensile strengths among the groups. It is concluded that the use of posts did not reinforce the composite resin cores. Among the post/core groups Light-Post, Dentorama post and Fiber-Post resulted in the highest values of tensile strength while ParaPost resulted in the lowest value of tensile strength.

Foram analisadas in vitro a dureza superficial, a contração de polimerização e a rugosidade de 29 resinas compostas. Foram confeccionados 3 corpos-de-prova para cada material, com fotopolimerização por 80 segundos; após mais 5 minutos, determinou-se a dureza superficial Rockwell 30T; os espécimes foram então armazenados em água desionizada, a 37ºC, durante 168 horas, quando nova leitura da dureza foi realizada. Para avaliação da contração de polimerização, foram confeccionados 5 corpos-deprova para cada material; cada resina era inserida em uma matriz metálica, com uma cavidade em forma de “meia cana", cujas paredes das extremidades planas eram paralelas entre si, com fotopolimerização por 40 segundos; após 10 minutos, removia-se a amostra da matriz, cujo comprimento era medido para se estabelecer a contração inicial ocorrida; os espécimes eram então armazenados em estufa a 37ºC, durante 168 horas (1 semana), quando nova medida era tomada, para se determinar a contração final da resina. Os mesmos corpos-de-prova usados nos testes de dureza, após desgaste com lixas de papel até a de n.º 1.500, foram analisados num rugosímetro. Estatisticamente, todas as resinas mostraram aumento da dureza e da contração de polimerização, da medição imediata para a com 168 horas. Em termos globais, as que apresentaram os melhores resultados, analisando-se as três características simultaneamente, foram a Z-100 e a P-60, enquanto as com o pior desempenho foram a Solitaire e a Helioprogress. / In vitro surface hardness, polimerization shrinkage and roughness of 29 composite resins were stablished. For each material, it were made 3 specimens, photocured by 80 seconds; 5 minutes later, Rockwell 30T surface hardness was determined; the specimens were then imersed in deionized water, at 37ºC by 168 hours, when a new evaluation of hardness was effectued. In evaluating polymerization shrinkage, 5 specimens were made for each material; each resin was inserted in a metallic matrix, in which there was a cavitiy with the shape of a hemi-cilinder, whose flat surfaces were paralel between itself, com photopolimerization for 40 seconds; 10 minutes later, the lenght was measured to determine the inicial shrinkage; specimes were then stored in a stove, at 37ºC for 168 hours, when a new length measuring was effectued to determine the final shrinkage. The same specimens used for hardness were abraded with sand paper (till 1,500 mesh) and evaluated for roughness with a rugosimeter. All resins showed an increase in hardness and in polymerization shrinkage, since the inicial evaluation to that effectued 168 hours later. In a global way, by a simultaneous analysis of the 3 characteristics, the best results were presented by Z-100 and P-60; Solitaire and Helioprogress had the worst performance.