Orientador: Luis Alexandre Maffei Sartini Paulillo / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T02:10:27Z (GMT). No. of bitstreams: 1 Bueno_VanessaCastroPestanadaSilveira_D.pdf: 3504173 bytes, checksum: 488f4a8e60e6898ff6100d2f0988de61 (MD5) Previous issue date: 2009 / Resumo: O objetivo deste estudo foi avaliar in vitro a influência de diferentes proporções de cimentos resinosos e o uso de co-iniciadores químicos na resistência ao cisalhamento por extrusão, push - out, na interface de união dentina intra-radicular e pinos de fibra de vidro e ainda expressar o grau de infiltração do nitrato de prata na camada híbrida. Foram utilizadas 54 raízes bovinas, divididas em seis grupos experimentais. As técnicas de cimentação avaliadas foram: Grupo I - Clearfil SE Bond/ Panavia F na proporção base/ catalisador 1:1 (CP1), Grupo II - Clearfil SE Bond/ Panavia F 1:3 (CP3), Grupo III - Clearfil SE Bond/ ED primer/ Panavia F 1:1 (CPE), Grupo IV - Scotchbond Multi-Purpose/ RelyX ARC 1:1 (SR1), Grupo V - Scotchbond Multi-Purpose/ RelyX ARC 1:3 (SR3) e Grupo VI - Scotchbond Multi-Purpose/ Catalisador/ RelyX ARC 1:1 (SRC). O teste de Tukey para comparação múltipla (p<0,05) para o ensaio de resistência ao cisalhamento por extrusão de sistemas para a fixação dos pinos de fibra de vidro demonstrou que a maior média foi apresentada pelo sistema SRC (130,71Kgf) e a menor média foi apresentada pelo sistema CPE (16,57Kgf). Os resultados da nanoinfiltração, através da microscopia eletrônica de varredura (MEV), mostraram infiltração de prata na camada híbrida em todos os terços de todos os grupos estudados. Portanto, pôde-se concluir que o uso de co-iniciadores químicos favoreceu a técnica de cimentação com o adesivo Scotchbond Multi-Purpose e cimento RelyX ARC. Para o Clearfil SE Bond e Panavia F a alteração da proporção base/catalisador ou o uso de co-iniciadores químicos não aumentou os valores de resistência ao cisalhamento por extrusão / Abstract: The purpose of this in vitro study was to evaluate the push-out shearing resistance in the union interface of root dentin and fiber posts bonded with resin-based luting cement in different ratios between base and catalyst paste, the use of chemical catalysts and also demonstrate through nanoleakage, observed with SEM, the degree of silver nitrate infiltration in the hybrid layer. Fifty four bovine roots were divided into six experimental groups. For the fiber posts cementation, the following resin-based luting cements were used: Group I - Clearfil SE Bond+ Panavia F with 1:1 base/catalyst ratio (CP1), Group II - Clearfil SE Bond+ Panavia F with 1:3 base/catalyst ratio (CP3), Group III - Clearfil SE Bond + EDprimer + Panavia F with 1:1 base/catalyst ratio (CPE), Group IV - Scotchbond Multi-Purpose + Rely X with 1:1 base/catalyst ratio (SR1), Group V - Scotchbond Multi-Purpose + Rely X with 1:3 base/catalyst ratio (SR3) and Group VI - Scotchbond Multi-Purpose + activator + Rely X with 1:1 base/catalyst ratio (SRC). The push out test was performed using the universal essay machine EMIC D 500, capacity of 100KN in a speed up to the fracture calculated in MPa. The results were submitted to the Tukey test (p<0.05). The highest average was presented by CP1 system (130,71Kgf) and the lowest average was presented by CPE system (16,57Kgf). Moreover, the nanoleakage was evaluated with SEM and it revealed in the bond region the presence of silver in all portions of roots for all groups, however, for both Clearfil SE Bond and Scotchbond Multi-Purpose systems, in which the base/catalyst ratio was increased, it was observed some areas with a more effective adhesion. In accordance with the evaluated factors and considering the obtained results, it can be concluded that the use of chemical catalysts benefited the Scotchbond Multi-Purpose system; however, for the Clearfil SE Bond system, independent of the base/catalyst ratio used, no differences were noticed in the results / Doutorado / Dentística / Doutor em Clínica Odontológica

Orientadores: Mario Fernando de Goes, Marcela Rocha de Oliveira Carrilho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T06:17:38Z (GMT). No. of bitstreams: 1 Almeida_JulioCesarFranco_D.pdf: 499079 bytes, checksum: 777476c1e47008d96a6038604656dce4 (MD5) Previous issue date: 2009 / Resumo: O objetivo geral deste estudo foi avaliar in vitro os efeitos de variações na umidade dentinária no estabelecimento e durabilidade da união resina-dentina através da associação de materiais e técnicas que apresentam potencial para uso em restaurações adesivas. Para atender ao objetivo geral, dois estudos com objetivos específicos foram propostos: 1) avaliar os efeitos da condição de umidade da dentina na durabilidade da resistência da união (RU) à dentina obtida por meio da associação de oxalato de potássio com primers a base de água ou etanol. 2) avaliar os efeitos da técnica úmida utilizando etanol na durabilidade da RU à dentina obtida através do uso de primers com características hidrofílicas e hidrofóbicas. Os primers experimentais foram preparados utilizando-se a proporção 35% monômeros / 65% solventes (v/v), como se segue: HEMA/água, HEMA/etanol, Bis-GMA/etanol e um agente de união com características hidrofóbicas (Adper Scothbond Multi-Purpose adhesive, 3M/ESPE) foi usado nos dois estudos. A RU foi avaliada pelo teste de resistência à microtração 24 h após a realização do procedimento adesivo ou após 6 meses de armazenamento em água, utilizando-se dentes humanos hígidos recém extraídos para confecção das amostras de acordo com os objetivos específicos de cada estudo. Os resultados do estudo 1 mostraram que de uma maneira geral a associação de oxalato de potássio com primers a base de água e etanol reduziu significativamente a RU imediata e a longo prazo para os primers a base de água e etanol, independente da condição de umidade da dentina. Os resultados do estudo 2 indicaram que a técnica úmida com etanol resultou em maior RU imediata para os primers com características hidrofílicas e hidrofóbicas enquanto o armazenamento em água por 6 meses diminuiu a RU para o primer hidrofílico, independente da técnica utilizada. / Abstract: The overall goal of this investigation was to evaluate in vitro the effects of dentin moisture variations in the establishment and durability of the resin-dentin bonds by the association of materials and techniques with potential for use in adhesive restorative procedures. In order to meet the overall objective, two studies with specific goals were proposed. 1) to evaluate the effects of dentin moisture condition on the durability of the bond strength (BS) to dentin produced by the association of potassium oxalate with experimental water-and ethanolbased primers; 2) to evaluate the effects of the ethanol wet-bonding technique on the durability of the BS produced with the use of experimental primers with hydrophilic and hydrophobic characteristics. The experimental primers were prepared using the proportion 35% monomers / 65% solvents (v/v) as follows: HEMA/water, HEMA/ethanol, Bis-GMA/ethanol and the same bonding agent with hydrophobic characteristics was used in both studies (Adper Scothbond Multi- Purpose adhesive, 3M/ESPE). A microtensile bond strength test was performed 24 h after bonding procedures and 6 months after water storage, using freshly extracted noncarious human teeth for specimen preparation according to the specific goals of each study. In general, the results of study 1 showed that the association of potassium oxalate with water-and ethanol-based primers reduced significantly the immediate and long-term BS, regardless of the dentin moisture condition. The results of study 2 showed that the ethanol wet-bonding technique resulted in higher immediate BS for the hydrophilic and hydrophobic primers, while 6-month water storage reduced the BS for the hydrophilic primer, regardless of the employed bonding technique. / Doutorado / Doutor em Materiais Dentários

Orientador: Marcela Rocha de Oliveira Carrilho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T16:52:08Z (GMT). No. of bitstreams: 1 Silva_SafiraMarquesdeAndradee_D.pdf: 1576367 bytes, checksum: 1f6e7c3cd256a0690cb307270c1569c0 (MD5) Previous issue date: 2008 / Resumo: O objetivo geral desta pesquisa foi avaliar materiais e procedimentos empreendidos para incrementar a durabilidade das restaurações adesivas. Os objetivos específicos foram: 1) avaliar o efeito da aplicação de uma camada adicional de adesivo e de um agente de união com característica hidrofóbica e livre de solventes na permeabilidade da dentina hibridizada com adesivos convencionais de 2 passos; 2) avaliar os efeitos decorrentes da aplicação do oxalato de potássio na durabilidade da interface de união obtida com adesivos convencionais e 3) determinar se a aplicação prévia do oxalato de potássio na dentina condicionada interfere na dureza Knoop dos adesivos. No primeiro estudo, a permeabilidade dentinária foi mensurada utilizando-se um medidor automático de fluxo, antes e após a aplicação dos sistemas adesivos nas condições experimentais citadas. Os resultados mostraram que nenhum dos adesivos foi capaz de prevenir a passagem de fluidos através da sua estrutura polimerizada. Porém, a aplicação de uma camada de um agente de união hidrofobico e livre de solventes reduziu significantemente a permeabilidade da dentina hibridizada com adesivos convencionais de 2 passos. Já no segundo estudo, testes de resistência adesiva (RA) foram realizados 24 horas após o procedimento adesivo ou após 12 meses de armazenagem em água. Os espécimes foram preparados para observação em microscopia eletrônica de varredura para avaliação do modo de fratura. Os resultados mostraram que a associação do oxalato de potássio aos sistemas adesivos reduziu significantemente a RA dos mesmos. Após o período de armazenagem, a RA foi significantemente reduzida em todos os grupos. No entanto, esta queda foi significantemente menor para os grupos tratados com oxalato. Finalmente, no terceiro estudo, testes de dureza foram realizados em microdurômetro e expressos como dureza Knoop (KHN). Os resultados mostraram que a associação do oxalato de potássio aos sistemas adesivos convencionais reduziu a KHN inicial dos mesmos. / Abstract: The general aim of this study was to evaluate materials and techniques that are thought to increase the longevity of adhesive restorations. The specific aims of this study were: 1) to test whether the application of an extra layer of the respective adhesive or the application of a hydrophobic, non-solvated bonding agent would interfere on the permeability of dentin hybridized with two-step etch-and-rinse adhesives; 2) to test whether the pretreatment of acid-etched dentin with potassium oxalate gel has an effect on the durability of resin-dentin interface created with etch-and-rinse adhesives; and 3) to determine whether the hardness of etch-and-rinse adhesives is affected by the pretreatment of acid-etched dentin with potassium oxalate gel. In the first study, dentin permeability was measured with an automatic record device, before and after dentin surfaces were bonded with the adhesives in the cited experimental conditions. The results showed that none of the adhesives or experimental treatments was capable to block completely the fluid transudation across the treated dentin; however, the application of the hydrophobic nonsolvated bonding agent resulted in significant reductions in the fluid flow rate. In the second study, the resin-dentin bond strength of the adhesives was tested immediately (i.e. 24 hours) and after 12 months of storage. The results showed that the pretreatment of dentin with potassium oxalate affect negatively the baseline resin-dentin bond strength of dentin specimens. After storage, the bond strength of resin-bonded interfaces was significantly reduced for all tested groups. Nevertheless, the decrease in bond strength values was significantly lower for oxalate-treated specimens than for controls. Finally, in the third study, the specimens' hardness was determined with a hardness tester and express as Knoop Hardness (KHN). The results showed that the baseline KHN of the adhesives applied to acid-etched dentin pretreated with potassium oxalate was significantly lower than that exhibited by their respective controls. / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

Este estudo avaliou a influência do uso do digluconato de clorexidina como inibidor de metaloproteinase na resistência adesiva e dureza da camada de adesivo e camada hibrida de uma resina composta à dentina humana, por meio de ensaio de microtração e nanoedentação. Os fatores de variação estudados foram dois sistemas adesivos com estratégias de aplicação distintas Adper Scotchbond Multi-Purpose (3M ESPE, St. Paul, MN, USA) e Clearfil SE Bond (Kuraray Co., Osaka, Japan), e ainda foram realizados tratamentos no substrato dentinário utilizando duas concentrações de digluconato de clorexidina sendo estas 2% e 0,2% e grupos controle sem tratamento com clorexidina. As unidades experimentais foram compostas por 48 molares humanos hígidos divididos aleatoriamente em 6 grupos (n=8). Nestes foram aplicados os procedimentos adesivos e realizados os tratamentos de superfície, com clorexidina, previamente aos procedimentos adesivos. Após esta etapa foram confeccionadas as restaurações com espessura de 5mm sobre as superfícies dentinárias. Após 24h de armazenamento em água destilada, os dentes restaurados foram cortados para a obtenção de corpos de prova em forma de palito, com secção transversal de aproximadamente 1mm2. De cada grupo foram selecionados aleatoriamente 5 palitos para o ensaio de dureza. O restante dos palitos viáveis de cada dente foram submetidos ao teste de microtração a uma velocidade de 0,5mm/min até que ocorresse a fratura da interface adesiva. Para o teste de nanoedentação cada um dos 5 palitos referentes aos 6 grupos estudados receberam 10 endentações, sendo 5 na camada de adesivo e 5 na camada hibrida, com distância de 10m entre si. Essas endentações foram realizadas com ultramicrôdurometro (DUH-W211S, Shimadzu Co., Tokyo, Japan). Os dados referentes aos testes de microtração dos seis grupos foram submetidos à análise de variância e teste de Tukey (p<0,05). As médias dos grupos foram: Grupo 1: Clearfil SE controle ( 28.50±0.47); Grupo 2: Adper Scotchbond controle (43.90±7.26); Grupo3: Clearfil SE/ clorexidina 2% (30.43±6.59); Grupo 4: Adper Scotchbond/ clorexidina 2% (39.21±4.69); Grupo 5: Clearfil SE 0,2%( 27.28±7.05); Grupo 6: Adper Scotchbond/ clorexidina 0,2% (35.70±6.43). Na comparação entre as médias dos grupos obteve-se que nenhum dos adesivos testados apresentou alteração na sua resistência de união com o uso do digluconato de clorexidina a 2% ou a 0,2% em análise imediata. Os grupos em que foi utilizado o adesivo Scotchbond apresentaram maiores valores de resistência de união que os grupos em que foi utilizado o sistema adesivo autocondicionante (Clearfil) independente da realização ou não do tratamento de superfície com digluconato clorexidina. Os valores de dureza da camada de adesivo não apresentaram diferenças estatisticamente significantes entre os grupos controle ou entre tratamentos, apenas o grupo com tratamento prévio Clearfil SE/Clorexidina 0,2% apresentou maior valores de dureza na camada de adesivo quando comparado ao grupo Scotchbond com a mesma concentração de clorexidina. Quanto aos valores de dureza da camada híbrida o grupo controle Clearfil SE quando comparado ao grupo Clearfil SE/Clorexidina 2% apresentou menor valor de dureza da camada hibrida. O Scotchbond controle apresentou menor valor de dureza na camada hibrida quando comparado ao grupo Scotchbond com clorexidina a 0,2%. O uso do digluconato de clorexidina nas concentrações 2% e 0,2% em dentina humana, apesar de ter apresentado discretas alterações na dureza da camada hibrida e camada de adesivo, não tiveram a capacidade de afetaram os valores de adesão à dentina dos diferentes adesivos testados. / This study evaluated the influence of the use of chlorhexidine gluconate as an inhibitor of metalloproteinase bond strength and hardness of the adhesive layer and hybrid layer of a composite resin to dentin, using microtensile test and nanoindentation. The variation factors studied were two adhesive systems with different implementation strategies Adper Scotchbond Multi-Purpose (3M ESPE, St. Paul, MN, USA) and Clearfil SE Bond (Kuraray Co., Osaka, Japan), and were still held treatments to dentin using two concentrations of chlorhexidine digluconate and these 2% and 0.2% untreated control groups with chlorhexidine. The experimental units were composed of 48 human molars were randomly divided into 6 groups (n = 8). These procedures were applied adhesives and surface treatments performed with chlorhexidine prior to bonding procedures. After this step the restorations were made with 5mm thickness on the dentin surfaces. After 24 hours storage in distilled water, the samples were cut to obtain specimens toothpick shaped cross-section of approximately 1mm2. Each group were randomly selected 5 toothpicks for hardness testing. The remaining viable sticks of each tooth were subjected to microtensile testing at a crosshead speed of 0.5 mm / min until the fracture of the adhesive interface. To test nanohardness each of the five toothpicks referring to six groups received 5 indentations in the adhesive layer and 5 indentations in the hybrid layer with 10m away from each other. These indentations were performed with the equipament DUH-W211S (Shimadzu Co., Tokyo, Japan). The data relating to microtensile test of the six groups were subjected to analysis of variance and Tukey test (p <0,05). The means of the groups were: Group 1: Clearfil SE control (28.50 ± 0:47), Group 2: Adper Scotchbond control (43.90 ± 7.26); Group3: Clearfil SE / 2% chlorhexidine (30.43 ± 6:59), Group 4: Adper Scotchbond / 2% chlorhexidine (39.21 ± 4.69), Group 5: Clearfil SE 0.2% (27.28 ± 07.05), Group 6: Adper Scotchbond / chlorhexidine 0.2% (35.70 ± 6:43). Comparing the means of the groups it was found that none of the adhesives tested showed a change in its bond strength with the use of chlorhexidine gluconate 2% or 0.2% in immediate analysis. The groups that used Scotchbond showed higher bond strength than the groups that used the adhesive system (Clearfil) regardless of performance or not the surface treatment with chlorhexidine digluconate. The hardness values of the adhesive layer did not show statistically significant differences between the control groups or between treatments, the group previously treated with Clearfil SE / Chlorhexidine 0.2% showed higher hardness values in the adhesive layer when compared to Scotchbond with the same concentration of chlorhexidine. As for the hardness of the hybrid layer control group Clearfil SE when compared to Clearfil SE / 2% Chlorhexidine showed lower hardness value of the hybrid layer. The Scotchbond control showed lower hardness value in the hybrid layer when compared to Scotchbond with 0.2% chlorhexidine.The use of chlorhexidine gluconate at concentrations 2% and 0.2% in human dentin, despite having discrete changes in the hardness of the hybrid layer and adhesive layer, did not have the ability to affect the values of adhesion to dentin of different adhesives tested.

Diante da grande preocupação atual por sorrisos que também embelezem um rosto, a escolha por materiais estéticos impulsiona pesquisas, que tem como objetivo não só melhorar a qualidade, mas, facilitar o uso desses materiais pelos profissionais. Assim, a proposta desse trabalho foi avaliar a influência da ciclagem mecânica na resistência de união de uma resina composta associada a um sistema adesivo convencional e um autocondicionante à dentina humana hígida por meio de teste de microtração. Para o estudo, foram utilizados 40 terceiros molares humanos hígidos, nos quais as faces oclusais foram lixadas até a obtenção de uma superfície plana com exposição do tecido dentinário. Os dentes foram divididos, aleatoriamente, em quatro grupos (n=10) de acordo com o sistema adesivo utilizado e a realização ou não da ciclagem mecânica: G1 Sistema adesivo Adper Single Bond 2 sem ciclagem mecânica (SB); G2 Sistema adesivo Clearfil SE Bond sem ciclagem mecânica (CF); G3 - Sistema adesivo Adper Single Bond 2 com ciclagem mecânica (SBC); G4 - Sistema adesivo Clearfil SE Bond sem ciclagem mecânica (CFC). Blocos de resina composta foram confeccionados nas superfícies dentinárias após aplicação do sistema adesivo correspondente. Após esse passo, os espécimes dos grupos 3 e 4 passaram por ciclagem mecânica enquanto o restante ficou armazenado em água destilada, mantidos em estufa à 37ºC até o momento do recorte dos espécimes para o teste de microtração. Os corpos de prova foram seccionados em planos perpendiculares à área de união para obtenção de espécimes com área de secção transversal aproximada de 1,0 mm², que foram tracionados, em máquina de ensaios universal, a velocidade de 0,5mm/min. Os resultados de resistência de união foram analisados usando o teste estatístico análise de variância e os modos de fratura foram avaliados em lupa estereoscópica (25X). Não foram encontradas diferenças estatísticas entre os grupos (p<0,05). Pôde-se concluir que não houve influência da ciclagem mecânica nos valores de resistência de união da resina composta associada a ambos os sistemas adesivos utilizados. / In face of an increasing concern about a smile profile that also enhances the overall facial appearance (esthetics), the choosing for more esthetic restorative materials, set in motion researches that have as objective not only the improvement of the quality, but also the easiness of use of these materials by clinicians. The purpose of this in vitro study was to evaluate, by means of a micro tensile test, the influence of the mechanical cycling, on the bond strength of a resin composite, associated to a total etch and a self etching adhesive systems, on the surfaces of sound human dentin. For this study, forty freshly extracted third molars had their oclusal surfaces grounded parallel-flat, until the dentin surfaces were completely exposed. The teeth were randomly divided in four groups (n=10) in accordance with the type of adhesive system and the mechanical cycling treatment, being: G1 Adper Single Bond 2 without mechanical cycling (SB); G2 Clearfill SE Bond without mechanical cycling (CF); G3 - Adper Single Bond 2 with mechanical cycling (SBC); G4 - Clearfill SE Bond without mechanical cycling (CFC).Following the application of the adhesive systems, regarding to each experimental condition, blocks of Z-250 composite were built, on the dentinal surfaces. After this step, the G3 and G4 specimens were submitted to the mechanical cycling test, while the G1 and G2 specimens were kept stored in distilled water at 37°C, until the moment of sectioning for the microtensile test. The specimens were seccionated perpendicularly to their adhesive area to obtain beam shaped specimens with approximate cross-section area of 0.8mm2, which were readily submitted to the microtensile test in a universal test machine with a crosshead speed of 0.5mm/min. The fracture modes were evaluated by means of a stereoscopic microscope (25x). There were no significant statistical differences founded in the bond strength values among the tested groups.

Este estudo teve como objetivo a análise da interface de adesão à dentina humana, de um sistema restaurador adesivo à base de silorano. Foram confeccionadas cavidades com 4mm X 3mm X 5mm em 40 molares humanos extraídos divididos em 4 grupos aleatoriamente: Grupos SB e SB-6m: sistema adesivo (Adper&#x2122; Single Bond) + resina composta (Filtek Z250); Grupos P90 e P90-6m: sistema adesivo (P90 System Adhesive) + resina composta (Filtek P90&#x2122;). Em todos os grupos, as restaurações foram inseridas em 4 incrementos oblíquos. Após a restauração, os dentes foram seccionados em fatias de 0,8mm de espessura em uma máquina de cortes com um disco de diamante. Uma fatia de cada dente foi separada aleatoriamente para análise em microscópio óptico para verificação de fendas na interface adesiva. As demais fatias foram seccionadas em palitos (0,8mm X 0,8mm) para os testes de microtração em uma máquina de ensaios universal EMIC. Os e dos grupos SB e P90 permaneceram em água deionizada em estufa a 370C por 24 horas e os grupos SB-6m e P90-6m permaneceram em água deionizada em estufa a 370C por um período de 6 meses. Os resultados de resistência de união foram submetidos à análise de variância a 2 critérios ANOVA e a presença de fendas internas foi analisada pelo testeChi-quadrado. Houve diferença estatisticamente significante na resistência de união entre os materiais (p>0,05) e tempo de armazenagem. Quanto à presença de fendas internas, foi evidenciada sua presença em todos os grupos, sem diferença etatisticamente significante entre eles (p>0,05). Conclui-se que não houve diferença entre os sistemas restauradores á base de Bis-GMA e de silorano os 2 períodos avaliados (24h e 6 meses). / This study aimed to analyse the adhesive interface to human dentin of a silorane based adhesive system. Cavities were fabricated with 4.0 mm X 3mm X 5mm in 40 extracted human molars randomly divided into 4 groups: Groups SB and SB-6m: adhesive system (Adper&#x2122; Single Bond) + composite (Filtek Z250); Groups P90 and P90- 6m: adhesive system (P90 System Adhesive) + composite (Filtek&#x2122; P90). In all groups, the restorations were inserted in 4 oblique increments. After 24 hours, teeth were sectioned buccolingually into 0.8mm slices with diamond saw. One slice of each tooth was randomly separated for microscope analysis. The other slices were sectioned into 0.8mm X0.8mm sticks for microtensile tests in a universal testing machine EMIC. Sticks of groups SB and P90 remained in deionized water at 370C C for 24 hours and sticks of groups SB-6m and P90-6m remained in deionized water at 370C for a period of six months. After storage period . The results of bond strength were analysed by Two-way ANOVA and the presence of internal gaps was analyzed by chi-square test. There was no significant difference in bond strength between materials (p> 0.05) and storage time. Regarding the presence of internal rifts, their presence was evident in all groups, with no statistically significant difference between them (p> .05).

Os refrigerantes são potentes agentes erosivos que podem provocar perda de estrutura dentária e requerer o tratamento restaurador adesivo, dependendo do grau de comprometimento. Pelas diferentes propriedades apresentadas, estas bebidas podem afetar a adesão à dentina de diferentes formas. Este estudo teve como objetivo avaliar a resistência de união (RU) em dentina erodida tratada com solução de clorexidina a 2%. Sessenta terceiros molares tiveram a superfície dentinária do terço oclusal exposta e foram distribuídos em 3 grupos, de acordo com o protocolo erosivo: controle, sem desafio (C), desafio erosivo com Coca-Cola (CC) e desafio erosivo com Coca-Cola Light (CL). As ciclagens erosivas foram por ciclos de 5-min de imersão 3x/dia durante 5 dias. Em seguida, metade dos dentes foi tratado com solução de clorexidina a 2% (1,5ul) e o restante com água deioinizada (1,5ul) e o processo adesivo realizado com Adper Single Bond 2® e resina composta Filtek Z350®. Os espécimes foram mantidos em estufa a 37oC por 24 horas. Após esse período, todos os espécimes foram seccionados em palitos (0,80mm2 a 1mm2). Um terço dos palitos obtidos de cada grupo foi testado imediatamente (I-24 h) pelo teste de microtração. Os espécimes remanescentes foram envelhecidos em saliva artificial por 6 meses (6m) e 1 ano (1a) antes do teste. Os dados obtidos da microtração foram analisados por meio dos testes de ANOVA a três critérios e Tukey (p<0,05). O modo de fratura foi analisado e classificado em adesivo, misto e coesivo em dentina ou resina composta. Simultaneamente, uma fatia (mesiodistal) de cada espécime foi analisado por microscopia confocal para análise da interface resina/dentina e formação de tag nos tempos de envelhecimento. Os valores médios de resistência adesiva (MPa ± dp; 24 horas/6 meses /1 ano) foram: C(38,57 ± 15,36/26,67 ± 19,37/12,21 ± 11,24); C-Chx2%(41,93 ± 9,97/31,12 ± 17,02/11,86 ± 10,4); CC(21,80 ± 7,09/8,33 ± 10,71/4,70 ± 9,04); CC-Chx2%(19,85 ± 7,87/24,32 ± 11,7/6,19 ± 12,37); CL (22,70 ± 9,63/10,25 ± 15,6/4,93 ± 5,54); CL-Chx 2% (22,40 ± 7,34/20,94 ± 14,68/16,05 ± 13,91). A resistência de união à dentina erodida foi significativamente inferior ao do grupo controle, independentemente do tempo de armazenagem dos espécimes. Tanto a dentina normal e erodida, apresentaram redução dos valores de resistência de união ao longo do tempo. Apesar de os espécimes tratados com solução de clorexidina a 2% manterem os valores de resistência de união por 6 meses, eles reduziram após 1 ano. De acordo com as imagens por microscopia confocal, não houve diferenças observadas na qualidade geral da camada híbrida e formação de tags entre os grupos. A solução de digluconato de clorexidina a 2% pode ser uma alternativa para manter a estabilidade da interface de união adesiva ate os 6 meses. A resistência de união mais estável à dentina erodida por Coca-Cola Light comparada à dentina erodida por Coca-Cola ao longo do tempo, sugere a implicação de suas propriedades na adesão. / Soft drinks are potent erosive agents, which can provoke loss of dental structure and require adhesive restorative treatment, depending on the compromising level. Due to the different properties, these beverages can affect bonding to dentin in different manners. The aim of this study was to evaluate the bond strength (BS) to eroded dentin treated with 2% chlorhexidine solution. Sixty third human molars had their oclusal thirds removed to expose flat dentin and were divided into three groups, according to erosive protocol: Control (C) with no surface treatment, erosive challenge with Regular Coke (CC), erosive challenge with Light Coke (CL). The erosive challenge was performed by cycles of 5-min immersions, 3x/day during 5 days. After that, half of the teeth were treated with 2% chlorhexidine solution (1,5ul) and the remaining with deionized water (1,5ul) before adhesion procedure with Adper Single Bond 2® and FiltekTMZ350®. Specimens were stored at 37oC in deionized water for 24 hours. After this period, all specimens were sectioned into sticks (&#x2248;0.81 mm2 to 1mm2). A third of the specimens were tested immediately (I-24 h), for microtensile test. The remaining sticks aged in artificial saliva for 6 months (6m) and 1 year (1y) before testing. The failure mode was analyzed and classified as adhesive, mixed and cohesive in dentin or resin. Bond strength data was analyzed by three-way ANOVA and Tukey tests (p<0.05). Simultaneously, one slice (mesial-distal) of each specimen was analyzed by confocal microscopy for analysis of the interface resin/dentin and tag formation over the aging time. Means and standard-deviation (MPa) of each group (I, 6m and 1y) were: C (38.57±15.36, 26.67±19.37, 12.21±11.24), C-Chx 2% (41.93±9.97, 31.2±17.02, 11.86±10.4), CC (21.80±7.09, 8.33±10.71, 4.70±9.04), CC-Chx 2% (19.85±7.87, 24.32±11.7, 6.19±12.37) CL (22.70±9.63, 10.25±15.6, 4.93±5.54) and CL-Chx 2% (22.40±7.34, 20.94±14.68, 16.05±13.91). Adhesive and/or mixed failures were frequently observed in all specimens. Bond strength of eroded dentin specimens was lower than of the normal dentin specimens, for all testing times. Both normal and eroded dentin showed decrease on µTBS values with time. Although the specimens treated with 2% chlorhexidine solution maintained the bond strength values for 6 months, they reduced significantly, after 1 year. after this period the bond strength values went down. According to confocal microscopy images, no difference in the overall quality of hybrid layer and tags formation among groups was observed. The use of 2% chlorhexidine solution could be an alternative to maintain the stability of bonding interface. More stable bonding strength to eroded dentin with Coca-Light over time, compared to dentin eroded by Regular Cola suggests the implication of their properties on bonding.

Este estudo avalia a resistência de união à microtração de dois cimentos resinosos (RelyXTM U200 - 3M/ESPE e RelyXTM ARC - 3M/ESPE), na fixação de restauração cerâmica, em função do tipo de tratamento ao substrato dentinário: G1, sem tratamento (cimento autoadesivo RelyX U200); G2, sistema adesivo autocondicionante de dois passos (ClearfilTM SE Bond, Kuraray /RelyXTM ARC); e G3, sistema adesivo convencional de três passos (AdperTM ScotchbondTM Multi- Purpose, 3M/ESPE /RelyXTM ARC). Trinta dentes bovinos foram selecionados, limpos e armazenados em solução neutra de timol a 0,1% a 37oC, sendo divididos aleatoriamente em três grupos experimentais (n=10). O esmalte da face vestibular foi desgastado para expor a superfície dentinária com área de 8 mm x 8 mm e submetido, em seguida, a planificação com lixas de carbeto de silício no 180, 320 e 600. Trinta blocos cerâmicos de dissilicato de lítio, IPS e-max - Ivoclar Vivadent, medindo 8 mm x 8 mm x 2 mm, foram confeccionados e suas superfícies de cimentação jateadas com partículas de óxido de alumínio (50&#x3BC;m). Previamente à cimentação, todos os blocos cerâmicos tiveram suas superfícies internas condicionadas com ácido fluorídrico e foram aplicados agentes silano. Os tratamentos em dentina e os procedimentos de cimentação seguiram as normas dos fabricantes correspondentes para cada grupo. Decorridas 24 horas da cimentação, os conjuntos dente/cimento/cerâmica foram seccionados em forma de vigas, com área aproximada de 1 mm2, adaptados à máquina universal de ensaios (INSTRON) para realização do teste de microtração, utilizando-se a célula de carga de 500N com velocidade de 0,5 mm/minuto. Os valores médios de resistência à microtração (MPa) encontrados foram: G1 (16,16 ± 7,16), G2 (27,92 ± 6,17) e G3 (25,06 ± 6,09). Os dados foram submetidos à análise de variância e ao teste de Tukey em nível de significância de 5%. O cimento resinoso autoadesivo RelyXTM U200 apresentou menor potencial de resistência de união com diferença estatística significante, quando comparado ao cimento resinoso convencional RelyXTM ARC e tratamento prévio com os adesivos convencional de três passos e autocondicionante de dois passos. Entretanto, a associação do cimento RelyXTM ARC tanto ao sistema adesivo convencional quanto ao acondicionante apresentou valores médios similares de resistência de união aos substratos dentinário e cerâmico. Dentre os tipos de fratura, após o teste de microtração, o cimento RelyXTM U200 demonstrou maior ocorrência de falhas do tipo adesiva em dentina (AD), com menor interação adesiva junto à dentina. A associação do sistema adesivo convencional ao cimento resinoso convencional evidenciou menor ocorrência de fraturas AD e maior ocorrência junto à cerâmica, quando comparada à associação do sistema adesivo autocondicionante ao cimento resinoso convencional, apesar de os resultados de resistência de união demonstrarem similaridade de valores e estatística. / This study evaluates the microtensile bond strength of two resin cements (RelyXTM U200 - 3M/ESPE and RelyXTM ARC - 3M/ESPE), in the retention of ceramic restorations according to the treatment type of the dentin substrate; G1: no treatment (RelyX U200 self-adhesive cement); G2: two-step self-etch adhesives (ClearfilTM SE Bond, Kuraray /RelyXTM ARC); and G3: three-step etch and rinse adhesives (AdperTM ScotchbondTM Multi-Purpose, 3M/ESPE /RelyXTM ARC). Thirty bovine teeth were selected, cleaned and stored in a neutral 0,1% thymol solution at 37oC, divided randomly into three experimental groups (n=10). The facial surface enamel was scaled in order to expose an area of 8mm x 8mm of the dentin surface, and subsequently planed with no 180, 320 and 600 silico n carbide sandpaper. Thirty lithium disilicate ceramic blocks, IPS e-max Ivoclar Vivadent, measuring 8mm x 8mm x 2mm were made and their surfaces sandblasted with aluminum oxide particles (50&#x3BC;m). Before cementation, the internal surfaces of all the ceramic blocks were conditioned with hydrofluoric acid and silanized. The dentin treatments and the cementation procedures followed the manufacturers norms for each group. Twentyfour hours after cementation, the tooth/cement/ceramic blocks were sectioned into beam-like structures, each with an approximate area of 1mm2, adapted to the universal testing machine (INSTRON) in order to test microtensile strength, with the load cell set at 500N, at a speed of 0.5mm/min. The mean values found for microtensile strength (MPa) were: G1 (16,16 ± 7,16), G2 (27,92 ± 6,17) and G3 (25,06 ± 6,09). The data were submitted to analysis of variance and to Tukeys test, with a 5% significance level. The self-adhesive resin cement RelyXTM U200 presented the lowest potential bond strength, with a statistically significant difference when compared to the conventional resin cement RelyXTM ARC and prior treatment with three-step etch and rinse adhesives and two-step self-etch adhesives. However the association of the RelyXTM ARC cement, both with the conventional adhesive system and with the self-etch adhesives produced similar mean values for bond strength in the dentin and ceramic substrates. Among the types of fracture, following the test for microtensile strength, the RelyXTM U200 cement presented the highest incidence of faults of the dentin adhesive (DA) type, and the lowest adhesive interaction with the dentin. The association of the conventional adhesive system with conventional resin cement presented a lower incidence of DA fractures and a higher incidence along the ceramics, when compared to the association of the self-etch adhesive system and conventional resin cement, despite the similarity in the numbers and statistics of the bond strength results.

O LASER tem sido utilizado previamente a polimerização de sistemas adesivos em dentina como uma estratégia para melhorar as suas propriedades. O objetivo deste estudo foi investigar o efeito do LASER de diodo na sorção (SB), solubilidade e grau de conversão das principais categorias de sistemas adesivos. Quatro sistemas adesivos foram testados: convencional de 3 passos (Adper&#x2122; Scotchbond&#x2122; Multi-Purpose-MP), convencional de 2 passos (Adper&#x2122; Single Bond 2-SB), autocondicionante de 2 passos (Clearfil&#x2122; SE Bond-SE) e o sistema universal (Adper&#x2122; Single Bond Universal-SU). O adesivo fluido foi dispensado numa matriz de teflon (6.0 x 6.0 x 1 m),irradiado com laser de diodo com 970 nm e polimerizado com luz LED. Para o teste de sorção e solubilidade foram preparados espécimes em uma matriz de teflon quadrada (n=10): MP, SB, SE e SU (sem irradiação) e MP-L, SB-L, SE-L e SU-L (grupos com irradiação). Essa mensuração foi monitorando a mudança de massa depois dos ciclos de armazenamento de desidratação/ água. Para o grau de conversão, espécimes similares eram preparados e divididos 8 grupos iguais (n=5), utilizando a espectroscopia infravermelho transformada de Fourrrier (FTIR) com reflectância total atenuada (ATR). Cada espécime era comprimido contra o cristal do ATR (diamante/ZnSe) com um pressão micrométrica. As amostras não polimerizadas (&#x2248;3.0&#x3BC;L, n=5) de cada adesivo era escaneada para calcular o grau de conversão. Para sorção (&#x3BC;g/mm3) houve diferença estatisticamente significante para ambos os fatores (p<0.05) sem interação entre eles SB> SU> MP> SE. Para a solubilidade (&#x3BC;g/mm3), somente o fator adesivo foi significante (p<0.05): SB>SU>MP=SE. A irradiação do LASER antes da polimerização aumentou o grau de conversão dos sistemas adesivos SBL> MP-L> SE-L> MP> SB> SE> SU-L> SU. A irradiação aumentou a sorção, mas não afetou a solubilidade dos sistemas adesivos. Além disso, a irradiação com LASER de diodo melhorou o grau de conversão de três sistemas adesivos testados. / Laser irradiation has been used over the dentin bonding systems (DBS) prior to polymerization as a strategy to improve their properties. The aim of this study was to investigate the effect of diode laser on water sorption (WS), solubility (WSB) and conversion degree (DC) of main categories of DBS. Four bonding agents were tested: 3-step total-etch (Adper&#x2122; Scotchbond&#x2122; Multi-Purpose-MP), 2-step total-etch (Adper&#x2122; Single Bond 2-SB), 2-step self-etch Clearfil&#x2122; SE Bond-SE) and universal system (Adper&#x2122; Single Bond Universal-SU). The fluid DBSs were dispensed into Teflon molds (6.0 x 6.0 x 1mm), irradiated with a 970 nm diode laser and then polymerized with a LED curing unit. For WS/WSB tests, square-shaped DBS were prepared (n=10): MP, SB, SE and SU (control groups/ no laser irradiation) and MP-L, SB-L, SE-L and SU-L (laser irradiated groups). WS/WSB were measured by monitoring the mass changes after dehydration/water storage cycles. For DC tests, similar square-shaped specimens were prepared and assigned into eight similar groups (n=5), using Fourier transform infrared spectroscopy (FT-IR) with attenuated total reflectance (ATR). Each cured specimen was compressed against the ATR crystal (diamond/ZnSe) with a micrometric, low-pressure clamp. Uncured resin samples (&#x2248;3.0&#x3BC;L, n=5) of each adhesive were also scanned for DC calculation. For WS (&#x3BC;g/mm3), both factors were statistically significant (p<0.05), without interaction between them SB>SU>MP>SE. For WSB (&#x3BC;g/mm3), only DBS was a significant factor (p<0.05): SB>SU>MP=SE. Laser irradiation immediately before photopolymerization has increased the DC (%) of the tested adhesives: SB-L> MPL> SE-L> MP> SB> SE> SU-L> SU. Irradiation with diode laser improved the conversion degree of all tested dentin bonding systems. Furthermore the diode laser increased the sorption, but did not affect their water solubility.

Conselho Nacional de Desenvolvimento CientÃfico e TecnolÃgico / FundaÃÃo Cearense de Apoio ao Desenvolvimento Cientifico e TecnolÃgico / O objetivo desse estudo in vitro foi avaliar o efeito do flavonÃide epigalocatequina-3-galato (EGCG) na resistÃncia de uniÃo à dentina nos perÃodos imediato e apÃs 6 meses de armazenamento. Trinta terceiros molares humanos recÃm-extraÃdos tiveram o esmalte oclusal removidos, obtendo-se uma superfÃcie plana de dentina. Os dentes foram divididos em 5 grupos (n=6) de acordo com a soluÃÃo de re-hidrataÃÃo da dentina. As superfÃcies expostas de dentina foram condicionadas com Ãcido fosfÃrico a 35% por 15s, lavadas por 30s, e secas com jatos de ar. Os dentes dos grupos G1, G2, G3, G4 e G5 foram re-hidratados, respectivamente, com Ãgua destilada, EGCG a 0,02%, 0,1%, 0,5% e clorexidina a 2%. Cada soluÃÃo de re-hidrataÃÃo foi mantida em contato coma superfÃcie dentinÃria por 60s. O sistema adesivo - Adper Single Bond 2 (3M ESPE) foi aplicado de acordo com a instruÃÃes do fabricante. Cinco incrementos de 1 mm de espessura de resina composta foram aplicados e fotoativados individualmente por 20 segundos. Os dentes foram armazenados em Ãgua destilada a 37ÂC por 24h. Em seguida, foram confeccionados cortes seriados perpendiculares entre si, atravÃs da interface de uniÃo, para obter espÃcimes em forma de palito com a Ãrea de secÃÃo transversal de aproximadamente 1 mm2. Metade dos espÃcimes foi testada imediatamente enquanto a outra metade foi armazenada em soluÃÃo de azida de sÃdio a 0,3 mMol/l a 37ÂC por seis meses. Cada espÃcime foi tracionado a velocidade de 0,5mm/minuto em uma mÃquina universal de ensaios. Os valores de resistÃncia de uniÃo foram estatisticamente avaliados por ANOVA a dois critÃrios e Student-Newman-Keuls, com nÃvel de significÃncia de 95%. A mÃdia (desvio padrÃo) dos valores de resistÃncia de uniÃo (em MPa) foram os seguintes: No perÃodo imediato - G1= 34,17 (7,75); G2= 31,39 (7,82); G3= 34,74 (9,14); G4= 27,11 (7,78); G5= 34,68 (7,30). No perÃodo de 6 meses - G1= 27,67 (6,98); G2= 31,75 (10,58); G3= 35,99 (10,91); G4= 31,18 (9,29); G5= 31,62 (5,78). O EGCG a 0,02 % e a 0,1% nÃo afetou a resistÃncia de uniÃo, no perÃodo imediato (p>0,05). ApÃs 6 meses de armazenamento, o EGCG em diferentes concentraÃÃes manteve a resistÃncia de uniÃo. EGCG pode ser usado como uma alternativa para melhorar a durabilidade das restauraÃÃes adesivas, pois preserva a resistÃncia de uniÃo das interfaces.