1 |
Eletrólitos sólidos poliméricos à base de polissacarídeos: síntese e caracterização. / Solid polymer electrolytes based on polysacharide: synthesis and characterization.Regiani, Anelise Maria 10 November 2000 (has links)
A síntese e a caracterização de um novo tipo de eletrólito sólido polimérico são descritas neste trabalho. Os materiais preparados consistiram de filmes de hidroxietil celulose ou hidroxipropil celulose entrecruzadas com diisocianatos de poli(óxido de etileno) e poli(óxido de propileno) ou enxertadas com monoisocianato de poli(óxido de propileno). Todos estes isocianatos foram sintetizados a partir das respectivas aminas comerciais. Filmes de hidroxietil celulose entrecruzada com hexametileno diisocianato ou enxertados com fenil isocianato também foram estudados. Como técnicas de caracterização foram utilizadas espectroscopia no infravermelho, no ultravioleta e de ressonância magnética nuclear, análises térmicas e difração de raios-X. Os filmes dopados com LiClO4 foram caracterizados utilizando-se as mesmas técnicas e a condutividade foi determinada através do método de impedância complexa. Os resultados foram da ordem de 10-5 Scm-1 a 60oC. Este valor permitiu concluir que as cadeias de derivado de celulose parecem não influenciar no fenômeno de condução; aparentemente este encontra-se mais relacionado ao tipo de isocianato utilizado na formação do filme. Os resultados de condutividade e de mobilidade de cadeia polimérica indicam que os sistemas aqui estudados podem ser aplicados como eletrólitos sólidos poliméricos. Os filmes com isocianatos comerciais, no entanto não apresentaram resultado de condução interessante. / The synthesis and characterization of new types of solid polymer electrolytes based on hydroxyethyl and hydroxypropyl cellulose grafted with different polyethers were investigated. The synthesis is based on the reaction between the cellulose derivative and mono and difunctional isocyanates prepared from amines of polyethylene oxide and polypropylene oxide. It were also synthesized films of hydroxyethyl cellulose grafted with hexamethylene diisocyanate and phenylisocyanate. These materials were characterized through techniques of infrared, ultraviolet and nuclear magnetic ressonance spectroscopies, thermal analysis and X-ray diffraction. The films of polysaccharide and polyether that contained LiClO4 showed conductivity values of the order of 10-5 Scm-1 at 60oC. The value of this parameter seems to be independent of the cellulose derivative parameters and it is better related to the type of isocyanate grafted on the polysaccharide chain. The conductivity and chain mobility results show that the systems studied here can be applied as solid polymer electrolytes. The materials synthesized using commercial isocyanates as grafting reactant did not show interesting conductivity response.
|
2 |
Eletrólitos sólidos poliméricos a base de quitosana / Solid polimeric electrolyte based on chitosanDanczuk, Marins 28 November 2007 (has links)
Polímeros naturais são muito interessantes para obtenção de eletrólitos sólidos (ESPs). A grande vantagem é devida as suas propriedades de biodegradação por causa de sua procedência como também baixo custo de obtenção e boas propriedades físico-químicas. Estes polímeros contem na suas estrutura heteroatomos e por esta razão podem complexar prótons ou íons de lítio levando a condução iônica. Dentre diversos polímeros naturais os ESPs a base de Quitosana mostram boas características opto-eletroquímicas e podem ser aplicados em dispositivos eletrocrômicos. Nesta dissertação estão apresentados os resultados de preparação e caracterização de novos eletrólitos sólidos poliméricos (ESPs) obtidos através da plastificação da Quitosana com Glicerol, Sorbitol e Etileno Glicol, onde o próprio solvente, Ácido Clorídrico (HCl), é o doador de prótons responsáveis pala condução iônica dos ESPs. Alem disso foram estudadas também as amostras contendo LiCF3SO3. A caracterização dos materiais na forma de filmes foi realizada utilizando-se as técnicas básicas de caracterização de materiais tais como: análises térmicas (DSC), análises estruturais (raios-X), medidas óticas (UV-Vis), visualização da superfície das amostras através de microscopia eletrônica de varredura (MEV), espectroscopia (FTIR), Titulação Potenciométrica e como a mais importante: medidas de condutividade iônica por espectroscopia de impedância complexa (EIE). Os filmes de ESPs contendo Glicerol apresentaram-se flexíveis, transparentes (acima de 80% de transmitância na região do visível de espectro eletromagnético )e visualmente com boa aderência ao vidro e ao aço inox. A plastificação com diferentes quantidades de Glicerol, mas mantendo a mesma concentração de HCl, revelou que a amostra contendo 59% de Glicerol apresentou os melhores valores de condutividade iônica. Para esta quantidade de plastificante foi feito o estudo da influência de concentração do Ácido Clorídrico (HCl) nos valores de condutividade iônica. Este ensaio demonstrou que a amostra com 0,048 mol.L-1 apresentou maior valor de condutividade, sendo 9,54.10-4Scm-1 a temperatura ambiente. Ainda com adição de 48% do Glicerol e a inserção de 13% em massa do LiCF3SO3 foi obtida a condutividade de 2,19x10-5Scm-1. Os filmes plastificados com Etileno Glicol apresentaram melhor valor de condutividade iônica de 2,4.10-4Scm-1 a temperatura ambiente, para amostra contendo 68% de plastificante e concentração de 0,048 molL-1 de HCl. Também são transparentes, flexíveis e aderentes. Os filmes de Quitosana plastificada com Sorbitol não apresentaram boas condutividades, i.e. de ordem de 10-6 Scm-1 a temperatura ambiente para amostra contendo 59% de Sorbitol e 0,048 mol.L-1, contudo são transparentes, mas não são aderentes ao vidro e ainda são quebradiços. Os resultados demonstraram que os novos ESPs obtidos a base de filmes de Quitosana plastificada com EG e Glicerol são ótimos candidatos a serem utilizados em dispositivos eletrocrômicos. / Natural polymers are very interesting matrix to obtain solid polymeric electrolytes (SPE). The principal advantage comes from its particularly interesting biodegradation properties due to the natural precedence and also very low cost and good physical and chemical properties. These polymers contain heteroatoms in its structure and for this reason can complex protons or lithium ions leading to the ionic conduction. Among different natural polymers, chitosan-based SPEs show good opto-electrochemical characteristics and can be applied in electrochemical devices. This work presents the results of chitosan-based electrolytes, which were characterized by impedance spectroscopy (EIE), thermal analysis (DSC) and scanning microscopy (SEM). The SPEs samples were obtained from chitosan plasticized with glycerol, ethylene glycol and sorbitol and containing HCl and lithium salt LiClO4. Different compositions of SPEs i.e. salt and plasticizer quantities were investigated, where it was observed that the ionic conductivity results obtained for these SPEs varied from 10-6 S/cm to 10-4 S/cm at room temperature depending on the sample and increased following Arrhenius ionic conductivity models. The best results of ionic conductivity values of 9,54.10-4Scm-1 were obtained for SPEs of chitosan plasticized with 48% of glycerol and containing 0,048 molL-1 of HCl. The samples containing 68% of ethylene glycol showed ionic conductivity of 2,4.10-4Scm-1 at room temperature and the samples with 59% of sorbitol showed the ionic conductivity values of 10-6 Scm-1. Thermal analysis using calorimetry (DSC) was performed in order to observe the change in glass transition temperature caused by the changes performed on the samples. Good conductivity results combined with transparency and good adhesion to the electrodes have shown that chitosan-based SPEs are very promising materials to be used as solid electrolytes in electrochromic devices.
|
3 |
Eletrólitos sólidos poliméricos a base de quitosana / Solid polimeric electrolyte based on chitosanMarins Danczuk 28 November 2007 (has links)
Polímeros naturais são muito interessantes para obtenção de eletrólitos sólidos (ESPs). A grande vantagem é devida as suas propriedades de biodegradação por causa de sua procedência como também baixo custo de obtenção e boas propriedades físico-químicas. Estes polímeros contem na suas estrutura heteroatomos e por esta razão podem complexar prótons ou íons de lítio levando a condução iônica. Dentre diversos polímeros naturais os ESPs a base de Quitosana mostram boas características opto-eletroquímicas e podem ser aplicados em dispositivos eletrocrômicos. Nesta dissertação estão apresentados os resultados de preparação e caracterização de novos eletrólitos sólidos poliméricos (ESPs) obtidos através da plastificação da Quitosana com Glicerol, Sorbitol e Etileno Glicol, onde o próprio solvente, Ácido Clorídrico (HCl), é o doador de prótons responsáveis pala condução iônica dos ESPs. Alem disso foram estudadas também as amostras contendo LiCF3SO3. A caracterização dos materiais na forma de filmes foi realizada utilizando-se as técnicas básicas de caracterização de materiais tais como: análises térmicas (DSC), análises estruturais (raios-X), medidas óticas (UV-Vis), visualização da superfície das amostras através de microscopia eletrônica de varredura (MEV), espectroscopia (FTIR), Titulação Potenciométrica e como a mais importante: medidas de condutividade iônica por espectroscopia de impedância complexa (EIE). Os filmes de ESPs contendo Glicerol apresentaram-se flexíveis, transparentes (acima de 80% de transmitância na região do visível de espectro eletromagnético )e visualmente com boa aderência ao vidro e ao aço inox. A plastificação com diferentes quantidades de Glicerol, mas mantendo a mesma concentração de HCl, revelou que a amostra contendo 59% de Glicerol apresentou os melhores valores de condutividade iônica. Para esta quantidade de plastificante foi feito o estudo da influência de concentração do Ácido Clorídrico (HCl) nos valores de condutividade iônica. Este ensaio demonstrou que a amostra com 0,048 mol.L-1 apresentou maior valor de condutividade, sendo 9,54.10-4Scm-1 a temperatura ambiente. Ainda com adição de 48% do Glicerol e a inserção de 13% em massa do LiCF3SO3 foi obtida a condutividade de 2,19x10-5Scm-1. Os filmes plastificados com Etileno Glicol apresentaram melhor valor de condutividade iônica de 2,4.10-4Scm-1 a temperatura ambiente, para amostra contendo 68% de plastificante e concentração de 0,048 molL-1 de HCl. Também são transparentes, flexíveis e aderentes. Os filmes de Quitosana plastificada com Sorbitol não apresentaram boas condutividades, i.e. de ordem de 10-6 Scm-1 a temperatura ambiente para amostra contendo 59% de Sorbitol e 0,048 mol.L-1, contudo são transparentes, mas não são aderentes ao vidro e ainda são quebradiços. Os resultados demonstraram que os novos ESPs obtidos a base de filmes de Quitosana plastificada com EG e Glicerol são ótimos candidatos a serem utilizados em dispositivos eletrocrômicos. / Natural polymers are very interesting matrix to obtain solid polymeric electrolytes (SPE). The principal advantage comes from its particularly interesting biodegradation properties due to the natural precedence and also very low cost and good physical and chemical properties. These polymers contain heteroatoms in its structure and for this reason can complex protons or lithium ions leading to the ionic conduction. Among different natural polymers, chitosan-based SPEs show good opto-electrochemical characteristics and can be applied in electrochemical devices. This work presents the results of chitosan-based electrolytes, which were characterized by impedance spectroscopy (EIE), thermal analysis (DSC) and scanning microscopy (SEM). The SPEs samples were obtained from chitosan plasticized with glycerol, ethylene glycol and sorbitol and containing HCl and lithium salt LiClO4. Different compositions of SPEs i.e. salt and plasticizer quantities were investigated, where it was observed that the ionic conductivity results obtained for these SPEs varied from 10-6 S/cm to 10-4 S/cm at room temperature depending on the sample and increased following Arrhenius ionic conductivity models. The best results of ionic conductivity values of 9,54.10-4Scm-1 were obtained for SPEs of chitosan plasticized with 48% of glycerol and containing 0,048 molL-1 of HCl. The samples containing 68% of ethylene glycol showed ionic conductivity of 2,4.10-4Scm-1 at room temperature and the samples with 59% of sorbitol showed the ionic conductivity values of 10-6 Scm-1. Thermal analysis using calorimetry (DSC) was performed in order to observe the change in glass transition temperature caused by the changes performed on the samples. Good conductivity results combined with transparency and good adhesion to the electrodes have shown that chitosan-based SPEs are very promising materials to be used as solid electrolytes in electrochromic devices.
|
4 |
Eletrólitos sólidos poliméricos à base de polissacarídeos: síntese e caracterização. / Solid polymer electrolytes based on polysacharide: synthesis and characterization.Anelise Maria Regiani 10 November 2000 (has links)
A síntese e a caracterização de um novo tipo de eletrólito sólido polimérico são descritas neste trabalho. Os materiais preparados consistiram de filmes de hidroxietil celulose ou hidroxipropil celulose entrecruzadas com diisocianatos de poli(óxido de etileno) e poli(óxido de propileno) ou enxertadas com monoisocianato de poli(óxido de propileno). Todos estes isocianatos foram sintetizados a partir das respectivas aminas comerciais. Filmes de hidroxietil celulose entrecruzada com hexametileno diisocianato ou enxertados com fenil isocianato também foram estudados. Como técnicas de caracterização foram utilizadas espectroscopia no infravermelho, no ultravioleta e de ressonância magnética nuclear, análises térmicas e difração de raios-X. Os filmes dopados com LiClO4 foram caracterizados utilizando-se as mesmas técnicas e a condutividade foi determinada através do método de impedância complexa. Os resultados foram da ordem de 10-5 Scm-1 a 60oC. Este valor permitiu concluir que as cadeias de derivado de celulose parecem não influenciar no fenômeno de condução; aparentemente este encontra-se mais relacionado ao tipo de isocianato utilizado na formação do filme. Os resultados de condutividade e de mobilidade de cadeia polimérica indicam que os sistemas aqui estudados podem ser aplicados como eletrólitos sólidos poliméricos. Os filmes com isocianatos comerciais, no entanto não apresentaram resultado de condução interessante. / The synthesis and characterization of new types of solid polymer electrolytes based on hydroxyethyl and hydroxypropyl cellulose grafted with different polyethers were investigated. The synthesis is based on the reaction between the cellulose derivative and mono and difunctional isocyanates prepared from amines of polyethylene oxide and polypropylene oxide. It were also synthesized films of hydroxyethyl cellulose grafted with hexamethylene diisocyanate and phenylisocyanate. These materials were characterized through techniques of infrared, ultraviolet and nuclear magnetic ressonance spectroscopies, thermal analysis and X-ray diffraction. The films of polysaccharide and polyether that contained LiClO4 showed conductivity values of the order of 10-5 Scm-1 at 60oC. The value of this parameter seems to be independent of the cellulose derivative parameters and it is better related to the type of isocyanate grafted on the polysaccharide chain. The conductivity and chain mobility results show that the systems studied here can be applied as solid polymer electrolytes. The materials synthesized using commercial isocyanates as grafting reactant did not show interesting conductivity response.
|
5 |
Obtenção e Caracterização de Eletrólitos Sólidos de Céria-Gadolínia / Preparation and Characterization of Ceria-Gadolinia Solid ElectrolytesRocha, Renata Ayres 07 December 2001 (has links)
Soluções sólidas de CeO2:Gd2O3 foram obtidas a partir de três técnicas de síntese que se utilizam de matrizes poliméricas: técnica dos precursores poliméricos ou citratos, técnica do citrato amorfo e técnica do PVA. O principal objetivo deste trabalho é a obtenção de pós reativos e cerâmicas sinterizadas densas. Para a caracterização dos materiais, foram analisadas as resinas precursoras, o pó calcinado a duas temperaturas e os compactos sinterizados. Os principais resultados mostram que: as soluções sólidas podem ser obtidas a temperaturas relativamente baixas; os pós apresentam tamanho nanométrico de partículas; a densificação é dependente da técnica de síntese e do teor de dopante. A técnica do PVA deve ser utilizada com cuidado, principalmente quando há possibilidade de ocorrer auto-ignição durante a decomposição térmica da resina precursora. Utilizando-se a técnica dos precursores poliméricos, o teor de carbono residual foi mais elevado do que nas outras duas técnicas, como esperado. A técnica do citrato amorfo foi a que permitiu obter cerâmicas mais densas. A resistividade elétrica da cerâmica sinterizada é função do teor de dopante, do teor de pureza e da porosidade, como sugerido na literatura. / CeO2:Gd2O3 solid solutions have been prepared by the following techniques based on polymeric matrices: the citrate, the amorphous citrate and the PVA techniques. The main purpose was to obtain reactive powders for preparing highly dense sintered ceramic pieces. The precursor resin, calcined powders and sintered compacts were studied by several techniques for complete characterization. The main results show that solid solutions may be obtained at relatively low temperatures and that powder particles are in the nanosize range, whatever is the technique used for the synthesis of the solid solution. However, the densification of sintered compacts is found to be dependent on dopant content and synthesis technique. The PVA technique should be used with caution, mainly due to combustion that may occur during precursor decomposition. The residual carbon content was found to be higher for powder prepared by the citrate technique. Specimens with high densification were obtained following the amorphous citrate technique. Electrical resistivity results are in agreement with previous results that suggest a dependence of the porosity of the sintered compacts on the dopant content and also on the material chosen for precursor.
|
6 |
Obtenção e Caracterização de Eletrólitos Sólidos de Céria-Gadolínia / Preparation and Characterization of Ceria-Gadolinia Solid ElectrolytesRenata Ayres Rocha 07 December 2001 (has links)
Soluções sólidas de CeO2:Gd2O3 foram obtidas a partir de três técnicas de síntese que se utilizam de matrizes poliméricas: técnica dos precursores poliméricos ou citratos, técnica do citrato amorfo e técnica do PVA. O principal objetivo deste trabalho é a obtenção de pós reativos e cerâmicas sinterizadas densas. Para a caracterização dos materiais, foram analisadas as resinas precursoras, o pó calcinado a duas temperaturas e os compactos sinterizados. Os principais resultados mostram que: as soluções sólidas podem ser obtidas a temperaturas relativamente baixas; os pós apresentam tamanho nanométrico de partículas; a densificação é dependente da técnica de síntese e do teor de dopante. A técnica do PVA deve ser utilizada com cuidado, principalmente quando há possibilidade de ocorrer auto-ignição durante a decomposição térmica da resina precursora. Utilizando-se a técnica dos precursores poliméricos, o teor de carbono residual foi mais elevado do que nas outras duas técnicas, como esperado. A técnica do citrato amorfo foi a que permitiu obter cerâmicas mais densas. A resistividade elétrica da cerâmica sinterizada é função do teor de dopante, do teor de pureza e da porosidade, como sugerido na literatura. / CeO2:Gd2O3 solid solutions have been prepared by the following techniques based on polymeric matrices: the citrate, the amorphous citrate and the PVA techniques. The main purpose was to obtain reactive powders for preparing highly dense sintered ceramic pieces. The precursor resin, calcined powders and sintered compacts were studied by several techniques for complete characterization. The main results show that solid solutions may be obtained at relatively low temperatures and that powder particles are in the nanosize range, whatever is the technique used for the synthesis of the solid solution. However, the densification of sintered compacts is found to be dependent on dopant content and synthesis technique. The PVA technique should be used with caution, mainly due to combustion that may occur during precursor decomposition. The residual carbon content was found to be higher for powder prepared by the citrate technique. Specimens with high densification were obtained following the amorphous citrate technique. Electrical resistivity results are in agreement with previous results that suggest a dependence of the porosity of the sintered compacts on the dopant content and also on the material chosen for precursor.
|
7 |
Preparação e caracterização de eletrólitos sólidos poliméricos a partir dos derivados de celulose - hidroxietilcelulose e hidroxipropilcelulose / Preparation and characterization of solid polymeric electrolytes based on hydroxypropylcellulose and hydroxyethlcelluloseMachado, Gilmara de Oliveira 19 April 2004 (has links)
Esta tese apresenta os resultados da obtenção de eletrólitos sólidos poliméricos a partir dos derivados de celulose - hidroxipropilcelulose (HPC) e hidroxietilcelulose (HEC), ambas comerciais. Para atingir os objetivos do projeto, os dois derivados passaram por diferentes processos sendo que a HEC foi modificada fisicamente por meio de plastificação com glicerol e HPC foi alterada quimicamente. A transformação química consistiu nas reações de oxidação de grupos hidroxila da HPC em grupos cetona que, em seguida, foram submetidos as reações de enxertia com diamina de poli(óxido de propileno) [Jeffamina] resultando em redes por meio de ligações imina. A adição do sal perclorato de lítio, em diferentes concentrações, na matriz plastificada ou entrecruzada, resultou na obtenção de eletrólitos sólidos poliméricos, todos na forma de filmes. A caracterização destes eletrólitos foi realizada com técnicas básicas de caracterização de materiais como: análises térmicas (DSC, TGA), análise térmica dinâmico-mecânica (DMTA), análises estruturais (raios-X), medidas espectroscópicas (IR, UVNIS), análise elementar, microscopia eletrônica de varredura (SEM), e, como a mais importante, medidas de condutividade iônica utilizando a técnica de espectroscopia de impedância eletroquímica (EIS). / The present thesis reports the preparation and characterization of new types of solid polymeric electrolytes (SPE) based on cellulose derivatives such as hydroxypropylcellulose (HPC) and hydroxyethylcellulose (HEC), both commercial products. Aiming to reach this purpose both derivatives were subjected to modification processes, where HEC were physically modified by plasticization process with glycerol and HPC were submitted to chemical reactions. The latter ones were promoted by the oxidation of HPC hydroxyl groups and ketone groups and then subjected to grafting with diamine poly(propylene oxide) (Jeffamine), resulting in the imine bond network formation. Different concentrations of lithium salt were added to the plasticized and grafted samples, resulting in solid polymeric electrolytes, all in the film form. The characterization of these samples was performed by thermal analysis (DSC, TGA and DMTA), X-ray diffraction (XDR), scanning electron microscopy (SEM), ultraviolet/visible/near-infrared spectroscopy (UV/Vis/NIR) and, as most important, measured of ionic conductivity using the technique of electrochemical impedance spectroscopy (EIS).
|
8 |
Preparação e caracterização de eletrólitos sólidos poliméricos a partir dos derivados de celulose - hidroxietilcelulose e hidroxipropilcelulose / Preparation and characterization of solid polymeric electrolytes based on hydroxypropylcellulose and hydroxyethlcelluloseGilmara de Oliveira Machado 19 April 2004 (has links)
Esta tese apresenta os resultados da obtenção de eletrólitos sólidos poliméricos a partir dos derivados de celulose - hidroxipropilcelulose (HPC) e hidroxietilcelulose (HEC), ambas comerciais. Para atingir os objetivos do projeto, os dois derivados passaram por diferentes processos sendo que a HEC foi modificada fisicamente por meio de plastificação com glicerol e HPC foi alterada quimicamente. A transformação química consistiu nas reações de oxidação de grupos hidroxila da HPC em grupos cetona que, em seguida, foram submetidos as reações de enxertia com diamina de poli(óxido de propileno) [Jeffamina] resultando em redes por meio de ligações imina. A adição do sal perclorato de lítio, em diferentes concentrações, na matriz plastificada ou entrecruzada, resultou na obtenção de eletrólitos sólidos poliméricos, todos na forma de filmes. A caracterização destes eletrólitos foi realizada com técnicas básicas de caracterização de materiais como: análises térmicas (DSC, TGA), análise térmica dinâmico-mecânica (DMTA), análises estruturais (raios-X), medidas espectroscópicas (IR, UVNIS), análise elementar, microscopia eletrônica de varredura (SEM), e, como a mais importante, medidas de condutividade iônica utilizando a técnica de espectroscopia de impedância eletroquímica (EIS). / The present thesis reports the preparation and characterization of new types of solid polymeric electrolytes (SPE) based on cellulose derivatives such as hydroxypropylcellulose (HPC) and hydroxyethylcellulose (HEC), both commercial products. Aiming to reach this purpose both derivatives were subjected to modification processes, where HEC were physically modified by plasticization process with glycerol and HPC were submitted to chemical reactions. The latter ones were promoted by the oxidation of HPC hydroxyl groups and ketone groups and then subjected to grafting with diamine poly(propylene oxide) (Jeffamine), resulting in the imine bond network formation. Different concentrations of lithium salt were added to the plasticized and grafted samples, resulting in solid polymeric electrolytes, all in the film form. The characterization of these samples was performed by thermal analysis (DSC, TGA and DMTA), X-ray diffraction (XDR), scanning electron microscopy (SEM), ultraviolet/visible/near-infrared spectroscopy (UV/Vis/NIR) and, as most important, measured of ionic conductivity using the technique of electrochemical impedance spectroscopy (EIS).
|
9 |
Eletrólitos sólidos poliméricos a base de alginato de sódio / Solid polymer electrolytes based in sodium alginate.Yurika Okamoto Iwaki 22 February 2010 (has links)
Este trabalho teve como objetivo principal a preparação e caracterização de filmes de alginato de sódio plastificado com glicerol. Foram preparadas amostras de filmes variando-se a concentração de ácido acético ou de perclorato de lítio, com a finalidade de otimizá-los como eletrólitos sólidos poliméricos (ESP) em dispositivos eletroquímicos, como sensores e baterias. Após o preparo dos filmes, estes foram caracterizados por análise elementar (AE), microscopia eletrônica de varredura (MEV), difração de raios-X, termogravimetria (TG), análise térmica mecânico dinâmica (DMTA), espectroscopia no UV-VIS, espectroscopia de infravermelho (IR) e espectroscopia de impedância eletroquímica (EIE). Os filmes preparados com alginato de sódio foram plastificados com 0,6 g de glicerol e apresentaram transparência nos comprimentos de onda da luz visível, boa condutividade iônica e maleabilidade. Através dos difratogramas de raios-X pode-se observar que os filmes possuem predominantemente caráter amorfo. O filme de alginato de sódio dopado com 0,3 mL ácido acético apresentou a melhor condutividade (8,7x10-5 S cm-1 a temperatura ambiente e de 1,15x10-3 S cm-1 a 80°C). Para amostras com quantidades maiores de ácido acético os filmes tornaram-se quebradiços e opacos. Para as amostras preparadas com perclorato de lítio a melhor condutividade obtida foi com o filme preparado utilizando 15% em massa de perclorato de lítio: 3,1x10-4 S cm-1 a temperatura ambiente e 1,2x10-3 S cm-1, a 80°C. As análises dos valores de condutividade em função da temperatura das amostras de alginato de sódio revelaram que este segue o modelo Vogel-Tamman-Fulcher (VTF) de condução, onde a movimentação das cadeias poliméricas auxilia na condução iônica. O valor de energia de ativação foi de 36,14 kJ mol-1 para a amostra com 0,3 mL de ácido acético foi de 36 kJ mol-1 para a amostra com 0,4 mL de ácido. Para os filmes preparados com 15% em massa de perclorato de lítio foi de 18,43 kJ mol-1. Essas novas membranas demonstraram ser candidata promissora para aplicação em diversos dispositivos eletroquímicos. / The aim of this study was the preparation and characterization of sodium alginate membranes plasticized with glycerol. The samples were obtained with different concentration of acetic acid or lithium perchlorate in order to use them as solid polymer electrolytes (SPE) in electrochemical devices, such as sensors and batteries. The films were characterized by elemental analysis (EA), scanning electron microscopy (SEM), X-ray, thermogravimetry (TG), dynamic-mechanical thermal analysis (DMTA), UV-visible spectroscopy, infrared spectroscopy (IR) and electrochemical impedance spectroscopy (IES). The samples plasticized with 0.6 g of glycerol showed good transparency, good ionic conductivity and flexibility. X-ray diffractograms evidenced predominantly amorphous state of the samples. The best ionic conductivity results of 8.7 x 10 -5 S cm -1 at room temperature and 1.15 x 10 - 3 S cm -1 at 80 ° C were obtained with sodium alginate samples containing 0.3 mL of acetic acid. Samples with larger amounts of acid became brittle and opaque. The best conductivity values of 3.1 x10 -4 S cm -1 at room temperature and 1, 2 x10 -3 S cm -1 at 80 ° C were obtained for the samples containing 15 wt.% of lithium perchlorate.. The analysis of the conductivity as a function of temperature revealed that they follow the Vogel-Tamman-Fulcher (VTF) conductivity model. The activation energy were 36, 14 kJ mol -1 for the sample with 0.3 mL of acetic acid and 36 kJ mol -1 for the sample with 0.4 mL of acid. The sample with 15 wt.% of lithium perchlorate showed activation energy of 18.43 kJ mol -1. This new ionic conducting membranes are good candidates to be used as electrolytes in electrochemical devices.
|
10 |
Eletrólitos sólidos poliméricos a base de alginato de sódio / Solid polymer electrolytes based in sodium alginate.Iwaki, Yurika Okamoto 22 February 2010 (has links)
Este trabalho teve como objetivo principal a preparação e caracterização de filmes de alginato de sódio plastificado com glicerol. Foram preparadas amostras de filmes variando-se a concentração de ácido acético ou de perclorato de lítio, com a finalidade de otimizá-los como eletrólitos sólidos poliméricos (ESP) em dispositivos eletroquímicos, como sensores e baterias. Após o preparo dos filmes, estes foram caracterizados por análise elementar (AE), microscopia eletrônica de varredura (MEV), difração de raios-X, termogravimetria (TG), análise térmica mecânico dinâmica (DMTA), espectroscopia no UV-VIS, espectroscopia de infravermelho (IR) e espectroscopia de impedância eletroquímica (EIE). Os filmes preparados com alginato de sódio foram plastificados com 0,6 g de glicerol e apresentaram transparência nos comprimentos de onda da luz visível, boa condutividade iônica e maleabilidade. Através dos difratogramas de raios-X pode-se observar que os filmes possuem predominantemente caráter amorfo. O filme de alginato de sódio dopado com 0,3 mL ácido acético apresentou a melhor condutividade (8,7x10-5 S cm-1 a temperatura ambiente e de 1,15x10-3 S cm-1 a 80°C). Para amostras com quantidades maiores de ácido acético os filmes tornaram-se quebradiços e opacos. Para as amostras preparadas com perclorato de lítio a melhor condutividade obtida foi com o filme preparado utilizando 15% em massa de perclorato de lítio: 3,1x10-4 S cm-1 a temperatura ambiente e 1,2x10-3 S cm-1, a 80°C. As análises dos valores de condutividade em função da temperatura das amostras de alginato de sódio revelaram que este segue o modelo Vogel-Tamman-Fulcher (VTF) de condução, onde a movimentação das cadeias poliméricas auxilia na condução iônica. O valor de energia de ativação foi de 36,14 kJ mol-1 para a amostra com 0,3 mL de ácido acético foi de 36 kJ mol-1 para a amostra com 0,4 mL de ácido. Para os filmes preparados com 15% em massa de perclorato de lítio foi de 18,43 kJ mol-1. Essas novas membranas demonstraram ser candidata promissora para aplicação em diversos dispositivos eletroquímicos. / The aim of this study was the preparation and characterization of sodium alginate membranes plasticized with glycerol. The samples were obtained with different concentration of acetic acid or lithium perchlorate in order to use them as solid polymer electrolytes (SPE) in electrochemical devices, such as sensors and batteries. The films were characterized by elemental analysis (EA), scanning electron microscopy (SEM), X-ray, thermogravimetry (TG), dynamic-mechanical thermal analysis (DMTA), UV-visible spectroscopy, infrared spectroscopy (IR) and electrochemical impedance spectroscopy (IES). The samples plasticized with 0.6 g of glycerol showed good transparency, good ionic conductivity and flexibility. X-ray diffractograms evidenced predominantly amorphous state of the samples. The best ionic conductivity results of 8.7 x 10 -5 S cm -1 at room temperature and 1.15 x 10 - 3 S cm -1 at 80 ° C were obtained with sodium alginate samples containing 0.3 mL of acetic acid. Samples with larger amounts of acid became brittle and opaque. The best conductivity values of 3.1 x10 -4 S cm -1 at room temperature and 1, 2 x10 -3 S cm -1 at 80 ° C were obtained for the samples containing 15 wt.% of lithium perchlorate.. The analysis of the conductivity as a function of temperature revealed that they follow the Vogel-Tamman-Fulcher (VTF) conductivity model. The activation energy were 36, 14 kJ mol -1 for the sample with 0.3 mL of acetic acid and 36 kJ mol -1 for the sample with 0.4 mL of acid. The sample with 15 wt.% of lithium perchlorate showed activation energy of 18.43 kJ mol -1. This new ionic conducting membranes are good candidates to be used as electrolytes in electrochemical devices.
|