Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / This investigated the use of equiangular channel press (ECAP) in samples of pure niobium at room temperature up to 14 passes, using the Bc route, with a matrix with intersection angle between the channels of θ = 90º and 120º, with and curvature angle Ψ = 0°. During ECAP (equal channel angular pressing) deformation a bar is pressed through a rigid matrix consisting of two channels of the same cross-section, which intersect at an angle θ. The microstructure of the deformed samples has been analyzed with the aid of optic microscopy, scanning electron microscopy and Vickers Hardness (HV). With the deformation of pure niobium through ECAP, it was possible to refine the structure and increase the hardness due to the increase of the number of passes and the type of matrix. The results indicated that deformation of the niobium with a pass in the matrices of 90 ° and 120 ° was enough to produce the refinement of the microstructure and practically double the hardness values in relation to the material without deformation. The maximum microstructural refinement, steady state, occurred with 8 passes in the 120 ° matrix and 6 passes in the 90 ° matrix, indicating a higher deformation severity of the last matrix. The microstructures analyzed by scanning electron and optical microscopes revealed the microstructural changes with the increase of the number of passes and the type of matrix. / Este trabalho investigou o uso da prensagem em canais equiangulares (ECAP) em amostras de nióbio puro na temperatura ambiente até 14 passes, utilizando a rota Bc, com matrizes contendo ângulo de intersecção entre os canais de θ = 90º e 120°. Durante a deformação ECAP uma barra é pressionada através de uma matriz rígida consistindo de dois canais de mesma seção transversal, os quais se interceptam a um ângulo θ. A microestrutura das amostras deformadas foi analisada com auxílio de microscopia óptica, microscopia eletrônica de varredura e dureza Vickers (HV). Com a deformação do nióbio puro através do ECAP foi possível refinar a estrutura e aumentar a dureza em função do aumento do número de passes e do tipo de matriz. Os resultados indicaram que deformação do nióbio com um passe, nas matrizes de 90º e 120°, foi suficiente para produzir o refinamento da microestrutura e praticamente dobrar os valores de dureza em relação ao material sem deformação. O refinamento microestrutural máximo, estado estacionário, ocorreu com 8 passes na matriz de 120° e 6 passes na matriz de 90°, indicando maior severidade de deformação da última matriz. As microestruturas analisadas por microscopias ótica e eletrônica de varredura revelaram as mudanças microestruturais com o aumento do número de passes e com o tipo de matriz. / São Cristóvão, SE

Made available in DSpace on 2016-03-15T19:36:54Z (GMT). No. of bitstreams: 1 Maria Claudia Lopes Guerra.pdf: 9968717 bytes, checksum: 7d0e4986884ffa382a835b641ed76573 (MD5) Previous issue date: 2015-06-12 / Fundo Mackenzie de Pesquisa / The ECAP (Equal Channel Angular Pressing) is a mechanical process of Severe Plastic Deformation (SPD) where a sample is subjected to a shearing force when passing through the region of intersection of two channels. The main goal of this method is Severe Plastic Deformation achieve a microstructure with ultrafine grains, which have much higher than the equivalent coarse grain materials physical properties, such as an increase in strength and toughness simultaneously. What makes this increasingly interesting technique is that as there is no reduction cross section is possible to obtain plastic strain accumulation and therefore gain in grain order of nanometer scale. The great advantage of ECAP is to achieve a much higher degree of strain hardening than obtained by conventional methods of plastic deformation, and consequently a grain refining much higher as well. The importance of the study of severe plastic deformation process is on improving the mechanical performance of the materials and the possibility of a better understanding of the mechanisms of strain hardening, which may indicate a new path for producing high-strength materials, possibly scaled industrial. In this work are presented the microstructural, mechanical and electrical analysis of the aluminum alloy AA 1050 samples, commonly used for electrical purposes, with ultrafine grains (typical grain size below a micron) resulting from processing by ECAP, based on the method of SPD. / A PCE (Prensagem em Canais Equiangulares) consiste num processo mecânico de Deformação Plástica Intensa (DPI) onde um corpo de prova é sujeito a um esforço de cisalhamento ao passar pela região de intersecção de dois canais. Os principais objetivos desse método de Deformação Plástica Intensa é alcançar uma microestrutura com grãos ultrafinos, os quais possuem propriedades físicas muito superiores aos equivalentes materiais de grãos grosseiros, como um aumento em resistência mecânica e tenacidade simultâneas. O que torna esta técnica cada vez mais interessante é que como não há redução da seção transversal é possível obter acumulo de deformação plástica e com isso obter grãos na ordem de escala nanométrica. A grande vantagem do PCE é alcançar um grau de encruamento muito superior do que obtido por métodos convencionais de deformação plástica, e consequentemente, um refino de grão muito superior também. A importância do estudo do processo de deformação plástica intensa está na melhoria do desempenho mecânico dos materiais e na possibilidade de uma melhor compreensão dos mecanismos de encruamento, fato que pode indicar um novo caminho para a produção de materiais de alta resistência mecânica, possivelmente em escala industrial. Nesse trabalho são apresentadas as análises microestruturais, mecânicas e elétricas de amostras de ligas de alumínio AA 1050, comumente utilizadas para fins elétricos, com estrutura de grãos ultrafinos (tamanho de grão típico abaixo de um micrometro) resultantes do processamento por PCE, baseada no método de DPI.