Submitted by Daniele Amaral (daniee_ni@hotmail.com) on 2016-09-15T12:52:47Z No. of bitstreams: 1 TeseALL.pdf: 6666981 bytes, checksum: 706c82c0c9656012bd6e5a239f13e404 (MD5) / Approved for entry into archive by Marina Freitas (marinapf@ufscar.br) on 2016-09-16T19:50:05Z (GMT) No. of bitstreams: 1 TeseALL.pdf: 6666981 bytes, checksum: 706c82c0c9656012bd6e5a239f13e404 (MD5) / Approved for entry into archive by Marina Freitas (marinapf@ufscar.br) on 2016-09-16T19:50:10Z (GMT) No. of bitstreams: 1 TeseALL.pdf: 6666981 bytes, checksum: 706c82c0c9656012bd6e5a239f13e404 (MD5) / Made available in DSpace on 2016-09-16T19:50:14Z (GMT). No. of bitstreams: 1 TeseALL.pdf: 6666981 bytes, checksum: 706c82c0c9656012bd6e5a239f13e404 (MD5) Previous issue date: 2015-08-12 / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Enamel formation is a two-step complex process by which proteins are first secreted to forming an extracellular matrix, followed by massive protein degradation simultaneously with the completion of mineralization. Excessive exposure to fluoride can disrupt this process and drive to a condition known as dental fluorosis. Recently it has been reported that genetic factors may influence the responses of mineralized tissues to fluoride, a phenomenon observed in A/J and 129P3/J mice strain. The present study aimed to map the protein profile of mouse enamel. Enamel matrix samples were obtained from A/J and 129P3/J mice and analyzed by two-dimensional electrophoresis and liquid chromatography, coupled to mass spectrometry. A total of 120 proteins were identified, from which 113 are well characterized, both experimentally and functionally. Seven proteins were classified as uncharacterized proteins. After functional enrichment, 9 proteins were significantly related to the terms "odontogenesis and tissue biomineralization”. Surprisingly, the COL1A1 and COL1A2 protein were found on secretory stage enamel of both strains. Protein interaction analysis showed interaction between the ENAM and other types of collagen. Another interesting finding was the possibility of uncharacterized sequence Q8BIS2 be an extracellular matrix protein involved on degradation of matrix proteins. These findings suggest that collagen is present on dental enamel and it seems to have a role in amelogensis. Furthermore, the existence of an new enzyme could be the key to elucidation of the mechanisms involved in the enamel biomineralization and the genetic susceptibility to dental fluorosis. / O desenvolvimento do esmalte dentário é um processo complexo no qual as proteínas da matriz do esmalte interagem para conduzir a deposição e o crescimento dos cristais de hidroxiapatita. Fatores como a exposição excessiva ao fluoreto podem atrapalhar esse processo, resultando em uma patologia conhecida como fluorose dentária. Recentemente tem sido relatado que fatores genéticos podem influenciar as respostas dos tecidos mineralizados ao fluoreto, fenômeno observado nas linhagens de camundongos A/J, tida como susceptível e 129P3/J, tida como resistente. Neste sentido, este estudo objetivou mapear as proteínas do esmalte de incisivos de camundongos A/J e 129P3/J, a fim de que se possa melhor entender os mecanismos moleculares envolvidos na patogênese da fluorose dentária. Para isso, amostras de matriz de esmalte foram obtidas de camundongos das linhagens A/J e 129P3/J e analisadas por eletroforese bidimensional e cromatografia liquida, associadas a espectrometria de massas. Foi identificada um total de 120 proteínas, das quais 113 são proteínas bem caracterizadas, tanto experimentalmente quanto funcionalmente, e 7 proteínas que foram classificadas como proteínas não caracterizadas. Após enriquecimento funcional utilizando ferramentas de bioinformática, verificou-se que 9 proteínas estavam significativamente relacionadas aos termos “odontogênese e biomineralização de tecidos”. Dentre essas, as proteínas COL1A1 e COL1A2 chamaram atenção, uma vez que o colágeno não é associado à amelogênese. As proteínas estavam presentes no esmalte em fase de secreção de ambas as linhagens, e, além disso, a análise de interação in silico mostrou a existência de interação física entre a enamelina e outros tipos de colágeno. Outro achado interessante foi a possibilidade da sequência não caracterizada Q8BIS2 ser uma proteína extracelular da matriz envolvida na degradação das proteínas de matriz. Em conclusão, os resultados levam a crer que o colágeno está presente no esmalte e é provável que tenha participação na amelogênese. Além disso, a existência de uma enzima ainda não caracterizada pode ser a chave para elucidação dos mecanismos envolvidos na biomineralização bem como na susceptibilidade genética à fluorose dentária. / 2008/03489-2 e 2009/53852-9

Made available in DSpace on 2014-06-11T19:24:07Z (GMT). No. of bitstreams: 0 Previous issue date: 2005-07-29Bitstream added on 2014-06-13T20:11:59Z : No. of bitstreams: 1 firoozmand_lm_me_sjc.pdf: 463529 bytes, checksum: fe72af5f2a85d677bf7c84e0aa8b1439 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / O objetivo deste trabalho foi verificar a influência da opacidade de cor, tipos de aparelhos fotopolimerizadores (luz halogena X led azul) e aplicação tópica do FFA 1,23% na microdureza da resina composta. A resina composta Esthet-X (Dentisply), nas cores A2 e A2-O foram inseridas em uma matriz de aço-inoxidável em cavidades de 5mm de diâmetro e 2mm de profundidade e fotopolimerizadas por aparelhos; de luz halogena, XL 3000 (3M) ou de LED azul, Optilight LD II (Gnatus), por 40s. Formaram-se 4 grupos com trinta amostras, sendo analisadas a superfície e a base das amostras. Estas foram armazenadas em água destilada, por 24h e posteriormente embutidas em RAAQ. Realizou-se a leitura da microdureza inicial em Microdurômetro Digital Vickers, utilizando 50g de carga por 30s de permanência. A seguir, foi aplicado o FFA 1,23% por 48 min e uma segunda leitura da microdureza foi realizada. O teste estatístico de ANOVA e Tukey (5%) demonstrou que a microdureza da superfície foi sempre maior que a da base. O aparelho de luz halógena apresentou maiores valores médios de microdureza da resina (57,61 HV) que o aparelho de LED (42,53 HV). Foram encontradas diferenças significantes entre os valores médios de microdureza ao se variar a opacidade, sendo que em profundidade, a resina A2-O apresentou os menores valores. A aplicação do FFA 1,23% promoveu menores valores de microdureza na resina. A opacidade da resina composta, o tipo e fonte polimerizadora, bem como a utilização tópica do FFA 1,23% influenciam no grau de microdureza resina. / The aim of this study was to verify the influence of resin opacity, light curing units (halogen light X blue LED) and topic application of 1.23% acidulated phosphate fluoride (APF) on the resin hardness. The composite resin Esthet-X (Dentsply), shade A2 and A2-O was put in stainless steel molds of 5 mm diameter and 2 mm depth, and cured with a halogen light curing unit, XL 3000 (3M) or a blue LED unit, Optilight LD II (Gnatus), for 40s. Four groups with thirty samples were separated and the top and bottom of samples were analyzed. They were stored for 24h and afterwords, built-in acrylic resin. Vickers hardness measurements were made in Vickers Digital Microhardmeter, using 50g load and 30s time. The APF 1.23% was applied for 48 min and a second hardness measurement was done. Statistic test ANOVA and Tukey (5%) demonstrated that top hardness were always higher than bottom. The halogen unit presented higher hardness values (57.61 HV) than LED unit (42.53 HV). Significant differences were found between the hardness values when the opacity was varied, and depth wise the A2-O resin presented the lowest values. The use of 1.23% APF on the resin resulted in the lowest values of hardness. The resin opacity, the light curing unit and the use of 1.23% APF have all influence on the resin hardness.

Made available in DSpace on 2014-10-09T12:35:37Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:03:58Z (GMT). No. of bitstreams: 1 18221.pdf: 475984 bytes, checksum: d5ed50df9b4585d0998e12d282f7f294 (MD5) / Tese (Doutoramento) / IPEN/T / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP

Made available in DSpace on 2015-03-26T13:51:58Z (GMT). No. of bitstreams: 1 texto completo.pdf: 568781 bytes, checksum: e6beb96802418d9a09f3cb5c6661297e (MD5) Previous issue date: 2013-08-30 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The use P solubilizing microorganisms are an alternative for a sustainable use of P against a backdrop of depletion of high-grade ores. Nevertheless, the chemical characteristics of rock phosphates (RP), particularly the level of toxic elements, can affect the efficiency of microbial solubilization. Fluoride (F-) released from fluorapatites has been shown to significantly inhibit P solubilization by Aspergillus niger, stimulating the search for alternatives to overcome F- toxicity. Thus, the aim of this study was to select A. niger mutants efficient at P solubilization in the presence of F-. Three selected mutants were also characterized as to their P solubilization mechanisms and the solubilization potential of different P sources. Twenty-nine mutants were obtained that presented changes in their phosphate solubilization activity in comparison to the wild type (WT). The mutant FS1-331 showed higher solubilization of Araxá RP, while FS1-555 promoted higher soluble P when grown in media with calcium phosphate supplemented with F- and in those with pure P sources. These mutants also showed higher tolerance to F- than the WT and displayed changes in the production of organic acids. The higher production of oxalic acid by FS1-331 and FS1-555 correlated with their improved capacity of Araxá RP solubilization. A mutant with decreased P solubilization capacity showed lower production of organic acids, corroborating the importance of these compounds for RP solubilization. FS1-331 was more efficient at solubilizing Araxá, Catalão, and Patos de Minas RPs than the WT and FS1-555. The variation in P solubilization capacity of the mutants obtained in this work may help clarify the RP solubilization mechanisms by A. niger. Moreover, the mutants with better performance selected in this work show potential for use in microbial RP solubilization systems with P sources rich in fluoride. / O uso dos micro-organismos solubilizadores de fosfato (P) é uma alternativa para o uso sustentável do P tendo em vista a diminuição das reservas fosfáticas de alta qualidade. As características químicas dos fosfatos de rocha (FR), em especial o nível de elementos tóxicos, podem influenciar a eficiência de solubilização microbiana. O fluoreto (F-) liberado de fluorapatitas inibi significativamente o processo de solubilização por Aspergillus niger FS1. Assim, o objetivo deste estudo foi selecionar mutantes de A. niger eficientes na solubilização de fosfato na presença de F-. Três mutantes selecionados foram também caracterizados quanto aos mecanismos de solubilização de fosfato e ao potencial de solubilização de diferentes fontes de P. Vinte e nove mutantes com alterações na solubilização de fosfato foram obtidos. O mutante FS1-331 demonstrou maior potencial de solubilização de fosfato de Araxá, enquanto que o mutante FS1-555 aumentou o P solubilizado em meio de cultura com fosfato de cálcio suplementado com F- e naqueles com fontes sintéticas de P. Os mutantes avaliados mostraram maior tolerância ao F- do que o tipo selavagem e tiveram a produção de ácidos orgânicos alterada. A maior produção de ácido oxálico pelos mutantes FS1-331 e FS1-555 relacionou-se com o melhor desempenho dessas estiprpes na solubilização de fosfato de Araxá. Um mutante com solubilização de P diminuída (FS1-375) apresentou menor produção de ácidos orgânicos quando comparado ao tipo selvagem, corroborando a importância desses compostos para o processo de solubilização de FRs. O mutante FS1-331 foi o mais eficiente na solubilização dos FRs de Araxá, Catalão e Patos de Minas. A variação na solubilização de P das estirpes fúngicas estudadas pode contribuir para a melhor compreensão do processo de solubilização de fosfatos por A. niger. Além disso, os mutantes mais eficientes obtidos apresentam alto potencial de aplicação em sistemas microbianos de solubilização de fosfatos com fontes de P ricas em fluoreto.

Orientador: Doris Hissako Sumida / Banca: Cléa Adas Saliba Garbin / Banca: Marília Afonso Rabelo Buzalaf / Resumo: Nos últimos anos, tem havido uma redução acentuada nos índices de cárie dentária em diversas regiões do mundo, fato que tem sido atribuído à exposição às substâncias fluoretadas, principalmente na forma de água de abastecimento público e dentifrício. Simultaneamente, nota-se a ocorrência do aumento da prevalência de fluorose dentária. Estudo realizado em 25 pacientes (15 a 30 anos de idade) com fluorose endêmica mostrou que 40% destes tinham a tolerância à glicose prejudicada, porém esta anomalia foi revertida com a remoção do excesso do flúor na água consumida. O NaF ocasiona inibição da glicólise, diminuição da secreção de insulina e hiperglicemia. Muitas destas respostas sugerem que o NaF pode ocasionar resistência à insulina. Se isto for confirmado, é recomendável diminuir a concentração de fluoreto nos dentifrícios utilizados principalmente por crianças diabéticas, pois a ingestão de pasta dental contendo flúor pode levar à piora na situação de saúde destas crianças. Sabendo-se que o fluoreto pode alterar o metabolismo de carboidratos, tornou-se fundamental caracterizar o efeito do NaF sobre: 1) a sensibilidade à insulina; 2) o grau de fosforilação em tirosina do substrato do receptor de insulina - pp185 (IRS-1/IRS-2); 3) a fluoremia, glicemia e insulinemia. Para tanto, foram utilizados ratos Wistar machos (1 mês de idade) castrados. Após 30 dias da castração, os animais foram divididos aleatoriamente em dois grupos: 1) grupo controle (CN), o qual foi submetido ao tratamento sem NaF, mas com uma solução de NaCl (9,54 mg/kg p.c.) que contém a mesma quantidade de sódio em relação à do grupo fluoreto de sódio; 2) grupo NaF (FN) que será submetido ao tratamento com NaF (4,0 mg de flúor/kg p.c.) na água de beber e na ração durante 42... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Over the last years, there has been a significant reduction in the incidence of dental caries in several regions of the world. This has been attributed to ingestion of fluoridated products, especially in the form of public water supplies and toothpaste. Simultaneously, there has been an increase in the prevalence of dental fluorosis. A study conducted in 25 patients (15 to 30 years of age) with endemic fluorosis showed that 40% of these had to impaired glucose tolerance, but this anomaly was reversed by removing the excess of fluoride from drinking water. NaF causes glycolysis inhibition, decrease on insulin secretion and hyperglycemia. These responses suggest that NaF can cause insulin resistance. If this is confirmed, the use of dentifrices with lower fluoride content is recommended, especially for diabetic children, for whom excessive F consumption may lead to worsening the condition of these children's health. Knowing that F can interfere with carbohydrate metabolism, we felt it was important and fundamental to undertake a study to examine the chronic effect of NaF on: 1) insulin sensitivity; 2) pp185 (IRS-1/IRS-2) tyrosine phosphorylation in gastrocnemius muscle and liver of rats; 3) fluoremia, glycemia and insulinemia. For this study, castrated Wistar male rats (1 month of age) were used. Thirty days after castration, the animals were randomly divided in two groups: 1) control group (CN) which was subjected to treatment without NaF, but with a solution of NaCl (9.54 mg / kg bw) which contains the same amount of sodium in relation to the group NaF; 2) group NaF (FN) that was submitted to treatment with NaF administered in the drinking water and F contained in food pellets (F total inferred: 4.0 mg F / Kg bw / day in the form of NaF) during 42 days. After 6 weeks, the following experiments were conducted: 1) assessment... (Complete abstract, click electronic address below) / Mestre

Resumo: O objetivo deste estudo foi avaliar a rugosidade superficial e o processo de corrosão do titânio comercialmente puro (Ti cp), após simular períodos de contato com fluoretos de 5 (G5), 10 (G10), 15 (G15) e 20 (G20) anos, bem como avaliar a aderência de S. mutans nestas superfícies. Para cada respectivo período, discos de Ti cp foram previamente polidos e então imersos em solução fluoretada a 0,15% (1500 ppm, pH 5,3) ou em água destilada como controle (G0). A rugosidade média (Ra), rugosidade média quadrática (Rms) e a área superficial projetada (Área) foram avaliadas por microscopia de força atômica (MFA) antes e após a imersão. As mesmas superfícies foram examinadas por microscopia eletrônica de varredura (MEV e EDX) e a aderência dos S. mutans avaliada pela contagem das unidades formadoras de colônia (UFC/ml). Todos os grupos teste aumentaram significativamente a Ra, Rms e Área após a imersão em solução fluoretada. Entretanto, na comparação entre os grupos (Kruskall- Wallis), somente a Área foi estatisticamente diferente. Os grupos G10 (p=0,008), G15 (p=0,014) e G20 (p<0,001) apresentaram maior Área quando comparados com G0. A análise por MEV mostrou a presença de corrosão por pits e uma superfície irregular em todos os grupos teste. O G0 não sofreu alteração em nenhum parâmetro avaliado. O EDX mostrou a presença de compostos de Ti-FNa incorporados à superfície do G20. Na contagem das UFC/ml, o grupo G20 apresentou maior aderência que G0 e G5. Conclui-se que os íons fluoretos em baixa concentração foram capazes de promover corrosão do Ti cp em todos os grupos teste e alteraram a Área do Ti cp ao longo do tempo. Adicionalmente, a aderência bacteriana mostrou-se maior no período mais longo de exposição. / Abstract: The aim of this study was to evaluate the superficial roughness and the corrosion process of commercially pure titanium Ti cp, after simulating different periods of fluoride contact: 5 (G5), 10 (G10), 15 (G15) e 20 (G20) years, as well as the adherence of S mutans in those surfaces. For each respective period, Ti cp discs were previously polished and than submersed in fluoride solution 0.15% (1500 ppm, pH 5.3) or distilled water as control group (G0). The average roughness (Ra), root mean square roughness (Rms) and scanned area (Area) were assessed for atomic force microscopy (AFM) before and after the immersion. The same surfaces were examined for scanned electron microscopy (SEM, EDX) and S mutans adherence calculated by the counting of colony forming units (CFU/ml). All test groups increased significantly the Ra, Rms and Area after the immersion in fluoride solution. However, the comparison among the groups (Kruskall-Wallis), only the area showed significant difference. The groups G10 (p=0.008), G15 (p=0.014) and G20 (p<0.001) showed higher Area compared with G0. The SEM analysis showed the presence of corrosion by pits and irregular surface in all test groups. The G0 did not change for any parameter evaluated. The EDX showed the presence of Ti-F-Na in the surface of samples from G20. In the counting of CFU/ml, the G20 resulted in higher bacteria adherence compared with G0 and G5 (ANOVA, p=0.015). In conclusion the fluoride ions in low concentration promoted corrosion in Ti cp from all test groups and altered the Area of Ti cp over the time. Moreover, the longer is the period of immersion in fluoride solution, higher is the bacteria adherence. / Orientador: Ricardo Samih Georges Abi Rached / Coorientador: Luis Geraldo Vaz / Banca: Osvaldo Luiz Bezzon / Banca: Gelson Luis Adabo / Mestre

Orientador: Maria Amélia Máximo de Araújo / Banca: Maria Amélia Máximo de Araújo / Banca: Maria Antonia Pereira / Banca: João Carlos da Rocha / Resumo: O objetivo deste trabalho foi verificar a influência da opacidade de cor, tipos de aparelhos fotopolimerizadores (luz halogena X led azul) e aplicação tópica do FFA 1,23% na microdureza da resina composta. A resina composta Esthet-X (Dentisply), nas cores A2 e A2-O foram inseridas em uma matriz de aço-inoxidável em cavidades de 5mm de diâmetro e 2mm de profundidade e fotopolimerizadas por aparelhos; de luz halogena, XL 3000 (3M) ou de LED azul, Optilight LD II (Gnatus), por 40s. Formaram-se 4 grupos com trinta amostras, sendo analisadas a superfície e a base das amostras. Estas foram armazenadas em água destilada, por 24h e posteriormente embutidas em RAAQ. Realizou-se a leitura da microdureza inicial em Microdurômetro Digital Vickers, utilizando 50g de carga por 30s de permanência. A seguir, foi aplicado o FFA 1,23% por 48 min e uma segunda leitura da microdureza foi realizada. O teste estatístico de ANOVA e Tukey (5%) demonstrou que a microdureza da superfície foi sempre maior que a da base. O aparelho de luz halógena apresentou maiores valores médios de microdureza da resina (57,61 HV) que o aparelho de LED (42,53 HV). Foram encontradas diferenças significantes entre os valores médios de microdureza ao se variar a opacidade, sendo que em profundidade, a resina A2-O apresentou os menores valores. A aplicação do FFA 1,23% promoveu menores valores de microdureza na resina. A opacidade da resina composta, o tipo e fonte polimerizadora, bem como a utilização tópica do FFA 1,23% influenciam no grau de microdureza resina. / Abstract: The aim of this study was to verify the influence of resin opacity, light curing units (halogen light X blue LED) and topic application of 1.23% acidulated phosphate fluoride (APF) on the resin hardness. The composite resin Esthet-X (Dentsply), shade A2 and A2-O was put in stainless steel molds of 5 mm diameter and 2 mm depth, and cured with a halogen light curing unit, XL 3000 (3M) or a blue LED unit, Optilight LD II (Gnatus), for 40s. Four groups with thirty samples were separated and the top and bottom of samples were analyzed. They were stored for 24h and afterwords, built-in acrylic resin. Vickers hardness measurements were made in Vickers Digital Microhardmeter, using 50g load and 30s time. The APF 1.23% was applied for 48 min and a second hardness measurement was done. Statistic test ANOVA and Tukey (5%) demonstrated that top hardness were always higher than bottom. The halogen unit presented higher hardness values (57.61 HV) than LED unit (42.53 HV). Significant differences were found between the hardness values when the opacity was varied, and depth wise the A2-O resin presented the lowest values. The use of 1.23% APF on the resin resulted in the lowest values of hardness. The resin opacity, the light curing unit and the use of 1.23% APF have all influence on the resin hardness. / Mestre

Neste estudo avaliou-se o efeito de diferentes protetores de superfície na liberação de flúor (LF) e na resistência à tração diametral (TD) de dois cimentos de ionômero de vidro (CIV) convencionais restauradores, Chemfil e Chemflex (Dentsply). Manipulou-se os cimentos segundo as recomendações do fabricante, os espécimes confeccionados foram divididos em cinco grupos: grupo1 sem protetor (controle); grupo2 vaselina sólida; grupo3 verniz (Cavitine, S.S.White); grupo4 verniz fluoretado (Duraflur, Denstply); grupo5 adesivo (Magic Bond, Vigodent). Confeccionou-se para o teste de LF 40 espécimes para cada CIV, com dimensões de 4 mm de diâmetro por 6 mm de comprimento, divididos aleatoriamente entre os grupos e estocados individualmente em potes plásticos contendo 5 ml de água deionizada. Registrou-se o nível de fluoreto no período de 04 horas, 24 horas, 03 dias, 07 dias e 14 dias após a confecção, em um analisador Expandable Íon Analyser EA 960, sendo os resultados calculados em &#956;gF/ cm2. Confeccionou-se para o ensaio de TD 120 espécimes para cada CIV, com dimensões de 4 mm de diâmetro por 6 mm de comprimento, divididos aleatoriamente entre os grupos. Realizou-se ensaios mecânicos, com 1 dia e 14 dias após a confecção e estocagem individual dos espécimes em potes plásticos contendo 5 ml de água deionizada, em uma máquina universal de ensaios EMIC DL 500 MF, realizou-se um terceiro teste após 14 dias de ciclos de des-remineralização. Tratou-se estatisticamente os dados obtidos por ANOVA e por Student Newman-Keuls (p<0,05). No teste de LF os resultados demonstraram que o Chemfil liberou uma quantidade significantemente maior de flúor do que o Chemflex. Durante o período do teste a vaselina e o verniz tiveram um comportamento semelhante, mostrando uma menor LF do que o grupo controle nas primeiras 4 horas, com uma maior liberação na análise seguinte (24 horas). Os espécimes protegidos com vaselina e verniz, tiveram uma liberação de flúor semelhante ao grupo controle nos períodos de 3, 7 e 14 dias. O verniz fluoretado mostrou uma forte influência nas primeiras 24 horas. A partir da terceira análise observou-se uma maior liberação de flúor para o Chemfil em comparação com o Chemflex. Em relação ao emprego de um protetor superficial resinoso, encontrou-se tanto para Chemfil quanto para o Chemflex uma redução drástica na liberação de fluoreto, em todos os tempos analisados. No ensaio de TD o Chemfil não mostrou diferença estatisticamente significante quando os resultados de TD do seu grupo controle foram avaliados nos diferentes ensaios (24 horas, 14 dias e des-re), o mesmo acontecendo com o Chemflex. Ao se avaliar a influência dos diferentes protetores de superfície nos CIVs utilizados no presente trabalho observou-se que, para o Chemfil os protetores de superfície tiveram pouca influência no comportamento do material, se comportando na maioria das vezes de forma similar ao grupo controle. Em contrapartida, para o material Chemflex a utilização de um protetor de superfície, como o verniz fluoretado e o adesivo, permitiu maiores valores de resistência à TD. Conclui-se que quando se objetiva o uso do CIV por um curto período o Chemfil sem protetor parece ser o mais indicado, porém se o uso do CIV for por um longo período o Chemflex com a proteção do verniz fluoretado é o mais indicado. / This study evaluated the effect of different protective coatings on the fluoride release (FR) and on the diametral tensile strength (DTS) of two conventional restorative glass ionomer cements (GIC), Chemfil e Chemflex (Dentsply). The cements were manipulated according to the manufacturer's recommendation. The especimens were divided into five groups: group 1 uncoated (control group); group 2 petroleum jelly; group 3 dental varnish (Cavitine, S.S.White); group 4 - fluoride varnish (Duraflur, Denstply); group 5 dentin adhesive (Magic Bond, Vigodent). To the FR test were made 40 especimens to each CIV, with dimensions of 4mm in diameter by 6 mm in length divided randomly into the groups and kept individually in plastic containers with 5 mL of deionized water. The fluoride level was registered within 04 hours, 24 hours, 3 days, 7 days and 14 days after the confection in an Expandable Íon Analyser EA 960, and the results were calculated in &#956;gF/ cm2. To the DTS test 120 especimens were made to each GIC, with dimensions of 4mm in diameter by 6mm in length divided randomly into the groups. Mechanical tests were made within 1 day and 14 days after the confection and saving of specimens individually in plastic containers with 5 mL of deionized water, in an universal tests machine EMIC DL 500 MF, and a third test was made after 14 days of des-remineralization cycles. The data was statistically treated by ANOVA and by Student Newman-Keuls (p<0,05). In the FR test the results showed that the Chemfil released a significant bigger amount of fluoride then the Chemflex. During the tests period, the petroleum jelly and the dental varnish had a similar behavior, presenting lower fluoride release then the control group in the first 4 hours, with a greater release in the second analysis (within 24 hours). The especimens protected by petroleum jelly and dental varnish had a fluoride release similar to the control group on the periods of 3, 7 and 14 days. The fluoride varnish showed a great influence in the first 24 hours. From the third analysis on, each ionomer materials characteristics became prominent, and was noticed a bigger fluoride release on the Chemfil in comparison to the Chemflex. In relation to the coated with dentin adhesive, there was a drastic decrease of fluoride release for Chemfil and Chemflex, in all of the analysis periods. In the DTS test Chemfil didnt show statistically significant difference when the diametral tensile strength of the control group was evaluated in the various periods of time (24 hours, 14 days and de-remineralization), which also happened to Chemflex. When evaluating the influence of different surface protectors on the GIC used at this study, it was noticed that for the Chemfil the surface coating had little influence on the materials behavior, having on most of the time, the same behavior as the control group. However, to the Chemflex material, the use of a surface coating such as the fluoride varnish or the dentin adhesive allowed bigger values of diametral tensile strength. The conclusion is that when the use of GIC is wanted for a short period of time the Chemfil uncoated seems the most indicated. However, if the period of use is longer, the Chemflex with the fluoride varnish protection is the most indicated.

O presente estudo teve como objetivos avaliar se a aplicação de verniz fluoretado com periodicidade semestral em crianças pré-escolares reduz o número de crianças com lesões de cárie em dentina na dentição decídua, diminui a incidência de lesões de cárie em esmalte e dentina, está inversamente associado à ocorrência de dor e abscesso dentário e produz quaisquer efeitos adversos. A população de estudo consistiu de 200 crianças na faixa etária de 12 a 48 meses, recrutadas em uma unidade de saúde pública da cidade do Rio de Janeiro, as quais foram alocadas aleatoriamente nos grupos teste (verniz fluoretado Duraphat) e controle (verniz placebo). Para o registro da incidência de cárie, as crianças foram examinadas na linha de base e a cada seis meses, durante um ano, por dois odontopediatras previamente treinados e calibrados (Kappa=0,85). A ocorrência de dor, abscesso e efeitos adversos foi verificada a partir de entrevistas com os responsáveis. Os participantes, os seus responsáveis, os operadores e os examinadores desconheciam a qual grupo cada criança pertencia. No final do período de acompanhamento, 71 crianças do grupo teste e 77 do grupo controle foram avaliadas. Constatou-se que, nos grupos teste e controle, o número de crianças com novas lesões de cárie em dentina foi igual a 13 e 20 (teste Qui-quadrado, p=0,34) e que a média do incremento de cárie considerando apenas lesões em dentina (c3eos) foi de 1,1(dp=3,4) e de 1,4(dp=2,8), respectivamente (teste de Mann-Whitney, p=0,29). Uma criança apresentou dor de dente e abscesso dentário e outras duas crianças apresentaram apenas dor de dente. Todas pertenciam ao grupo teste. Com relação aos efeitos adversos, encontrou-se que uma criança pertencente ao grupo controle relatou ardência na cavidade bucal após a aplicação do placebo e que o responsável por um participante do grupo teste sentiu-se incomodado com a coloração amarelada dos dentes da criança após a aplicação do verniz fluoretado. Concluiu-se que a aplicação de verniz fluoretado com periodicidade semestral em crianças pré-escolares é segura e parece contribuir para o controle da progressão de cárie. Contudo, é necessário um período de acompanhamento mais longo para se obter evidência conclusiva a respeito da efetividade dessa intervenção. Não houve associação entre a ocorrência de dor e abscesso dentário e o uso profissional do verniz fluoretado. / The aims of this study were to evaluate whether the application of fluoride varnish in preschool children at six-month intervals reduces the number of children with dentin caries and decreases the incidence of enamel and dentinal caries lesions in the primary dentition. We also sought to assess whether this intervention is inversely associated with the occurrence of tooth abscess and dental pain and to describe any possible side effects. The study population comprised 200 children, 12 to 48 months of age. They were enlisted in a public health center in the city of Rio de Janeiro and were randomly assigned to the test group (Duraphat fluoride varnish) or the control group (placebo varnish). To record caries incidences, the children were examined at the baseline and every six months, during the period of one year, by two trained and calibrated pediatric dentists (Kappa=0.85). The presence of pain, abscess and side effects were recorded through interviews with the childrens caregivers. The children, their caregivers, the operators and the examiners did not know which group each child belonged. At the end of the follow-up period, 71 children of test group and 77 of the control group were analyzed. We found that 13 children in the test group and 20 children in the control group presented new dentinal caries lesions (Chi-square test, p= 0.34) and that the mean caries increment at the dentin level was 1.1(dp= 3.4) and 1.4 (dp=2.8) in the test and the control groups respectively (Mann-Whitney test, p=0,29). One child reported dental pain and tooth abscess, and two other children reported only dental pain. All three children belonged to the test group. One child reported a burning sensation in the mouth following application of the placebo varnish and one parent of a child in the test group felt upset about the yellowish discoloration of the childs teeth after the application of the fluoride varnish. We concluded that the six-monthly application of fluoride varnish in preschool children is safe and appears to contribute to the control of caries progression. However, a longer follow-up period is necessary before conclusive evidence can be drawn regarding the effectiveness of this intervention. We did not find an association between the occurrence of tooth abscess and dental pain, and the professional use of fluoride varnish.

The primary prevention of dental caries includes the regular reduction of dental plaque, the adequate nutrition with reduced frequency of sugar intake and the application of topical and/or alimentary fluorides. The caries-protective effect of fluorides is based on the stabilization of demineralization/remineralization processes in the surface of teeth. The alimentary fluoride intake involves its nutritional sources, fluoride supplements when administered and unintentionally swallowed fluoride toothpastes. The fluoride intake, besides its verifiable and significant contribution to the control of cariogenic conditions in the oral cavity, brings some risk in the period of permanent teeth development. That is why the fluoride intake in childhood ought to be well set up and controlled for achieving the maximum benefit in caries reduction and for minimizing the risk for the enamel development. The assessment on fluoride content in its most significant nutritional sources and the model estimates of fluoride intake in preschool children have been conducted with the aim at contributing the solution of the benefit/risk strategy of fluoride caries prevention. The fluoride content was estimated in bottled waters for preschool children, in instant milk formulas, in herbal teas for children and in instant products of...