The diploma thesis deals with selected fracture tests and evaluation of fracture parameters of cement-based composite. One part of the thesis deals with cement-based composite with glass spherical aggregate of a single fraction of 2 mm. After production, the beams with dimensions of 20×40×200mm exposed to temperatures in the range from 100 to 1000 °C for one hour. Using the non-destructive ultrasonic pulse method, the degree of damage caused by termal load was determined. Selected specimen with central edge notch were then tested in three-point bending and fragments after these tests were tested in compression. In the second part, attention was paid to the evaluation of fracture tests conducted on specimen from drill-cores taken from selected objects located at the former Transgas Gas Control Center in Prague. The specimen were provided with a chevron notch before being tested in three-point bending. The measured data was modified by the GTDiPS program and in the case of the glass composite the StiCrack program was used to evaluate fracture parameters.

The diploma thesis is focused on the evaluation of mechanical fracture parameters of concrete after exposure to high temperatures. In the introductory theoretical part general principles of fracture mechanics with the concentration on a linear elastic fracture mechanics and non-linear fracture models for the concrete are summarized. The meaning of the three-point bending fracture test used for determination of fracture parameters is also explained. Further the influence of high temperatures on the partial components of concrete and general modeling of temperature loading is described. The practical part is concerned with the evaluation of fire experiments on the concrete panels including numerical simulations using GiD and ATENA software. The evaluation of data obtained from the three-point bending test carried out on specimens with initial stress concentrator taken from concrete panels is a main part of the diploma thesis. The values of modulus of elasticity, effective fracture toughness, work of fracture and fracture energy are determined from the measured F–d and F–CMOD diagrams after their proper corrections in the GTDiPS application. The evaluation of the selected mechanical fracture parameters was performed by StiCrack software using effective crack model and work of fracture method and DKFM_BUT software using the double-K fracture model. Finally, the attention is paid to the analysis of the obtained data.