The aim of this work was to synthesise water-soluble QDs using different precursors and stabilizers and to determine the toxicity of the synthesized QDs by in vivo imaging. Experiments were performed on water-soluble QDs (MPA-CdTe, MPA-CdTe/ZnS, MSA-CdTe, MSA-CdTe/ZnS, GSH-CdTe, GSH-CdTe/ZnS, TGA-CdTe, TGA-CdTe/ZnS, GSH-ZnSe and GSH-ZnSe/ZnS ) and toxicity was measured. Synthesized QDs were characterized by high intensity (fluorescence spectroscopy), FWHM and zeta potential (ZS Zetasizer) were selected due to their suitability for this task. The toxicity of QDs was determined by the MTT assay on the cell line HEK 293. The experiments show that a core/shell structure is less toxic than a core structure. The results indicate that the toxicity of our synthesized QDs is the lowest for MPA-CdTe (core structure) and MPA-CdTe/ZnS (core/shell structure).

The aim of this work was to synthesise water-soluble QDs using different precursors and stabilizers and to determine the toxicity of the synthesized QDs by in vivo imaging. Experiments were performed on water-soluble QDs (MPA-CdTe, MPA-CdTe/ZnS, MSA-CdTe, MSA-CdTe/ZnS, GSH-CdTe, GSH-CdTe/ZnS, TGA-CdTe, TGA-CdTe/ZnS, GSH-ZnSe and GSH-ZnSe/ZnS ) and toxicity was measured. Synthesized QDs were characterized by high intensity (fluorescence spectroscopy), FWHM and zeta potential (ZS Zetasizer) were selected due to their suitability for this task. The toxicity of QDs was determined by the MTT assay on the cell line HEK 293. The experiments show that a core/shell structure is less toxic than a core structure. The results indicate that the toxicity of our synthesized QDs is the lowest for MPA-CdTe (core structure) and MPA-CdTe/ZnS (core/shell structure).