Finite element mesoscopic analysis of damage in microalloyed continuous casting steels at high temperature/Analyse mésoscopique par éléments finis de lendommagement à haute température des aciers microalliés de coulée continueCastagne, Sylvie 12 February 2007 (has links)
This thesis addresses the problem of damage at elevated temperature with a view to analysing transverse cracking during the continuous casting of microalloyed steels. Based on the results of a previous project undertaken at the University of Liège to simulate the continuous casting process at the macroscopic level, the present research aims at studying the damage growth using a finite element mesoscopic approach that models the grains structure of the material. The developments are done at the mesoscopic scale using information from both the microscopic and macroscopic levels.
In order to determine the constitutive laws governing the damage process at the mesoscopic scale, the physical mechanisms leading to the apparition of cracks during steel continuous casting are first investigated. It is acknowledged that in the studied temperature range (800 to 1200 °C), the austenitic grain boundary is a favourable place for cracks to initiate and propagate. The mechanisms of voids nucleation, growth and coalescence are established, the cavities evolving under diffusion and creep deformations.
Having identified the damage mechanisms occurring under continuous casting conditions, a numerical approach for the modelling of these phenomena at the grain scale is proposed. The mesoscopic model, which is implemented in the Lagrangian finite element code LAGAMINE developed at the University of Liège, is built on the basis of a 2D mesoscopic cell representative of the material. The finite element discretization comprises solid elements inside the grains and interface elements on the grains boundaries. An elastic-viscous-plastic law of Norton-Hoff type, which represents the thermo-mechanical behaviour of the material, is associated to the solid elements for the modelling of the grains; and a damage law accounting for cavitation and sliding is linked to the interface elements for the modelling of the damage growth at the grains boundaries. The transfer between the macroscopic and mesoscopic scales is realised by imposing the stress, strain and temperature fields, collected during the parent macroscopic simulation, as boundary conditions on the mesosopic cell.
Macroscopic experiments, analytical computations and finite element simulations, as well as literature review and microscopic analyses, are used to define the parameters of the material laws. The experimental results and the identification methodology leading to the definition of the set of parameters specific to the studied steel are described.
Finally, the influence of oscillation marks and process defects on cracks formation during the industrial process of continuous casting is analysed. The results are compared with in-situ observations and cracking risk indicators computed by the macroscopic model.
|
2 |
Approche unifiée de quelques problèmes non linéaires de mécanique des milieux continus par la méthode des éléments finis (grandes déformations des métaux et des sols, contact unilatéral de solides, conduction thermique et écoulements en milieu poreux)Charlier, Robert 20 March 1987 (has links)
La thèse a pour objet la simulation numérique de divers problèmes fortement non linéaires de la mécanique des milieux continus, en particulier en formage des métaux et en géomécanique. Le formalisme théorique puis numérique de la mécanique non linéaire des milieux continus, des couplages hydromécaniques et thermomécaniques et des modèles de comportement élastoplastique et élastoviscoplastique est développé étape par étape, permettant la construction du code aux éléments finis LAGAMINE. Celui-ci est ensuite utilisé pour simuler quelques problèmes spécifiques.
|
Page generated in 0.0308 seconds