<p>Carbon nanomaterials have a wide range of promising and exciting applications. One of the most heavily investigated carbon nanomaterial in recent history has been the carbon nanotube. The intense interest in carbon nanotubes can be attributed to the many exceptional characteristics which give them great potential to revolutionize modern mechanical, optical and electronic technologies. However, controlling these characteristics in a scalable fashion has been extremely difficult. Although some progress has been made in controlling the quality, diameter distribution and other characteristics of carbon nanotube samples, several issues still remain. The two major challenges which have stood in the way of their mainstream application are controlling their orientation and their electronic characteristics. Developing and understanding a Chemical Vapor Deposition based carbon nanotube synthesis method has been the major focus of the research presented here. Although several methods were investigated, including the so-called "fast-heating, slow-cooling" and large feeding gas flowrate methods, it was ultimately found that high-quality, perfectly aligned carbon nanotubes from a variety of metal catalysts could be grown on quartz substrates. Furthermore, it was found that using MeOH could selectively etch small-diameter metallic carbon nanotubes, which ultimately led to the productions of perfectly aligned single-walled carbon nanotube samples consisting almost entirely of semiconducting carbon nanotubes. Thiophene was utilized to investigate and support the hypothesized role of MeOH in producing these selectively gown semiconducting carbon nanotube samples. Additionally, this sulfur-containing compound was used for the first time to demonstrate a two-fold density enhancement in surface grown carbon nanotube samples. This method for selectively producing perfectly aligned semiconducting carbon nanotubes represents a major step towards the integration of carbon nanotubes into mainstream applications.</p><p>Although extremely useful in a variety of technologies, carbon nanotubes have proven impractical for use in H₂ storage applications. As such, microporous carbons have been heavily investigated for such ends. Microporous carbons have distinguished themselves as excellent candidates for H₂ storage media. They are lightweight and have a net-capacity of almost 100%, meaning that nearly all of the H₂ stored in these materials is easily recoverable for use in devices. However, developing a microporous carbon with the appropriately small pore diameters (~1nm), large pore volumes (>1cm<super>3</super>) and large surface areas (&#8805;3000m<super>2</super>/g) has proven exceedingly difficult. Furthermore, maintaining the ideal graphitic pore structure has also been an unresolved issue in many production means. Several microporous carbon synthesis methods were investigated herein, including inorganic and organically templated production schemes. Ultimately, thermally treating poly (etherether ketone) in CO₂ and steam environments was found to produce large surface area porous carbons (&#8805;3000m<super>2</super>/g) with the appropriately small pore diameters (<3nm) and large pore volumes (>1cm<super>3</super>) necessary for optimized storage of H2. Furthermore, the surface chemistry of these pores was found to be graphitic. As a result of these ideal conditions, these porous carbons were found to store ~5.8wt.% H₂ at 77K and 40bar. This represents one of the most promising materials presently under investigation by the United States Department of Energy H₂ Sorption Center of Excellence. </p><p>The success of both of these materials demonstrates the diversity and promise of carbon nanomaterials. It is hoped that these materials will be further developed and will continue to revolutionize a variety of vital technologies.</p> / Dissertation

Porous carbons are promising anode materials for next generation lithium batteries due to their large lithium storage capacities. However, their highsloping capacity during lithiation and delithiation as well as capacity fading due to intense formation of solid electrolyte interphase (SEI) limit their gravimetric and volumetric energy densities. Herein we compare a microporous carbide derived carbon material (MPC) as promising future anode for all solid state batteries with a commercial high performance hard carbon anode. The MPC obtains high and reversible lithiation capacities of 1000 mAh g 1 carbon in half cells exhibiting an extended plateau region near 0 V vs. Li/Liþ preferable for full cell application. The well defined microporosity of the MPC with a specific surface area of >1500 m2 g 1 combines well with the argyrodite type electrolyte (Li6PS5Cl) suppressing extensive SEI formation to deliver high coulombic efficiencies. Preliminary full cell measurements vs. nickel rich NMC cathodes (LiNi0.9Co0.05Mn0.05O2) provide a considerably improved average potential of 3.76 V leading to a projected energy density as high as 449 Wh kg 1 and reversible cycling for more than 60 cycles. 7Li Nuclear Magnetic Resonance spectroscopy was combined with ex situ Small Angle X ray Scattering to elucidate the storage mechanism of lithium inside the carbon matrix. The formation of extended quasi metallic lithium clusters after electrochemical lithiation was revealed.