Thesis (B.S.)--University of Missouri, School of Mines and Metallurgy, 1910. / The entire thesis text is included in file. Typescript. Illustrated by authors. Title from title screen of thesis/dissertation PDF file (viewed January 15, 2009) Oliver W. Holmes determined to be Oliver Wendell Holmes from "Forty-First Annual Catalogue. School of Mines and Metallurgy, University of Missouri."

Thesis (Ph. D.)--Hong Kong University of Science and Technology, 2004. / Includes bibliographical references (leaves 175-184). Also available in electronic version. Access restricted to campus users.

O presente trabalho avalia a evolução das microestruturas e das propriedades mecânicas em tubos API 5L X65 soldados por fricção com auxílio de um anel centralizador na posição de topo. A soldagem foi realizada em tubos de 114,3 mm (4,5’’) de diâmetro nominal e 8 mm de espessura. A avaliação mecânica foi realizada segundo normas ASTM para os ensaios de tração, dobramento de raiz, dobramento de face, ensaio de impacto Charpy V e perfis de microdurezas. Os ensaios de fadiga foram realizados para análise da vida em fadiga das juntas soldadas. Os ensaios mecânicos realizados comprovam que houve a união metalúrgica dos materiais, sendo registradas regiões com defeitos de falta de adesão o que prejudicou as propriedades mecânicas ocasionando rupturas com baixa ductilidade nas interfaces de soldagem nestes locais. Nos resultados dos ensaios de microdurezas houve um pequeno aumento das microdurezas registradas próximo às interfaces de soldagem e uma redução nas microdurezas registradas nas regiões de ZACs. Os resultados do ensaio de impacto Charpy -20 °C foi aceitável segundo a norma API 5L. As microestruturas formadas nas interfaces de soldagem são compostas por ferrita de Widmanstätten e ferrita poligonal com crescimento de grão quando comparado com o tamanho de grão do material de base. Nas regiões de ZACs houve um reordenamento de carbonetos aliado a refino de grão sendo registrada uma redução nas microdurezas destas regiões. / This paper assesses the evolution of microstructures and mechanical properties in pipes API 5L X65 welded by friction with the aid of centering ring on top position. The welding was performed in tubes of 114.3 mm (4.5'') nominal diameter and 8 mm in thickness. The mechanical evaluation was performed according to ASTM standards for tensile, root bending, face folding, Charpy V impact test and microhardness profile. Fatigue tests were performed to analyze the fatigue life of the welded joints. The mechanical tests prove that there was a metallurgical union of the materials, regions with lack of adhesion defects being recorded which affected the mechanical properties causing fractures with low ductility in the weld interfaces in these places. Microhardness test results registered a small increase in the microhardness near the weld interfaces and a reduction in the microhardness recorded in the HAZ regions. The results of the Charpy impact test at -20°C was acceptable according to API 5L. The microstructures formed at the weld interfaces are composed of Widmanstatten ferrite and polygonal ferrite with grain growth when compared to the grain size in the base material. In HAZ regions there was a reorganization of carbides combined with grain refinement, with a reduction in microhardness of these regions being registered.

O presente trabalho avalia a evolução das microestruturas e das propriedades mecânicas em tubos API 5L X65 soldados por fricção com auxílio de um anel centralizador na posição de topo. A soldagem foi realizada em tubos de 114,3 mm (4,5’’) de diâmetro nominal e 8 mm de espessura. A avaliação mecânica foi realizada segundo normas ASTM para os ensaios de tração, dobramento de raiz, dobramento de face, ensaio de impacto Charpy V e perfis de microdurezas. Os ensaios de fadiga foram realizados para análise da vida em fadiga das juntas soldadas. Os ensaios mecânicos realizados comprovam que houve a união metalúrgica dos materiais, sendo registradas regiões com defeitos de falta de adesão o que prejudicou as propriedades mecânicas ocasionando rupturas com baixa ductilidade nas interfaces de soldagem nestes locais. Nos resultados dos ensaios de microdurezas houve um pequeno aumento das microdurezas registradas próximo às interfaces de soldagem e uma redução nas microdurezas registradas nas regiões de ZACs. Os resultados do ensaio de impacto Charpy -20 °C foi aceitável segundo a norma API 5L. As microestruturas formadas nas interfaces de soldagem são compostas por ferrita de Widmanstätten e ferrita poligonal com crescimento de grão quando comparado com o tamanho de grão do material de base. Nas regiões de ZACs houve um reordenamento de carbonetos aliado a refino de grão sendo registrada uma redução nas microdurezas destas regiões. / This paper assesses the evolution of microstructures and mechanical properties in pipes API 5L X65 welded by friction with the aid of centering ring on top position. The welding was performed in tubes of 114.3 mm (4.5'') nominal diameter and 8 mm in thickness. The mechanical evaluation was performed according to ASTM standards for tensile, root bending, face folding, Charpy V impact test and microhardness profile. Fatigue tests were performed to analyze the fatigue life of the welded joints. The mechanical tests prove that there was a metallurgical union of the materials, regions with lack of adhesion defects being recorded which affected the mechanical properties causing fractures with low ductility in the weld interfaces in these places. Microhardness test results registered a small increase in the microhardness near the weld interfaces and a reduction in the microhardness recorded in the HAZ regions. The results of the Charpy impact test at -20°C was acceptable according to API 5L. The microstructures formed at the weld interfaces are composed of Widmanstatten ferrite and polygonal ferrite with grain growth when compared to the grain size in the base material. In HAZ regions there was a reorganization of carbides combined with grain refinement, with a reduction in microhardness of these regions being registered.

O presente trabalho avalia a evolução das microestruturas e das propriedades mecânicas em tubos API 5L X65 soldados por fricção com auxílio de um anel centralizador na posição de topo. A soldagem foi realizada em tubos de 114,3 mm (4,5’’) de diâmetro nominal e 8 mm de espessura. A avaliação mecânica foi realizada segundo normas ASTM para os ensaios de tração, dobramento de raiz, dobramento de face, ensaio de impacto Charpy V e perfis de microdurezas. Os ensaios de fadiga foram realizados para análise da vida em fadiga das juntas soldadas. Os ensaios mecânicos realizados comprovam que houve a união metalúrgica dos materiais, sendo registradas regiões com defeitos de falta de adesão o que prejudicou as propriedades mecânicas ocasionando rupturas com baixa ductilidade nas interfaces de soldagem nestes locais. Nos resultados dos ensaios de microdurezas houve um pequeno aumento das microdurezas registradas próximo às interfaces de soldagem e uma redução nas microdurezas registradas nas regiões de ZACs. Os resultados do ensaio de impacto Charpy -20 °C foi aceitável segundo a norma API 5L. As microestruturas formadas nas interfaces de soldagem são compostas por ferrita de Widmanstätten e ferrita poligonal com crescimento de grão quando comparado com o tamanho de grão do material de base. Nas regiões de ZACs houve um reordenamento de carbonetos aliado a refino de grão sendo registrada uma redução nas microdurezas destas regiões. / This paper assesses the evolution of microstructures and mechanical properties in pipes API 5L X65 welded by friction with the aid of centering ring on top position. The welding was performed in tubes of 114.3 mm (4.5'') nominal diameter and 8 mm in thickness. The mechanical evaluation was performed according to ASTM standards for tensile, root bending, face folding, Charpy V impact test and microhardness profile. Fatigue tests were performed to analyze the fatigue life of the welded joints. The mechanical tests prove that there was a metallurgical union of the materials, regions with lack of adhesion defects being recorded which affected the mechanical properties causing fractures with low ductility in the weld interfaces in these places. Microhardness test results registered a small increase in the microhardness near the weld interfaces and a reduction in the microhardness recorded in the HAZ regions. The results of the Charpy impact test at -20°C was acceptable according to API 5L. The microstructures formed at the weld interfaces are composed of Widmanstatten ferrite and polygonal ferrite with grain growth when compared to the grain size in the base material. In HAZ regions there was a reorganization of carbides combined with grain refinement, with a reduction in microhardness of these regions being registered.