In this thesis, the author proposed and developed nanostructured materials based Surface Acoustic Wave (SAW) and conductometric transducers for gas sensing applications. The device fabrication, nanostructured materials synthesis and characterization, as well as their gas sensing performance have been undertaken. The investigated structures are based on two structures: lithium niobate (LiNbO3) and lithium tantalate (LiTaO3). These two substrates were chosen for their high electromechanical coupling coefficient. The conductometric structure is based on langasite (LGS) substrate. LGS was selected because it does not exhibit any phase transition up to its melting point (1470°C). Four types of nanostructured materials were investigated as gas sensing layers, they are: polyaniline, polyvinylpyrrolidone (PVP), graphene and antimony oxide (Sb2O3). The developed nanostructured materials based sensors have high surface to volume ratio, resulting in high sensitivity towards di¤erent gas species. Several synthesis methods were conducted to deposit nanostructured materials on the whole area of SAW based and conductometric transducers. Electropolymerization method was used to synthesize and deposit polyaniline nanofibers on 36° YX LiTaO3 and 64° YX LiNbO3 SAW substrates. By varying several parameters during electropolymerization, the effect on gas sensing properties were investigated. The author also extended her research to successfully develop polyaniline/inorganic nanocomposites based SAW structures for room temperature gas sensing applications. Via electrospinning method, PVP fibres and its composites were successfully deposited on 36° YX LiTaO3 SAW transducers. Again in this method, the author varied several parameters of electrospinning such as distance and concentration, and investigated the effect on gas sensing performance. Graphene-like nano-sheets were synthesized on 36° YX LiTaO3 SAW devices. This material was synthesized by spin-coating graphite oxide (GO) on the substrate and then exposin g the GO to hydrazine to reduce it to graphene. X-ray photoelectron spectroscopy (XPS) and Raman characterizations showed that the reduced GO was not an ideal graphene. This information was required to understand the properties of the deposited graphene and link its properties to the gas sensing properties. Thermal evaporation method was used to grow Sb2O3 nanostructures on LGS conductometric transducers. Using this method, different nanoscale structures such as nanorods and lobe-like shapes were found on the gold interdigitated transducers (IDTs) and LGS substrate. The gas sensing performance of the deposited nanostructured Sb2O3 based LGS conductometric sensors was investigated at elevated temperatures. The gas sensing performance of the investigated nanostructured materials/SAW and conductometric structures provide a way for further investigation to future commerciallization of these types of sensors.

Made available in DSpace on 2016-06-02T19:55:30Z (GMT). No. of bitstreams: 1 3665.pdf: 6614955 bytes, checksum: 38fe505ba234583972871c7ff274e981 (MD5) Previous issue date: 2011-04-28 / Universidade Federal de Sao Carlos / Colloidal Pt nanoparticles were synthesized according to an adapted procedure from Song and co-workers [1], which it was based on the reduction of dihydrogen hexachloroplatinate by ethylene glycol in a basic solution, but using two PVP/Pt = 0,2 and 10 ratio. Both the ratio lead to monodisperse platinum nanoparticles with similar sizes (2.0 and 2.8 nm). Colloidal Pt nanoparticles solutions were incorporated into alumina during sol-gel synthesis and showed different stabilities when submitted to thermal treatment in synthetic air, He and H2 atmospheres. PVP/Pt ratio added to nanoparticles after synthesis was the main parameter considered to the stability of the particles on the support. Using a minor PVP/Pt ratio lead to particles agglomerates during calcinations step in synthetic air. On the other hand, when an excess of PVP was used stable and disperse particles were obtained during a severe thermal treatment. The anchoring of particles into support during incorporation stage could be the most plausible explanation for this. Platinum nanocatalysts supported on alumina and ceriaalumina showed catalytic activity for the water gas shift reaction. CO conversion data indicated that the increasing of CeO2 loading of 12 to 20% lead to an improvement in the catalytic activity. XPS measurements after pre-treatment in H2 confirmed the presence of Pt+on the catalyst surface containing ceria, suggesting some metal-support interaction. In situ characterization techniques allowed to a better understanding of species involved into water gas shift reaction mechanism. Through X-ray absorption near edge structure in the Pt edge measurements showed reduced Pt during reaction for all catalysts, suggesting that similar electronic density of sites was present. This was also observed in CO adsorbed DRIFTS measurements. Nevertheless, XANES spectra in the Ce edge showed some changes in oxidation state of Ce during the reaction, indicating the occurrence of redox mechanism, mediated by ceria. In situ DRIFTS experiments showed little concentrations of formates and carbonates species on the catalyst surface during the reaction, suggesting that more than one mechanism may occur simultaneously. / Nanopartículas de Pt foram preparadas seguindo um procedimento adaptado de Song e colaboradores [1], cuja metodologia consistiu na redução química do ácido hexacloroplatinico pelo etilenoglicol em meio básico, porém utilizando duas razões PVP/Pt = 0,2 e 10. Ambas as razões levaram a nanopartículas de Pt com tamanho similar (2,0 e 2,8 nm) e monodispersas. As soluções coloidais de nanoparticulas de Pt foram incorporada à alumina durante a síntese sol-gel e mostraram diferentes estabilidades quando submetidas a tratamentos térmicos em ar sintético, He e H2. A razão PVP/Pt utilizada na síntese das partículas foi o fator determinante na estabilidade das partículas no suporte. A adição de uma menor razão PVP/Pt levou a aglomeração das partículas durante a calcinação em ar sintético. Por outro lado, quando um excesso de PVP foi utilizado durante a síntese das partículas as mesmas se mostraram estáveis e dispersas no suporte quando submetidas ao mais severo tratamento. Isto foi relacionado ao ancoramento das partículas ao suporte durante a etapa de incorporação. Nanocatalisadores de Pt suportados em alumina e cério-alumina apresentaram atividade catalítica para a reação de deslocamento gás-água. Dados de conversão do CO indicaram que o aumento no teor de CeO2 de 12 para 20% levou a um aumento na atividade catalítica. Medidas de XPS após a etapa de pré-tratamento em H2 confirmaram a presença de Pt+na superfície dos catalisadores contendo ceria, sugerindo alguma interação metal-suporte. Técnicas de caracterização in situ possibilitaram um melhor entendimento do mecanismo das espécies envolvidas no mecanismo da reação de deslocamento gás-água. Medidas de XANES in situ na borda da Pt confirmaram a presença de Pt reduzida durante o curso da reação para todos os catalisadores, o que sugere a presença de sítios de Pt com densidade eletrônica similar. Isto também foi observado nas medidas de DRIFTS do CO adsorvido para os catalisadores estudados. No entanto, os espectros de XANES na borda do Ce confirmaram mudanças no estado de oxidação do Ce no decorrer da reação, indicando a ocorrência do mecanismo de reação redox, mediado pela ceria. Experimentos utilizando DRIFTS in situ identificaram pequenas concentrações de espécies do tipo formiatos e carbonatos na superfície dos catalisadores durante a reação, sugerindo que mais de um mecanismo pode ocorrer simultaneamente. Palavras chave: nanoparticulas, Platina, catalisador, reação de deslocamento gás-água, PVP.

Made available in DSpace on 2014-10-09T12:27:57Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:00:55Z (GMT). No. of bitstreams: 0 / Dissertacao (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP

Made available in DSpace on 2014-10-09T12:43:27Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:09:46Z (GMT). No. of bitstreams: 1 06632.pdf: 4097419 bytes, checksum: 1cde4c2787112f93fcca894974c568fd (MD5) / Tese (Doutoramento) / IPEN/T / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP

The surgical antisepsis is important in maintaining the sterile surgical field. The present study examined of three products for surgical antisepsis, as its immediate effectiveness and its influence on bacteria growth of the hands while wearing surgical gloves for 20, 40 and 60 minutes. After degermation the hands of dental students 21 was used 70% ethanol, PovidoneIodine to 10% and 2% chlorhexidine, for one minute in the form of immersion. Each subject participated in the sample of nine tests. Antiseptics were tested three times, according to the usage time of the surgical gloves. The microbiota of the hands of the subjects was assessed beforehand hygiene, after the immediate use of antiseptic and surgical gloves to determine changes in quality and quantity of bacteria on the hands. Prior to surgical antiseptic were found resident bacteria Staphylococcus epidermidis, Staphylococcus saprophyticus, Staphylococcus aureus and Escherichia coli, bacteria transient. The use of antiseptics eliminated transient bacteria and reduced the amount of bacteria present in the hands of residents significantly (p 0.05). It follows that all tested antiseptics may be used in pre surgical hand hygiene. / Submitted by Rogele Pinheiro (rogele.pinheiro@unisul.br) on 2017-10-23T17:16:15Z No. of bitstreams: 1 107683_Lindsay.pdf: 1331088 bytes, checksum: 90bc7b4a3829c88db6f8e94d24682bbe (MD5) / Approved for entry into archive by Caroline Correa da Cruz (caroline.cruz@unisul.br) on 2017-10-23T20:15:56Z (GMT) No. of bitstreams: 1 107683_Lindsay.pdf: 1331088 bytes, checksum: 90bc7b4a3829c88db6f8e94d24682bbe (MD5) / Made available in DSpace on 2017-10-23T20:15:56Z (GMT). No. of bitstreams: 1 107683_Lindsay.pdf: 1331088 bytes, checksum: 90bc7b4a3829c88db6f8e94d24682bbe (MD5) Previous issue date: 2012-05-28 / A antissepsia cirúrgica é importante na manutenção da assepsia do campo operatório. Este estudo avaliou o desempenho de três produtos para antissepsia cirúrgica, quanto a sua eficácia imediata e sua influência no crescimento bacteriano das mãos durante o uso de luvas cirúrgicas por 20, 40 e 60 minutos. Após a degermação das mãos de 21 acadêmicos de Odontologia, foi utilizado o álcool etílico a 70%, o PVP-I a 10% e a clorexidina a 2%, durante um minuto sob a forma de imersão. Cada sujeito da amostra participou de nove testes. Os antissépticos foram testados três vezes, de acordo com o tempo de uso das luvas cirúrgicas. A microbiota das mãos dos sujeitos foi avaliada antes da higienização das mãos, após o uso imediato do antisséptico e das luvas cirúrgicas para determinar as mudanças na qualidade e quantidade das bactérias presentes nas mãos. Antes da antissepsia cirúrgica foram encontradas as bactérias residentes Staphylococcus epidermidis, Staphylococcus saprofíticos, Staphylococcus aureus e as bactérias transitórias Escherichia coli. O uso dos antissépticos eliminou as bactérias transitórias e reduziu a quantidade de bactérias residentes presentes nas mãos de forma significativa (p0,05). Conclui-se que todos os antissépticos testados podem ser utilizados na higienização pré cirúrgica das mãos.

Made available in DSpace on 2014-10-09T12:27:57Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:00:55Z (GMT). No. of bitstreams: 0 / O açaí (Euterpe oleracea) é uma palmeira nativa do Brasil, distribuída por toda a bacia amazônica. Rico em ácidos graxos essenciais (principalmente o ácido oleico e o ácido linoleico), o óleo de açaí previne condições anormais da pele, como dermatites, escamações e ressecamento, e auxilia no processo de regeneração do tecido epitelial. Conhecendo-se os benefícios dos hidrogéis como curativos, esse trabalho objetivou desenvolver hidrogéis de poli(N-vinil-2- pirrolidona) (PVP) como um sistema de liberação de óleo de açaí para uso tópico em desordens cutâneas. Desconhecendo-se o comportamento do óleo de açaí frente à radiação, foi avaliada a composição de ácidos graxos do óleo antes e após ser submetido à radiação. Duas diferentes matrizes de hidrogel de PVP foram avaliadas quanto às suas características físicas e químicas por meio de ensaios de intumescimento, fração gel, propriedades mecânicas e citotoxicidade in vitro. As duas matrizes foram consideradas adequadas para serem utilizadas como sistema de liberação. Os dispositivos foram obtidos pela incorporação do óleo de açaí nas matrizes de hidrogel de PVP e submetidos aos ensaios de intumescimento, fração gel, propriedades mecânicas e citotoxicidade in vitro, além dos ensaios de caracterização por microscopia eletrônica de varredura e irritação cutânea primária in vivo. Os dois dispositivos de hidrogel de PVP foram submetidos ao ensaio de cinética de liberação por 24 h e o óleo de açaí liberado foi quantificado por cromatografia a gás acoplada a espectrometria de massas, e se mostraram satisfatórios para compor um sistema de liberação de ativos. / Dissertacao (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP

Made available in DSpace on 2014-10-09T12:26:52Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:06:12Z (GMT). No. of bitstreams: 0 / Os hidrogéis estão dentre as matrizes poliméricas mais utilizadas em tecnologia farmacêutica em razão de sua vasta aplicação e funcionalidade, especialmente em sistema de liberação de fármacos. Tendo em vista o grande avanço nas inovações dos produtos cosméticos, tanto por meio da introdução de novos princípios ativos quanto pelas matrizes utilizadas para liberação controlada dos mesmos, o objetivo deste trabalho foi incorporar e avaliar a liberação de um princípio ativo natural, o ArctAlg®, em membranas de hidrogel, de modo a obter um dispositivo de liberação para fins cosméticos. O ArctAlg® é um extrato aquoso que possui uma excelente ação anti-oxidante, lipolítica, anti-inflamatória e citoestimulante. Foi realizado o estudo das propriedades mecânicas, físicoquímicas e a biocompatibilidade in vitro das membranas de hidrogéis de poli(vinil- 2- pirrolidona) (PVP) e poli(vinil álcool) (PVA) obtidas pela reticulação por radiação ionizante. A caracterização físico-química das matrizes poliméricas foi obtida pelos ensaios de fração gel e intumescimento e o de biocompatibilidade in vitro pelo ensaio de citotoxicidade pelo método de incorporação do vermelho neutro. No ensaio de fração gel tanto o hidrogel de PVP quanto o de PVA apresentaram um alto grau de reticulação. O hidrogel de PVP apresentou uma maior porcentagem de intumescimento em relação ao de PVA e no ensaio de citotoxicidade os hidrogéis mostraram-se atóxicos. A propriedade citoestimulante do ArctAlg® foi verificada no ensaio de citoestimulação com células fibroblásticas de pele de coelho, em que foi evidenciado um aumento de cerca de 50% das células quando em contato com 0,5% do princípio ativo. As membranas de hidrogel preparadas com 3% de ArctAlg® foram submetidas ao ensaio de liberação em incubadora a 37ºC e as alíquotas coletadas durante o ensaio foram quantificadas por cromatografia líquida de alta eficiência (HPLC). Os resultados obtidos na cinética de liberação mostraram que as membranas de hidrogel de PVP liberaram cerca de 50% do ArctAlg® incorporado e as de PVA em cerca de 30%. No ensaio de citoestimulação do ArctAlg® liberado, o dispositivo de PVP apresentou um aumento em cerca de 80% da população celular em relação ao controle do ensaio, mostrando ser o dispositivo mais indicado para ser utilizado em processos de reparação cutânea. / Dissertacao (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP

Made available in DSpace on 2014-10-09T12:43:27Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:09:46Z (GMT). No. of bitstreams: 1 06632.pdf: 4097419 bytes, checksum: 1cde4c2787112f93fcca894974c568fd (MD5) / Tese (Doutoramento) / IPEN/T / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP

Denna litteraturanalys går igenom åtgärderna för de problem som förekommer vid skapandet av online pvp-spel. Några av de vanliga problem som kan stötas på innefattar fördröjning, paketförlust, fusk, skalbarhet, synkronisering, uppdateringsfrekvens och säkerhet. Dessa problem kan sedan negativt påverka andra aspekter av spelet, inte minst game feel. För att förhindra detta bör specifika åtgärder implementeras. Inom just online pvp-spel kan grunden till nätverkshanteringen skapas med en klient/server-uppsättning som skickar små och snabba datapaket med hjälp av nätverksprotokollet UDP. Ytterligare lösningar som “dumma klienter”, “client-side prediction”, “server reconciliation”, “interpolation”, historik och tidsstämplar i datapaketen kan användas för att förbättra spelupplevelsen. I kombination med varandra skapar dessa åtgärder en stabil nätverksinfrastruktur för ett online pvp-spel. Då vissa av dessa tekniker kan kräva en del prestanda både på klienten och servern kan framtida arbeten kring dessa lösningar fokusera på optimering.

Applying sizing material (poly n-vinylpyrrolidone or PVP) around graphite fibers enhances the mechanical properties of carbon fiber reinforced epoxy composites. Understanding the influence of the interphase region between the carbon fiber and epoxy matrix is crucial in enhancing the performance of carbon fiber reinforced epoxy composite materials. In this work, simulated interphase regions, in the form of pure and modified epoxies were synthesized in the laboratory. Several characterization techniques were used to identify the properties of these modified epoxies. They were: 1) Tensile Tests: 2) Fracture Toughness Tests; 3) Thermogravimetric Analysis (TGA): 4) Differential Scanning Calorimetry (nSC); 5) Fourier Transform Infrared (FTIR) Spectrometry: and ()) Water Absorption. Young's modulus, yield stress, yield strain. ultimate tensile stress. ultimate tensile strain, tensile toughness, fracture toughness, and strain energy release rate were obtained from tensile and fracture tests. DSC and FTIR experiments were employed in this study to show the miscibility of PVP and epoxy resin. The pure and modified epoxy samples were immersed in water for about a month to determine their water absorptivity. Almost all epoxies remained unchanged in stiffness, with the exception of the sample 40 wt. % PVP. Only the pure epoxy and light PVP loading epoxies exhibited yield points. The ultimate properties worsened significantly with the increase of PVP loading. A decreasing trend was found in fracture toughness as PVP loading increased. All pure and modified epoxies exhibited sharp glass transition temperatures and the T_g's followed the Fox prediction. Downward frequencies shifting of carhonyl and hydroxyl groups were obtained from the PVP/epoxy blends by infrared study. This was believed to show evidence of hydrogen bond formation. All epoxy and modified epoxies were swollen in water absorption experiments. The samples reached equilibrium after about one month and water absorptivity was found to be a function of PVP content. These experiments sought to demonstrate the characteristics of the interphase region of the composites. / Master of Science