Hot cracking is a serious problem that encounters during welding of aluminium-magnesium alloys. In the present study, solidification and liquation type of hot cracks in weld metal and the heat-affected zones of 5086-H32 aluminium alloy were investigated by using Modified Varestraint Test (MVT) with TIG-AC and TIG-DC welding. With determining the size, type and number of cracks, a relation was established between welding line energy and strain on the hot crack formation. This information was used to determine the hot crack safe parameter ranges. The hot cracking tendency as a function of applied parameters were discussed in the frame of temperature fields around the moving heat source. Moreover, the characteristic hot crack locations on the 5086-H32 MVT specimens were generalized. The results of the study indicated that the increase in line energy and strain increased the hot cracking tendency of the specified aluminium alloy. In the low line energy range, the main hot cracking mechanism is the solidification cracking which could be overcome by the use of a suitable filler material. At high line energy range, due to the increased amount of interdendritic liquid, the amount of solidification cracking decreases by healing mechanism. However, because of the enlarged-temperature-field around the weld zone, fraction of HAZ cracking increases. The comparison between the hot cracking tendencies in low and high line energies indicates that the low line energy ranges with low augmented strains resulted in hot crack safer parameters.