Survey work has resolved certain reported anomalies in this system.
In particular, TiNi was found to undergo two displacive phase transformations
at temperatures near room temperature. Below 50°C the pseudo
body-centered cubic compound undergoes a gradual distortion in an unusual
second order phase transformation producing the "transition phase”, the
existence of which is terminated by a typical martensitic burst transform
nation at 20°C which produces the "martensitic phase”. The crystal
structures of the parent phase and transformation products, and the transformation
characteristics have been studied with X-ray and electron diffraction,
electron microscopy, electrical resistance and density measurements. / Thesis / Master of Science (MS)
| Identifer | oai:union.ndltd.org:mcmaster.ca/oai:macsphere.mcmaster.ca:11375/29841 |
| Date | 04 1900 |
| Creators | Dautovich, Donald Peter |
| Contributors | Purdy, G. R., Metallurgy |
| Source Sets | McMaster University |
| Language | English |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0017 seconds