This Ph.D. thesis is dealing with catalytic polymerization of aniline (ANI) and partially also of substituted anilines with FeCl3/H2O2 catalyst system, in which according to obtained results both active species, Fe3+ and HO , participate in the overall polymerization mechanism, creating a synergic system. The Fe3+ /H2O2 catalyst system, also called Fenton's system can considerably lower contamination of forming neat polyanilines (PANIs) by side-products characteristic of stoichiometric polymerization. However, catalytically prepared PANIs exhibit reduced conductivity related most probably to side reactions involving radicals generated as integral components of the FeCl3/H2O2 system. Catalytic polymerization of ANI with FeCl3/H2O2 system was found to be the reaction of approx. 2nd order with respect to ANI and gives PANIs of a good quality only when [H2O2] in the reaction mixture was kept low, i.e., at under- stoichiometric ratios [H2O2]/[ANI]. At over-stoichiometric ratio [H2O2]/[ANI], PANIs of lowered conductivity, worse spectroscopic characteristics and increased size of PANI nanostructures were obtained; nevertheless, these PANIs were not over-oxidized to pernigraniline state. The reaction-time profiles of the open-circuit potential of reaction mixtures exhibited an inflection related to the...
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:311789 |
Date | January 2012 |
Creators | Bláha, Michal |
Contributors | Vohlídal, Jiří, Omastová, Mária, Trchová, Miroslava |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/doctoralThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0013 seconds