This study critically investigates the material and structural behaviour of Aer-Tech material. Aer- Tech material is composed of 10% by volume of foam mechanically entrapped in a plastic mortar. The research study showed that the density of the material mix controls all other properties such as fresh state properties, mechanical properties, functional properties and acoustic properties. Appreciably, the research had confirmed that Aer-Tech material despite being classified as a light weight material had given high compressive strength of about 33.91N/mm2. The compressive strength characteristics of Aer-Tech material make the material a potential cost effective construction material, comparable to conventional concrete. The material also showed through this study that it is a structural effective material with its singly reinforced beam giving ultimate moment of about 38.7KN. In addition, the Aer-Tech material is seen as a very good ductile material since, the singly reinforced beam in tension showed visible signs of diagonal vertical cracks long before impending rapture. Consequently, the SEM test and the neural network model predictions, carried out had showed how billions of closely tight air cells are evenly distributed within the Aer-Tech void system as well as the close prediction of NN model for compressive strength and density are same with the experimental results of compressive strength and density. The result shows that the Aer-Tech NN-model can simulate inputs data and predicts their corresponding output data.
| Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:685595 |
| Date | January 2015 |
| Creators | Dan-Jumbo, F. G. |
| Publisher | Coventry University |
| Source Sets | Ethos UK |
| Detected Language | English |
| Type | Electronic Thesis or Dissertation |
| Source | http://curve.coventry.ac.uk/open/items/699ca3a1-deec-4549-b907-0e06bcdad83f/1 |
Page generated in 0.0019 seconds