Orientadores: Mario Fernando de Goes, Luis Roberto Marcondes Martins / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T15:59:52Z (GMT). No. of bitstreams: 1
Cordeiro_NaraPereirad'Abreu_D.pdf: 3561839 bytes, checksum: 125cbc91719d6a902ce59502debf7873 (MD5)
Previous issue date: 2003 / Resumo: o objetivo deste estudo foi avaliar a resistência ao cisalhamento por extrusão (push out) entre a dentina intra-radicular e pinos de fibra de vidro nas regiões cervical, média e apical de raízes utilizando dois sistemas de cimentação adesiva. Foram selecionados vinte pré-molares inferiores unirradiculares recém extraídos por motivos ortodônticos, hígidos e livres de trincas. As coroas dos dentes foram removidas na altura da junção cemento esmalte. As polpas dentais foram removidas através de limas endodônticas e os condutos radiculares foram preparados com brocas de largo nO 5, com 8,Omm de penetração. As raízes foram divididas em dois grupos de 10: Grupo 1- pino fixados com o sistema adesivo autocondicionante ED Primer e cimento resinoso Panavia F; Grupo 2- pinos fixados com o sistema adesivo de frasco único Single Bond e cimento resinoso Rely X. Após a fixação dos pinos, as raízes foram mantidas em estufa a 37°C, por 24 h. A porção mais apical das raízes foi seccionada até a altura em que a raiz apresentasse 8,Omm de comprimento. Em seguida, as raízes foram seccionadas transversalmente e 3 discos de 2,7mm de altura foram obtidas e classificadas segundo a região cervical, média e apical do pino. O ensaio de resistência de união por extrusão foi realizado em máquina de ensaio universal Instron 4411 onde uma haste metálica com ponta ativa de 1,Omm de diâmetro produziu a carga para efetuar o deslocamento do pino do conduto radicular. Os valores médios de resistência de união por extrusão não apresentaram diferenças estatísticas significantes no terço cervical da raiz entre os dois materiais de fixação avaliados. Nas regiões média e apical do conduto, os valores de resistência de união apresentados pelo Sing/e Bond + Re/y X foram superiores e estatisticamente diferentes em relação aos valores apresentados pelo sistema ED Primer + Panavia F (p< 0,05). Para os dois materiais em estudo, não houve diferença estatística quando comparadas as regiões média e cervical do pino, porém apresentaram diferença estatística em relação à região apical (p< 0,05). Após o ensaio de cisalhamento por extrusão, os espécimes foram seccionados no sentido longitudinal para análise em microscopia eletrônica de varredura. A zona de interdifusão adesivo/dentina produzida pelo adesivo de frasco único Sing/e Bond apresentou-se mais espessa do que a zona de interdifusão apresentada pelo adesivo autocondicionante ED Primer. Houve áreas desmineralizadas com presença de túbulos dentinários abertos porém parcialmente preenchidos pela resina em ambos os grupos. Também foram observadas bolhas que variaram de tamanho e forma na camada de cimento junto à área da interface de união e mais constantes no terço apical das raízes. Palavras-chave: pino de fibra de vidro; cimento resinoso; sistema adesivo; resistência de união; "push out / Abstract: The purpose of this study was to evaluate the bond strength between fiber posts cemented in root dentin considering different depths of the roots (cervical, median and apical) and two luting materiais, through push out tests and to examine the integration among these components through scanning electron microscopy. Twenty sound bicuspids, tree trom cracks, extracted for orthodontic reasons, were selected. The crowns were removed at the cement enamel junction. The pulps were removed with endodontic reamers and the first 8,Omm of the canais were shaped with number 5 largo burs. The roots were divided into two groups of 10 each. The roots trom group 1 received fiber posts cemented with the self etching primer ED Primer and the composite resin Panavia F., while the roots of Group 2 received fiber posts cemented with the one bottle adhesive Single Bond and the composite resin Rely X. After the posts cementation, the roots were kept in humidity at 3-,0 C for 24 hours. The most apical part of the roots were sectioned until they were 8.0mm long. After that, the roots were sectioned transversally and three 2.7mm thick sections were obtained: cervical, median and apical. The push out test that evaluated bond strength between luting material and root dentin was carried out on an Instron (4411) testing machine. The specimens were positioned on a steel support platform with the post centered over a 2.0mm hole in the platform. A steel probe 1.0mm in diameter was centered over the post and used to apply force to the test specimens. Data from the push out test revealed no statistically significant differences at the cervical portion of the root between the two cementation systems tested. At the median and apical portion of the root, the bond strength values presented by the Sing/e Bond and Re/y X were superior and statistically different from those presented by ED Primer and Panavia F (P<O,05). After the push out test, the specimens were sectioned longitudinally for observation in scanning electron microscope. Afterwards, the specimens were gold sputtered to have their failure mode evaluated. The adhesive/dentin hybrid layer formed by the one bottle adhesive Sing/e Bond was thicker than the one formed by the self etching ED primer. There were zones of demineralization in the root dentin not filled with the adhesive for both groups. Many voids could be observed at the cernent layer close to the bonding area and they seemed to be more frequent at the apical portion of the roots / Doutorado / Dentística / Doutor em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288200 |
| Date | 03 December 2003 |
| Creators | Cordeiro, Nara Pereira d'Abreu |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Martins, Luís Roberto Marcondes, 1960-, Goes, Mario Fernando de, 1954-, Junior, Bruno Carlini, Neto, Sizenando Toledo Porto, Paulillo, Luis Alexandre Maffei Sartini, Sinhoreti, Mário Alexandre Coelho |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 90p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds