This study is dedicated to give a production route for a kind of low energy cement called alinite cement using the waste material of soda industry as the main raw material.
Soda solid waste, clay and minor amount of iron ore were mixed with certain quantities and burned at six different burning temperatures of 1050, 1100, 1150, 1200, 1350, and 1450 º / C. The resultant clinkers were investigated by mineralogical and chemical analysis. Mineralogical analyses were performed by X-Ray Diffraction (XRD) technique. XRD analyses revealed the formation of alinite phase in the clinkers. Chemical analyses were performed by X-Ray Fluorescence spectroscopy technique and by wet chemical analysis. Especially, free lime content of the clinkers was searched and an optimum burning temperature was determined.
In order to find the compressive strength of the alinite cement, larger amounts of alinite clinker were manufactured in wet rod shape raw mix in a laboratory type of furnace at 1200, 1350 and 1450 º / C.
The results have shown that forming alinite phase requires ~6wt % chlorine. Alinite clinker is obtained using soda waste at the temperature range between 1050 and 1200 º / C. However, the free CaO becomes much lower as 0.12 at 1200 º / C. Moreover, a lime saturation factor of 76, which is lower than ordinary Portland clinker is obtained. Satisfactory compressive strength was achieved by gypsum addition.
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/12612545/index.pdf |
| Date | 01 September 2010 |
| Creators | Gunes, Asli |
| Contributors | Yaman, Ozgur Ismail |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | M.S. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for METU campus |
Page generated in 0.0017 seconds