The in vitro production of ceramic implants used for cranial defect repair can be challenging and complex. In this thesis, a raw material in such a production has been mapped in order to optimize the production process. The current production leaves variations in the handling properties of the calcium phosphate cement (CPC), such as the viscosity and setting performance. The problems originate from the in-house recrystallization of the raw material monocalcium phosphate monohydrate (MCPM) with a 70% ethanol solution. The treatment of MCPM is strongly dependent on the relative humidity and the current process is not reliable and leaves unwanted fluctuations in the quality of MCPM. Various material and process parameters were investigated to get a deeper knowledge of MCPM in the specific process. The mapping resulted in new information about how the MCPM recrystallizes and how it depends on the evaporation of the ethanol solution during the treatment. Other findings were that the particle size distribution of MCPM is not the only factor controlling the viscosity of the CPC; the density and shape of the MCPM particles may also influence the handling properties. The mapping led to a process optimization suggestion where the amount of ethanol solution is adjusted to the relative humidity during the recrystallization to neutralize the effect of the humidity. The adjustment of ethanol solution volume means the evaporation can be controlled and in theory, constant quality of MCPM can be maintained. Unfortunately, the new method needs additional data to be fully effective but shows great potential.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:uu-486203 |
| Date | January 2022 |
| Creators | Hunhammar, Martin |
| Publisher | Uppsala universitet, Tillämpad materialvetenskap |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | UPTEC K, 1650-8297 ; 22035 |
Page generated in 0.0024 seconds