A comprehensive study of domain switching process in different ferroelastic and ferroelastic/ferroelectric perovskite structured ceramics has been performed. The effects of thermal fluctuations on domain switching dynamics were investigated in the ferroelastic and in the ferroelectric case under static and dynamic electric and mechanical conditions. In the ferroelastic case, domain switching behaviour was investigated for different compositions, using different types of mechanical tests. Compression tests were carried out to characterize the ferroelastic properties, such as coercive stress, hysteresis loop and irreversible strain. Creep experiments were performed to study the domain switching time dependence at different stress levels. Domain switching kinetics during creep was characterized by implementing a rate model, based on thermal activation rate theory, which allowed the activation volume to be estimated. A Rayleigh-type analysis was performed to study the effects of stress amplitude, loading rate, temperature and composition on ferroelastic switching. Rayleigh-type relationships were proposed to fit the results and the rate model developed was applied to quantify the effect of the loading rate on the Rayleigh loops. Alternative methodologies were developed to assess the effects of rate and temperature on the coercive stress, providing original sets of data. A further application of the rate model provided an estimation of the activation parameters (volume and enthalpy). In PZT 5A at the coercive field the activation volume was calculated to be 2.44 nm3, with a reasonable consistency with the value obtained from creep tests (7.49 nm3). In the ferroelectric case, domain switching was studied by generating P-E and butterfly hysteresis loops and by analysing creep-relaxation curves. In creep experiments, the polarization and the strain were measured simultaneously, during the application of a constant electric field. An insight into the evolution of domain structure and on domain switching mechanisms was gained, highlighting analogies and differences with the ferroelastic case. Experiments at different frequencies, allowed the activation volume to be estimated at the coercive field (77 nm3). The relatively large value indicates small rate dependence and suggests a domain structure with broad and mobile domain walls, being the preferred sites for the nucleation.
| Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:516672 |
| Date | January 2010 |
| Creators | Viola, Giuseppe |
| Publisher | Queen Mary, University of London |
| Source Sets | Ethos UK |
| Detected Language | English |
| Type | Electronic Thesis or Dissertation |
| Source | http://qmro.qmul.ac.uk/xmlui/handle/123456789/382 |
Page generated in 0.0137 seconds