The thesis is focused on assessment of fatigue behaviour of austempered ductile iron with nodular graphite. Optimal period of transformation was determined based on the best combination of stress and strain characteristics established by tensile test. Cyclic response and low-cycle fatigue life were studied under both stress-control and longitudinal strain-control mode at room temperature. For both modes, shapes of cyclic hardening curves are dependent on stress amplitude. Cyclic deformation curves (CDC) were fitted by power regression function. Results were compared with CDC established by multiple step test in both modes with verification of the influence of cyclic creep (high stress levels, stress-control mode). Experimental data of S-N curves are in agreement with the Manson-Coffin and the Basquin law. Fatigue and cyclic parameters were compared. Fatigue life time in high-cycle fatigue region was determined. Experimental data were fitted by suitable regression functions. Regression parameters and fatigue limit were established by means of each regression function. Experimental data in low- and high-cycle fatigue regions were used to construct S-N curve and to determine relevant parameters. Discontinuity of experimental data was not observed. Low-cycle fatigue behaviour was predicted. Approximation of tolerance bands was realized in high-cycle and both high and low cycle fatigue regions.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:233981 |
Date | January 2011 |
Creators | Zapletal, Josef |
Contributors | Věchet, Stanislav |
Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/doctoralThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0011 seconds