This thesis investigates the behaviour of UHPC as a fill material for precast deck panels subjected to negative bending. Two full-scale test specimens were constructed. The transverse joints between the panels, the shear pockets, and the deck haunches were all filled with UHPC. A total of four tests were performed including two static tests to failure and two fatigue tests, one of which was performed to failure. Testing consisted of a loading apparatus acting upwards on the deck soffit in an attempt to impose tensile stresses across the transverse joints, representing the conditions that a transverse joint in the negative moment region of a continuous bridge deck would experience. It was concluded that the transverse UHPC joint performed satisfactorily by transferring bending stresses and shear stresses across the joint from one panel to the adjacent panel. Overall, the test specimens displayed performance levels expected from conventional cast-in-place concrete deck alternatives. / February 2016
Identifer | oai:union.ndltd.org:MANITOBA/oai:mspace.lib.umanitoba.ca:1993/31018 |
Date | 11 January 2016 |
Creators | Amorim, David Rodrigues Coelho |
Contributors | Svecova, Dagmar (Civil Engineering), Mufti, Aftab (Civil Engineering) Shehata, Emile (Civil Engineering) Kuhn, David (Mechanical Engineering) |
Source Sets | University of Manitoba Canada |
Detected Language | English |
Page generated in 0.0012 seconds