Third-generation advanced high-strength steels (3G AHSS) are being developed to assist in vehicle light weighting so that fuel efficiency may be improved without sacrificing passenger safety. 3G-AHSS have received significant interest from the automotive industry as a critical candidate for their unique combination of high strength and ductility. However, due to selective oxidation of the principal alloying elements such as Mn, Si, Al, and Cr at the steel surface during the annealing stage prior to immersion in the galvanizing Zn(Al, Fe) bath, the process of continuous hot-dip galvanizing of these steel is challenging. This thesis determined the influence of annealing process parameters such as oxygen partial pressure and annealing time, on the selective oxidation and reactive wetting of an Fe-0.15C-5.56Mn-1.17Si-1Al (wt%) prototype 3G AHSS during intercritical annealing as well as continuous galvanizing.
Simulated annealing and galvanizing were conducted on the prototype Fe-0.15C-5.56Mn-0117Si-1Al (wt%) 3G steel; Intercritical annealing heat treatments were carried out at 690˚C in a N2-5 vol pct H2 process atmosphere under dew points of 223 K (–50 °C), 243 (–30 °C) and 268 K (–5 °C). MnO was the major oxide formed at the outmost layer of the external oxides on all annealed samples. The experimental parameters, on the other hand, had a substantial impact on the morphology, distribution, thickness, and surface oxide coverage.
The greatest Mn surface concentration as well as maximum surface oxide coverage and thickness was obtained by annealing the panels under the 223 K (–50 °C) and 243 (–30 °C) dp process atmospheres. The oxides formed under these process atmospheres largely comprised coarse, compact, and continuous film nodules. In contrast, MnO nodules formed under the 268 K (–5 °C) dewpoint process, exhibited wider spacing between finer and thinner nodules, which was consistent with the internal oxidation mode, while under 223 K (–50 °C) dp process atmosphere, generally external oxidation took place.
Poor reactive wetting was obtained for the panels annealed under the 223 K (–50 °C) dp process atmosphere for both the 60 s and 120 s holding times as well as the 243 K (–30 °C) dp process atmosphere for 120 s. This was attributed to the formation of a thick, compact oxide layer on the steel surface, which acted as a barrier between the substrate and Zn bath, preventing Fe dissolution from the substrate surface for the formation of the desired Fe2Al5Znx interfacial layer. However, a well-developed interfacial Fe-Al intermetallic layer was formed under the 268 K (–5 °C) and 243 (–30 °C) dp process atmospheres for intercritical annealing times of 60 s, which is indicative of a good reactive wetting since the thinner and nodule-like oxides on the steel surface after annealing encourage the reactive wetting. External oxides morphology plays a dominant role in facilitating the contact between Zn-alloy bath and the substrate via different mechanisms such as aluminothermic reduction which occurred for the sample annealed under the 268 K (–5 °C) dp process atmosphere. / Thesis / Master of Applied Science (MASc)
Identifer | oai:union.ndltd.org:mcmaster.ca/oai:macsphere.mcmaster.ca:11375/27029 |
Date | January 2021 |
Creators | Gol, Saba |
Contributors | McDermid, Joseph, Materials Science and Engineering |
Source Sets | McMaster University |
Language | English |
Detected Language | English |
Type | Thesis |
Page generated in 0.0016 seconds