The aim of this thesis is to describe behavior of cracks in layered polymer materials. Quasi-brittle fracture (through the initiation and subsequent crack propagation mechanism) under low stresses is the most common mode of failure of polymer materials. In this case plastic deformations are localized in the vinicity of the crack tip and linear elastic fracture mechanics description of the crack behavior can be used. The knowledge of fracture parameters change during the crack propagation in multilayer body is a key point for establishing of the maximum load and consequently for the assessment of the residua lifetime. In contrast to homogeneous bodies the estimation of stress intensity factors for multilayer (composite) structure is numerically more elaborated and the fracture mechanics approach is complicated by the existence of interfaces between single layers, where material parameters are changed by a step. Special attention is paid to the configuration of a crack growing close to the material interface and along the interface. For the crack with tip on the material interface the effective values of stress intensity factor based on the crack stability criteria are estimated. It is shown that under special conditions (depending mainly on the elastic mismatch of materials) the existence of material interface has positive influence on the lifetime of the multilayered structure.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:234216 |
| Date | January 2014 |
| Creators | Zouhar, Michal |
| Contributors | Klusák, Jan, Kučera, Jaroslav, Hutař, Pavel |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.002 seconds