Previous issue date: 2012-12-17 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / The MCM-41 mesoporous synthesis was done using rice hulls ash and chrysotile as
natural alternative silica sources. For the using of these sources, chemical and thermic
treatments were done in both materials. After chemical and thermic treatments, these
materials were employed on the MCM-41 mesoctructures synthesis. The natural materials
treated and employed in the synthesis were characterized by several techniques such as X-ray
diffraction, N2 adsorption and desorption, scanning electronic microscopy and
thermogravimetric analysis. MCM-41 standart samples synthetized with aerosil 200
commercial s?lica were used to evaluation. The formed material from rice hulls ash showed
values from BET specific area about 468 m?.g-1, N2 adsorption and desorption isotherms and
loss mass similar to reference materials. The silica from chrysotile calcined and leached was
employed to mesoporous materials synthesis. The BET specific area showed values about 700
m?.g-1, N2 adsorption and desorption isotherms type IV and loss mass similar to mesoporous
materials. The formed material from calcined and leached chrysotile, without calcination,
applied to phenol remotion carried high performance liquid chromatography and evaluated
with organophilic clays with different treatments. By the characterization techniques were
proved that mesoporous materials with lesser order that reference samples. The material
formed from rice hulls ash without the calcination step achieved better adsorption results than
organophilic clays / A s?ntese dos mesoporosos do tipo MCM-41 foram realizadas empregando materiais
naturais como cinza da casca de arroz e crisotila como fontes alternativas de s?lica. Para a
utiliza??o destas fontes, tratamentos t?rmicos e qu?micos foram realizados em ambos os
materiais. Os materiais naturais, ap?s tratamento t?rmico e qu?mico, foram empregados na
forma??o de mesoestruturas do tipo MCM-41. Os materiais naturais, tratados e empregados
na s?ntese foram caracterizados por diversas t?cnicas, como difra??o de raios-X, adsor??o e
dessor??o de N2, microscopia eletr?nica de varredura e an?lise termogravim?trica. Amostras
padr?es de MCM-41 sintetizadas com s?lica comercial pirolisada aerosil 200 foram utilizadas
como crit?rio de compara??o. O material formado a partir da cinza da casca de arroz
calcinada e lixiviada apresentou ?rea espec?fica de 468 m?.g-1, isotermas de adsor??o e
dessor??o de N2 t?picas de materiais mesoporosos e eventos de perda de massa semelhantes a
amostra de refer?ncia. A s?lica derivada da crisotila calcinada e lixiviada foram utilizadas
para a s?ntese de materiais mesoporosos. O material apresentou valores de ?rea espec?fica
BET de 700 m?.g-1, isotermas de adsor??o e dessor??o de N2 do tipo IV e perdas de massa
caracter?sticas de materiais mesoporosos. O material formado a partir da cinza da casca de
arroz, sem a etapa de calcina??o foi aplicado na adsor??o de fenol acompanhado por
cromatografia l?quida de alta efici?ncia (CLAE) e comparado com argilas organof?licas com
diversos tratamentos. Pelas t?cnicas de caracteriza??o comprova-se que os materiais s?o do
possuem menor ordena??o que a amostra de refer?ncia. O material formado a partir da cinza
da casca de arroz, e sem a etapa de calcina??o, obteve melhores resultados de adsor??o de
fenol, se comparado ?s argilas organof?licas
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/12763 |
| Date | 17 December 2012 |
| Creators | Schwanke, Anderson Joel |
| Contributors | CPF:50942611004, http://lattes.cnpq.br/5249001430287414, Ara?jo, Ant?nio Souza de, CPF:35530502415, http://lattes.cnpq.br/9770622597949866, Nascimento, Rubens Maribondo do, CPF:80732810400, http://lattes.cnpq.br/8671649752936793, Gusm?o, Katia Bernardo, CPF:51985764091, http://lattes.cnpq.br/8664708384378316, Pergher, Sibele Berenice Castella |
| Publisher | Universidade Federal do Rio Grande do Norte, Programa de P?s-Gradua??o em Ci?ncia e Engenharia de Materiais, UFRN, BR, Processamento de Materiais a partir do P?; Pol?meros e Comp?sitos; Processamento de Materiais a part |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds