The aim of this thesis is influence of precipitation hardening regime, specifically quench rate, on mechanical properties of aluminium alloy A356 (AlSi7Mg0.3). Samples were after solution treatment quenched into water with different temperatures and age hardened. Tensile strength tests, hardness tests and microstructure observations were done after heat tretment.