The thesis is focused on physical hyaluronan gels. The object of study is the interaction of hyaluronan (HyA) with oppositely charged surfactants in physiologic solution (0.15 M NaCl), leading to the formation of gel. In the first part of work have been determined the solids´ contents (X) in gels and their supernatants in percentage and their correlation with molecular weight concentration of original HyA solution and the ratio of binding sites on hyaluronan chain and surfactant CTAB. To conclude, decrease in HyA concentration results in higher values of X and vice versa. On the other hand, increase in the value of X with increasing molecular weight of HyA is not so significant. Analogous conclusions have been made for supernatants and the amount of solids in gel. Drying process has been recorded by drying curves. Swelling process has been used for the characterization of gels. The percentage of water that can be absorbed by dried gel, was determined. The results are in agreement with the measurements of solids´ content in gels. In the next part, the correlation between rheological properties of gels and HyA concentration, HyA molecular weight and concentration of CTAB have been studied by the oscillation and flow tests. The samples with the highest molecular weight and concentration have the most viscoelastic character. The flow test confirmed the assumed pseudoplastic behavior of gels. A very interesting trend arose while comparing HyA concentrations and viscosity in stock solutions and gels. Whereas in stock solution viscosity (at low shear rate) is lower with increasing of HyA concentration, the situation was exactly the opposite in gels. The results are in agreement with frequency tests and observed character of gels.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:216963 |
| Date | January 2013 |
| Creators | Kovářová, Lenka |
| Contributors | Márová, Ivana, Mravec, Filip |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0021 seconds