Evaluación in vitro de la microrugosidad superficial de dos resinas tipo Bulk Fill inmersas a dos bebidas rehidratantes con pH de 2,79 y 3,3 / In vitro comparison of superficial microroughness of two Bulk Fill resins composites inmersed into two soft drinks

Objetivo: Comparar in vitro la rugosidad superficial de una resina compuesta tipo BulkFill: Aura® BulkFill (SDI) con la resina Tetric N-Ceram® BulkFill (Ivoclar Vivadent) al ser inmersas a dos bebidas rehidratantes: Sporade® y Gatorade®.

Materiales y métodos: Se utilizaron 88 especímenes de resina divididos en cuatro grupos, confeccionados con una matriz metálica (10mm x 4mm). Se insertó las resinas con una espátula de resina, y se fotoactivó con la lámpara Elipar LedTM, con una intensidad de 1200 mW/cm2. Se sumergieron los especímenes en agua destilada. A las 24 horas, se midió la rugosidad con el rugosímetro Mitutoyo SJ-210P. Luego, se realizó la inmersión en bebidas rehidratantes y se midió la rugosidad final a los 7 días.

Resultados: La rugosidad inicial y final de las resinas Aura® BulkFill (SDI) y Tetric N-Ceram® BulkFill (Ivoclar Vivadent) presentaron diferencias significativas después de la inmersión en bebidas rehidratantes. Para los especímenes de Aura® BulkFill (SDI) al someterla a Sporade® se encontró una media inicial de 1.20 y una media final de 1.76 y los valores para Gatorade® fueron 0.77 y 1.73. Mientras que la rugosidad superficial de Tetric N-Ceram® BulkFill (Ivoclar Vivadent) al sumergirla en Sporade® fue 0.82 y 1.55, y en Gatorade® 0.77 y 1.73. Al comparar la diferencia de la rugosidad superficial final e inicial (deltas), la resina Aura® BulkFill presentó diferencias significativas mientras que, Tetric N-Ceram® BulkFill no tuvo diferencias al sumergirlas en ambas bebidas rehidratantes.

Conclusiones: Las resinas estudiadas incrementaron su rugosidad luego de ser inmersas a las bebidas mencionadas. / Objective: To compare in vitro the surface roughness of a BulkFill composite resin: Aura® BulkFill (SDI) with Tetric N-Ceram® BulkFill resin (Ivoclar Vivadent) when immersed in two rehydration drinks: Sporade® and Gatorade®.

Materials and methods: 88 resin specimens divided into four groups were used, with a metal matrix (10 mm x 4 mm). The resins were inserted with a resin spatula, and photo-activated with the Elipar LedTM lamp, with an intensity of 1200 mW/cm2. The specimens were immersed in distilled water. After 24 hours, the roughness was measured with the Mitutoyo SJ-210P rugosimeter. Then, the immersion in rehydration drinks was performed and the final roughness was measured after 7 days.

Results: The initial and final roughness of the resins Aura® BulkFill (SDI) and Tetric N-Ceram® BulkFill (Ivoclar Vivadent) showed significant differences after immersion in rehydration drinks. For specimens of Aura® BulkFill (SDI) when subjected to Sporade® an initial mean of 1.20 and a final average of 1.76 was found and the values for Gatorade® were 0.77 and 1.73. While the surface roughness of Tetric N-Ceram® BulkFill (Ivoclar Vivadent) when immersed in Sporade® was 0.82 and 1.55, and in Gatorade® 0.77 and 1.73. When comparing the difference of the final and initial surface roughness (deltas), the Aura® BulkFill resin showed significant differences while, Tetric N-Ceram® BulkFill did not have differences when immersing them in both rehydration drinks.

Conclusions: The resins studied increased their roughness after being immersed in the aforementioned beverages. / Tesis

Identiferoai:union.ndltd.org:PERUUPC/oai:repositorioacademico.upc.edu.pe:10757/628127
Date21 October 2019
CreatorsAvila Solis, Sandra Milagros
ContributorsHermoza, Mónica
PublisherUniversidad Peruana de Ciencias Aplicadas (UPC)
Source SetsUniversidad Peruana de Ciencias Aplicadas (UPC)
LanguageSpanish
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/bachelorThesis
Formatapplication/pdf, application/epub, application/msword
SourceUniversidad Peruana de Ciencias Aplicadas (UPC), Repositorio Académico - UPC
Rightsinfo:eu-repo/semantics/openAccess, Attribution-NonCommercial-ShareAlike 4.0 International, http://creativecommons.org/licenses/by-nc-sa/4.0/

Page generated in 0.0024 seconds