Avaliação de cimentos de ionômero de vidro modificados por resina frente à incorporação de nanopartículas de vitrocerâmica bioativa / Resin modified glass ionomer cements evaluation with additional bioactive glass-ceramics nanoparticles

Os materiais bioativos são materiais sintéticos que possuem superfícies ativas em que os minerais presentes em tecidos duros podem se ligar quimicamente. Há alguns estudos em Odontologia, onde partículas desses materiais foram incorporadas aos Cimentos de Ionômero de Vidro (CIVs) e Cimentos de Ionômero de Vidro modificados por resina (CIVMRs) com o objetivo de se obter bioatividade, e conseqüente remineralização dentária. O presente estudo teve como objetivo avaliar os efeitos da incorporação de nanopartículas de vitrocerâmica bioativa nas propriedades de resistência à compressão e rugosidade de CIVMRs. Fuji II LC e Vitremer foram considerados os grupos controles. Materiais experimentais foram feitos através da incorporação de 2, 5 e 10% em peso de Biosilicato nestes CIVMRs. Seis corpos-de-prova de cada material foram confeccionados para o teste de resistência à compressão, que foi realizado em máquina de ensaios universal (Emic), a uma velocidade de 1,0 mm/min, depois de mantidos por 24 horas em água destilada a 37°C. Para análise da rugosidade, foram confeccionados dois corpos-de-prova de cada material, armazenados em água destilada por sete dias, para terem suas superfícies analisadas por meio de Microscopia de Força Atômica. Os dados da resistência à compressão e rugosidade foram submetidos à análise estatística por meio da Análise de Variância (ANOVA) a dois critérios e para comparações múltiplas foi aplicado o teste de Tukey, com nível de significância de 5%. Apenas os cimentos com 2% de nanopartículas de vitrocerâmica bioativa obtiveram resistência à compressão semelhante ao grupo controle, as demais concentrações contribuíram para a diminuição dessa resistência. A incorporação de 5% de nanopartículas de vitrocerâmica bioativa aumentou a rugosidade superficial dos CIVMRs estudados. / Bioactive materials are synthetic materials that have active surfaces that are capable to chemically bond to dental structures. There are some studies where particles of these materials were incorporated in Glass-ionomer cements (GIC) and Resin-modified glass-ionomer cements (RMGIC) trying to achieve bioactivity and dental remineralization. The aim of this study was to evaluate the effects of the incorporation of bioactive glass-ceramics nanoparticles on the compressive strength and roughness of RMGIC. Fuji II LC and Vitremer were considered the control groups. Experimental materials were made adding 2, 5 and 10% (weight) of Biosilicate into these RMGIC. Six specimens of each material were made to be tested on compressive strength performed with a universal testing machine (Emic) at a crosshead speed of 1.0 mm / min, after they were stored in distilled water for 24 hour at 37°C. To roughness analysis, two specimens of each material were made and stored in distilled water for 7 days and their surfaces were analyzed with a Atomic Force Microscope. Data of compressive strength and roughness were statistically analyzed by ANOVA and Tukey test for multiple comparisons. Only the RMGICs with 2% of bioactive glass-ceramic nanoparticles obtained compressive strength similar to the control RMGICs, the other concentrations decreased their compressive strength values. The incorporation of 5% of bioactive glass-ceramic nanoparticles increased the roughness of the RMGICs.

Identiferoai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-27092011-102146
Date31 May 2011
CreatorsMaria Cristina Carvalho de Almendra Freitas
ContributorsMaria Fidela de Lima Navarro, Maria Teresa Atta, Ticiane Cestari Fagundes
PublisherUniversidade de São Paulo, Ciências Odontológicas Aplicadas, USP, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0022 seconds