This diploma thesis deals with research and preparation of bulk materials based on the Mg–Al–Ti system. The theoretical part summarizes the basic knowledge about magnesium alloys, focusing mainly on Mg–Al and Mg–Ti systems. Furthermore, basic information on powder metallurgy methods was included here, from the production of powder materials, through their compaction, to heat treatment and spark plasma sintering (SPS). The theoretical part ends with literature review on the current research of the Mg–Al–Ti system. In the experimental part, bulk materials based on the Mg–Al–Ti system was prepared using traditional methods of powder metallurgy, as well as using the SPS method. The microstructure of the material, elemental and phase composition was examined in this thesis. Subsequently, Vickers hardness and flexural strength were measured, and fractographic observation of the fracture surface was performed. It was found that the aluminum was completely dissolved during the heat treatment, but the titanium particles remained almost intact in the material and worked as a particulate reinforcement. Materials prepared by methods of conventional powder metallurgy showed increased porosity compared to materials prepared by the SPS, resulting in lower hardness and flexural strength. The hardness increased with increasing the amount of aluminum and titanium and with the amount of magnesium phase . Fractographic observation of the fracture surface suggests that a diffuse connection between the reinforcement and the matrix may have occurred after the sintering process.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:433026 |
| Date | January 2020 |
| Creators | Brescher, Roman |
| Contributors | Doskočil, Leoš, Březina, Matěj |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Slovak |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0021 seconds