CoordenaÃÃo de AperfeiÃoamento de NÃvel Superior / A soldagem de revestimentos de ligas de nÃquel à utilizada pelas indÃstrias de petrÃleo e gÃs como opÃÃo de construÃÃo e reparo de estruturas e equipamentos submetidos em ambiente de condiÃÃes severas com o intuito de apresentar desempenhos necessÃrios de resistÃncia à corrosÃo. Muitos trabalhos foram desenvolvidos com superligas de nÃquel AWS ERNiCrMo-3, AWS ERNiCrMo-4 e AWS ERNiCr-Mo14, para avaliar resistÃncias à corrosÃo e a Ãltima se mostrou bem superior, porÃm o seu custo tambÃm à bem mais elevado que as outras duas. Assim, o trabalho vem aliar a alta produtividade do processo de soldagem MIG/MAG â DA atravÃs da soldagem de revestimentos com as ligas AWS ERNiCrMo-3 e AWS ERNiCrMo-4 na intenÃÃo de se obter uma mistura que apresente tanto a composiÃÃo quÃmica prÃxima a da liga AWS ER NiCr-Mo-14 como desempenho de resistÃncia a corrosÃo, porÃm com menor custo. Estudos exploratÃrios foram realizados por meio de soldagem com simples deposiÃÃo para determinaÃÃo da faixa de velocidade de soldagem entre 50 e 100 cm/min, modo de operaÃÃo da fonte em corrente constante pulsada e gÃs de proteÃÃo ArgÃnio puro. Os revestimentos foram soldados com menor energia (7,5 kJ/cm), tecimento triangular, eletrodos posicionados um atrÃs do outro em relaÃÃo a velocidade de soldagem e sem defasagem entre as correntes. Nessa etapa variou-se Ãngulo de ataque e o percentual de sobreposiÃÃo dos cordÃes. A melhor condiÃÃo apresentada foi menor diluiÃÃo, 9,75%, e elevado reforÃo, 3,92 mm, sendo essa obtida utilizando-se a tocha inclinada de 15Â, e sobreposiÃÃes de 50%. A relativa baixa diluiÃÃo encontrada e o elevado reforÃo reduziram a necessidade de uma segunda camada, o que torna o processo uma boa opÃÃo para operaÃÃes de revestimento para indÃstria de petrÃleo e gÃs. / Weld overlayâs Nickel based alloy are used by the oil and gas industry as an option for construction and repair of structures and equipment subjected to severe environment conditions with the purpose to provide performance required like for corrosion resistance. Many works have been developed with Nickel based superalloys AWS ERNiCrMo-3, AWS ERNiCrMo-4 e AWS ERNiCrMo-14, evaluating among several characteristics the last alloy proved to be upper, but their cost is also higher than the other two. Therefore the present work intends to combine the high productivity of GMAW double wire for welding overlay applications using alloy with AWS ERNiCrMo-3, AWS ERNiCrMo-4 with the intention of obtain a mixture presenting both chemical composition similar to the AWS ER NiCrMo-14 such as corrosion resistance performance, but with less cost. Exploratory studies were performed by means of welding with simple deposition to determine the range of welding speed between 50 and 100 cm / min, the operating mode of the source constant current and pulsed pure argon shielding gas. The coatings were welded with low energy (7,56 kJ/cm), triangle weaving, electrodes positioned one behind the other in relation to the welding speed, without out of phase the currents. This step was varied angle of attack and the percentage of overlap the weld beads. The best condition was presented lower dilution, 9.75%, and a high thickness 3.92 mm and that obtained using the torch inclined at 15  and overlap of 50%. The relatively low dilution and high thickness found reduced the need for a second coating, which makes the process a good option for coating operations.
| Identifer | oai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:6982 |
| Date | 25 July 2013 |
| Creators | Kamilla Gilà Santiago |
| Contributors | Marcelo Ferreira Motta, Cleiton Carvalho Silva, Jair Carlos Dutra |
| Publisher | Universidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em Engenharia e CiÃncia de Materiais, UFC, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0084 seconds