Designing a Heat Treatment to Achieve Ductile Advanced High Strength Steels

Heat treatment is a way to significantly change materials properties. When presented with materials that lack certain mechanical properties, it is possible to change its chemical properties and microstructures by applying heat. This can help achieve better yield strength, ductility and toughness. This project discusses the effects of multiple distinct heat treatment methods for several materials in order to improve ductility and elongation without diminishing strength. The materials in question are High Aluminum Steel and Strenx 700MC steel, the first being under development and the second being a commercially available steel. These steels show promise to be used as high ductility, high strength, and 3rd generation steels. The heat treatments can change the mechanical proprieties of the base materials in order to optimize these steels for applications in vertical access solutions. The heat treatments in this project were Quenching and Partitioning (QP), Quenching and Tempering (QT), Austempering (AUST), Intercritical Heat Treatment (IHT) and other usual heat treatments such as Double normalizing (D-Norm). First, the most beneficial type of the above mentioned heat treatments was selected for each steel and series of heat treatments were performed in order to identify and optimize the best method for each steel. Then, heat treated samples underwent a series of tests to numerically quantify their properties and compare them to the existing steels in Alimak’s applications. The results show that Quenching and Partitioning is the most promising heat treatment for optimizing strength and ductility in High Aluminum Steel, with elongation values up to 19% together with yield strengths of 700 MPa. For Strenx 700MC a combination of temperature and time was found that gave an elongation of above 25% with a yield strength of 450 MPa. The explanation for the good properties was partly grain refinement and phase transformations during heat treatments.

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:ltu-79754
Date January 2020
CreatorsLaarich, Abdellatif
PublisherLuleå tekniska universitet, Institutionen för teknikvetenskap och matematik
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeStudent thesis, info:eu-repo/semantics/bachelorThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0019 seconds