Carbon fiber is extensively used in aircraft components and structures, where its superior strength-to weight ratio far exceeds that of any metal. Thirty percent of all carbon fiber is used in the aerospace industry. The purpose of this research was to determine the influence of material properties on the impact response of a laminate, whereby specimens were fabricated and cured under a vacuum and high temperature using three types of pre-impregnated (prepreg), carbon fibers, namely unidirectional fiber, plain weave woven fiber, and non-crimp fiber. Each carbon fiber panel, usually known for its low-impact properties, with respective type of prepregs, of 16 plies underwent impact testing using a low-velocity impactor and visual damage inspection by C-scan in order to measure the damage area and depth, before and after impact testing. These panels were treated with UV exposure and moisture conditioning for 20 days each. Water contact angles were taken into consideration to determine the hydrophobicity and hydrophillicity of the respective prepreg material. Experimental results and damage analysis show that UV exposure and moisture conditioning showcased the variation in impact response and behavior, such as load-carrying capacity, absorbed energy, and impact energy of the carbon fiber panels. This study illustrates that non-crimp carbon fiber laminates were far more superior relative to load capacity than woven and unidirectional laminates, with the NCF-AS laminate exhibiting the highest load capacity of 17,244 lb/in (pre-UV) with only 0.89% decrease after UV exposure. This same laminate also had a 1.54% decrease in sustaining impact and 31.4% increase in wettability of the panel. Moreover, the study shows how symmetric and asymmetric stacking sequences affect the impact behavior of non-crimp fiber laminates. These results may be useful for expanding the capacity of carbon fiber, lowering costs, and growing new markets, thus turning carbon fiber into a viable commercial product. / Thesis (M.S.)--Wichita State University, College of Engineering, Dept. of Mechanical Engineering
| Identifer | oai:union.ndltd.org:WICHITA/oai:soar.wichita.edu:10057/10957 |
| Date | 05 1900 |
| Creators | George, Jithin Mathew |
| Contributors | Asmatulu, Ramazan |
| Publisher | Wichita State University |
| Source Sets | Wichita State University |
| Language | en_US |
| Detected Language | English |
| Type | Thesis |
| Format | viii, 80 p. |
| Rights | Copyright 2014 Jithin Mathew George |
Page generated in 0.0015 seconds