Submitted by isabela.moljf@hotmail.com (isabela.moljf@hotmail.com) on 2016-08-04T17:39:56Z
No. of bitstreams: 1
joaopaulodasilvasudre.pdf: 2148062 bytes, checksum: c73715b2cb00a515bba21c95536911d3 (MD5) / Approved for entry into archive by Adriana Oliveira (adriana.oliveira@ufjf.edu.br) on 2016-08-05T11:49:24Z (GMT) No. of bitstreams: 1
joaopaulodasilvasudre.pdf: 2148062 bytes, checksum: c73715b2cb00a515bba21c95536911d3 (MD5) / Made available in DSpace on 2016-08-05T11:49:24Z (GMT). No. of bitstreams: 1
joaopaulodasilvasudre.pdf: 2148062 bytes, checksum: c73715b2cb00a515bba21c95536911d3 (MD5)
Previous issue date: 2015-05-06 / O objetivo deste estudo foi avaliar o efeito de diferentes tratamentos ácidos, variação da concentração e do tempo de exposição aos ácidos, hidrofluorídrico (HF) e fosfórico (H3PO4), sobre a rugosidade superficial e resistência de união de uma cerâmica vítrea reforçada por dissilicato de lítio cimentada com um cimento resinoso autoadesivo. Cem pastilhas da cerâmica IPS e.max Press® medindo 2 x 7 mm foram divididas em dez grupos de acordo com o tratamento de superfície (n=10): G1, controle, ou seja, sem tratamento; G2, G3 e G4 condicionamento com HF 5% por 20, 40 e 60 segundos, respectivamente; G5, G6 e G7, condicionamento com HF 10% por 20, 40 e 60 segundos, respectivamente; G8, G9 e G10 condicionamento com HF a 10% por 20,40 e 60 segundos respectivamente e, posteriormente, condicionamento com ácido fosfórico 37% por 5 segundos. A análise da rugosidade superficial foi feita em microscópio ótico confocal. As pastilhas representativas de cada grupo foram selecionadas e metalizadas para análise da morfologia superficial em microscopia eletrônica de varredura e em microscópio de força atômica. Para a análise de resistência de união ao microcisalhamento, sobre as superfícies devidamente tratadas, foi aplicado o silano RelyX Ceramic Primer® e aguardou-se 1 minuto para que se realizasse a cimentação. Foram cimentados três cilindros em cada pastilha com o cimento resinoso RelyXTM U200, e fotopolimerizados por 60 segundos cada. Os corpos de prova foram armazenados em água deionizada a 37°C por 24 horas (n=30). Terminado esse tempo, os corpos de prova foram submetidos ao teste de microcisalhamento em uma máquina de ensaios universal Emic DL 2000® com velocidade de 1 mm/minuto até que ocorresse a fratura. Os valores médios de ambos os testes foram submetidos à análise estatística ANOVA dois fatores e as médias comparadas pelo teste de Tukey com 5% de significância. Todas as superfícies fraturadas foram levadas ao estereomicroscópio com aumento de 50 vezes para verificar o padrão de falha ocorrido e alguns corpos de prova após a fratura, foram aleatoriamente escolhidos para representar cada tipo de falha, foram metalizados e levados ao microscópio eletrônico de varredura para caracterização da superfície. A maior rugosidade superficial foi obtida pelo grupo G6 (2,05±0,107) sendo superior estatisticamente aos demais. Já a menor rugosidade foi obtida pelo grupo controle G1 (0,567±0,057) e inferior estatisticamente aos demais. Os grupos G7 (1,785±0,037); G3 (1,608±0,03); G10 (1,551±0,046); G9 (1,449±0,047); G5 (1,443±0,06); G4 (1,422±0,103); G8 (1,339±0,036) e G2 (1,283±0,059) apresentaram valores intermediários de rugosidade. Dentre estes grupos, o G3 (22.75±1.97MPa) foi o que apresentou a maior média de resistência da união com falhas do tipo mista. Por outro lado, o G1 (5.25±1.29MPa) apresentou o menor valor médio de resistência da união com predominância de falhas adesivas. Assim, conclui-se que a concentração do ácido e o tempo influenciaram na rugosidade superficial, sendo maior para o
condicionamento com ácido HF a 10%. Para a resistência da união, o tempo de condicionamento e a interação deste com a concentração dos ácidos influenciou de forma significativa; sendo que o ácido HF de menor concentração, 5% por 40 segundos, foi o que apresentou maiores valores. / The objective of this study was to evaluate the effect of different acid treatments, the concentration variation and the time of exposure to hydrofluoric (HF) and phosphoric acids (H3PO4) on the surface roughness and bond strength of a glass-ceramic reinforced by cement lithium disilicate with a self-adhesive resin cement. One hundred tablets of the IPS e.max Press® ceramic measuring 2 x 7 mm were divided into ten groups according to the surface treatment (n = 10): G1, control, or untreated; G2, G3 and G4 etching with 5% hydrofluoric acid for 20, 40 and 60 seconds, respectively; G5, G6 and G7 etching with 10% hydrofluoric acid for 20, 40 and 60 seconds, respectively; G8, G9 and G10 etching with 10% hydrofluoric acid for 20, 40 and 60 seconds respectively, and subsequently etched with phosphoric acid at 37% for 5 seconds. Analysis of surface roughness was performed confocal optical microscope. Representative tablets of each group were selected and metallized for analysis of surface morphology in scanning electron microscopy and atomic force microscope. For the analysis of bond strength to microshear, on properly treated surfaces, the silane RelyX Ceramic Primer® was applied and waited up to 1 minute to the holding of the cementing. Three-cylinder in each tablet were cemented with resin cement RelyXTM U200, and light cured for 60 seconds. The specimens were stored in deionized water at 37C for 24 hours (n = 30). After this time, the specimens were submitted to microshear test in a universal testing machine Emic DL 2000® with speed of 1 mm/min until the fracture. The average values of both tests were submitted to ANOVA two factors and the means compared by Tukey test at 5% significance level. All fractured surfaces were taken to the stereomicroscope with 50X enlargement to verify the pattern of failure occurred and some specimens with significant fractures of each type of failure were metallized and taken to the scanning electron microscope for surface characterization. The increased surface roughness was obtained by the G6 group (2.05 ± 0.107 N) and statistically superior. Already the slightest roughness was obtained by G1 control group (0.567 ± 0.057) and statistically lower to others. The G7 (1.785 ± 0.037); G3 (1.608 ± 0.03); G10 (1.551 ± 0.046); G9 (1.449 ± 0.047); G5 (1.443 ± 0.06); G4 (1.422 ± 0.103); G8 (1.339 ± 0.036) and G2 (1.283 ± 0.059) showed intermediate roughness values. Among these groups, the G3 (22.75 ± 1.97 N) was presented the highest mean bond strength with failures of mixed type. Moreover, G1 (5.25 ± 1.29 N) had the lowest average value of the bond strength with a predominance of adhesive failures. Thus, it is concluded that the acid concentration and time influence the surface roughness, being greater for etching with 10% hydrofluoric acid. For the bond strength, the conditioning time and the interaction of this with the concentration of the acid had a significant influence; being that the hydrofluoric acid of lower concentration, 5% for 40 seconds, showed the highest values.
| Identifer | oai:union.ndltd.org:IBICT/oai:hermes.cpd.ufjf.br:ufjf/2295 |
| Date | 06 May 2015 |
| Creators | Sudré, João Paulo da Silva |
| Contributors | Assis, Neuza Maria Souza Picorelli, Salvio, Luciana Andrea |
| Publisher | Universidade Federal de Juiz de Fora, Programa de Pós-graduação em Clínica Odontológica, UFJF, Brasil, Faculdade de Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFJF, instname:Universidade Federal de Juiz de Fora, instacron:UFJF |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0063 seconds