Return to search

Obtenção de eletrólitos sólidos com composição Ce0,8 Gd0,2O1,9, para aplicações em células a combustível / Obtaining solid electrolyte with composition Ce0,8Gd0,2O1,9 for aplications in fuel cells

Dissertação (mestrado)—Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Mecânica, 2013. / Submitted by Alaíde Gonçalves dos Santos (alaide@unb.br) on 2013-08-15T14:51:42Z
No. of bitstreams: 1
2013_JesusMauricioGonzalesMartinez.pdf: 3449634 bytes, checksum: 289519a6cf57cd42823cdcebd9b91e51 (MD5) / Approved for entry into archive by Guimaraes Jacqueline(jacqueline.guimaraes@bce.unb.br) on 2013-09-02T14:29:38Z (GMT) No. of bitstreams: 1
2013_JesusMauricioGonzalesMartinez.pdf: 3449634 bytes, checksum: 289519a6cf57cd42823cdcebd9b91e51 (MD5) / Made available in DSpace on 2013-09-02T14:29:38Z (GMT). No. of bitstreams: 1
2013_JesusMauricioGonzalesMartinez.pdf: 3449634 bytes, checksum: 289519a6cf57cd42823cdcebd9b91e51 (MD5) / Este trabalho desenvolveu cerâmicas condutoras iônicas de céria dopada
com gadolínia formando o sistema Ce0,8Gd0,2O1,9, visando seu uso como eletrólito em células a combustível de óxido sólido. O pó foi sintetizado pelo método dos
precursores poliméricos (Pechini) a partir de nitratos hexahidratados de cério e
gadolínio, de maneira a obter uma resina, posteriormente caracterizada por análise térmica diferencial/termogravimétrica (ATD/TG) e espectroscopia de
infravermelho (FTIR). Com o objetivo de comparar a influência da temperatura de
calcinação na condutividade iônica nas amostras sinterizadas, esta resina foi
calcinada às temperaturas de 600 e 800 ºC, resultando em óxidos cristalinos nos
quais foi identificada a fase tipo fluorita por meio da difratometria de raios-X
(DRX). Parte do pó calcinado, às diferentes temperaturas, foi submetido à moagem mecânica por moinho de atrição. Finalmente foram obtidos corpos-de-prova por prensagem uniaxial a frio e sinterização a 1500 ºC, estes apresentaram densidades aparentes acima do 90% medidas pelo método de Arquimedes. Realizou-se a avaliação da morfologia através de microscopia eletrônica de varredura (MEV) e caracterização elétrica por meio de espectroscopia de impedância complexa (EIC). A caracterização elétrica mostrou que a maior eliminação do material orgânico obtida nas amostras calcinadas à temperatura de 800ºC, não garantiu um incremento da condutividade de contorno de grão, normalmente menor que a condutividade de grão e associada à presença de impurezas na amostra. Por outro lado, o comportamento elétrico das amostras mostrou-se altamente influenciado pela morfologia final do grão e do contorno de grão, que por sua vez é condicionada por cada um dos processos realizados (sínteses, calcinação, moagem e sinterização). _______________________________________________________________________________________ ABSTRACT / This work developed ion conductive ceramic of gadolinia doped ceria, forming Ce0,8Gd0,2O1,9 system, aiming its use as electrolyte in solid oxide fuel cells. The powder was synthesized by the polymeric precursor method (Pechini) from cerium and gadolinium nitrates hexahydrates, so as to obtain a resin which was characterized by differential thermal analysis/thermogravimetry (DTA / TG), and infrared spectroscopy (IR). Aiming to compare the calcination’s temperature influence on ionic conductivity in sintered samples, this resin was calcined at 600 and 800°C, resulting in crystalline oxides in which a fluorite phase type was identified by X-ray diffraction (XRD). Part of the calcined powder at different temperatures, was subjected to mechanical milling by attrition mill. Finally, test samples were obtained by uniaxially cold pressed and sinterization at 1500°C, with bulk densities above 90% measured by Archimedes method. Morphology evaluation was performed by scanning electron microscopy (SEM) and electrical characterization obtained by complex impedance spectroscopy (CIS). Electrical characterization showed that the major elimination of material organic in calcined samples at 800°C, did not guarantee an increase in grain boundary conductivity, usually lower than grain conductivity and associated with impurities presence in the sample. On the other hand, samples electrical behavior were strongly influenced by the morphology of the final grain and grain boundary, which in turn is conditioned by each one of the processes performed (synthesis, calcination, milling and sintering).

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/14069
Date21 June 2013
CreatorsGonzález Martínez, Jesús Mauricio
ContributorsSilva, Cosme Roberto Moreira da
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB
RightsA concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data., info:eu-repo/semantics/openAccess

Page generated in 0.0022 seconds