Zinc xanthates are active catalysts in stereoregular polymerization of propylene oxide and markedly more stable than that of known classical stereoregular catalysts. But steric control of zinc xanthates is weaker. To find more effective catalyst systems the isopropyl xanthates of Cu, Pb, Ni, Fe, Al and Sn are investigated and only copper (Cu(isoPr)Xt) and tin (Sn(isoPr)Xt) isopropyl xanthates were appeared to be active, but Cu(isoPr)Xt yielded only low molecular weight product. Therefore Sn(isoPr)Xt system was investigated in detail in polymerization of propylene oxide (PO). Polymerization of PO with this catalyst produced two contrasting polymers / high molar mass, crystalline (K-polymer) and low molar mass (D-polymer). Formation of double bonds in D-polymer was thought to be due to as an anionic
process. Polymerization reactions were studied by changing polymerization conditions and reacting catalyst with predetermined amount of water. It& / #8217 / s found that Sn(isoPr)Xt have considerably low efficiency than that of Zn(isoPr)Xt catalyst. The yield linearly increases by increasing catalyst concentration. The propagation is competed by termination or transfer process hence overall activation energy is negative. Some mechanistic features of this system was also discussed.
The catalytical activity of carbamates in this field has also been reported, without any information about catalytical efficiency and stereoregularity of the process. Therefore zinc diethyl dithiocarbamate was also studied and found as an active catalyst in stereoregular polymerization but it showed weaker efficiency in the PO polymerization than that of Zn(isoPr)Xt catalyst (about 12 times weaker).
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/1225028/index.pdf |
| Date | 01 September 2003 |
| Creators | Tas, Huseyin |
| Contributors | Alyuruk, Kemal |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | M.S. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for public access |
Page generated in 0.0015 seconds