Polybutadiene, the homopolymer of 1,3-butadiene, is a synthetic rubber especially important in the production of tires. Industrially, it is polymerized using multi-site catalysts that do not offer significant control over molecular weight distribution resulting in polymers with poor mechanical properties. Single-site polymerization of 1,3-butadiene results in narrow molecular weight distribution and thus increased impact resistance and durability. Complexes of chromium and neodymium bearing bis-phosphinimine pincer ligands have been synthesized and studied for their behavior in 1,3-butadiene polymerization in combination with methylaluminoxane. The complexes that were active produced highly cis-1,4-polybutadiene with high molecular weight and narrow polydispersities. The co-polymerization of acrylonitrile and 1,3-butadiene with the bis-phosphinimine chromium (III) complexes and methylaluminoxane to produce nitrile-butadiene rubber was also explored. The insertion of 1,3-butadiene into nickel-methyl and nickel-hydride complexes bearing the bis-phosphinimine pincer ligands was examined using nuclear magnetic resonance spectroscopy and will also be discussed.
Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:OTU.1807/31406 |
Date | 19 December 2011 |
Creators | Resanovic, Sanja |
Contributors | Stephan, Douglas |
Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
Language | en_ca |
Detected Language | English |
Type | Thesis |
Page generated in 0.3552 seconds