Partial discharge testing is a nondestructive method of identifying possible premature insulation breakdown. Magnet wires are used in various electrical equipment like injection coils, solenoids, small transformers and motors. Winding wires used in high voltage systems are subjected to several stresses during operation, which considerably lowers their lifetime. A prolonged combined effect of these stresses causes aging of the wires, inception of partial discharge activity, and degradation of the organic material in the enamel coating and varnish used by the manufacturer. The tests were conducted for AWG 30 and AWG 31 twisted magnet wire samples. The samples are aged under accelerated conditions of high frequency, temperature, and pulsed voltages. As well as conventional sinusoidal voltages. This thesis is focused on the results of voltage, frequency, and temperature stresses on the magnet wires. The partial discharge inception voltage (PDIV) and breakdown voltages are measured for different twisted wire samples. A software tool is utilized to study these partial discharge patterns. Evaluation of the parameters charge intensity, pulse count, and pulse phase position are presented in 2- and 3-dimensional plots.
Identifer | oai:union.ndltd.org:MSSTATE/oai:scholarsjunction.msstate.edu:td-5129 |
Date | 10 December 2005 |
Creators | Mani, Ashwini |
Publisher | Scholars Junction |
Source Sets | Mississippi State University |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | Theses and Dissertations |
Page generated in 0.0023 seconds