Preparation, structural analysis, and electrochemical performance of a new cathodic battery material, consisting of a nanocomposite of poly(vinylferrocene) (PVFc) (Eox: 0.4 V vs. Ag/AgCl) and reduced graphene oxide (rGO), are described. The nanocomposite shows the highest charge-discharge efficiency (at a rate of 100 A g-1) ever reported for any organic / organomatellic battery material. Remarkably, the composite is “thickness scalable” up to 0.21 mAh cm-2 (770 mC cm−2 at 29 μm film thickness) on a flat surface with > 99% coloumbic efficiency, exhibiting a specific capacity density of 114 mAh g−1. The composite material is binder free and the charge storing material (PVFc) accounts for > 88% of the total weight of the cathodic material. The secret behind such a performance is the electrostatic interaction between the redox polymer in its oxidized state (exhibiting positive charge) and the original filler i.e., graphene oxide (GO) with negative surface charge. This self-assembling step is analyzed by zeta potential measurements, and a modeling study confirms the experimentally found heavy polymer loading on the GO (in aqueous solution). The efficient self-assembly led to composites with high ratio of redox polymer / GO where all polymers are in close contact with GO sheets. The stable colloidal solution was casted on the surface of a flat current collector and the insulating GO was electrochemically transformed to conductive reduced graphene oxide (rGO). The GO / rGO transformation was catalyzed by methyl viologen dichloride (MV++) working as a redox shuttle (solublized in the aqueous electrolyte) and thereby accelerating the electron transfer to GO. Complete GO / rGO transformation and the quantitative ion breathing of the composite are found by means of electrochemical quartz crystal microbalance and electrochemical AFM.
| Identifer | oai:union.ndltd.org:uni-osnabrueck.de/oai:repositorium.ub.uni-osnabrueck.de:urn:nbn:de:gbv:700-2017012715280 |
| Date | 27 January 2017 |
| Creators | Beladi Mousavi, Seyyed Mohsen |
| Contributors | Prof. Dr. Lorenz Walder, Prof. Dr. Martin Steinhart |
| Source Sets | Universität Osnabrück |
| Language | English |
| Detected Language | English |
| Type | doc-type:doctoralThesis |
| Format | application/zip, application/pdf |
| Rights | Namensnennung 3.0 Unported, http://creativecommons.org/licenses/by/3.0/ |
Page generated in 0.0018 seconds