An experimental methodology for wear assessment of extracted polyethylene hip implants was designed in this diploma thesis. Methodology uses optical 3D scanner and optical profilometer for analysis of wear. Designed methodology for wear analysis was validated by gravimetric method. The results of validation were in good agreement with the increase of wear rate. Validation results show that the methodology is not suited for wear assessment of metal and ceramic implants which have small wear rates. On the other hand the methodology is more than useful for wear assessment of polyethylene implants. Designed methodology for wear assessment was applied on the set of thirteen extracted polyethylene hip implants. Results of the wear analysis were wear volumes and linear wear noted in the wear maps. Roughness of the surface was measured on explanted cups and results were noted in the roughness map. On articulating surface of the cups different areas were observed for measured roughness. Those areas were described as area with machining marks from manufacturing process, polished area from combination of abrasive and adhesive wear, polished area from micro-contact fatigue and area including plastic deformation.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:241862 |
| Date | January 2016 |
| Creators | Přikryl, Adam |
| Contributors | Morovič, Ladislav, Vrbka, Martin |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0025 seconds